ASTM D2835-1989(2007) Standard Specification for Lubricant for Installation of Preformed Compression Seals in Concrete Pavements《混凝土铺面用预制压缩密封物安装用润滑剂的标准规范》.pdf

1、Designation: D 2835 89 (Reapproved 2007)Standard Specification forLubricant for Installation of Preformed Compression Sealsin Concrete Pavements1This standard is issued under the fixed designation D 2835; the number immediately following the designation indicates the year oforiginal adoption or, in

2、the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope*1.1 T

3、his specification covers a lubricant suitable for facili-tating the insertion and positioning of preformed elastomericcompression seals in prepared voids (usually contractionjoints) in concrete pavement.1.2 The requirements of the lubricant are based on theperformance of the lubricant as measured by

4、 its solids content,homogeneity, consistency and drying rate.1.3 The values stated in inch-pound units are to be regardedas the standard. The metric equivalents of U.S. customary unitsmay be approximate.1.4 The following precautionary caveat pertains only to thetest method portion, Section 7 of this

5、 specification. Thisstandard does not purport to address all of the safety concerns,if any, associated with its use. It is the responsibility of the userof this standard to establish appropriate safety and healthpractices and determine the applicability of regulatory limita-tions prior to use.2. Ref

6、erenced Documents2.1 ASTM Standards:2D 1084 Test Methods for Viscosity of AdhesivesD 1644 Test Methods for Nonvolatile Content of Varnishes3. Classification3.1 The lubricant shall be based on polychloroprene, con-taining only soluble phenolic resins blended together withantioxidants and acid accepto

7、rs in a suitable mixture of organicsolvents.4. Requirements4.1 HomogeneityThe lubricant shall be uniform and con-tain no lumps or agglomerates.4.2 Solids ContentThe nonvolatile content of the lubri-cant shall be no less than 24.0 weight %.4.3 ConsistencyThe lubricant shall exhibit a viscosity inone

8、of the following ranges:4.3.1 Type Ifor hand or machine application, 3000 to8000 cP.4.3.2 Type IIfor machine application, 8000 to 15 000 cP.4.4 Drying RateA bond between lubricant-coated papersprepared after 8-min drying time shall separate completely inless than 10 s when a 50-g load is applied in

9、shear. A similarbond prepared after 20-min drying time shall remain unsepa-rated for a minimum of 10 s when a 50-g load is applied inshear.5. Basis of Purchase5.1 Each lot of lubricant shall be accompanied by themanufacturers certified test results attesting compliance withthis specification, unless

10、 an alternative agreement is concludedby the manufacturer and the purchaser.6. Sampling6.1 The lubricant samples shall be a 1-quart (1-litre) aliquotconsisting of a composite taken when possible from three ormore separate containers chosen at random. Samples also shallbe taken from containers which

11、appear to be nonrepresentativeand shall be tested separately. Before a sample is withdrawn,the contents in the container shall be mixed to uniformconsistency. The sample shall be placed immediately in anairtight-glass jar or metal can until tested.7. Test Methods7.1 HomogeneityStir the test sample b

12、y hand for 2 minwith a spatula. Withdraw the spatula and examine the lubricantas it flows from the spatula for lumps or agglomerates.Particles smaller in diameter than 0.015 in. (0.38 mm) shall notbe considered cause for rejection.1This specification is under the jurisdiction of ASTM Committee D04 o

13、n Roadand Paving Materials and is the direct responsibility of Subcommittee D04.34 onPreformed Joint Fillers, Sealers and Sealing Systems.Current edition approved Dec. 1, 2007. Published January 2008. Originallyapproved in 1969. Last previous edition approved in 2003 as D 2835 89 (2003).2For referen

14、ced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1*A Summary of Changes section appears at the end of this standard.Copyri

15、ght ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.Copyright by ASTM Intl (all rights reserved); Sun Sep 28 03:10:13 EDT 2008Downloaded/printed byGuo Dehua (CNIS) pursuant to License Agreement. No further reproductions authorized.NOTE 1At the

16、consumers request, compliance with the 0.015-in.(0.38-mm) requirement shall be determined by a sample diluted 1+4 withXylene through a 40-mesh sieve.7.2 Solids ContentDetermine in accordance with MethodA of Test Methods D 1644.7.3 ConsistencyDetermine in accordance with Method Bof Test Methods D 108

17、4. Use a No. 4 spindle at 20 rpm at a testtemperature of 77 6 0.9F (25 6 0.5C).7.4 Drying Rate:7.4.1 Apparatus:7.4.1.1 Film Applicator,32-in. (50-mm) wide, 5 to 25-mils(0.127 to 0.635-mm) clearance set at 14 mils (0.356 mm).7.4.1.2 Nonabsorbent Stiff Paper Surface,4312 by 6-in. (100by 150-mm).7.4.1.

18、3 Brush-Out Panels.47.4.1.4 Stop Watch.7.4.1.5 Wire.7.4.1.6 Weights, 50-g, and 500-g.7.4.1.7 Aluminum Plate,18 by 1 by 2-in. (3 by 25 by50-mm).7.4.2 Procedure:7.4.2.1 Condition the lubricant for at least3hat73.4 63.6F (23 6 2C). Apply a series of 2 in. wide (wet thickness)(14 6 2.5-mils) 0.356 6 0.0

19、64-mm films of the lubricant tofour separate nonabsorbent paper surfaces. A film applicator asspecified in 7.4.1.1 has been found to produce a wet film in thespecified range with this class of materials, but the depositedfilm thickness from any specific spreader and lubricant systemshould be checked

20、 to determine the conformance to thespecified thickness. Films should be at least 4 in. (100 mm)long, centered on the paper and parallel to the long axis of thesheet. Allow to dry in a horizontal position in a draft-free area.The time upon completion of the casting of the second film ofeach pair cas

21、t is recorded as the initial drying time for that pairof films.7.4.2.2 After several minutes drying, cut off at least 112 in.(40 mm) from the bottom of the cast films and discard. Afterdrying 8 min overlap the cut edges of the first pair 1 in. andplace face-to-face to form a 1 by 2-in. area lap shea

22、r bond.Take care to align the two films so that a force applied alongtheir center lines will impose a direct shear force without atwisting movement. Form the bond by placing the overlappedpapers on a horizontal smooth surface, placing a18-in. thick, 1by 2-in. aluminum plate over the bond area, and p

23、lacing a 500g laboratory weight on this plate for 10 s. Hang the bondedpieces immediately in a vertical position and attach a 50-gweight with a small loop of wire, weighing less than 1 g, to thelower piece of paperboard forming the bond.Align the point ofsupport and the point of attachment for the w

24、eight on the centerlines of the cast films.7.4.2.3 Record the time needed for the 50-g load to com-pletely separate the bonded pieces with the aid of a stop watch.If separation is not complete in 1 min, discontinue the test andrecord the separation time as more than 1 min.7.4.2.4 Repeat the above pr

25、ocedure with a pair of cast filmswhich are allowed to dry for 20 min before forming a bond.7.4.2.5 Testing should be conducted at 73.4 6 3.6F (23 61C) and at a relative humidity of 50 6 5%.8. Precision and Bias8.1 No statement is made about either the precision or biasof this specification for measu

26、ring Homogeneity and DryingRate, since the result merely states whether there is conform-ance to the criteria for success specified in the procedure.9. Packaging and Package Marking9.1 PackagingThe material shall be packaged in standardcommercial containers, so constructed as to ensure acceptanceby

27、common or other carrier for safe transportation at the lowestrate to the point of delivery, unless otherwise specified in thecontract or order.9.2 MarkingShipping containers shall be marked with thefollowing information:9.2.1 Manufacturers name or trademark, product code, andbatch or lot number,9.2.

28、2 Date of manufacture and recommended time limit ofstorage before use,9.2.3 Weight per gallon of lubricant to the nearest110 lb(0.05 kg)/gal,9.2.4 Special handling instructions during product transfer,and9.2.5 Special precautions required because of product tox-icity, flammability, or other such inf

29、ormation pertinent to theproper storage and use of the product.3The sole source of supply of the apparatus known to the committee at this timeis the Gardner Ultra Applicator, available from Gardner Laboratories, Inc., P.O. Box5728, Bethesda, MD, Catalog No. Ag 3816J. If you are aware of alternatives

30、uppliers, please provide this information to ASTM International Headquarters.Your comments will receive careful consideration at a meeting of the responsibletechnical committee,1which you may attend.4The sole source of supply of the apparatus known to the committee at this timeis the Morest Co., Inc

31、., 211 Center St., New York, NY 10013. If you are aware ofalternative suppliers, please provide this information to ASTM InternationalHeadquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee,1which you may attend.D 2835 89 (2007)2Copyright by

32、ASTM Intl (all rights reserved); Sun Sep 28 03:10:13 EDT 2008Downloaded/printed byGuo Dehua (CNIS) pursuant to License Agreement. No further reproductions authorized.SUMMARY OF CHANGESCommittee D04 has identified the location of selected changes to this standard since the last issue(D 2835 98 (1998)

33、 that may impact the use of this standard.(1) Section 1.2 was revised to delete “resistance to aging”.(2) Section 1.3 was added and the following section renum-bered.(3) The 10-g weight was deleted from 7.4.1.6.(4) The temperature range was broadened in 7.4.2.1 and7.4.2.5.(5) The 4th sentence in Sec

34、tion 7.4.2.2 was revised to correctan omission in the previous published issues.(6) Section 8 on Precision and Bias was added.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are e

35、xpressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not rev

36、ised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you m

37、ay attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United St

38、ates. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).D 2835 89 (2007)3Copyright by ASTM Intl (all rights reserved); Sun Sep 28 03:10:13 EDT 2008Downloaded/printed byGuo Dehua (CNIS) pursuant to License Agreement. No further reproductions authorized.