ASTM D3163-2001(2014) Standard Test Method for Determining Strength of Adhesively Bonded Rigid Plastic Lap-Shear Joints in Shear by Tension Loading《用抗拉荷载法在剪切胶粘剂粘接刚性塑料搭接接头的抗剪切强度的标准试.pdf

1、Designation: D3163 01 (Reapproved 2014)Standard Test Method forDetermining Strength of Adhesively Bonded Rigid PlasticLap-Shear Joints in Shear by Tension Loading1This standard is issued under the fixed designation D3163; the number immediately following the designation indicates the year oforiginal

2、 adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This test method is intended to complement Test MethodD1002 and ext

3、end its application to single-lap shear adhesivejoints of rigid plastic adherends. The test method is useful forgenerating comparative shear strength data for joints madefrom a number of plastics. It can also provide a means bywhich several plastic surface treatments can be compared.1.2 The values s

4、tated in SI units are to be regarded as thestandard. The values in parentheses are for information only.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and

5、health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2D907 Terminology of AdhesivesD1002 Test Method for Apparent Shear Strength of Single-Lap-Joint Adhesively Bonded Metal Specimens by Ten-sion Loading (Metal-to-Metal)D20

6、93 Practice for Preparation of Surfaces of Plastics Priorto Adhesive BondingD4896 Guide for Use of Adhesive-Bonded Single Lap-JointSpecimen Test Results3. Terminology3.1 DefinitionsMany of the terms used in this test methodare defined in Terminology D907.4. Significance and Use4.1 Due to the increas

7、ed use of adhesive-bonded plastics asa result of the inherent advantages afforded by bonded ratherthan mechanically fastened joints, particularly the alleviationof stress raisers and stress cracking, there is a need for standardtests by which joints of various plastic substrates and adhesivescan be

8、compared. This test method is intended to meet such aneed.4.2 This test method is limited to test temperatures belowthe softening point of the subject adherends, and is notintended for use on anisotropic adherends such as reinforcedplastic laminates.4.3 The misuse of strength values obtained from th

9、is testmethod as allowable design-stress values for structural jointscould lead to product failure, property damage, and humaninjury. The apparent shear strength of an adhesive obtainedfrom a given small single-lap specimen may differ from thatobtained from a joint made with different adherends or b

10、y adifferent bonding process. The normal variation of temperatureand moisture in the service environment causes the adherendsand the adhesive to swell and shrink. The adherends andadhesive are likely to have different thermal and moisturecoefficients of expansion. Even in small specimens, short-term

11、environmental changes can induce internal stresses or chemicalchanges in the adhesive that permanently affect the apparentstrength and other mechanical properties of the adhesive. Theproblem of predicting joint behavior in a changing environ-ment is even more difficult if a different type of adheren

12、d isused in a larger structural joint than was used in the smallspecimen.4.3.1 The apparent shear strength measured with a single-lap specimen is not suitable for determining allowable designstresses for designing structural joints that differ in any mannerfrom the joints tested without thorough ana

13、lysis and under-standing of the joint and adhesive behaviors.4.3.2 Single-lap tests may be used for comparing andselecting adhesives or bonding processes for susceptibility tofatigue and environmental changes, but such comparisons mustbe made with great caution since different adhesives may1This tes

14、t method is under the jurisdiction of ASTM Committee D14 onAdhesives and is the direct responsibility of Subcommittee D14.40 on Adhesives forPlastics.Current edition approved March 1, 2014. Published March 2014. Originallyapproved in 1973. Last previous edition approved in 2008 as D3163 01 (2008).DO

15、I: 10.1520/D3163-01R14.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr

16、 Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1respond differently in different joints. See Guide D4896 forfurther discussion of the concepts relative to interpretation ofadhesive bonded single-lap joints.5. Apparatus5.1 Testing Machine, conforming to the requirements of

17、 andhaving the capabilities of the machine prescribed in TestMethod D1002. The grips are self-aligning and capable ofsecurely grasping the specimen throughout the test, withoutallowing the specimen to slip.5.2 Temperature-Controlling Equipment, capable of main-taining the test temperature to 63C (65

18、F). If ambientlaboratory conditions are employed the same degree of controlis required.6. Test Specimen6.1 Make specimens that conform to the form and dimen-sions set forth in Test Method D1002 where possible. However,due to the low yield points in plastics compared with those ofmetals, it may not a

19、lways be feasible to limit test specimengeometry to that called for in Test Method D1002. Thereforeadherend thicknesses and joint overlaps must be chosen so thatfailure occurs preferentially in the joint and not in the substrate.Thicker adherends allow the stress on the bonded area to beincreased, b

20、efore either tensile failure or yield occurs in theadherend. Recognize, however, that depending on the surfacetreatment and adhesive used, the bond strength may often begreater than the tensile yield strength of the adherend. Use datacollected by this test method only for comparative purposeswhen th

21、e investigator is certain that the specimen configura-tions and joint geometries of the specimens being compared areidentical.6.2 The surface preparation used on the adherend dependson the subject plastic adherend. Procedures such as thoserecommended in Practice D2093 serve as a useful guide.6.3 App

22、ly the adhesives in accordance with the manufac-turers recommendations. Choose adhesives such that the curetemperature does not adversely affect the mechanical proper-ties of the adherends.6.4 Cut test specimens from the bonded panels pictured inFig. 1. Cut the specimens without overheating or other

23、wisephysically damaging the adherend or bonded interface. Indi-vidual specimens may also be prepared if desired.7. Procedure7.1 Place the specimens in the grips of the testing machineso that the applied load coincides with the long axis of the testspecimen. Load the specimen to failure at a rate of

24、8.3 to 9.7MPa (1200 to 1400 psi) of shear area per minute (approxi-mately 0.05 in./min cross head speed).FIG. 1 Standard Test Panel and Specimen ConfigurationD3163 01 (2014)27.2 Condition specimens for definite periods of time underspecified conditions before testing if desired. Afterconditioning, i

25、t is recommended that all specimens be stabi-lized in the test environment for 1 h before testing.8. Calculation8.1 Calculate the bond area to the nearest 0.06/cm2(0.01in.2). Record both load at failure and type of failure (percentcohesive and apparent adhesive). Calculate failing stress asmegapasca

26、ls (pounds force per square inch) of shear area.9. Report9.1 Report the following information:9.1.1 Complete identification of the adhesive tested, includ-ing type, source, date manufactured, manufacturers codenumber, form, etc.9.1.2 Complete identification of the plastic used, itsthickness, and the

27、 method of cleaning and preparing its surfaceprior to bonding.9.1.3 Method of adhesive application (brush, spray, rollercoat, tape, etc.).9.1.4 Conditions present at time of bonding (temperature,etc.).9.1.5 Length of overlap used.9.1.6 Conditioning of joint prior to testing.9.1.7 Maximum, minimum, a

28、nd average values of the fail-ing load.9.1.8 Number of test specimens tested.9.1.9 Type of failure. Include estimated percent cohesionfailure, unbonded area, apparent failure in adhesion, and failurein the adherend.9.1.10 Test temperature employed.9.1.11 Average thickness of adhesive layer after for

29、mationof the joint, within 0.0127 mm (0.0005 in.). Describe themethod of obtaining the thickness of the adhesive layerincluding procedure, location of measurements, and range ofmeasurements.NOTE 1The length of overlap, L, may be varied where necessary. Thelength of the test specimen in the jaws, how

30、ever, must not be varied. Thedistance from the end of the overlap to the end of the jaws should be 63mm (212 in.) in all tests.NOTE 2The thickness of the adherend, t, may be varied to strengthenthe adherend relative to the strength of the bonded area. A maximumthickness of 4.76 mm (316 in.) is recom

31、mended, however, to minimize theeffects of offset.10. Precision and Bias10.1 The precision and bias statement for this test methodhas not yet been determined. Archival and round-robin infor-mation is being reviewed, and the results are expected bySeptember 2004.11. Keywords11.1 adhesive bonds; plast

32、ic; shear strength; tensionASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infri

33、ngement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standar

34、d or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your view

35、s known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).D3163 01 (2014)3