ASTM D3955-2004 Standard Specification for Electrical Insulating Varnishes《电绝缘清漆标准规范》.pdf

1、Designation: D 3955 04An American National StandardStandard Specification forElectrical Insulating Varnishes1This standard is issued under the fixed designation D 3955; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of la

2、st revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers the tests and values for elec-trical insulating varnishes, as supplied, which are suitable fo

3、rthe impregnation and treatment of electrical coils and windingsapplied by dip process.1.2 Varnishes, flexible or rigid, included in this specificationare:Grade DAAir-dryGrade DOOrganic solvent containing, baking,Grade DMReactive diluent containing,Grade DSSilicone,Grade DWWater containing, andGrade

4、 DTThixotropic.1.3 The values stated in inch-pound units are to be regardedas the standard. The values given in parentheses are forinformation only.NOTE 1This specification resembles IEC 60455 in title only. Thecontent is significantly different.2. Referenced Documents2.1 ASTM Standards:2D 93 Test M

5、ethods for Flash-Point by Pensky-MartensClosed Cup TesterD 115 Test Methods for Testing Solvent Containing Var-nishes Used for Electrical InsulationD 1711 Terminology Relating to Electrical InsulationD 2519 Test Method for Bond Strength of ElectricalInsulating Varnishes by the Helical Coil TestD 305

6、6 Test Method for Gel Time of Solventless VarnishesD 3145 Test Method for Thermal Endurance of ElectricalInsulating Varnishes by the Helical Coil MethodD 3251 Test Method for Thermal Endurance Characteristicsof Electrical Insulating Varnishes Applied over Film-Insulated Magnet WireD 3278 Test Method

7、s for Flash Point of Liquids by SmallScale Closed-Cup ApparatusD 4733 Test Methods for Solventless Electrical InsulatingVarnishesD 4880 Test Method for Salt Water Proofness of InsulatingVarnishes Over Enamelled Magnet WireD 5637 Test Method for Moisture Resistance of ElectricalInsulating VarnishesD

8、5638 Test Method for Chemical Resistance of ElectricalInsulation Varnishes2.2 Military Specifications:3MIL-PRF-17672 Hydraulic Fluid, Petroleum, InhibitedMIL-PRF-17331 Lubricating Oil, Synthetic Base P-D-680,Dry Cleaning SolventMIL-D-16791 Detergent, General Purpose, (Liquid, Non-Ionic)2.3 Other Sta

9、ndards:3NEMA MW1000 Magnet WireIEC 60455 Resin Based Reactive Compounds Used forElectrical Insulation3. Terminology3.1 DefinitionsFor definitions of terms used in this speci-fication refer to Terminology D 1711.4. Flexible or Rigid Classification4.1 This specification covers both flexible and rigid,

10、 solvent(including water) and solventless insulating varnishes.5. Thermal Classification5.1 The thermal classification of insulating varnishes cov-ered by this specification is determined by using Test MethodsD 3145 and D 3251 in conjunction with 18 AWG magnet wireconforming to MW 35-C and MW 16-C i

11、n accordance withNEMA MW1000. Determine the temperature index at 20 000h.1This specification is under the jurisdiction of ASTM Committee D09 onElectrical and Electronic Insulating Materials and is the direct responsibility ofSubcommittee D09.01 on Electrical Insulating Varnishes, Powders, and Encaps

12、u-lating Compounds.Current edition approved March 1, 2004. Published March 2004. Originallyapproved in 1980. Last previous edition approved in 1999 as D 395599.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of

13、 ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Available from Global Engineering Documents, 15 Inverness Way, EastEnglewood, CO 80112.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United State

14、s.5.2 The thermal class is determined from the temperatureindex range as follows:Thermal Class Temperature Index Range130 130.0 to 154.9155 155.0 to 179.9180 180.0 to 199.9200 200.0 to 219.9220 220.0 and above6. General Specifications and Qualification Requirements6.1 All varnishes supplied under th

15、is specification mustconform to the limits outlined in Table 1, and must meet, orexceed, all specification requirements.6.2 A varnish supplied under this specification is to bemanufactured from one specific formula and one specificprocess at one or more plants of the same company.6.3 Changes involve

16、d solely with percent nonvolatile con-tent or compatible solvent system, do not require requalifica-tion, if agreed upon between supplier and user.6.4 If any formula or process changes are desired afterqualification approval has been granted, conduct the tests inTable 1, except for thermal class.6.5

17、 If varnishes from different suppliers are to be mixed orused in a common tank or container, determine their compat-ibility by Test Methods D 115. They must be compatible, bothin the liquid and solid state, with the varnish currently beingused in the system.6.6 Varnishes containing silicone in any p

18、ortion, must notbe mixed with non-silicone varnishes.6.7 The qualification requirements of the varnish shall be asmutually agreed upon between supplier and user, with tests tobe performed in accordance with the appropriate methods, andlimits as shown in Table 1.6.8 Preconditioning: Grade DA Varnishe

19、s OnlyPrecondition all Grade DA varnish specimens, both flexibleand rigid, in air at room temperature for seven days prior tocarrying out dielectric strength and bond strength tests shownin Table 1.7. Hazards7.1 It is unsafe to use varnish at temperatures above theflash point without adequate ventil

20、ation, especially if thepossibility exists that flames or sparks are present. Storevarnish in sealed containers.8. Sampling8.1 Obtain varnish samples and appropriate thinner eitherfrom the manufacturer or directly from shipping containerssupplied from the manufacturer. Suitable samples may also beob

21、tained from material in process. It is important that new, orthoroughly cleaned sampling containers be used. The samplemay be obtained by any of a number of procedures commonlyused in the industry. Normally, the sample is simply pouredfrom the shipping container. The sample container should havea ti

22、ght fitting cover to minimize the loss of solvents. A dippingladle may be used, or, if it is desirable to obtain a sample fromvarious levels, use appropriate sampling techniques.8.2 The quantity of sample is that required as indicated in9.1.9. Quality Conformance Tests9.1 General RequirementsFrom ea

23、ch batch of varnish,take a 2-qt (2-L) sample and test. The values must meet thelimits listed for specification requirements shown in Table 1, oras agreed upon between supplier and user.9.2 Inspection and Preparation for DeliverySelectsamples and inspect to verify conformance with the require-ments i

24、n Section 6.10. Keywords10.1 varnish, air-dry; varnish, electrical; varnish, silicone;varnish, solvent containing; varnish, thixotropic; varnish, watercontainingD3955042TABLE 1 Specification RequirementsGradeASTMTest MethodMinimum Thermal ClassClassType of MagnetWire Overwhich Varnish isAppliedDA DO

25、 DM DS DW DT130 MW 35-C andMW 16-CD 3251 andD 3145Class 130 for both wire types and both test methods155 MW 35-C andMW 16-CD 3251 andD 3145Class 155 for both wire types and both test methods180 MW 35-C andMW 16-CD 3251 andD 3145Class 180 for both wire types and both test methods200 MW 35-C andMW 16-

26、CD 3251 andD 3145Class 200 for both wire types and both test methods220 MW 35-C andMW 16-CD 3251 andD 3145Class 220 for both wire types and both test methodsDielectric strength, V/mil, min, onmetal panelsD 115/D 4733Conditioned 24 h at 23Cand 50 % RH1500 2000 1500 1800 2000 1500Conditioned 24 h at 2

27、3Cand 96 % RH975 1500 1125 1350 1500 1125Conditioned 24 h at 23Cin deionized water900 1500 1125 1350 1500 1125Bond strength (minimum pounds)over 18 AWGMW 16-C or MW 35-CD 2519Flexible at 77F/300F (25C/150C)5/0 10/1 10/1 6/0.5 20/1 15/2Rigid at 77F/300F (25C/150C) NAA20/3 25/4 NA 25/3 30/5Salt water

28、proofness D 4880over MW 35-C or MW 16-C 100B100B100B100B100B100BMoisture resistance D 5637percent retained, min 50 50 50 50 50 50Chemical resistance D 5638minimum percent retained after 168 h at 73F (23C)Hydraulic fluidC50 50 50 50 50 50Lubricating oilD50 50 50 50 50 50Cleaning fluidE50 50 50 50 50

29、50Distilled water 50 50 50 50 50 50Detergent solutionF50 50 50 50 50 50Storage life, months minG12126666Viscosity (cps at 77F (25C) D 115/D 4733 801200 1001200 1001300 80240 1001300 15 000H5000IThixotropic index, min D 4733 NA NA NA NA NA 1.1% Nonvolatile matter, min D 115 30 40 NA 40 35 NAVariation

30、 in specific gravity/density (%of reported value)D 115/D 4733 61.0 61.0 61.0 61.0 61.0 61.0Build as received (mils, min) D 115/D 4733 0.9 0.9 0.3 0.5 0.8 1.1Flash point (F (C), min) D 93/D 3278 73 (23)J73 (23)J200 (93)J73 (23)J194 (90)J200 (93)JDrying time (h at F (C) max D 115 3 at230 (110)2at300 (

31、150)NA 6 at390 (200)2at300 (150)NAVariation in gel time (% of reportedvalue)D 3056 NA NA 610.0 NA NA 610.0ANot applicable.BPassing is defined as 7 of 9 specimens still passing at specified time.CIn accordance with MIL-PRF-17672.DIn accordance with MIL-PRF-17331.EIn accordance with P-D-6801,1,2-trich

32、loro 1,2,2-trifluoroethane.FDetergent per MIL-D-16791, non-ionic detergent (1 lb per 214 gal water).GAs warranted by the manufacturer.HMaximum at 2 r/min.IMaximum at 20 r/min.JOr as agreed to by supplier and user.D3955043ASTM International takes no position respecting the validity of any patent righ

33、ts asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any

34、time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments wil

35、l receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by AST

36、M International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).D3955044