ASTM D4295-1989(2017) Standard Classification for Rubber Compounding Materials&x2014 Zinc Oxide《橡胶配合材料的标准分类&x2014 氧化锌》.pdf

1、Designation: D4295 89 (Reapproved 2017)Standard Classification forRubber Compounding MaterialsZinc Oxide1This standard is issued under the fixed designation D4295; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last re

2、vision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This classification system covers the compounding ma-terial commercially known as zinc oxide. The types of zincoxide used in

3、the rubber industry are related to the productionprocess used. Typical chemical and physical properties areincluded.2. Referenced Documents2.1 ASTM Standards:2D280 Test Methods for Hygroscopic Moisture (and OtherMatter Volatile Under the Test Conditions) in PigmentsD3037 Test Method for Carbon Black

4、Surface Area byNitrogen Adsorption (Withdrawn 1999)3D3280 Test Methods for Analysis of White Zinc PigmentsD4075 Test Methods for Rubber Compounding MaterialsFlame Atomic Absorption AnalysisDetermination ofMetalsD4315 Test Methods for Rubber Compounding MaterialZinc Oxide3. Significance and Use3.1 Zi

5、nc oxide is an important rubber compounding mate-rial. It is used to activate the organic accelerators to increasethe rate of vulcanization and to enhance physical properties. Itis also a vulcanizing agent for halogen-containing elastomers.4. Classification of Zinc Oxides by Types4.1 American Proces

6、s or Direct TypeWhen zinc oxide ismanufactured by the reduction and reoxidation of a zinc-bearing material, such as a zinc ore by a carbonaceous fuel, itis called American process or direct type. American processzinc oxide is produced with widely varying chemical propertiesand physical characteristi

7、cs. Nodular-type particle shape, asobserved by the light microscope, is generally preferred forrubber compounding. Due to wide variations in the materialprocessed and in the process itself, the properties of Americanprocess zinc oxide can only be characterized in a general way.4.2 French Process or

8、Indirect TypeWhen zinc oxide ismanufactured by the burning of zinc vapor (produced byboiling zinc metal in a retort or zinc boiler), it is called Frenchprocess or indirect type. It is characterized by a high degree ofchemical purity resulting from the use of high purity (99.9%zinc). As generally pro

9、duced, the particles are nodular in shapeas observed by the light microscope.4.3 Secondary Zinc Oxide Type:4.3.1 ChemicalWhen zinc oxide is manufactured as aby-product of a chemical reaction, it is considered a secondarytype. The chemical and physical properties can vary widelydepending on the raw m

10、aterial source and the type of reaction.4.3.2 MetallurgicalWhen zinc oxide is manufacturedfrom burning zinc vapor produced by boiling die cast scrapzinc, galvanized zinc dross, or other scrap zinc units withoutpurification, it is considered a secondary type. The chemicalpurity can vary widely and is

11、 dependent on the purity of thefeed metal.5. Composition and Properties5.1 Typical properties for untreated zinc oxide by types aredescribed in Table 1.5.2 Treated Zinc OxideZinc oxide for use in rubber isoften surface treated, most frequently with a fatty acid such aspropionic acid.5.2.1 A fatty ac

12、id treated zinc oxide will typically containabout 0.5 % less zinc oxide than the corresponding untreatedgrade.5.2.2 The typical fatty acid treated zinc oxide shows agreater heat loss, about 0.2 %, than the corresponding untreatedgrade due to partial vaporization of the fatty acid.1This classificatio

13、n is under the jurisdiction of ASTM Committee D11 onRubber and Rubber-like Materials and is the direct responsibility of SubcommitteeD11.20 on Compounding Materials and Procedures.Current edition approved Feb. 1, 2017. Published February 2017. Originallyapproved in 1983. Last previous edition approv

14、ed in 2012 as D4295 89 (2012).DOI: 10.1520/D4295-89R17.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3The l

15、ast approved version of this historical standard is referenced onwww.astm.org.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United StatesThis international standard was developed in accordance with internationally recognized principles on standar

16、dization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.1ASTM International takes no position respecting the validity of any patent rights asserted

17、in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the

18、responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive ca

19、reful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM Internatio

20、nal, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the

21、 ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 1 Typical Properties of Zinc OxidePropertyASTMMethodAmericanType(Direct)French Type (Indirect) Secondary

22、 TypesClass 1 Class 2 Class 3 ChemicalMetallurgicalClass 1 Class 2% Zinc oxide D3280 99.0 99.5 99.5 99.5 95.0 99.0 99.0% Lead D4075 0.10 0.002 0.002 0.002 0.10 0.10 0.10% Cadmium D4075 0.05 0.005 0.005 0.005 0.05 0.05 0.05% Sulfur D3280 0.15 0.02 0.02 0.02 0.15 0.02 0.02% Heat loss at 105C D280 0.25 0.30 0.25 0.25 0.50 0.25 0.25% Sieve residue, 45 m D4315 0.10 0.05 0.05 0.05 0.10 0.10 0.10Surface area, m2/g D3037 3.5 9.0 5.0 3.5 40.0 5.0 3.5D4295 89 (2017)2