ASTM D4654-1987(2009) Standard Test Method for Sulfate Basicity in Leather《皮革中硫酸盐盐基度的标准试验方法》.pdf

1、Designation: D 4654 87 (Reapproved 2009)Standard Test Method forSulfate Basicity in Leather1This standard is issued under the fixed designation D 4654; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A nu

2、mber in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This test method is intended for use in calculating thesulfate basicity of mineral tanned leather.1.2 This standard does not purport to a

3、ddress all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2D 2807 Test

4、 Method for Chromic Oxide in Leather (Per-chloric Acid Oxidation)D 4655 Test Methods for Sulfates in Leather (Total, Neu-tral, and Combined Acid)3. Significance and Use3.1 This test method is used to determine the percent of totalchromic oxide that is combined with hydroxyl and may serveas a measure

5、 of chrome fixation.4. Apparatus and Reagents4.1 The apparatus and reagents shall be as described in TestMethods D 2807 and D 4655.5. Sampling, Test Specimens and Test Units5.1 The test specimen shall be as described in Test MethodsD 2807 and D 4655.5.2 Unless otherwise specified in the detail speci

6、fications,two specimens from the composite sample shall be tested.5.3 The percent basicity of the sample for test shall be theaverage of the test results obtained from the specimens tested.6. Procedure6.1 The chromic oxide shall be determined as described inTest Method D 2807. The combined sulfate s

7、hall be deter-mined as described in Method D 4655.7. Calculation of Results7.1 Express the percent basicity of the specimen accordingto Schorlemmers system. In this system, the percent basicity isthe percent of the total chromic oxide that is combined withhydroxyl. Conversely, the percent acidity is

8、 the percent of thetotal chromic acid that is combined with sulfate or other acidanions. Percent basicity is therefore 100 % acidity.sulfate basicity, % 5 100 2 % combined sulfate3 52.8/% total chromic oxide (1)7.2 When other metals that form hydrolysable sulfates arepresent, add their equivalent pe

9、rcent of chromic oxide to thechromic oxide present before calculating percent basicity. Usethe following conversion factors: % Al2O33 1.49, %ZrO23 0.82, and % Fe2O33 0.95.7.3 Report the results to the nearest 0.1 %.8. Precision and Bias8.1 This test method is adopted from the procedures of theAmeric

10、an Leather ChemistsAssociation where it has long beenin use and where it was approved for publication before theinclusion of precision and bias statements were mandated. Theoriginal inter-laboratory test data is no longer available. Theuser is cautioned to verify by the use of reference material ifa

11、vailable that the precision and bias of this test method isadequate for the contemplated use.9. Keywords9.1 chrome fixation; Schorlemmers system; sulfate basicity1This test method is under the jurisdiction of ASTM Committee D31 on Leatherand is the direct responsibility of Subcommittee D31.06 on Che

12、mical Analysis.Current edition approved April 1, 2009. Published July 2009. Originallyapproved in 1987. Last previous edition approved in 2003 as D 4654 87 (2003).2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book

13、 of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.ASTM International takes no position respecting the validity of any patent rights a

14、sserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time

15、 by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will re

16、ceive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM In

17、ternational, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).D 4654 87 (2009)2