ASTM D4846-1996(2016) Standard Test Method for Resistance to Unsnapping of Snap Fasteners《按扣抗不易扣紧性的标准试验方法》.pdf

1、Designation: D4846 96 (Reapproved 2016)Standard Test Method forResistance to Unsnapping of Snap Fasteners1This standard is issued under the fixed designation D4846; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last r

2、evision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This test method covers the determination of the forcerequired to disengage snap fasteners by a pull perpendicular toand par

3、allel with the plane of the snap fastener.1.2 This test method requires attachment of snaps to speci-mens using specifications provided by the producers of thesnaps.1.3 This test method is used to establish correlation to wearconditions and for comparing different brands and types ofsnap fasteners.1

4、.4 The values stated in SI units are to be regarded as thestandard. The values stated in the parentheses are for informa-tion only.1.5 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establi

5、sh appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2D76 Specification for Tensile Testing Machines for TextilesD123 Terminology Relating to TextilesD1776 Practice for Conditioning and Testing T

6、extiles3. Definitions3.1 lateral holding strength, nthe force required to disen-gage a snap fastener resulting from a pull in the plane parallelto the material to which the snap fastener is attached.3.2 snap action, nthe force required to disengage a snapfastener resulting from a pull exerted perpen

7、dicular to the planeof material to which the snap fastener is attached.3.3 snap fastener, na device for attaching one material toanother consisting of matching male and female parts, each ofwhich is attached to a separate material so that the parts can bejoined by a low compressive force and separat

8、ed by a lowperpendicular tensile force.3.4 For definitions of other textile terms used in this testmethod, refer to Terminology D123.4. Summary of Test Method4.1 Snap fasteners mounted on strips of material near theend are tested on standard tensile testing machines equippedfor testing the strength

9、of textile fabrics and having sensitivityfor accurate low force levels.4.2 Tests are made on snap fasteners before laundering withthe option of testing again after a pre-determined number oflaunderings or other types of refurbishing.5. Significance and Use5.1 This test method may be used for accepta

10、nce testing ofcommercial shipments of snap fasteners, but caution is advisedsince information on between laboratory precision is incom-plete. Comparative tests as directed in 5.1.1 are advisable.5.1.1 In case of a dispute arising from differences inreported test results when using Test Method D4846

11、foracceptance testing of commercial shipments, the purchaser andseller should conduct comparative tests to determine if there isstatistical bias between their laboratories. Competent statisticalassistance is recommended for the investigation of bias. As aminimum, the two parties should take a group

12、of test speci-mens that are as homogeneous as possible and that are from alot of material of the type in question. The test specimens thenshould be assigned randomly in equal numbers to eachlaboratory for testing. The average results from the twolaboratories should be compared using Students t-test

13、forunpaired data and an acceptable probability level chosen by thetwo parties before testing is begun. If a bias is found, either itscause must be found and corrected or the purchaser and sellermust agree to interpret future test results in the light of theknown bias.6. Apparatus6.1 Tensile Testing

14、MachineA constant rate of extension(CRE) type or constant rate of traverse (CRT) type testing1This test method is under the jurisdiction of ASTM Committee D13 on Textilesand is the direct responsibility of Subcommittee D13.54 on Subassemblies.Current edition approved Oct. 1, 2016. Published October

15、2016. Originallyapproved in 1988. Last previous edition approved in 2011 as D4846 96 (2011).DOI: 10.1520/D4846-96R16.2For referenced ASTM standards, visist the ASTM wbsite, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandardsvolume information, refer to

16、the standards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1machine conforming to Specification D76 with a rate oftraverse of 305 mm (12 in.)/min, or a rate agreed upon betweenpurchaser and s

17、eller, and a scale which will produce accurateresults at very low force levels. There may be no overallcorrelation between the results obtained with the CRE and CRTtensile testing machines. In the case of controversy, however,the CRE method shall prevail.6.2 JawsThe back jaws of the clamps on the te

18、nsiletesting machine should be at least the same width as the frontjaws. The front jaws must be 25.4 mm (1 in.) wide.6.3 Aluminum PlateA plate is required measuring 50 by100by4mm(2by4by18 in.) with dowel pins inserted (seeFig. 1).6.4 Attaching MachineA hand operated, foot operated, orautomatic machi

19、ne for attaching snap fastener parts conform-ing to specifications of seller.7. Sampling7.1 Lot SampleAs a lot sample for acceptance testing, takeat random the number of shipping cartons of snap fasteners orshipping cartons of garments directed in an applicable materialspecification or other agreeme

20、nt between the purchaser and theseller. Consider shipping cartons of snap fasteners or shippingcartons of garments to be the primary sampling units.NOTE 1An adequate specification or other agreement between thepurchaser and the seller requires taking into account the variabilitybetween shipping cart

21、ons, units within a shipping carton, and betweenspecimens from a unit within a shipping carton, to provide a sampling planwith a meaningful producers risk, consumers risk, acceptable qualitylevel, and limiting quality level.7.2 Laboratory SampleAs a laboratory sample for accep-tance testing, proceed

22、 as follows:7.2.1 Unattached Snap FastenersTake one box or card ofunattached snap fasteners at random from each shipping cartonin the lot sample. If the male and female parts are packedseparately, take one box of each from each shipping carton inthe lot sample.7.2.2 Attached Snap FastenersTake one g

23、arment fromeach shipping carton in the lot sample.7.3 Test Specimens:7.3.1 Unattached Snap FastenersFrom each box or cardin the laboratory sample, take five snap fasteners at random. Ifthe male and female parts are packed separately, for each pairof boxes from a shipping carton in the lot sample, ta

24、ke fivemale parts at random and match them with five female partstaken at random.7.3.2 Attached Snap FastenersFrom each garment in thelaboratory sample, take five snap fasteners at random ongarments with more than five. If less than five, take all snapfasteners from each garment.8. Conditioning8.1 C

25、ondition the specimens by bringing them from the dryside to approximate moisture equilibrium for testing in thestandard atmosphere for testing textiles as directed in PracticeD1776.9. Procedure9.1 Preparing Specimens:9.1.1 Attaching Loose Snap FastenersWhen snap fasten-ers are to be attached to a ma

26、terial typical to intendedproduction, the pinch setting and other conditions specified bythe seller must be used. Cut fabric specimens to dimensions of38 by 89 mm (1.5 by 3.5 in.) and attach male part to one fabricspecimen and female part to the other fabric specimen, bothapproximately 19 mm (34 in.

27、) from the ends or edge of thefabric specimens (see Fig. 2).9.1.2 Cutting Specimens From GarmentsCut specimenfrom garments so that the snap fasteners are approximately 19mm (34 in.) from the end of a specimen measuring 38 by 89mm (1.5 by 3.5 in.). Cut the specimen as close to thesedimensions as poss

28、ible where snap fastener spacings limitspecimen size cut from garments.9.1.3 Marking of SpecimensSnap the fastener partstogether, keeping the edges of the two pieces of material inalignment. From the center of the snap fastener measure 38FIG. 1 Aluminum Plate FIG. 2 Specimen and Snap Fastener Arrang

29、ement for TestingD4846 96 (2016)2mm (1.5 in.) in each direction and place marks across the twopieces of material to provide a 76 mm (3 in.) overall length andvisual reference.9.2 Determination of Snap ActionSet the distance be-tween the upper and lower clamps of the testing machine for 76mm (3 in.).

30、 Clamp the aluminum plate loosely in the jaw of theupper clamp to prevent the specimen from twisting. Insert thefemale end of the specimen so that the lower edge of the jawin the upper clamp is even with the mark placed on the materialand tighten the clamp. Clamp the male end of the specimen inthe j

31、aw of the lower clamp so that the two snapped halves arestraight and the pull is perpendicular to the plane of the snapfastener and material (see Fig. 3). Apply the load until the snapfastener disengages. Remove the male end of the specimenfrom the lower clamp, reset the distance between clamps to 7

32、6mm (3 in.), snap the male specimen to the female specimen,align the pieces so that the fabric material edges are straightand tighten the lower clamp. Apply the load until the snapfastener disengages. Record the nature of the failure and theload at failure to the nearest 0.4 N (0.1 lbf). Repeat this

33、procedure until the specimen has been tested three times.9.3 Determination of Lateral Holding StrengthUse thesame specimens prepared from snap action tests. Use the sameprocedure specified in 9.2 except that the male specimen isclamped in the upper clamp and the force is applied in a planeparallel t

34、o the material and snap fastener (see Fig. 4).10. Report10.1 State that the tests were made as directed in TestMethod D4846. Describe the material or product beingsampled and the method of sampling used. Describe thematerial and end product.10.2 Report the following information:10.2.1 Type of testin

35、g machine and load range used.10.2.2 Individual and average results.10.2.3 Note any fabric or snap fastener failure beside resultswith F for fabric and S for snap fastener. Disregard fabricfailures.10.3 Report the units of force in newtons (N) or poundsforce (lbf).11. Precision and Bias311.1 Summary

36、:11.1.1 In comparing two averages, the differences shouldnot exceed the following critical differences in 95 cases out of100 when all of the observations are taken by the samewell-trained operator using the same piece of test equipmentand specimens randomly drawn from the same sample ofmaterial and

37、tested on the same day.Snap action .61 lbs for averages of 4Lateral holding strength 4.30 lbs for averages of 411.1.2 The size of the differences is likely to be affectedadversely by different circumstances. The true values of snapaction and lateral holding strength can be defined only in termsof sp

38、ecific test methods. Within this limitation, the proceduresin this test method for determining these properties have noknown bias.11.2 Interlaboratory Test DataAn interlaboratory test wasrun in 1996 in which randomly drawn samples of five materialswere tested in five laboratories. Each laboratory us

39、ed twooperators, each of whom tested four specimens of each3Supporting data available from ASTM Headquarters. Request RR:D13-1080.FIG. 3 Specimen Clamping for Snap Action TestFIG. 4 Specimen Clamping for Lateral Holding StrengthTABLE 1 Critical Differences Between Two Averages for Single-Material Co

40、mparisonsNames of thePropertiesNumber ofObservationsin AverageSingle-OperatorPrecisionWithin-LaboratoryPrecisionBetween-LaboratoryPrecisionSnap action 1 1.21 1.50 1.582 .85 1.24 1.335 .54 1.05 1.1510 .38 .98 1.08Lateral holding strength 1 8.6 8.6 9.02 6.1 6.1 6.65 3.8 3.8 4.610 2.7 2.7 3.7D4846 96 (

41、2016)3material. The components of variance expressed as standarddeviations were calculated to be the values listed in Table 1 andTable 2.11.3 Critical DifferencesFor the components of variancelisted in Table 3 and Table 4, two averages of observed valuesshould be considered significantly different a

42、t the 95 % prob-ability level if the difference equals or exceeds the criticaldifferences listed in Table 1 and Table 2.11.4 BiasThe procedures in Method D4846 for measuringthe properties listed in Tables 1-4 have no bias because thevalue of these properties can be defined only in terms of a testmet

43、hod.12. Keywords12.1 snap fasteners; strengthTABLE 2 Critical Differences Between Two Averages for Multi-Material ComparisonsNames of thePropertiesNumber ofObservationsin AverageSingle-OperatorPrecisionWithin-LaboratoryPrecisionBetween-LaboratoryPrecisionSnap action 1 1.64 1.87 2.432 1.41 1.67 2.275

44、 1.24 1.53 2.1710 1.18 1.48 2.14Lateral holding strength 1 11.5 11.5 12.52 9.8 9.8 10.95 8.6 8.6 9.910 8.1 8.1 9.5TABLE 3 Components of Variance as Standard Deviations forMulti-MaterialNames of the PropertiesSingle-OperatorComponentWithin-LaboratoryComponentBetween-LaboratoryComponentSnap action .44

45、 .32 .17Lateral holding strength 3.10 0 .91D4846 96 (2016)4ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such pat

46、ent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited eit

47、her for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair

48、hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this stand

49、ard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 4 Components of Variance as Standard Deviations forMulti-MaterialNames of the PropertiesSingle-OperatorComponentWithin-LaboratoryComponentBetween-LaboratoryComponentSnap action .84 .32 .