1、Designation: D 4906 95 (Reapproved 2006)Standard Test Method forTotal Solids and Ash Content in Leather Finishing Materials1This standard is issued under the fixed designation D 4906; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision,

2、 the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This test method covers the total solids and ash contentof finishing materials.1.2 The values stated in

3、SI units are to be regarded as thestandard.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulato

4、ry limitations prior to use.2. Significance and Use2.1 This test method is intended for use in determining thetotal solids content and the ash content of a finishing materialbefore its use on any leather.3. Apparatus3.1 Two Tared Platinum Dishes.3.2 Drying Oven, that operates at 43C 6 3C and 93C 63C

5、.3.3 Desiccator, with calcium chloride or other desiccant.3.4 Muffle Furnace, capable of maintaining temperatures of(600C 6 25C).4. Sampling4.1 One 5- g and one 10-g sample of the finishing materialshall be weighed with accuracy to within 0.001 g.5. Procedure5.1 Total Solids:5.1.1 Place the samples,

6、 which have been weighed inplatinum dishes, in the oven for 16 h at 43C followed by 2 hat 93C. (If two ovens at different temperatures are notavailable, increase the temperature in the first oven for the 2-hheating.)5.1.2 Remove the dishes from the oven, place them in adesiccator for1htocool to room

7、 temperature and weigh.Return the dishes to the oven for1hat93C and, after coolingin a desiccator for 1 h, weigh again.5.1.3 If the weight loss in the 1-h drying period did notchange the total solids percentage more than 0.1 %, report theresults. If greater than 0.1 % loss was obtained from the last

8、1-h drying period, then repeat the drying until the change isless than 0.1 %.5.2 Ash:5.2.1 Place each platinum dish, containing the residue fromthe total solids determination, in a muffle furnace at 600C 625C for 2 h.5.2.2 If difficulty is encountered in completely burning offthe carbon, leach the r

9、esidue with hot water (filtering throughashless filter paper) and further ignite this residue in the mufflefurnace.5.2.3 To the dish containing the cooled ash, add the filtrate;evaporate to dryness and heat for 30 min at 600C 6 25C. Theproduct shall then be cooled in a dessicator and weighed.6. Calc

10、ulation6.1 The percent total solids of the finishing material shall becalculated as follows:Total solids, percent 5AB3 100 (1)where:A = final weight of solid matter after drying, andB = the original weight of the sample.6.2 The percent ash content of the finishing material shall becalculated as foll

11、ows:Ash content, percent 5CB3 100 (2)where:C = final weight of ash, andB = the original weight of the sample.7. Report7.1 The total solids in the finishing material is the average ofthe duplicate results and shall be reported in percent.1This test method is under the jurisdiction of ASTM Committee D

12、31 on Leather, is the direct responsibility of Subcommittee D31.06 on Chemical Analysis and hasbeen produced in cooperation with the American Leather Chemists Association.(Method K 1-1956).Current edition approved Oct. 1, 2006. Published November 2006. Originallyapproved in 1989. Last previous editi

13、on approved in 2001 as D 490695 (2001).1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.7.2 The ash content of the finishing material, likewise, is theaverage of the duplicate results and shall also be reported inpercent.8. Precision

14、and Bias8.1 No justifiable statement can be made on the precisionand bias of this test method because the original interlaboratorytest data is no longer available.8.2 However, the user is cautioned to verify by the use ofreference materials, if available, that the precision and bias ofthis test meth

15、od is adequate for the contemplated use.9. Keywords9.1 ash; finishes; finishing materials; total solidsASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that d

16、etermination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved

17、 or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel

18、that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).D 4906 95 (2006)2