1、Designation: D4970/D4970M 162Standard Test Method forPilling Resistance and Other Related Surface Changes ofTextile Fabrics: Martindale Tester1This standard is issued under the fixed designation D4970/D4970M; the number immediately following the designation indicates theyear of original adoption or,
2、 in the case of revision, the year of last revision. A number in parentheses indicates the year of lastreapproval. A superscript epsilon () indicates an editorial change since the last revision or reapproval.1NOTEIn 10.1, the standard atmosphere for testing textiles shown in brackets was corrected f
3、rom 70 6 20F to70 6 2F in April 2017.2NOTEIn 6.6.2, the conversion of 105 mm was corrected to 4.13 in. editorially in June 2017.1. Scope1.1 This test method covers the determination of the resis-tance to the formation of pills and other related surface changeson textile fabrics using the Martindale
4、tester. The proceduregenerally is applicable to all types of fabrics, being particularlysuitable for woven fabrics.NOTE 1For other methods, if testing the pilling resistance of textiles,refer to Test Methods D3511/D3511M, D3512/D3512M, and D3514.1.2 This test method is not suitable for fabrics thick
5、er than3 mm 0.125 in. because such fabrics cannot be mounted inthe specimen holder.1.3 The fabric may be laundered or dry cleaned beforetesting.1.4 The values stated in either SI units or inch-pound unitsare to be regarded separately as standard. The values stated ineach system may not be exact equi
6、valents; therefore, eachsystem shall be used independently of the other. Combiningvalues from the two systems may result in non-conformancewith the standard.1.5 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user o
7、f this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.1.6 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Pri
8、nciples for theDevelopment of International Standards, Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade (TBT) Committee.2. Referenced Documents2.1 ASTM Standards:2D123 Terminology Relating to TextilesD3511/D3511M Test Method for Pilling Resistance andOthe
9、r Related Surface Changes of Textile Fabrics: BrushPilling TesterD3512/D3512M Test Method for Pilling Resistance andOther Related Surface Changes of Textile Fabrics: Ran-dom Tumble Pilling TesterD3514 Test Method for Pilling Resistance and Other RelatedSurface Changes of Textile Fabrics: Elastomeric
10、 PadD4850 Terminology Relating to Fabrics and Fabric TestMethodsD7018 Terminology Relating to Glass Fiber and Its Products2.2 ASTM Adjuncts:3ADJD3512 Set of 5 Photographic Standards for RandomTumble Pilling Test3. Terminology3.1 For all terminology relating to D13.59, Fabric TestMethods, General, re
11、fer to Terminologies D4850 and D7018.3.1.1 The following terms are relevant to this standard:cycle, fuzz, movement, pilling resistance, pills.3.2 For all other terms related to textiles, refer to Terminol-ogy D123.4. Summary of Test Method4.1 Pilling and other changes in the surface appearance,such
12、as fuzzing, that occur in normal wear are simulated on alaboratory testing machine. Fabrics are mounted on the Mar-tindale Tester, and the face of the test specimen is rubbedagainst the face of the same mounted fabric in the form of a1This test method is under the jurisdiction of ASTM Committee D13
13、on Textilesand is the direct responsibility of Subcommittee D13.60 on Fabric Test Methods,Specific.Current edition approved Jan. 1, 2016. Published February 2016. Originallyapproved in 1999. Last previous edition approved in 2010 as D4970 101. DOI:10.1520/D4970-16E02.2For referenced ASTM standards,
14、visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Available from ASTM International Headquarters. Order Adjunct No.ADJD3512.Copyright ASTM Int
15、ernational, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards
16、, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.1geometric figure, that is, a straight line, which becomes agradually widening ellipse, until it forms another straight linein the opposite direction and traces the same figure again under
17、light pressure for a specific number of movements. The degreeof fabric pilling or surface appearance change produced by thisaction is evaluated by comparison of the tested specimen withvisual standards that may be actual fabrics, or photographs offabrics, showing a range of pilling resistance. The o
18、bservedresistance to pilling is reported using an arbitrary rating scale.5. Significance and Use5.1 Acceptance TestingThis method of testing fabricsresistance to pilling is not recommended for acceptance testing.If it is used for acceptance testing, it should be used withcaution because interlaborat
19、ory data are not available. In somecases the purchaser or supplier may have to test a commercialshipment of one or more specific materials by the best availablemethod even though the method has not been recommended foracceptance testing. Although this test method is not recom-mended for acceptance t
20、esting, it is useful because it is usedwidely outside the United States.5.2 If there is a disagreement arising from differences invalues reported by the purchaser and the supplier when usingthis test method, the statistical bias, if any, between thelaboratory of the purchaser and the laboratory of t
21、he suppliershould be determined with comparison being based on testingspecimens randomly drawn from one sample of material of thetype being evaluated. Competent statistical assistance is rec-ommended for the investigation of bias. A minimum of twoparties should take a group of test specimens, which
22、are ashomogeneous as possible and which are from a lot of materialof the type in question. The test specimens then should beassigned randomly in equal numbers to each laboratory fortesting. The average test results from the two laboratoriesshould be compared using an acceptable statistical protocol
23、andprobability level chosen by the two parties before the testing isstarted. Appropriate statistical disciplines for comparing datamust be used when the purchaser and supplier cannot agree. Ifa bias is found, either its cause must be found and corrected, orthe purchaser and the supplier must agree t
24、o interpret futureresults with consideration for the known bias.5.3 The pilling of textile fabrics is a very complex propertybecause it is affected by many factors that include type of fiberor blends, fiber dimensions, yarn and fabric construction, andfabric finishing treatments. The pilling resista
25、nce of a specificfabric in actual wear varies more with general conditions of useand individual wearers than in replicate fabric specimenssubjected to controlled laboratory tests. This experience shouldbe borne in mind when adopting levels of acceptability for aseries of standards.5.4 Finishes and f
26、abric surface changes may exert a largeeffect on pilling. It is recommended that fabrics be tested afterlaundering or drycleaning, or both. Testing before refurbishingalso may be advisable. Prior agreement between interestedparties should determine the state of the test.5.5 Pills vary appreciably in
27、 size and appearance anddepend on the presence of lint and degree of color contrast.These factors are not evaluated when pilling is rated solely onthe number of pills. The development of pills may be accom-panied by other surface phenomena, such as loss of cover,color change, or the development of f
28、uzz. Since the overallacceptability of a specific fabric is dependent on both thecharacteristics of the pills and the other factors affecting thesurface appearance, it is suggested that fabrics tested in thelaboratory be evaluated subjectively with regard to theiracceptability and not rated solely o
29、n the number of pillsdeveloped.Aseries of standards, based on graduated degrees ofsurface change of the fabric type being tested, may be set up toprovide a basis for subjective ratings. The visual standards aremost advantageous when the laboratory test specimens corre-late closely in appearance with
30、 worn fabrics and show a similarratio of pills to fuzz. Counting the pills and weighing theirnumber with respect to their size and contrast, as a combinedmeasure of pilling resistance, is not recommended because ofthe excessive time required for counting, sizing, and calcula-tion.FIG. 1 Martindale A
31、brasion TesterFIG. 2 Apparatus for Fabric EvaluationD4970/D4970M 16225.6 The degree of fabric pilling is evaluated by comparingthe tested specimens with visual standards, which may beactual fabrics or photographs of fabrics, showing a range ofpilling resistance. The observed resistance to pilling is
32、 reportedon an arbitrary scale ranging from 5 to 1 (no pilling to verysevere pilling).5.7 This test method is applicable to a wide variety ofwoven and knitted fabrics that vary in pilling propensity as aresult of variations in fiber, yarn and fabric structure, andfinish. The applicability of this te
33、st method to nonwovenfabrics has not been determined.6. Apparatus and Materials6.1 Martindale Tester (see Fig. 1). Using a lissajous figureof 60 mm as described in Terminology D4850 and having a38 mm sample holder.NOTE 2Apparatus and accessories are available commercially.6.2 Standard Felt, of mass
34、750 6 50 g/m222 6 1.5 oz/yd2and 3 6 0.3 mm 0.12 6 0.01 in. thick.6.3 Polyurethane Foam Backing0.12 6 0.04 in. 3 60.01 mm thick, 1.94 lbf/ft329 to 31 kg/m3 density, and 38.23to 47.22 lbf 170 to 210 N hardness.NOTE 3Apparatus and accessories are available commercially.6.4 Apparatus for Fabric Evaluati
35、onFacilities for illumi-nation (cool white fluorescent tube) and simultaneous viewingtest specimens and fabric or photographic rating standards.Apparatus and options for visual evaluation are listed in Table1.6.5 Standard In-House Pilling Test Fabric, having an estab-lished pilling resistance rating
36、 for checking machine perfor-mance. No universal standard fabric is available. Each testfacility must decide on an appropriate fabric.6.6 Rating Standards:6.6.1 Fabric, a series of tested specimens of a specific fabrictype, which show degrees of pilling or other distortion, or both,for the fabric to
37、 be tested. Store the fabric rating standards andhandle them under conditions that will preserve their originalform and appearance. Mounting with thick cardboard framingaround the specimens is recommended.6.6.2 PhotographicA set of five photographs 105 mm4.13 in., numbered 1 to 5, illustrating varyi
38、ng degrees ofpilling from “very severe pilling” to “no pilling.”36.6.3 Digital imaging or rating system, or both.6.7 Fabric Punches or Press Cutters, 38 mm 1.5 in. and140 mm 5.5 in. in diameter.6.8 Facilities for Laundering Samples, if needed.6.9 Facilities for Drycleaning Samples, if needed.7. Samp
39、ling7.1 Primary Sampling UnitConsider rolls of fabric orfabric components of fabricated systems to be the primarysampling unit, as applicable.7.2 Laboratory Sampling UnitFrom each primary sam-pling unit take one full-width piece of fabric that is 1 m 1 ydin length along the selvage (machine directio
40、n), after firstremoving a 1 m 1 yd length. For fabric components offabricated systems use the entire system,8. Test Specimens: Selection, Number, and Preparation8.1 Unless otherwise specified, samples should be washedor drycleaned before cutting the test specimens. Conditionsappropriate for the fabr
41、ic end-use or conditions agreed upon byinterested parties should be used.8.2 Cut a pair of circular specimens from each swatch in thelaboratory sample with one of each pair of specimens being 38mm 1.5 in. in diameter and the other 140 mm 5.5 in. indiameter.8.3 Take the specimens evenly-spaced across
42、 the width ofthe laboratory sample or from two different panels in agarment. Specimens should be staggered in such a manner thatno specimens contain the same yarns. Avoid areas withwrinkles and other distortions. Unless otherwise specified, donot cut specimens nearer the selvage less than110 of the
43、widthof the fabric.9. Preparation of Apparatus9.1 Maintenance CheckFollow instruction manual forproper maintenance of apparatus.10. Conditioning10.1 Condition specimens in the standard atmosphere fortesting textiles, which is 21 6 1C 70 6 2F and 65 % RH62 % relative humidity for at least 4 h prior t
44、o testing.11. Procedure11.1 Make all tests in the standard atmosphere for testingtextiles.11.2 Mount one 140-mm 5.5-in. diameter of standard feltand one fabric specimen on each table (see Fig. 1). Place one38-mm 1.5-in. diameter disk of 3-mm polyurethane foam anda specimen of the same fabric in each
45、 of the holders, makingsure the face of the fabric is exposed for both specimens.11.3 Place the specimen holders on the same table as theother fabric specimen and insert a spindle into each specimenholder to give a pressure on the larger specimen of approxi-mately 3 kPa 0.44 psi. This pressure is th
46、e same as any othersetup but without additional weights.11.4 Start the machine and allow it to run for 100 move-ments. Run additional movements in increments of 100 up toTABLE 1 Viewing Apparatus and OptionsApparatus Specimen PreparationASTM Lightbox (Fig. 2)A0.78 rad 45LightboxB0.78 rad 45LightboxB
47、flatLightboxBcritical angleAs determined by the buyer and supplierAThe source of supply of the apparatus known to the committee at this time isStandard Scientific Supply Co., 601 West Market Street, Bethlehem, PA180185208. If you are aware of alternate suppliers, please provide this informa-tion to
48、ASTM Headquarters. Your comments will receive careful consideration at ameeting of the responsible technical committee, which you may attend.BAvailable commercially.D4970/D4970M 16231000 movements as directed in a material specification orcontract. Rate the specimen at each specified interval asdire
49、cted in Section 12 and record the final rating.12. Evaluation12.1 Place the 38-mm 1.5-in. disk specimen squarely onthe double-faced tape in the viewing cabinet (see Fig. 2).12.1.1 Using the viewing apparatus and option selectedfrom Table 1 and either suitable fabric or photographicstandards, subjectively rate the face of each specimen incomparison to the original specimen, using the following scale:For pilling:5no pilling4slight pilling3moderate pilling2severe pilling1very severe pillingFor fuzzing:5no fuz