ASTM D5171-2000(2006) Standard Test Method for Impact Resistance of Plastic Sew-Through Flange Buttons《塑料熔合法兰按扭耐冲击的标准试验方法》.pdf

1、Designation: D 5171 00 (Reapproved 2006)Standard Test Method forImpact Resistance of Plastic Sew-Through Flange Buttons1This standard is issued under the fixed designation D 5171; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the

2、 year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This test method covers the determination of impactresistance of plastic sew-through flange buttons.1.2 The

3、values stated in either acceptable metric units orother units shall be regarded separately as standard. The valuesexpressed in each system may or may not be exact equivalents:therefore, each system must be used independently of the other,without combining values in any way.1.3 This standard does not

4、 purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards

5、:2D 123 Terminology Relating to TextilesD 618 Practice for Conditioning Plastics for TestingD 5497 Terminology Relating to Buttons3. Terminology3.1 Definitions:3.1.1 button, na knob, disc, or similar object which whenforced through a narrow opening or buttonhole, fastens onepart of a garment or othe

6、r flexible substrate to another (See alsosew-through flange button)3.1.1.1 DiscussionAlthough the primary purpose of but-tons is to serve as fasteners, buttons can also be used asdecoration.3.1.2 face, nin buttons, that portion which will be ex-posed after attaching to the substrate.3.1.3 impact res

7、istance, nresistance to fracture under thesudden application of an external force.3.1.4 ligne size, na unit of measure for button diameter:one ligne equals 0.635 mm (0.025 in.)3.1.5 sew-through flange buttons, na button that has twoor more holes in its flange for passage of a needle and threadso tha

8、t the button can be attached to a flexible substrate.3.1.6 For other textile terminology used in this method,refer to Terminology D 123.3.1.7 For definitions of button terms used in this method,refer to Terminology D 5497.4. Summary of Test Method4.1 Individual buttons are placed on a surface center

9、edunder a tube through which a preselected mass falls from apreselected height. After the mass impacts the button theimpacted button is removed and visually examined using a 5Xmagnifying glass for breakage, cracking, or chipping.5. Significance and Use5.1 This test method may be used to determine th

10、e ability ofa button to resist breaking under impact, for example inpressing the end item, which could cause the button to fail.NOTE 1In the development of this test method it was found that thefollowing factors influenced the ability of a button to resist failure underimpact conditions: resin formu

11、lation, shape ligne size, thickness, numberand spacing of holes. Buttons may also pass this test but fail during thepressing of a garment due to the presence of heat during pressing.5.1.1 If there are differences of practical significance be-tween the reported test results for two laboratories (or m

12、ore),comparative tests should be performed to determine if there isa statistical bias between them, using competent statisticalassistance. As a minimum, test samples should be used that areas homogeneous as possible, that are drawn from the materialfrom which the disparate rest results were obtained

13、, and thatare randomly assigned in equal numbers to each laboratory fortesting. Other materials with established test values may beused for this purpose. The test results from the two laboratoriesshould be compared using a statistical test for unpaired data, ata probability level chosen prior to the

14、 testing series. If a bias isfound, either its cause must be found and corrected, or futuretest results must be adjusted in consideration of the knownbias.5.2 Test Method D 5171 for the determination of the impactresistance of buttons may be used for acceptance testing ofcommercial shipments of butt

15、ons but caution is advisable sinceinformation is lacking on precision.1This test method is under the jurisdiction of ASTM Committee D13 on Textilesand is the direct responsibility of Subcommittee D13.54 on Subassemblies.Current edition approved June 1, 2006. Published July 2006. Originally approvedi

16、n 1991. Last previous edition approved in 2000 as D 517100.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1C

17、opyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.6. Apparatus6.1 Impact Resistance Testing MachineThe impact resis-tance tester consists of a tube through which a plunger ofstandard mass drops onto the button from a predeterminedheight.

18、 The button is centrally positioned based on ligne size,by means of a locating jig, on a flat metal surface. The energyof impact is determined by the mass of the plunger and theheight of the drop.6.2 Magnifying Glassa 5X magnifying glass is used tovisually examine the buttons after impact.6.3 Measur

19、ing Devicemeasuring calipers or micrometer,to determine the ligne size of buttons.7. Sampling7.1 Laboratory SampleAs a laboratory sample, randomlyselect a quantity of buttons, approximately 100 to 200, from aFIG. 1 Impact-Resistance TesterD 5171 00 (2006)2carton and from contained boxes, that adequa

20、tely representsthe material, from which test specimens may be selected.7.2 Test SpecimensRandomly select 15 buttons from thelaboratory sample for testing. If test specimens are submittedfor preproduction approval, testing 1 dozen buttons is accept-able.8. Conditioning8.1 Condition the specimens as d

21、irected in Practice D 618using procedure E. Following conditioning, prepare the speci-mens for testing as instructed in 9.4 of practice D 618.Preconditioning is not required.9. Procedure9.1 Determine Button Ligne SizeUsing a set of calipers ora micrometer slowly bring the instrument faces or anvils

22、intocontact with the button to obtain the button diameter. Dividethe measured diameter in mm (in) by the constant 0.635 mm(0.025 in.) and record to the nearest whole number as the lignesize.9.2 Determine Impact ResistancePlace specimen in cen-tering device for ligne size of button so it lies at the

23、center ofthe vertical tube. Allow the mass to fall from a predeterminedand reproducible height onto the button. Lift the mass andremove the specimen from the metal base.10. Evaluation10.1 Visually examine the tested specimens with a 5Xmagnifying glass for cracking, chipping, and breakage, any ofwhic

24、h constitutes damage. Test the remaining specimens.11. Report11.1 State that the specimens were tested as directed in TestMethod D 5171. Describe the material or product sampled.11.1.1 Total number of specimens,11.1.2 Button ligne size,11.1.3 Height of fall and mass of plunger, if the standardcondit

25、ions are not used.11.1.4 Number of specimens damaged due to (1) cracking,(2) chipping (3) breakage.12. Precision and Bias12.1 No information is presented about either the preciisionor bias of this test method since the test result is nonquantita-tive.12.2 BiasNo justifiable statement can be made on

26、the biasof Test Method D 5171 for testing the impact resistance ofbuttons since the true value cannot be established by anaccepted referee method.13. Keywords13.1 button; impact resistance; strengthASTM International takes no position respecting the validity of any patent rights asserted in connecti

27、on with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible

28、 technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consi

29、deration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Ba

30、rr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).D 5171 00 (2006)3