ASTM D5359-1998(2010) Standard Specification for Glass Cullet Recovered from Waste for Use in Manufacture of Glass Fiber《用于玻璃纤维的从废物中回收的碎玻璃的标准规范》.pdf

1、Designation: D5359 98 (Reapproved 2010)Standard Specification forGlass Cullet Recovered from Waste for Use in Manufactureof Glass Fiber1This standard is issued under the fixed designation D5359; the number immediately following the designation indicates the year oforiginal adoption or, in the case o

2、f revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification describes glass cullet recovered frommunicipal waste destined for disposal.

3、 The recovered cullet isintended for use in the manufacture of glass fiber used forinsulation-type products.2. Referenced Documents2.1 ASTM Standards:2C162 Terminology of Glass and Glass ProductsD4129 Test Method for Total and Organic Carbon in Waterby High Temperature Oxidation and by Coulometric D

4、e-tectionE688 Test Methods for Waste Glass as a Raw Material forGlass Manufacturing3. Terminology3.1 For definitions of terms used in this specification, referto Terminology C162.4. General Requirements4.1 Glass cullet from municipal waste is primarily soda-lime bottle glass and shall be one of thre

5、e grades dependingupon the total usage rate requirement of the user. The threegrades shall satisfy the following chemical composition, colormix, contamination, and particle size requirements as listed inSection 4:4.2 Chemical CompositionSee Table 1.4.3 Color MixColor is an indicator of the oxidation

6、 stateof container cullet. SO3gas solubility in the glass melt is afunction of the glass oxidation state. Changes in the oxidationstate of cullet added to the fiberglass batch can shift the glassoxidation state causing the release of dissolved SO3gas, whichcan upset the furnace.Achange in the glass

7、oxidation state alsomeans a change in the glass FeO content. This affects the heattransfer in the melt and can affect furnace efficiency and glassquality. See Table 2.4.4 ContaminantsFree metals, magnetic or nonmagnetic,are not oxidized in the glass melting process and, therefore, areinsoluble. Meta

8、ls will pool on the furnace floor and leakthrough joints causing premature wear of refractories andelectrical shorts, which can lead to glass leaks. Some metalswill attack and destroy precious metal skimmers and thermo-couples and molybdenum electrodes. Examples are silver, tin,lead, and aluminum.4.

9、4.1 Other inorganic materials and refractories will notmelt in the glass melting process. Other inorganics can beporcelains, ceramics, or high-temperature glasses. Refractoriescan be remnants of furnace construction materials or mineralscontained as unmelted inclusions in the cullet. See Table 3.4.4

10、.1.1 The container cullet mixture must not contain glasstypes or other materials whose composition contains anythingthat is either harmful to the fiberglass production process orwhich affects the users ability to meet Federal or stateenvironmental, safety, or health laws. Examples of suchmaterials a

11、re anything which contains elements or oxides ofphosphorus, arsenic, antimony, and chlorides.1This specification is under the jurisdiction of ASTM Committee D34 on WasteManagement and is the direct responsibility of Subcommittee D34.03 on Treatment,Recovery and Reuse.Current edition approved Jan. 1,

12、 2010. Published January 2010. Originallyapproved in 1993. Last previous edition approved in 2004 as D535998(2004).DOI: 10.1520/D5359-98R10.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volum

13、e information, refer to the standards Document Summary page onthe ASTM website.TABLE 1 Chemical CompositionGrade 1 2 3Use Range 0 to5%inbatch 5to15%inbatch 15%inbatchOxide Weight%6Range%Weight%6Range%Weight%6Range%SiO26877 NA 6877 1.00 6877 1.00Al2O307 NA 07 0.50 07 0.50CaO 515 NA 515 0.50 515 0.50M

14、gO 05 NA 05 0.50 05 0.50Na2O 818 NA 818 0.50 818 0.50K2O 04 NA 04 0.50 04 0.50Fe2O315 % in batchColorWeight%6Range%Weight%6Range%Weight%6Range%Flint 0100 NA 0100 5 0100 3dGreen 0100 NA 0100 5 0100 3Amber 15%inbatchContaminant Type Weight % Weight % Weight %Magnetic Material 0.3 0.2 0.1Nonmagnetic Metals 0.01 0.005 0.005Other InorganicMaterial+ 12 Mesh NA 0.0 0.0+ 20 Mesh NA 0.2 0.120 Mesh NA 0.3 0.2Refractories+ 12 Mesh NA 0.0 0.0+ 20 Mesh NA 0.2 0.120 Mesh NA 0.3 0.2D5359 98 (2010)2