ASTM D6072-1996(2002) Standard Guide for Obtaining Samples of Geosynthetic Clay Liners《土工合成粘土衬垫获得样品的标准指南》.pdf

1、Designation: D 6072 96 (Reapproved 2002)Standard Guide forObtaining Samples of Geosynthetic Clay Liners1This standard is issued under the fixed designation D 6072; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last re

2、vision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This practice covers procedures for sampling geosyn-thetic clay liners (GCLs) for the purpose of laboratory testing.These pr

3、ocedures are designed to ensure that representativesamples are obtained and properly packaged for submittal to atesting laboratory.1.2 The procedures in this practice may be applied tosamples of unhydrated GCLs obtained at the project site or atthe production facility, prior to shipment to the proje

4、ct site.1.3 It is assumed that the number of samples to be obtainedhas already been determined in the project specification,standard test method, or by prior agreement between thepurchaser and seller. This practice covers only the methods forobtaining a pre-arranged number of samples and does notdes

5、cribe methods for obtaining individual specimens from thesample.1.4 The values stated in SI units are to be regarded as thestandard.1.5 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establ

6、ish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:D 4354 Practice for Sampling of Geosynthetics for Testing2D 4439 Terminology for Geosynthetics2D 4873 Guide forIdentification, Storage, and H

7、andling ofGeosynthetic Rolls and Samples23. Terminology3.1 Definitions:3.1.1 geosynthetic clay liner (GCL), na manufacturedhydraulic barrier consisting of clay bonded to a layer or layersof geosynthetics.3.1.2 sample, na portion of a material which is taken fortesting or for record purposes (See Pra

8、ctice D 4354).3.1.3 specimen, na specific portion of a material orlaboratory sample upon which a test is performed or which istaken for that purpose (See Practice D 4354).3.1.4 For definitions of other geosynthetic terms used in thispractice, refer to Terminology D 4439.4. Significance and Use4.1 Th

9、is practice provides a method by which samples ofGCL may be obtained for laboratory testing. The practiceapplies to materials obtained either at a job site or at aproduction facility.4.2 GCL samples obtained in accordance with this practicewill be considered representative of the actual manufactured

10、GCL.4.3 The quantity of GCL received by the laboratory shouldbe sufficient for the preparation of several representative testspecimens for a variety of standardized physical, hydraulic,and mechanical tests commonly performed on GCLs.4.4 The procedures in this practice should be used by plantand fiel

11、d personnel for obtaining GCL samples for laboratorytesting.5. Procedure5.1 In accordance with the project specifications or withPractice D 4354, divide the shipment or other given quantity ofGCL into lots, and select lot and laboratory samples. This willusually involve the selection of a certain nu

12、mber of finishedGCL rolls from which samples will be cut.5.2 Affix on the packaging of the GCL rolls to be sampledadhesive labels or other markings which clearly identify thatthe roll is to be sampled.5.3 Record the label information from each roll to besampled for future incorporation into within t

13、he qualityassurance/quality control (QA/QC) documentation for theGCL.5.4 Segregate the rolls identified for sampling. Refer toappropriate ASTM standard practices for the proper equipmentand techniques for handling the GCL rolls.5.5 Inspect the packaging of the selected GCL rolls fordamage. Describe

14、and record the damage, if any.5.6 Remove the outer packaging from the GCL as carefullyas possible, taking precautions not to damage the GCL and topreserve the packaging as much as possible for re-use aftersampling is completed.5.7 Obtain samples from the selected GCL rolls. The surfaceon which the G

15、CL is cut shall be smooth, hard, and free of1This practice is under the jurisdiction of ASTM Committee D35 on Geosyn-thetics and is the direct responsibility of Subcommittee D35.04 on GeosyntheticClay Liners.Current edition approved December 10, 1996. Published December 1997.2Annual Book of ASTM Sta

16、ndards, Vol 04.09.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.irregularities and potential contaminants. All samples shall beobtained by cutting across the full width of the roll end,perpendicular to the edges. Samples shall be c

17、ut with a sharputility knife or other implement capable of making a clean,straight cut through all components of the GCL. Unlessotherwise specified, the cut shall be made at a point that is 1.0m from the exposed end of the roll.NOTE 1At the discretion of the engineer, shorter or narrower samples,or

18、both, may be obtained provided that the packaging procedures in thisguide are followed.5.8 A unique sample number shall be written on the sample.Additional markings should be made on the sample to identifythe machine direction and the top/bottom sides of the GCL.5.9 The GCL sample shall then be manu

19、ally rolled around acore at least 75 mm in diameter, in the same direction as thecut. Care should be taken to wind the GCL without slack. Widestrapping tape (50 mm) shall then be wound around the samplein at least two places to secure the loose end. Bentonite lossfrom the sample may be minimized by

20、applying the tapearound the roll ends.5.10 At least two layers of plastic sheeting shall be used towrap the GCL sample roll for shipment to the laboratory, so asto minimize GCL sample disturbance or changes in moisturecontent. A thin cellophane material may be used for the innerwrapping, provided it

21、 is wound securely and repeatedly aroundthe rolled sample. The outer sheeting shall be at least 0.15 mm(6 mils) in thickness and shall be wrapped to minimize theamount of GCL shifting within the wrapping.5.11 To ensure proper sample chain-of-custody tracking, allshipping documents shall indicate the

22、 sample number, projectname and contact, and laboratory name and contact.5.12 If an additional sample from the same GCL roll isrequired for testing, 5.7 through 5.11 of this practice may berepeated on the exposed end of the roll until a sufficient amountof GCL is obtained.NOTE 2Additional material c

23、ut from the same roll is still consideredpart of the same sample therefore should not be designated any differentlythan those samples previously obtained from the same roll.5.13 Samples should be transmitted to the laboratory in amanner that minimizes the amount elapsed time, samplehandling, disturb

24、ances (such as moisture, vibration, impact,etc.) that could occur in transit. Expedited delivery will help toensure that moisture content changes are minimized.NOTE 3These packaging procedures were developed under the as-sumption that the area from which specimens are obtained is at least 75mm from

25、the edges of the sample.6. Keywords6.1 GCL; geosynthetic clay liner; sampleASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity

26、 of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments

27、 are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not

28、received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).D 60722