ASTM D6162-2000a Standard Specification for Styrene Butadiene Styrene (SBS) Modified Bituminous Sheet Materials Using a Combination of Polyester and Glass Fiber Reinforcements《用聚合物.pdf

1、Designation: D 6162 00aStandard Specification forStyrene Butadiene Styrene (SBS) Modified BituminousSheet Materials Using a Combination of Polyester and GlassFiber Reinforcements1This standard is issued under the fixed designation D 6162; the number immediately following the designation indicates th

2、e year oforiginal adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers prefabricated modified

3、bitumi-nous sheet materials reinforced with a combination of polyesterfabric and glass fiber, with or without granules, which usestyrene butadiene styrene (SBS) thermoplastic elastomer as theprimary modifier and are intended for use in the fabrication ofmultiple ply roofing and waterproofing membran

4、es.1.2 This specification is intended as a material specificationonly. Issues regarding the suitability of the specific roofconstructions or application techniques are beyond this scope.1.3 The specified tests and property limits used to charac-terize the sheet materials are intended to establish mi

5、nimumproperties. In-place roof system design criteria such as fireresistance, field strength, impact/puncture resistance, materialcompatibility, uplift resistance, and others, are factors beyondthe scope of this material specification.1.4 The values stated in SI units are to be regarded as thestanda

6、rd. The values given in parentheses are for informationonly.2. Referenced Documents2.1 ASTM Standards:D 1079 Terminology Relating to Roofing, Waterproofing,and Bituminous Materials2D 5147 Test Methods for Sampling and Testing ModifiedBituminous Sheet Materials Used in Roofing and Water-proofing23. T

7、erminology3.1 Definitions For definitions of terms used in thisspecification, refer to Terminology D 1079:3.1.1 elongation at 5 % of maximum load, nthe elonga-tion measured on the load-elongation curve at which point theload has dropped to 5 % of its maximum value.4. Classifications4.1 Modified bitu

8、minous sheet materials reinforced with acombination of polyester fabric and glass fiber reinforcement,Type I, Type II and Type III are covered by this specification.4.2 The following grades are used to describe the materialsurfacing:4.2.1 Grade GGranule surfaced.4.2.2 Grade SSmooth surfaced.5. Mater

9、ial and Manufacture5.1 In the process of manufacture, the reinforcement issaturated with asphalt or modified asphalt and is impregnatedand coated on both sides with an SBS modified bituminouscoating. The SBS modified bituminous coating shall be per-mitted to be compounded with a mineral stabilizer.5

10、.2 The Grade G sheet is surfaced on the weather side withmineral granules, except for any selvage. To prevent sticking inthe roll, the reverse side and any selvage shall be permitted tobe covered with a mineral or any other surfacing that will notinterfere with adhesion or bonding of the lap during

11、applica-tion.5.3 Sheet material intended for application by heat welding(torching) shall meet the minimum bottom coating requirementfound in Table 1.6. Physical Properties6.1 The sheet shall conform to the minimum physicalproperties prescribed in Table 2.6.2 The finished product shall not crack nor

12、be so sticky asto cause tearing or other material damage upon being unrolledat any product temperature between 4 and 60C (40 and140F).7. Dimensions, Mass, and Permissible Variations7.1 The finished product shall conform to the followingdimensions and variations:7.1.1 The width of the roll shall be a

13、s agreed between thepurchaser and the seller and shall not vary more than 1 %.7.1.2 The area of the roll shall be no less than as agreedbetween the purchaser and the seller.7.1.3 The selvage width shall be within 6.4 mm ( in.) ofthe nominal selvage width and shall be not less than 76.2 mm1This speci

14、fication is under the jurisdiction of ASTM Committee D08 onRoofing, Waterproofing, and Bituminous Materials and is the direct responsibility ofSubcommittee D08.04 on Felts and Fabrics.Current edition approved June 10, 2000. Published August 2000. Originallypublished as D 616297. Last previous editio

15、n D 616200.2Annual Book of ASTM Standards, Vol 04.04.1Copyright ASTM, 100 Barr Harbor Drive, West Conshohocken, PA 19428-2959, United States.(3 in.) in width without a laying line and 63.5 mm (2.5 in.) inwidth if the sheet has a laying line. If a laying line is provided,the line must not be less tha

16、n 76.2 mm (3 in.) from the edge ofthe sheet.7.2 The mass and thickness of the finished product shall beas prescribed in Table 1.8. Workmanship, Finish and Appearance8.1 The finished product shall be coated completely in acontinuous, unbroken film and shall be free of such defects asholes, tears, cra

17、cks, wrinkles or permanent deformations,TABLE 1 Dimensions and Masses of SBS Modified Bituminous Sheet Materials Using a Combination of Polyester and Glass FiberReinforcementsDescription Type I Type II Type IIIThickness, min, mm (mils),Grade S 1.8 (70) 2.0 (80) 2.0 (80)Grade G 2.8 (110) 3.3 (130) 3.

18、5 (135)Net mass per unit area, min.,g/m2, (lbs/100 ft2)Grade S 2197 (45) 2441 (50) 2685 (55)Grade G 2929 (60) 3661 (75) 4150 (85)Bottom coating thickness, heat weldingapplication products, min, mm (mils)Grade S 1.0 (40) 1.0 (40) 1.0 (40)Grade G 1.0 (40) 1.0 (40) 1.0 (40)TABLE 2 Physical Properties o

19、f SBS Modified Bituminous Sheet Materials Using a Combination of Polyester and Glass FiberReinforcementsAPropertyType IGrade: G and SType IIGrade: G and SType IIIGrade: G and SMaximum load at 18 6 2C(0 6 3.6F), MD and XMD, min,before and after heat conditioning,kN/m (lbf/in.) 13.1 (75) 21.9 (125) 44

20、 (250)Elongation at 18 6 2C(0 6 3.6F), MD and XMD, min,at maximum load, before and afterheat conditioning, (%) 1 2 2Maximum load at 23 6 2C( 73.4 6 3.6F), MD and XMD, min,before and after heat conditioning,kN/m (lbf/in.) 13.1 (75) 14 (80) 44 (250)Elongation at 23 6 2C(73.4 6 3.6F), MD and XMD, min,a

21、t maximum load, before and afterheat conditioning, (%) 2 4 3Elongation at5%ofmaximum load23 6 2C (73.4 6 3.6F), MDand XMD, min, (%)as manufactured: 26 75 3after heat conditioning: 9 30 3Tear strength at 23 6 2C(73.4 6 3.6F), min, N (lbf) 289 (65) 400 (90) 1245 (280)Low temperature flexibility, max,b

22、efore and after heat conditioning,C (F) 18 (0) 18 (0) 18 (0)Dimensional stability, max (%) 0.5 0.5 0.5Compound stability at107C (225F) no failures no failures . . .Compound stability at91C (195F) . . . . . . no failuresGranule embedment, max, (g)(Grade G only) 2 2 2AThe properties in this table are

23、“as manufactured” unless otherwise noted.D 61622blisters, ragged or untrue edges, and areas of uncoated rein-forcement.8.2 The surface of the weather side shall be uniform infinish and texture.8.3 For Grade G material, the mineral granules shall bedistributed uniformly over the entire surface in an

24、even layerexcluding any selvage, shall be embedded firmly in the SBSmodified bituminous coating, and the line of demarcationbetween the granule-surfaced portion of the weather side andany selvage shall be straight and parallel to the edges of thesheet.8.4 When unrolled on a smooth plane, the sheet s

25、hall bestraight and true so that the lap will mate with the adjacentsheet within the tolerance for the lap without wrinkles, buckles,or fishmouths.9. Sampling and Test Methods9.1 Sample the material and determine the properties de-scribed in this specification in accordance with Test MethodsD 5147,

26、unless otherwise indicated.9.2 Elongation at 5 % of Maximum LoadSample thematerial and determine the elongation at 23 6 2C (73.4 63.6F) in accordance with Test Methods D 5147(Section 6) andas defined in 3.1.1.10. Inspection10.1 InspectionInspection shall be in accordance with therequirements of this

27、 specification.10.2 Inspection AlternativesAlternative inspection re-quirements shall be determined by and as agreed upon betweenthe purchaser and supplier.11. Rejection and Resubmittal11.1 Failure to ConformFailure to conform to any of therequirements as stated in this specification constitutes gro

28、undsfor rejection.11.2 Rejection RedressThe supplier shall have the right toinspect the rejected materials. The supplier and the purchasershall agree to the quantity of rolls deemed unacceptable. Thesupplier shall then have the right to submit the same number ofnew rolls as replacement.12. Packaging

29、 and Package Marking12.1 The finished material shall be furnished as rolls. Therolls shall be wrapped securely to prevent shifting of materialand to permit normal handling. If a roll contains a manufac-turing splice, the splice shall be marked clearly; no roll shallcontain more than one splice or tw

30、o pieces.12.2 Unless otherwise agreed upon by the supplier andpurchaser, each product package shall be marked plainly withthe suppliers name, the product name, the ASTM designationincluding type and grade, the net coverage, and the type ofbitumen, if not evident in the label name of the product.13.

31、Keywords13.1 glass fiber reinforcement; modified bituminous sheet;polyester reinforcement; styrene butadiene styrene (SBS);thermoplastic elastomerThe American Society for Testing and Materials takes no position respecting the validity of any patent rights asserted in connectionwith any item mentione

32、d in this standard. Users of this standard are expressly advised that determination of the validity of any suchpatent rights, and the risk of infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and

33、 must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM Headquarters. Your comments will receive careful consideration at a meeting of the responsib

34、letechnical committee, which you may attend. If you feel that your comments have not received a fair hearing you should make yourviews known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the above address or at610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website (www.astm.org).D 61623