ASTM D6887-2003e1 Standard Test Method for Testing Alkyd Compatibility with Resin or Resin Solutions《测定醇酸与树脂或与树脂溶液兼容性的标准试验方法》.pdf

1、Designation: D 6887 03e1Standard Test Method forTesting Alkyd Compatibility with Resin or Resin Solutions1This standard is issued under the fixed designation D 6887; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last

2、revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.e1NOTEResearch report was added editorially in September 2004.1. Scope1.1 This test method covers the procedure for determiningthe deg

3、ree of compatibility of an alkyd with a specific resin orresin solution.1.2 The most common use of this method is to test alkydcompatibility with a hydrocarbon resin or a solution of theresin in an aliphatic solvent, for lithographic ink vehicleapplications.1.3 This standard does not purport to addr

4、ess all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2D 6038 Test Me

5、thod for Determining the Compatibility ofResin/Solvent Mixtures by Precipitation Temperature3. Terminology3.1 Definitions:3.1.1 compatibility, nresin and solvent mixture forms aclear, homogenous, and stable solution. D 60383.1.2 incompatibility, nresin and solvent mixture does notform a clear, homog

6、enous, and stable solution.4. Summary of Test Method4.1 The required resin to alkyd ratio is mixed into a 150-mLbeaker and heated to 160C until clear and homogenous.4.2 The solution is placed into pre-labeled jars and cooled.4.3 Degree of compatibility is reported at 30 min and 24 hafter cooling to

7、room temperature.5. Significance and Use5.1 Incompatibility of the system can lead to loss of gloss,decreased color strength, rheological problems and grind issuesin the flush or pigment base.5.2 This method is used in the lithographic industry, espe-cially in pigment wetting applications, where the

8、 alkyd may ormay not be totally compatible with the resin selected for theapplication.6. Apparatus6.1 Beakers, 150 mL (4).6.2 Jars, with lids, 4 oz (4).6.3 Balance, capacity of at least 200 g, accurate to 60.1 g.6.4 Hot Plate, capable of heating to a minimum of 200C.6.5 Thermometer, 0 to 200C, 61C.6

9、.6 Spatula, or stirrer rods.7. Test Samples7.1 Alkyd to be tested.7.2 Resin or resin solution.8. Procedure8.1 Label each jar and beaker with the resin, alkyd and ratiobeing tested.8.2 Weigh into the beaker the following materials:MaterialRatio2:1 3:1 4:1 5:1Resin/Resin Solution 16.0 g 18.0 g 20.0 g

10、20.0 gAlkyd 8.0 g 6.0 g 5.0 g 4.0 g8.3 Place the beakers on the hot plate and heat to 160C. Stirwith spatula or stir rod until clear.8.4 Pour the blend from each beaker into the appropriatelylabeled jar then cool to room temperature.8.5 Wait 30 min then visually observe degree of clarity ofeach test

11、 sample.NOTE 1Some applications may require a longer waiting time such as24 h. If this is the case, record compatibility of the solution after 24 h.1This test method is under the jurisdiction of ASTM Committee D01 on Paintand Related Coatings, Materials, and Applications and is the direct responsibi

12、lity ofSubcommittee D01.37 on Ink Vehicles.Current edition approved March 10, 2003. Published May 2003.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards

13、 Document Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.9. Report9.1 Report the highest ratio where the blend remained clearafter 30 min or 24 h (time should be agreed upon by user of thistest method

14、 and application).9.2 If the mixtures are clear at all ratios tested, then the resincan be considered compatible to the highest ratio tested.10. Precision and Bias310.1 An inter-laboratory study was conducted in which sixlaboratories tested the compatibility of two hydrocarbon resinswith two alkyds.

15、 All laboratories agreed on the compatibility/incompatibility of each hydrocarbon resin with each alkyd.However, since the test is non-quantitative, it is not possible tocompute repeatability, reproducibility or bias.11. Keywords11.1 aliphatic solvent; alkyd; compatibility; hydrocarbonresin; lithogr

16、aphic ink; pigment wetting; resin solutionsASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and

17、the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision

18、 of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shou

19、ldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtai

20、ned by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).3Supporting data have been filed at ASTM International Headquarters and maybe obtained by requesting Research Report RR: D011128.D688703e12