ASTM D7452-2008 952 Standard Test Method for Evaluation of the Load Carrying Properties of Lubricants Used for Final Drive Axles Under Conditions of High Speed and Shock Loading.pdf

1、Designation: D 7452 08An American National StandardStandard Test Method forEvaluation of the Load Carrying Properties of LubricantsUsed for Final Drive Axles, Under Conditions of High Speedand Shock Loading1This standard is issued under the fixed designation D 7452; the number immediately following

2、the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This test method cover

3、s the determination of the anti-scoring properties of final drive axle lubricating oils whensubjected to high-speed and shock conditions. This test methodis commonly referred to as the L-42 test.21.2 The values stated in foot-pound units are to be regardedas standard. For example, torque is stated i

4、n foot-pound units,the values for temperature are stated in degrees Fahrenheit, andthe test lubricant sample volume is stated in pints. The valuesgiven in parentheses are mathematical conversions to SI unitsthat are provided for information purposes only, and are notconsidered standard. SI units are

5、 provided for all parametersexcept where there is no direct equivalent such as the units forscrew threads, national pipe threads/diameters, and tubing size.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of

6、 this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use. Specific warninginformation is given in Sections 4 and 7.2. Referenced Documents2.1 ASTM Standards:3D 235 Specification for Mineral Spirits (Petroleum Spirits

7、)(Hydrocarbon Dry Cleaning Solvent)E29 Practice for Using Significant Digits in Test Data toDetermine Conformance with Specifications2.2 Society of Automotive Engineers Standards:4SAE J308 Information Report on Axle and Manual Trans-mission LubricantsSAE J2360 Lubricating Oil, Gear Multipurpose (Met

8、ric)Military Use3. Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 coast side, nthe convex side of the pinion and theconcave side of the ring gear which are in contact duringdeceleration in a forward gear. CRC Manual 2153.1.2 drive side, nthe concave side of the pinion and thecon

9、vex side of the ring gear which are in contact duringacceleration in a forward gear. CRC Manual 2153.1.3 scoring, non the ring and the pinion gear teeth, thedisplacement of metal by local momentary welding from thegear tooth, resulting in the development of a matt, or frosteddull surface. CRC Manual

10、 2154. Summary of Test Method4.1 Charge a specially prepared light duty hypoid rear axle(Dana Model 44 ASTM Part No. 044AA100-1)6with thelubricant sample to be tested (see 10.1). Mount the axlebetween two load absorbing dynamometers which are drivenwith a V-8 gasoline engine through a manual transmi

11、ssion.4.2 Condition the test axle with light loads at differentspeed, torque and temperature conditions on both the drive andcoast sides of the gears. (WarningHigh-speed rotatingequipment, electrical shock, high-temperature surfaces.) Afterconditioning, subject the test axle to high speed and shockl

12、oadings at higher temperatures.4.3 Rate the drive and coast side of the pinion and ring gearsat the end of test (EOT) for scoring distress.5. Significance and Use5.1 Final drive axles are often subjected to severe servicewhere they encounter high speed shock load conditions,characterized by sudden a

13、ccelerations and decelerations. Thissevere service can lead to scoring distress on the ring gear and1This test method is under the jurisdiction of ASTM Committee D02 onPetroleum Products and Lubricants and is the direct responsibility of SubcommitteeD02.B0.10 on Standards Acceleration.Current editio

14、n approved May 1, 2008. Published June 2008.2Until the next revision of this test method, the ASTM Test Monitoring Center(TMC) will update changes in this test method by means of information letters.Information letters may be obtained from the ASTM Test Monitoring Center, 6555Penn Avenue, Pittsburgh

15、, PA 15206, Attention: Administrator. The TMC is also asource of reference oils.3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page

16、onthe ASTM website.4Available from Society of Automotive Engineers (SAE), 400 CommonwealthDr., Warrendale, PA 15096-0001, http:/www.sae.org.5CRC Rating Manual, No. 21, Coordinating Research Council, Atlanta, GA.6Parts and Model 44 Maintenance Manual available from Dana Corporation,P.O. Box 2424, For

17、t Wayne, IN 46801.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.pinion surface. This test method measures anti-scoring prop-erties of final drive lubricants.5.2 This test method is used or referred to in the followingdocuments:5.2.

18、1 American Petroleum Institute (API) Publication1560.75.2.2 SAE J308 and SAE J2360.6. Apparatus6.1 This test method provides a description of essentialapparatus features, including mandatory equipment type andperformance specifications where established.6.2 Test AxleThe test unit consists of a Dana

19、model 44rear axle, 45 to 11 (4.09) ratio, and uncoated gears. (DanaASTM part number 044AA100-1.6See 10.1.)6.3 Cover PlateModify the rear cover plate of the test unitto provide an inspection port and thermocouple fitting. Locatethe thermocouple fitting by using the locating fixture shown inFig. A2.1.

20、 An optional14 in. NPT (National Pipe Thread) drainfitting may be added.6.4 Axle Shaft AssembleUse a Ford Axle shaft assembly,(Dana Part No. 26762-14X6) or equivalent with this testmethod.6.5 Hinge Plate Stand AssemblyMount and secure the testunit in place on the hinge plate assembly, see Figs. A2.6

21、-A2.9.6.6 Temperature Control SystemThe temperature controlapparatus consists of a thermocouple, a temperature recordingsystem, temperature controller and a cooling system that is ableto maintain lubricant temperature at specified conditions.6.6.1 ThermocoupleInstall the thermocouple such that theth

22、ermocouple tip is flush with the cover plate lip by placing thecover plate face on a flat surface and inserting the thermo-couple into the cover plate until the thermocouple tip is flushwith the flat surface. For recording and control of the testlubricant temperature, use a18-in. (3.2-mm) diameter J

23、 or Ktype closed tip style thermocouple.6.6.2 Temperature Recording SystemThroughout the test,ensure the temperature recording system records the tempera-ture of the test oil at a minimum frequency of 1 Hz.6.6.3 Temperature ControllerProportional-Integral-Derivative (PID) type; percent output adjust

24、able.6.6.4 Axle CoolingUse three spray nozzles to distributewater over the cover plate and axle housing as shown in Fig.A2.2. Actuate the water control valve by the temperature PIDcontrol system.6.6.4.1 Depending on how the system is plumbed, use spraynozzles in any combination of the following part

25、 numbers:Straight Male NPT (Part No. 3/8GG-SS22), 90 Male NPT(Part No. 3/8GGA-SS22), Straight Female NPT (Part No.3/8G-SS22), and 90 Female NPT (Part No. 3/8GA-SS22).8,96.6.4.2 Use a single control valve to control the coolingwater supply. The control shall be a12 in. (12.7 mm) two-way,C linear trim

26、, air to close, Research Control valve. Use a singlePID loop to maintain the axle lubricant temperature control forboth the Standard and Canadian version test. A separate PIDloop control for each version is not permitted. See Annex A1.6.6.4.3 Use only38 or12 in. line material to the spraynozzles.6.6

27、.4.4 Use a minimum supply water pressure of 25 psig(172 kPa) to the control valve.6.6.4.5 Use an axle containment box as shown in Fig.A2.10. The purpose is to contain water.6.6.4.6 Use a locating pin or stop block as an indexingdevice to ensure that all subsequent axle installations areconsistently

28、installed perpendicular with the axle housingcover to engine and transmission drive-shaft centerline.6.7 Torque MeterInclude in the test equipment a torquemeter installed in the drive shaft (see Figs. A2.3-A2.5)tomeasure the torque applied to the pinion. Install a Himmelsteininline torque meter Mode

29、l numbers MCRT28061T(1-4) orMCRT2661TN(1-4)9,10without a foot mount and a range of10 000 lb-in. (1130 N-m) shall be installed to measure piniontorque. Additional suffix letters only indicate allowable op-tions.6.8 Signal ConditioningUse a Himmelstein Models 701or 711 strain gage conditioner for sign

30、al conditioning. Set thelow pass cut-off frequency at 10 Hz.6.9 Digital Data Acquisition SystemSystem requires ca-pability of measuring a minimum of five channels at samplingfrequencies outlined in Section 10.6.9.1 Do not use hardware or software filtering for thepinion torque channel during data ac

31、quisition periods of thetest.6.10 DynamometersTwo axle dynamometers (MidwestDynamatic, Model 3232)9,11with suitable control equipmentcapable of maintaining specified test conditions.6.11 Engine Speed ControlSystem requires a device tomaintain steady state conditions and also provide adjustablethrott

32、le acceleration and deceleration rates to attain specifiedshock loading torques.6.11.1 Throttle Controller SystemUse a Foxboro/JordanController, Model AD7530.9,12Use a power transformer fromAcme Electric Corp. PN T-1-81058 or equivalent, primaryvolts 120X240, secondary volts 16/32 center tap, 0.500

33、kVA inconjunction with the Foxboro/Jordan Controller.7API Publication 1560, Lubricant Service Designations for Automotive ManualTransmissions, Manual Transaxles, and Axles, American Petroleum Institute,Washington, DC.8The sole source supply of the apparatus known to the committee at this time isSpra

34、y Systems Company, and can be purchased through E. I. Pfaff Company, 3443Edwards Road, Suite D, Cincinnati, OH 45208.9If you are aware of alternative suppliers, please provide this information toASTM International Headquarters. Your comments will receive careful consider-ation at a meeting of the re

35、sponsible technical committee,1which you may attend.10The sole source supply of the apparatus known to the committee at this timeis S. Himmelstein and Company, 2490 Pembroke Avenue, Hoffman Estates, IL60195.11Available from Dyne Systems, P.O. Box 18 W209 N17391 Industrial Drive,Jackson, WI 53037.12A

36、vailable from Fox/Jordan, Inc., 5607 West Douglas Avenue, Milwaukee, WI53218.D74520826.12 Connecting ShaftsUse connecting shafts of equallength 6 1 in. (25.4 mm) and less than 30 in. (762 mm) longfrom flange face to flange face. Use a tubing diameter of 3.5 60.2 in. (88.9 6 5.1 mm) OD, with a wall t

37、hickness of 0.095 60.005 in. (2.41 6 0.13 mm) if tubing is required to fabricate theshafts. Ensure the shafts are dynamically (spin) balanced andstrong enough to handle torques up to 2100 lbf-ft (2847 N-m).Use an operating angle of 0 6 0.5.6.13 Power TrainThe power train consists of a gasolinepowere

38、d V-8 GM performance Ramjet 5.7L marine enginecoupled with a five speed manual transmission capable ofsupplying specified shock loading torques. The engine andtransmission operating angle shall be 0 6 0.5.6.13.1 All recommended replacement parts are availablethrough local General Motors dealers. A l

39、ist of these replace-ment parts are shown in Table 1. Do not make modifications tothe engine that would affect the engines factory displacementor compression ratio.6.14 Drive ShaftWelded steel tubing, 3.5 6 0.2 in. (88.96 0.51 mm) outside diameter, 0.095 6 0.005 in. (2.41 6 0.13mm) wall thickness, 3

40、4.5 6 1 in. (876.3 6 25.4 mm) long fromcenter weld to center weld. (See Figs. A2.3-A2.5.) Dynami-cally (spin) balance the drive shaft and torque meter. Theoperating angle shall be 0 6 0.5.6.14.1 Transmission U-Joint(Spicer 5-178X).136.14.2 Pinion U-Joint(Spicer 5-153X).6.14.3 Flange YokeConnects tra

41、nsmission yoke throughu-joint to drive shaft.6.14.4 Pinion Drive Shaft Slip YokeConnects the driveshaft through the u-joint to the axle yoke.6.14.5 Flange AdaptorManufacture flange adapter tospecifications in Figs. A2.4 and A2.5.6.15 Spring PlateManufacture spring plates to specifica-tion as shown i

42、n Fig. A2.8.6.16 Spring Plate Rod ConnectionMount a rod connect-ing the spring plate to the gear stand using12 in. (0.953 cm)spherical rod ends. See Figs. A2.6 and A2.7.7. Reagents and Materials7.1 Sealing CompoundWhere necessary, use PermatexNo. 2 or equivalent.7.2 Cleaning SolventUse solvent meeti

43、ng ASTM D 235Type II, Class C requirements for Aromatic Content (02%vol), Flash Point (142F/61C, min) and Color (not darker than+25 on Saybolt Scale or 25 on Pt-Co Scale). (WarningHealth hazard, combustible.) Obtain a Certificate of Analysisfor each batch of solvent from the supplier.7.3 Contact Pat

44、tern Marking CompoundWayne MetalWorking Compound # M 99B 111A14or equivalent.7.4 Test OilUse 3.5 pt (1655 cc) of test lubricant.8. Preparation of Apparatus8.1 Cleaning of Reusable HardwareClean as necessarywith cleaning solvent (see 7.2) all reusable parts including:axle shafts, thermocouples, axle

45、housing cover, and all associ-ated drain pans and funnels used for the addition of andcollection of test oil.8.2 Preparation of Axle:8.2.1 Pretest contact pattern procedure (see Annex A6).8.2.2 Record break and turn.8.2.3 Record the backlash reported from the manufacturer.The readings shall be betwe

46、en 0.004 and 0.012 in. (0.102 to0.305 mm).8.2.3.1 Measure and record backlash at four equally spacedlocations. Report the average and the four readings.8.2.4 Proceed to 8.2.9 if contact pattern and backlash areacceptable. Proceed to 8.2.5 if the contact pattern or backlashneeds adjustment.8.2.5 Foll

47、ow Dana Model 44 Maintenance Manual6ifcontact pattern or backlash needs to be adjusted.8.2.6 Assemble the gear unit using Dana Model 44 Main-tenance Manual.6Apply gear contact pattern grease on thedrive and coast side of the ring. Place a 30 6 5 lbf-ft (40.7 66.8 N-m) turning torque on the ring and

48、pinion. Rotate ring andpinion through the gear contact pattern grease on the drive andcoast side.8.2.7 Proceed to 8.2.8 if the contact pattern and backlash areacceptable. If the contact pattern requires further adjustment,repeat 8.2.5 and 8.2.6 until an acceptable pattern is obtained.8.2.8 Measure a

49、nd record backlash at four equally spacedlocations. Report the average and the four readings.8.2.9 Clean the gear with cleaning solvent (see 7.2) whengear contact pattern and backlash are at acceptable levels.8.2.10 CleaningWash the test unit in cleaning solvent (see7.2), paying particular attention to the pinion bearing to removeall preservative oil. Blow dry with clean dry compressed air.8.2.11 Lubricate the carrier bearing, pinion bearings, differ-ential gears, and the ring and pinion gears using the testlubricant.13Available from a