ASTM D7793-2016 7959 Standard Specification for Insulated Vinyl Siding《绝缘乙烯基线的标准规格》.pdf

1、Designation: D7793 16Standard Specification forInsulated Vinyl Siding1This standard is issued under the fixed designation D7793; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number in parentheses ind

2、icates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification establishes requirements for insulatedvinyl siding, which is vinyl siding with integral foam plasticinsulating material, where the vinyl sid

3、ing is manufacturedfrom rigid PVC compound. Compliance with this standardrequires insulated vinyl siding to demonstrate a thermal insu-lation value of R-2.0 or greater. Other performance require-ments and test methods addressed by this standard includematerials properties and dimensions, warp, shrin

4、kage, impactstrength, expansion, appearance, thermal distortion resistance,and windload resistance. Methods of indicating compliancewith this specification are also provided.NOTE 1Insulated vinyl siding is composed of two major components:the vinyl siding and the insulating material. It is intended

5、that the vinylsiding portion comply with Specification D3679. Applicable portions ofSpecification D3679 are included in this specification. Additional require-ments that pertain only to the insulation as a separate material, or to thecombination of vinyl siding and insulation as a whole, are also in

6、cluded.For further explanation, see Appendix X1.1.2 Insulated vinyl siding shall be tested with the insulationmaterial in place or removed, as specified in the applicablerequirement or test method.1.3 The use of PVC recycled plastic in this product shall bein accordance with the requirements in Sect

7、ion 4.1.4 Insulated vinyl siding produced to this specificationshall be installed in accordance with Practice D4756. Refer-ence shall also be made to the manufacturers installationinstructions for the specific product to be installed.1.5 The values stated in inch-pound units are to be regardedas sta

8、ndard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.1.6 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this s

9、tandard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.NOTE 2There is no known ISO equivalent to this standard.2. Referenced Documents2.1 ASTM Standards:2C297/C297M Test Method for Flatwise Tensile Strength ofSandwich Con

10、structionsC578 Specification for Rigid, Cellular Polystyrene ThermalInsulationC591 Specification for Unfaced Preformed Rigid CellularPolyisocyanurateThermal InsulationC1199 Test Method for Measuring the Steady-State ThermalTransmittance of Fenestration Systems Using Hot BoxMethodsC1289 Specification

11、 for Faced Rigid Cellular Polyisocyanu-rate Thermal Insulation BoardC1363 Test Method for Thermal Performance of BuildingMaterials and Envelope Assemblies by Means of a HotBox ApparatusD618 Practice for Conditioning Plastics for TestingD635 Test Method for Rate of Burning and/or Extent andTime of Bu

12、rning of Plastics in a Horizontal PositionD696 Test Method for Coefficient of Linear Thermal Expan-sion of Plastics Between 30C and 30C with a VitreousSilica DilatometerD1042 Test Method for Linear Dimensional Changes ofPlastics Caused by Exposure to Heat and MoistureD1183 Practices for Resistance o

13、f Adhesives to CyclicLaboratory Aging ConditionsD1435 Practice for Outdoor Weathering of PlasticsD2244 Practice for Calculation of Color Tolerances andColor Differences from Instrumentally Measured ColorCoordinatesD2457 Test Method for Specular Gloss of Plastic Films andSolid PlasticsD3679 Specifica

14、tion for Rigid Poly(Vinyl Chloride) (PVC)SidingD3892 Practice for Packaging/Packing of PlasticsD4226 Test Methods for Impact Resistance of Rigid Poly-(Vinyl Chloride) (PVC) Building Products1This specification is under the jurisdiction of ASTM Committee D20 onPlastics and is the direct responsibilit

15、y of Subcommittee D20.24 on Plastic BuildingProducts.Current edition approved Nov. 1, 2016. Published November 2016. Originallyapproved in 2012. Last previous edition approved in 2013 as D7793 - 13.DOI:10.1520/D7793-16.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact A

16、STM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Consho

17、hocken, PA 19428-2959. United States1D4756 Practice for Installation of Rigid Poly(Vinyl Chlo-ride) (PVC) Siding and SoffitD5206 Test Method for Windload Resistance of Rigid Plas-tic SidingD5947 Test Methods for Physical Dimensions of SolidPlastics SpecimensD7209 Guide for Waste Reduction, Resource

18、Recovery, andUse of Recycled Polymeric Materials and Products (With-drawn 2015)3D7445 Specification for Rigid Poly(Vinyl Chloride) (PVC)Siding with Foam Plastic Backing (Backed Vinyl Siding)E84 Test Method for Surface Burning Characteristics ofBuilding MaterialsE1753 Practice for Use of Qualitative

19、Chemical Spot TestKits for Detection of Lead in Dry Paint FilmsG147 Practice for Conditioning and Handling of Nonmetal-lic Materials for Natural and Artificial Weathering Tests2.2 American Society of Civil Engineers (ASCE):4ASCE 7-02 Minimum Design Loads for Buildings and OtherStructures2.3 Internat

20、ional Code CouncilEvaluation Services (ICC-ES):AC05 Acceptance Criteria for Sandwich Panel Adhesives2.4 International Standards Organization (ISO):ISO/IEC Guide 65 General requirements for bodies operat-ing product certification systems2.5 Federal Standards:16 CFR Part 460 Labeling and Advertising o

21、f Home Insu-lation3. Terminology3.1 Definitions:3.1.1 center-pinningan installation technique in which thesiding panel is fastened tightly through the nail slot at thecenter length of the panel, in order to cause thermal expansionand contraction to occur equally in both directions from thecenter.3.1

22、.2 cohesive failurein the context of tensile testing,internal separation of the adhesive within the adhesive layer,resulting in attachment of adhesive material to the surface ofboth substrates3.1.3 insulation; insulating materialfoam plastic materialthat is combined at the factory with a vinyl sidin

23、g profile toform insulated vinyl siding.3.1.4 insulated vinyl sidinga vinyl cladding product soldwith manufacturer-installed foam plastic insulating material asan integral part of the cladding product. The vinyl claddingportion of insulated vinyl siding meets the definition of vinylsiding.3.1.5 nomi

24、nalthe value that a manufacturer consistentlyuses to represent a specific property or dimension of a vinylsiding product in public claims including, but not limited to,product literature, advertisements, quotations, and certificatesof conformance.3.1.6 process average thicknessthe rolling, arithmeti

25、cmean of average specimen thicknesses measured in accordancewith 6.5 for a specific product during all productions runs forthe most recent six-month period.3.1.7 vertical coverageThe net vertical distance of thewall covered by a single insulated vinyl siding panel, disre-garding any portions of the

26、panel that are overlapped byadjacent panels above or below.3.1.8 temperate northern climatein weather testing, aNorth American metropolitan area testing site located within73 to 100W longitude and 37 to 45N latitude.3.1.9 vinyl sidinga shaped material, made principallyfrom rigid poly(vinyl chloride)

27、 (PVC), that is used to cladexterior walls of buildings. In this standard, vinyl siding refersto the rigid profile to which the insulation is attached.4. Materials and Manufacture4.1 Vinyl Siding:4.1.1 The vinyl siding, exclusive of foam plastic insulatingmaterial, shall be made of one or more layer

28、s of poly(vinylchloride) (PVC) compound. Any layers of materials other thanpoly (vinyl chloride) (PVC) compound shall be kept to lessthan 20 % by volume. This limitation does not apply to theinsulation material.4.1.2 Where rigid PVC recycled plastic as defined in GuideD7209 is used, the vinyl siding

29、 containing the PVC recycledplastic shall meet all of the requirements of Sections 3, 4, and5.4.1.3 The vinyl siding material, exclusive of insulationmaterial, when tested in accordance with Test Method D635,shall not exceed an average extent of burn of 4 in. (100 mm),with an average time of burn no

30、t to exceed 10 seconds. Aminimum sample thickness of 0.035 in. (0.9 mm) is required.(WarningThe flammability testing data, conclusions, andrecommendations of Test Method D635 relate solely to themeasurement and description of properties for classification ofthe vinyl siding material in response to f

31、lame under controlledlaboratory conditions and shall not be used for the descriptionor appraisal of the fire hazard of vinyl siding under actual fireconditions.)4.2 Foam Plastic Insulation:4.2.1 The foam plastic insulation shall be made of one of thefollowing materials:4.2.1.1 Expanded polystyrene c

32、omplying with SpecificationC578.4.2.1.2 Extruded polystyrene complying with SpecificationC5784.2.1.3 Polyisocyanurate complying with SpecificationC591 or Specification C12894.2.2 The foam plastic insulation shall have a Flame SpreadIndex not greater than 75 and a Smoke Developed Index notgreater tha

33、n 450 when tested separately under Test MethodE84.4.3 Adhesives:3The last approved version of this historical standard is referenced onwww.astm.org.4Available from American Society of Civil Engineers (ASCE), 1801 AlexanderBell Dr., Reston, VA 20191, http:/www.asce.org.D7793 1624.3.1 The suitability

34、for outdoor use of an adhesive used tobond the vinyl siding and the insulation, if any, shall bedetermined by the following procedure.4.3.1.1 Prepare a minimum of 10 specimens consisting oftwo Douglas fir-larch blocks or other appropriate substrates,bonded by the adhesive, in accordance with Test Me

35、thodC297/C297M. Each block is to be 2.0 inches square. Theadhesive shall be applied and cured in accordance with theadhesive manufacturers instructions.(1) The material selected for use as the substrate shall becapable of withstanding the accelerated aging described in4.3.1.2 without damage or deter

36、ioration of the substrate.NOTE 3Other appropriate substrates, such as metal or plastic, com-patible with the adhesive according to the manufacturers guidelines, canbe used in place of the Douglas fir-larch blocks. Because in accordancewith 4.3.1.4.1 at least 75 % of samples must fail in a cohesive m

37、ode, asubstrate should be selected that is expected to be stronger than theadhesive and which will form a tight bond with the adhesive.4.3.1.2 Subject 50 percent of the specimens to acceleratedaging under Test Method D1183, Test Condition C, for threecycles.The low-temperature portion of the cycle i

38、s not requiredto be colder than -40F (-40C) and the relative humidityduring this portion of the cycle shall not be greater than 10 %RH.4.3.1.3 Condition and test all of the specimens in accor-dance with Test Method C297/C297M.4.3.1.4 Acceptable PerformanceAcceptable performanceof the adhesive is dem

39、onstrated by one of the following means:(1) When tested in accordance with 4.3.1.3, the samplesdemonstrate performance in accordance with either (a), (b), or(c).(a) For a valid test, the mode of failure for no fewer than75 % of the specimens shall be cohesive. Only specimens thatfailed cohesively ar

40、e counted in the following. The averageultimate tensile strength of the samples that were subjected toaccelerated aging shall not be less than 80 % of the averageultimate tensile strength of the specimens that were subjectedto conditioning only.(b) None of five aged specimens fails cohesively under

41、atensile load less than or equal to 100 psi at a pull rate(crosshead speed) of 0.02 in./min. Only specimens that failcohesively or do not fail are counted. Specimens that failnon-cohesively under a load at or below 100 psi are discardedand another specimen is tested until five specimens have eitherf

42、ailed cohesively, or have not failed at or below 100 psi.Adhesives qualified under this method are limited to use withfoam insulation having a tensile strength not greater than 100psi.(c) The following applies when the average elongation atyield of the specimens that were subjected to conditioning o

43、nlyis 200 % or greater: the average stress of the aged specimens isnot less than 80 percent of that of the specimens that weresubjected to conditioning only, when measured at an elonga-tion 75 % of the elongation at yield for each specimen.(2) As an alternative, adhesives that are covered by acurren

44、t report, issued by an agency accredited under ISO Guide65, as a Type I, Class 2 adhesive in accordance with Accep-tance Criteria AC05, will have exhibited acceptable perfor-mance under the above procedure.NOTE 4Compatibility of the adhesive with the vinyl siding andinsulation used in the insulated

45、vinyl siding is evaluated separately, under5.2.4.4.4 Insulated Vinyl Siding:4.4.1 Insulated vinyl siding shall not contain elemental lead(Pb) or compounds of that material other than traces incidentalto raw materials or the manufacturing process. This limitationapplies to both PVC substrate and to a

46、ny cap or film material,as well as the insulation material. Compliance with thisrequirement shall be demonstrated by one of the methods in6.16.5. Physical Requirements5.1 Requirements Applicable to Vinyl SidingThe provi-sions of 5.1.1 5.1.8 apply only to the vinyl siding, exclusiveof any insulation

47、material. Where necessary to perform testing,the insulation material shall be removed.5.1.1 Length and WidthThe nominal length and width ofthe vinyl siding shall be as agreed upon between the purchaserand the seller.The actual length shall not be less than14 in. (6.4mm) of the nominal length and the

48、 actual width shall be within6116 in. (1.6 mm) of the nominal width when measured inaccordance with 6.3 and 6.4.5.1.2 ThicknessThese requirements pertain only to mea-surements of the portions of the vinyl siding that are exposedafter installation of the panel, measured in accordance with theprocedur

49、e in 6.5. The average thickness of each specimen shallbe no less than 0.035 in. No individual measurement shall bethinner than 0.003 in. below the nominal thickness. Theprocess average thickness as defined in 3.1.6 shall be nothinner than 0.001 in. below the nominal thickness.5.1.3 CamberAfull length of vinyl siding (typically 10 or12 ft (3.05 or 3.61 m) shall not have a camber greater than18in. (3.2 mm) when measured in accordance with 6.6.5.1.4 Heat ShrinkageThe average heat shrinkage shall notexceed 3.0 % when determined by the method described