1、Designation: E81 96 (Reapproved 2017)Standard Test Method forPreparing Quantitative Pole Figures1This standard is issued under the fixed designation E81; the number immediately following the designation indicates the year of originaladoption or, in the case of revision, the year of last revision.Anu
2、mber in parentheses indicates the year of last reapproval.Asuperscriptepsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This test method covers the use of the X-ray diffracto-meter to prepare quantitative pole figures.1.2 The test method consists of several e
3、xperimental proce-dures. Some of the procedures (1-5)2permit preparation of acomplete pole figure. Others must be used in combination toproduce a complete pole figure.1.3 Pole figures (6) and inverse pole figures (7-10) are twodimensional averages of the three-dimensional crystallite ori-entation di
4、stribution. Pole figures may be used to constructeither inverse pole figures (11-13) or the crystallite orientationdistribution (14-21). Development of series expansions of thecrystallite orientation distribution from reflection pole figures(22, 23) makes it possible to obtain a series expansion of
5、acomplete pole figure from several incomplete pole figures. Polefigures or inverse pole figures derived by such methods shall betermed calculated. These techniques will not be describedherein.1.4 Provided the orientation is homogeneous through thethickness of the sheet, certain procedures (1-3) may
6、be used toobtain a complete pole figure.1.5 Provided the orientation has mirror symmetry withrespect to planes perpendicular to the rolling, transverse, andnormal directions, certain procedures (4, 5, 24) may be used toobtain a complete pole figure.1.6 The test method emphasizes the Schulz reflectio
7、n tech-nique (25). Other techniques (3, 4, 5, 24) may be consideredvariants of the Schulz technique and are cited as options, butnot described herein.1.7 The test method also includes a description of thetransmission technique of Decker, et al (26), which may beused in conjunction with the Schulz re
8、flection technique toobtain a complete pole figure.1.8 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of
9、regulatory limitations prior to use.1.9 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recom-mendations issued by the World Tra
10、de Organization TechnicalBarriers to Trade (TBT) Committee.2. Summary of Test Method2.1 The test method consists of characterizing the distribu-tion of orientations of selected lattice planes with respect tosample-fixed coordinates (6). The distribution will usually beobtained by measurement of the
11、intensity of X rays diffractedby the sample. In such measurements the detector and associ-ated limiting slits are fixed at twice the appropriate Braggangle, and the diffracted intensity is recorded as the orientationof the sample is changed (1-6, 25, 26, 27). After the measureddata have been correct
12、ed, as necessary, for background,defocusing, and absorption, and normalized to have an averagevalue of unity, the results may be plotted in stereographic orequal-area projection.2.2 The geometry of the Schulz (25) reflection method isillustrated in Fig. 1. Goniometers employing this geometry arecomm
13、ercially available. The source of X rays is indicated by L.Slit S1 limits divergence of the incident beam in the plane ofprojection. Slit S2 limits divergence perpendicular to the planeof projection. The sample, indicated by crosshatching, may betilted about the axis FF, which is perpendicular to th
14、ediffractometer axis and lies in the plane of the sample. The tiltangle was denoted by Schulz (25). The sample positionshown in Fig. 1 corresponds to = 0 deg, for which approxi-mate parafocusing conditions exist at the detector slit, S3. Withthe application of a defocusing correction, this method is
15、 usefulover a range of colatitude from 0 deg to approximately 75deg.2.2.1 Tilting the sample about FF , so as to reduce thedistance between L and points in the sample surface above theplane of projection, causes X rays diffracted from these pointsto be displaced to the left of the center of S3, whil
16、e X raysdiffracted from points in the sample surface below the plane of1This test method is under the jurisdiction of ASTM Committee E04 onMetallography and is the direct responsibility of Subcommittee E04.11 on X-Rayand Electron Metallography.Current edition approved June 1, 2017. Published June 20
17、17. Originallyapproved in 1949. Last previous edition approved in 2011 as E81 96 (2011). DOI:10.1520/E0081-96R17.2The boldface numbers in parentheses refer to the list of references at the end ofthis test method.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA
18、19428-2959. United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recommendations issued by the World Trade Organization Te
19、chnical Barriers to Trade (TBT) Committee.1projection are displaced to the right of the center of S3. Thedisplacement is equal to 2D tan cos , where D is the distanceabove or below the plane of projection. The integrated, or total,diffracted intensity is influenced only slightly by tilting thesample
20、 (28). Insofar as possible, the detector slit shall be ofsufficient width to include the defocused line profile corre-sponding to the maximum sample tilt for which measurementsare to be made. Because of interferences from neighboringdiffraction peaks and physical limitations on sample size anddetect
21、or slit width, it is necessary to limit vertical divergence ofthe incident beam. A widely used pole figure goniometer witha focal spot to the center of the sample distance of 172 mmemploys a 0.5-mm slit located 30 mm from the center of thesample for this purpose. Measured intensities may be correcte
22、dfor defocusing by comparison with intensities diffracted by arandomly oriented specimen of similar material, or byemploy-ing the theoretically calculated corrections (28).2.3 The geometry of the transmission technique of Decker,et al (26) is shown in Fig. 2. In contrast to the reflectionmethod, X r
23、ays diffracted from different points in the samplediverge, making the resolution of adjacent peaks more difficult.The ratio of the diffracted intensity at = 5, 10, , 70 deg,to the diffracted intensity at = 0 deg, calculated in accordancewith the expression given by Decker, et al (26) for linearabsor
24、ption thickness product, t, = 1.0, 1.4, , 3.0, and, for = 5, 10, , 25 deg is given in Table 1. These data may beused as a guide to determine the useful range of for a givent and . If, for example, I/I0is restricted to values 0.5, onearrives at the series of curves shown in Fig. 3.3. Significance and
25、 Use3.1 Pole figures are two-dimensional graphicrepresentations, on polar coordinate paper, of the averagedistribution of crystallite orientations in three dimensions. Datafor constructing pole figures are obtained with X-raydiffractometers, using reflection and transmission techniques.3.2 Several a
26、lternative procedures may be used. Someproduce complete pole figures. Others yield partial polefigures, which may be combined to produce a complete figure.4. Apparatus4.1 Source of X RaysA beam of characteristic X rays ofsubstantially constant intensity is required. Characteristic Ka-lpha radiation
27、of chromium, iron, cobalt, nickel, copper,molybdenum, and silver have all been used successfully,depending on the chemical composition of the specimen.Insofar as possible, the radiation selected shall provide suffi-cient angular dispersion to permit the resolution of peaks to bemeasured, and shall n
28、ot produce excessive fluorescence in thesample. Linear absorption coefficients (29) for selected ele-ments are given in Table 2. Lower energy radiation (Cr, Fe, Co,Ni, Cu) is generally preferred for reflection pole figure mea-surements as it provides greater angular dispersion. Higherenergy radiatio
29、n (Mo, Ag) is generally preferred for transmis-sion measurements.4.2 SlitsSuitable slits shall be provided to limit horizon-tal(in the plane of projection of Figs. 1 and 2) and vertical(perpendicular to the plane of projection of Figs. 1 and 2)divergence of the incident beam. Horizontal divergences
30、of 1 to3 deg for reflection and 0.5 deg for transmission are typical.Vertical divergences of 0.2 deg for reflection and 1 deg fortransmission are typical. Insofar as possible, the receiving slitshall be of sufficient width to include the diffracted peak.Receiving slits corresponding to 1 deg 2theta
31、are typical.4.3 Specimen HolderReflection Method:4.3.1 The specimen holder for the reflection method shallpreferably employ the Schulz reflection geometry illustrated inFig. 1 and described in 2.2. It is desirable that the specimenholder be equipped with a means for oscillating the sample inthe plan
32、e of its surface without changing the orientation of thesample. It is also desirable that the magnitude of the oscillationbe variable. The specimen holder shall preferably be providedwith automatic means for changing colatitude and longitude ofthe sample.4.3.2 Alternative reflection geometries inclu
33、de those ofBakarian (1), Field and Marchant (27), and Jetter and Borie (2).The method of Bakarian requires machining a number ofcylindrical specimens whose axes are perpendicular to thesheet normal direction. Each specimen provides intensity dataalong one parallel of longitude. The method of Jetter
34、and Borieentails the preparation of a spherical specimen. In the methodsof Bakarian and of Jetter and Borie, the sample shall, insofar aspossible, be prepared from homogeneous material. Thesemethods have the advantage that intensity data need not becorrected for absorption or defocusing. They do not
35、 permitFIG. 1 Geometry of Reflection Method.FIG. 2 Geometry of Transmission Method.E81 96 (2017)2oscillation of the sample. Equipment is not currently commer-cially available for these methods.4.3.3 The method of Field and Marchant (27) requires anabsorption correction. If this method is used in con
36、junctionwith the transmission method of Decker, et al (26),itisnecessary to use either different orders of reflection or differentradiations in order to obtain a complete pole figure.4.4 Specimen HolderTransmission MethodIf the trans-mission method is used, the specimen holder shall employ thegeomet
37、ry of Decker, et al (26), shown in Fig. 2 and describedin 2.3. It is desirable that the specimen holder be equipped witha means for oscillating the sample in the plane of its surfacewithout changing the orientation of the sample. The specimenholder shall preferably be providedwith automatic means fo
38、rchanging colatitude and longitude of the sample.4.5 DetectorThe detector shall preferably be of an energy-dispersive type, for example, a solid state, proportional, orscintillation counter, and used in conjunction with a pulseheight selector circuit to discriminate against X rays whoseenergies diff
39、er markedly from that of the characteristic K-alpharadiation being used. Reduction of the characteristic K-betaradiation requires the use of a monochromator or appropriatebeta filter. Pd, Zr, Ni, Co, Fe, Mn, and V are appropriate betafilters for Ag, Mo, Cu, Ni, Co, Fe, and Cr, respectively.5. Test S
40、pecimens5.1 For the reflection method, the sample shall be ofsufficient thickness that loss of intensity due to transmissionthrough the sample may be ignored. If a maximum loss of 1 %the incident beam is acceptable, the specimen must have alinear absorption thickness product equal to or greater than
41、 2.3sin . For an iron sample with molybdenum K-alpha radiation,this requires that t be greater than 0.4, 0.6, and 0.7 for the(110), (200), and (211) reflections, respectively.5.1.1 Surface preparation is particularly important in thereflection method. Calculations due to Borie (30), who as-sumed a s
42、awtooth surface of spacing a on a material with linearabsorption coefficient , indicate that the product a should beless than 0.5 if significant intensity losses are to be avoided.For an iron sample with cobalt K-alpha radiation, = 416cm1, corresponding to a 12 m.5.2 For the transmission method, max
43、imum intensity isobtained for a linear absorption thickness product equal to cos. For an iron sample with molybdenum K-alpha, this corre-sponds to t equal to 0.98, 0.97, and 0.95 for the (110), (200),TABLE 1 (I/I0) 1000t 5 10 15 20253035404550556065705 1.0 992 984 976 966 954 939 918 890 851 796 703
44、 617 480 3131.4 991 978 962 941 915 882 840 786 719 636 533 412 277 1461.8 989 972 948 917 878 828 768 695 608 508 395 276 162 0702.2 988 966 935 893 842 778 702 614 515 406 294 186 095 0342.6 986 960 922 871 807 731 643 544 436 326 219 126 057 0173.0 985 954 909 849 775 687 589 481 370 261 164 086
45、034 00910 1.0 984 969 952 934 912 887 855 815 762 694 603 486 344 1911.4 983 962 938 908 873 831 779 716 640 548 440 320 198 0941.8 981 956 924 884 836 779 710 630 538 435 325 215 119 0492.2 980 950 911 861 801 730 649 556 455 348 242 147 074 0272.6 978 944 898 839 768 686 593 492 385 280 183 103 04
46、7 0163.0 977 938 885 817 737 644 543 436 328 226 139 073 030 00915 1.0 976 952 927 900 868 832 789 735 668 583 477 349 209 0851.4 975 946 912 874 829 776 714 640 553 453 342 227 123 0461.8 973 939 898 850 792 725 648 560 462 358 252 155 078 0272.2 972 933 885 826 758 678 590 492 389 286 190 110 052
47、0172.6 970 927 872 804 725 636 538 435 331 232 146 080 036 0113.0 968 921 859 783 695 597 493 386 283 190 115 060 025 00720 1.0 968 935 901 863 822 774 718 649 566 465 345 214 093 0001.4 966 928 885 836 781 717 643 557 460 354 243 140 058 0001.8 964 921 870 811 743 666 579 484 381 278 180 099 039 00
48、02.2 963 915 857 788 709 621 525 424 321 224 139 074 028 0002.6 961 909 843 766 678 582 479 375 274 185 111 057 020 0003.0 960 903 831 746 650 547 440 335 238 155 090 044 015 00025 1.0 959 917 872 824 771 710 639 555 455 339 214 096 0001.4 957 909 856 796 728 651 565 468 362 253 151 065 0001.8 955 9
49、02 840 770 690 602 505 402 298 200 115 048 0002.2 953 895 826 746 657 560 456 352 253 164 092 038 0002.6 952 889 812 724 627 523 417 314 219 139 076 031 0003.0 950 883 800 705 601 493 384 283 194 121 065 025 000FIG. 3 versus t for I/I0= 0.5, = 5, 10, , 25 deg.E81 96 (2017)3and (211) reflections, respectively. Thus, a suitable transmis-sion sample can also be used for reflection measurements.5.3 Ordinarily test specimens are obtained from thickersections by reducing them mechanically so far as possible andthen etc