ASTM E2599-2009 Standard Practice for Specimen Preparation and Mounting of Reflective Insulation Materials and Radiant Barrier Materials for Building Applications to Assess Surface.pdf

1、Designation: E 2599 09Standard Practice forSpecimen Preparation and Mounting of Reflective InsulationMaterials and Radiant Barrier Materials for BuildingApplications to Assess Surface Burning Characteristics1This standard is issued under the fixed designation E 2599; the number immediately following

2、 the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This practice describ

3、es a procedure for specimen prepa-ration and mounting when testing reflective insulation materi-als and radiant barrier materials to assess flame spread andsmoke development as surface burning characteristics usingTest Method E84.1.2 This practice is for reflective insulation materials andradiant ba

4、rrier materials intended for mechanical fastening tosubstrates or building structural members, or intended to bemounted to a substrate with an adhesive.1.3 Specimens of reflective insulation materials and radiantbarrier materials intended for mechanical fastening shall beprepared and mounted in acco

5、rdance with 6.1. Specimens ofreflective insulation materials and radiant barrier materialsintended to be mounted to a substrate with an adhesive shall beprepared and mounted in accordance with 6.2.1.4 This practice shall apply to reflective insulation materi-als and radiant barrier materials as defi

6、ned in Section 3.1.5 This practice shall apply to reflective plastic coreinsulation materials as defined in 3.2.3. Reflective plastic coreinsulation materials are one specific type of reflective insula-tion materials.1.6 This practice shall not apply to rigid foam plastics withor without reflective

7、facers.1.7 Testing is conducted in accordance with Test MethodE84.1.8 This practice does not provide pass/fail criteria that canbe used as a regulatory tool.1.9 Use the values stated in inch-pound units as the standardin referee decisions. The values in the SI system of units aregiven in parentheses

8、, for information only; see IEEE/ASTM SI-10 for further details.1.10 This fire standard cannot be used to provide quantita-tive measures.1.11 Fire testing of products and materials is inherentlyhazardous and adequate safeguards for personnel and propertyshall be employed in conducting these tests. F

9、ire testinginvolves hazardous materials, operations and equipment. Thispractice gives instructions on specimen preparation and mount-ing but the fire-test-response method is given in Test MethodE84. See also Section 8.1.12 The text of this practice references notes and footnoteswhich provide explana

10、tory material. These notes and footnotes(excluding those in tables and figures) shall not be consideredrequirements of the standard.1.13 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to estab

11、lish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2C 168 Terminology Relating to Thermal InsulationC 1224 Specification for Reflective Insulation for BuildingApplicationsC 1313 Specification

12、 for Sheet Radiant Barriers for Build-ing Construction ApplicationsE84 Test Method for Surface Burning Characteristics ofBuilding MaterialsE 176 Terminology of Fire StandardsE 2231 Practice for Specimen Preparation and Mounting ofPipe and Duct Insulation Materials to Assess SurfaceBurning Characteri

13、sticsIEEE/ASTM SI-10 International System of Units (SI): TheModern Metric System3. Terminology3.1 Definitions: For definitions of terms used in this practiceand associated with fire issues, refer to the terminologycontained in Terminologies E 176. For definitions of termsused in this practice and as

14、sociated with thermal insulationissues refer to Terminology C 168.3.2 Definitions of Terms Specific to This Standard:1This practice is under the jurisdiction of ASTM Committee E05 on FireStandards and is the direct responsibility of Subcommittee E05.22 on SurfaceBurning.Current edition approved Marc

15、h 1, 2009. Published March 2009.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM International

16、, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.3.2.1 radiant barrier, na low emittance (0.1 or less)surface used in the construction of a radiant barrier system.3.2.1.1 DiscussionRadiant barrier materials are defined inSpecification C 1313.3.2.2 reflective insu

17、lation, nthermal insulation consistingof one or more low emittance surfaces bounding one or moreenclosed air spaces.3.2.2.1 DiscussionReflective insulation materials are de-fined in Specification C 1224.3.2.3 reflective plastic core insulation, nan insulationmaterial packaged in rolls, that is less

18、than 0.5 in. (12.7 mm)thick, with at least one exterior low emittance surface (0.1 orless) and a core material containing voids or cells.3.2.3.1 DiscussionReflective plastic core insulation mate-rials are one specific type of reflective insulation materials.4. Summary of Practice4.1 This practice de

19、scribes a procedure for specimen prepa-ration and mounting when testing reflective insulation materi-als and radiant barrier materials to assess flame spread andsmoke development as surface burning characteristics usingTest Method E84.4.2 Reflective insulation materials and radiant barrier mate-rial

20、s intended for mechanical fastening to substrates or buildingstructural members, or intended to be mounted to a substratewith an adhesive shall be tested in accordance with thespecimen preparation and mounting procedures described inthis practice, using Test Method E84.4.3 Reflective insulation mate

21、rials and radiant barrier mate-rials intended to be used as pipe and duct insulation materialsshall be mounted and tested in accordance with Test MethodE 2231.5. Significance and Use5.1 Reflective insulation materials and radiant barrier mate-rials are evaluated in accordance with Test Method E84 to

22、comply with building or mechanical code requirements. Thispractice describes, in detail, a specimen mounting procedurefor reflective insulation and radiant barrier materials.5.2 The material shall be representative of the materialsused in actual field installations.5.3 Specimen preparation and mount

23、ing procedures formaterials not described in this practice shall be added as theinformation becomes available.5.4 The limitations for this procedure are those associatedwith Test Method E84.5.5 This practice shall not apply to rigid foam plastics withor without reflective facers.6. Specimen Preparat

24、ion and Mounting6.1 Mechanically Attached Specimens:6.1.1 Specimens shall be mechanically attached to three,steel or aluminum test frames. Each test frame shall benominally 8.25 ft (2.5 m) by 22 - 24 in.(559 - 610 mm) wideby 2 in. (51 mm) deep, made from 2 by 2 by 3/16 in. (51 by 51by 5 mm) aluminum

25、 or steel angles or equivalent. No screeningor netting shall be attached to the opening of the frames wherethe test specimen is attached. See Fig. 1.6.1.2 Each test shall be conducted using a factory or fieldjoint along the longitudinal centerline of the test specimen,with a longitudinal seam create

26、d in the approximate centerlineusing the same method of closure used in actual field installa-tions.6.1.3 It shall be permitted to represent the field joint byintroducing a longitudinal slit cut along the longitudinalcenterline of the specimen facing and applying the manufac-turers recommended field

27、 closure system (if applicable).6.1.4 The reflective insulation or the radiant barrier speci-mens shall be of a width sufficient to cover the angle framingfor attachment. Specimens shall be placed on the horizontallegs of the angle. See SectionA-Aof Fig. 1. The specimen shallbe attached to each of t

28、he horizontal legs using self-tappingscrews, through bolts or similar fastening technique. Fastenersshall be placed a maximum of 24 in. (610 mm) on-center downthe length on both sides of each 8-ft. (2.4 m) frame.6.1.5 Mount the three frames with the attached specimenend-to-end on the ledges of the E

29、84furnace without using anyauxiliary support. The specimen shall face the interior of thetest chamber. The tunnel lid shall rest on the frame as to createa nominal 2-in. air gap between the insulation and lid.6.1.6 The two transverse butt joints formed by the threeframes are to be left uncovered or

30、taped in accordance withmanufacturers application instructions.6.2 Adhesively Attached Specimens:6.2.1 Specimens shall be adhesively attached to a substrate.The substrate shall be representative of that used in actual fieldinstallation. The substrate shall consist of flat sheets cut to sizeas approp

31、riate for mounting in Test Method E84.6.2.2 Each test shall be conducted using a factory or fieldjoint along the longitudinal centerline of the test specimen,with a longitudinal seam created in the approximate centerlineusing the same method of closure used in actual field installa-tions.6.2.3 It sh

32、all be permitted to represent the field joint byintroducing a longitudinal slit cut along the longitudinalcenterline of the specimen facing and applying the manufac-turers recommended field closure system (if applicable).6.2.4 Specimens shall be mounted to the substrate using theadhesive that is rep

33、resentative of that used in actual fieldinstallation. The adhesive shall be applied per the manufactur-ers installation directions.6.2.5 The specimens shall be of a width sufficient to coverthe substrate and the attachment of the specimen to theadhesive shall be in accordance with manufacturers inst

34、alla-tion directions.6.2.6 Mount the substrates with the attached specimensend-to-end on the ledges of the E84furnace without using anyauxiliary support. The specimen shall face the interior of thetest chamber.6.2.7 The transverse butt joints formed by the substrateswith the attached specimens are t

35、o be left uncovered or tapedin accordance with manufacturers application instructions.6.3 For materials that are asymmetrical in cross-section,each side of the material shall be tested separately.E25990927. Testing of Specimens7.1 All testing shall be conducted using the methodologydescribed in Test

36、 Method E84.8. Operator Safety8.1 The primary concerns for operator safety are associatedwith the fire-test-response procedure, Test Method E84, andnot with the specimen preparation procedure. Safety recom-mendations are included in Test Method E84.9. Report9.1 Report a detailed description of the s

37、pecimen prepara-tion and mounting used.9.2 Report all the information required in the reportingsection of Test Method E84, including observations, graphicalresults and the values of the flame spread index and of thesmoke developed index in each test.10. Keywords10.1 fire; fire test; flame spread; in

38、sulation; radiant barrier;reflective insulation; reflective plastic core; smoke developed;Steiner tunnelFIG. 1 Mounting Frame (three required)E2599093APPENDIXX1. COMMENTARYX1.1 IntroductionIt has been shown that the carefulreplication of realistic fire scenarios is the most appropriatemeans of fire

39、testing of products and systems. However, this isnot always achievable within the confines of a standard testmethod.X1.2 The use of any standard fire test method intrinsicallycarries some limitations, including the source of heat or flame,the specimen size and orientation, the specimen location andt

40、he fire-test-response characteristics measured.X1.3 Fire tests on reflective insulation and sheet radiantbarriers are often conducted by using Test Method E84.X1.3.1 The source of heat and flame in Test Method E84isa set of two gas burners supplying approximately 300 000BTU/h (87.9 kW) onto the test

41、 specimen from underneath fora period of 10 min.X1.3.2 The approximate specimen sizes in Test MethodE84are 24 ft (7.3 m) long by 20 to 24 in. (510-610 mm) wide.The recommended specimen thickness is up to 4 in. (102 mm)thick.X1.4 The mounting method using the 2 in. (51 mm) air gapis applicable for ma

42、terials installed over open framing or whenthe materials are mechanically installed against a substrate.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that

43、determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapprove

44、d or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel

45、 that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).E2599094