ASTM F1665-2008 Standard Specification for Poly(Vinyl Chloride) (PVC) and Other Conforming Organic Polymer-Coated Steel Barbed Wire Used With Chain-Link Fence《与链接栅栏一起使用的聚氯乙烯涂层刺钢丝的标.pdf

1、Designation: F 1665 08Standard Specification forPoly(Vinyl Chloride) (PVC) and Other Conforming OrganicPolymer-Coated Steel Barbed Wire Used With Chain-LinkFence1This standard is issued under the fixed designation F 1665; the number immediately following the designation indicates the year oforiginal

2、 adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers PVC and other conformingorganic polymer-

3、coated steel barbed wire consisting of twopolymer-coated strands, with four-point barbs of zinc-coatedsteel or aluminum alloy wire. PVC and other organic polymercoatings hereinafter will be designated as polymer coating.1.2 Barbed wire strand wire, produced from three classes ofwire coatings, is cov

4、ered as follows:1.2.1 Class 1, consisting of a polymer coating extruded overzinc-coated or aluminum-coated or zinc-5 % aluminum-mischmetal alloy-coated steel wire;1.2.2 Class 2a, consisting of a polymer coating extrudedand adhered to zinc-coated or aluminum-coated or zinc-5 %aluminum-mischmetal allo

5、y-coated steel wire; and1.2.3 Class 2b, consisting of a polymer coating fused andadhered to zinc-coated or aluminum-coated or zinc-5 %aluminum-mischmetal alloy-coated steel wire.1.3 The values stated in inch-pound units are to be regardedas the standard. The values given in parentheses are forinform

6、ation only.2. Referenced Documents2.1 ASTM Standards:2A 90/A 90M Test Method for Weight Mass of Coating onIron and Steel Articles with Zinc or Zinc-Alloy CoatingsA 370 Test Methods and Definitions for Mechanical Testingof Steel ProductsA 428/A 428M Test Method for Weight Mass of Coatingon Aluminum-C

7、oated Iron or Steel ArticlesA 700 Practices for Packaging, Marking, and LoadingMethods for Steel Products for ShipmentD 1499 Practice for Filtered Open-Flame Carbon-Arc Ex-posures of PlasticsF 552 Terminology Relating to Chain Link FencingF 934 Specification for Colors for Polymer-Coated ChainLink F

8、ence MaterialsG 152 Practice for Operating Open Flame CarbonArc LightApparatus for Exposure of Nonmetallic MaterialsG 153 Practice for Operating Enclosed Carbon Arc LightApparatus for Exposure of Nonmetallic Materials2.2 Federal Standard:3Fed. Std. No. 123 Marking for Shipments (Civil Agencies)2.3 M

9、ilitary Standards:3MIL-STD-129 Marking for Shipment and StorageMIL-STD-163 Steel Mill Products, Preparation for Ship-ment and Storage3. Terminology3.1 DefinitionsFor definitions of terms such as fabric(chain-link fence), PVC, and polymer coating, see Terminol-ogy F 552.4. Classification4.1 Polymer-c

10、oated steel barbed wire is supplied in a choiceof two types as follows:4.1.1 Type I (Standard), with barbs spaced on 5-in. (127-mm) centers; and4.1.2 Type II (High Security), with barbs spaced on 3-in.(76-mm) centers.5. Ordering Information5.1 Orders for barbed wire purchased in accordance withthis

11、specification shall include the following information:5.1.1 Quantity (expressed in number of spools);5.1.2 Length of spools (1320 or 1000 ft (402 or 305 m); see9.4);5.1.3 Class of a polymer coating to be applied to metallic-coated steel strand wire;5.1.4 Color of coating;5.1.5 Type of barbs (galvani

12、zed steel or aluminum alloy; see6.3);1This specification is under the jurisdiction of ASTM Committee F14 on Fencesand is the direct responsibility of Subcommittee F14.40 on Chain Link Fence andWire Accessories.Current edition approved Feb. 1, 2008. Published February 2008. Originallyapproved in 1995

13、. Last previous edition approved in 2001 as F 1665 01.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Availa

14、ble from Standardization Documents Order Desk, DODSSP, Bldg. 4,Section D, 700 Robbins Ave., Philadelphia, PA 19111-5098, http:/www.dodssp.daps.mil.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.5.1.6 Type of barbed wire (Type I or I

15、I; see 4.1.1 and 4.1.2);5.1.7 Selection of type of metallic coating on the steel strandwire substrate, which shall be the choice of the producer unlessotherwise specified;5.1.8 Packaging requirements;5.1.9 ASTM designation and year of issue; and5.1.10 Certification, if required;5.2 Any tests require

16、d other than those covered specificallyin this specification must be stipulated by the purchaser in theorder or contract.5.3 All spools of barbed wire accepted by the purchasershall be billed on the basis of the number and original length.NOTE 1A typical ordering description is as follows: 20 spools

17、polymer-coated steel barbed wire, 1000-ft (305-m) spools, Class 2bcoating, olive green color, aluminum alloy barbs, Type II (high security),on pallets, certified this specification.6. Materials6.1 Base MetalThe base metal shall be steel of suchquality and purity that, when drawn to the size of wires

18、pecified, it shall be of uniform quality and have properties andcharacteristics as prescribed in this specification.6.2 Wire used for the manufacture of strand wire shall meetthe requirements of this specification. The polymer coatingshall be formulated and produced properly to conform to therequire

19、ments of this specification.6.3 Materials for Barbs:6.3.1 Zinc-Coated Steel Wire, if used for the barbs, shall be14 gage, 0.080 in. (2.03 mm), having a Class 3 zinc coating,minimum 0.70 oz/ft (215 g/m) when tested in accordance withTest Method A 90/A 90M.6.3.2 Aluminum Alloy Wire, if used for the ba

20、rbs, shall be 14gage, 0.080 in. (2.03 mm), Alloy 5000-H38, 6061-T94, orequal, as agreed upon between the manufacturer and thepurchaser at the time of purchase.6.3.3 The choice of either zinc-coated steel wire or alumi-num alloy wire for the barbs shall be that of the manufacturer,unless otherwise sp

21、ecified by the purchaser.7. Manufacture7.1 Class 1 polymer-coated wire shall have the coatingextruded onto the strand wire that conforms to the requirementsas given in Table 1.7.2 Class 2a polymer-coated wire shall have the coatingextruded and adhered to the strand wire that conforms to therequireme

22、nts as given in Table 1.7.3 Class 2b polymer-coated wire shall have the coatingfused and adhered to the strand wire that conforms to therequirements as given in Table 1.8. Size and Construction8.1 All barbed wire furnished in accordance with thisspecification shall be fabricated from two strands of

23、14 gage,0.080-in. (2.03-mm) metallic-coated core, polymer-coatedsteel wire, with four-point barbs of 14 gage, 0.080-in. zinc-coated steel or aluminum alloy wire.9. Size and Permissible Variations9.1 Line WireThe permissible variation from the nominaldiameter of the wire shall be 60.004 in. (0.10 mm)

24、.9.2 BarbsDue to the mechanics of the manufacture whenforming the barbs, a certain amount of out-of-roundness can beexpected, and this precludes barbs from being subjected tochecks for other than nominal diameter and length. Measuredfrom the center of the two strand wires, the barb length shall be38

25、 in. (9.5 mm), minimum.9.3 Spacing of BarbsBarbs shall be spaced as indicated in4.1.1 or 4.1.2. The individual barb spacing shall be measuredfrom the edge of one barb at the strand to the correspondingedge of the adjacent barb. Cumulative spacing is established bycounting the total number of barbs i

26、n a 25-ft (7.6-m) length ofbarbed wire. Barbs are subject to relocation during fabricationand handling; therefore, a rigid interpretation of the spacingrequirement may lead to undue rejections. Any sample with93.5 % of the individual barb spacings conforming to thespecified spacing (634 in. (19 mm)

27、and containing a minimumof 55 barbs (5-in. (127-mm) spacing) or a minimum of 86barbs (3-in. (76-mm) spacing) in 25 ft shall be consideredacceptable.9.4 The length of barbed wire in each spool shall be 80 rods(402 m). This is equivalent to one-quarter mile, or 1320 ft. Atthe option of the manufacture

28、r, 1000-ft (305-m) spools may beoffered.10. Joints and Workmanship10.1 Splicing of individual wires by means of a wrap jointor an electric butt weld is permitted. Not more than threesplices or joints shall exist in any spool of barbed wire. Suchsplices or joints shall be made in a workmanlike manner

29、.10.2 The strands shall be twisted with a uniform length oflay. The direction of twisting may be either right or left hand.Alternate left and right hand twisting is not permitted.10.3 The barbs shall be sharp, well-formed, wrapped tightly,and spaced in accordance with 9.3.11. Weight of Metallic Coat

30、ing11.1 The minimum weight of zinc coating for the galva-nized barbs shall be 0.70 oz/ft (215 g/m). The minimum weightof the strand wire metallic coating shall conform to Table 1when tested in accordance with Test Method A 90/A 90M orTest Method A 428/A 428M, as applicable.12. Breaking Strength12.1

31、The minimum breaking strength of the stranded barbedwire shall be 760 lbf (3380 N) when tested in accordance withTest Methods and Definitions A 370. This breaking strengthvalue reflects that of both strand wires together as one unit.TABLE 1 Weight of Strand Wire Metallic CoatingsSpecified CoreDiamet

32、er of StrandWire, in. (mm)Minimum Weight ofZinc Coating, oz/ft(g/m)Minimum Weight ofAluminum Coating,oz/ft2(g/m2)Minimum Weight ofZinc-5 %Aluminum-MischmetalCoating, oz/ft (g/m)0.080 (2.03) 0.25 (75) 0.20 (61) 0.25 (75)F 1665 08213. Properties of Polymer-Coated Barbed Wire13.1 The polymer-coated bar

33、bed wire shall have a demon-strated ability to conform to the following requirements:13.2 Adhesion Tests:13.2.1 Class 2a shall conform to the requirements of 13.2.2.Class 2b shall conform to the requirements of 13.2.3.13.2.2 Three specimens from each lot shall be tested.Measure a distance of34 in. (

34、19 mm) from the end of thespecimen. With a regular hand grip wire stripper, exert maxi-mum hand pull parallel to the axis of the wire. Attempt toremove the measured portion of the polymer sleeve from thecore wire. The lot shall be acceptable if the polymer sleeve isnot capable of being removed from

35、the core wire on all threesamples.13.2.3 Three specimens from each lot shall be tested. Maketwo cuts parallel to the axis of the wire through the coating,approximately116 in. (1.6 mm) apart, at least12 in. (12.7 mm)long. With a knife, peel back a section of the coating between18 and14 in. (3.2 and 6

36、.4 mm) long to produce a tab. Attemptto remove the116-in. (1.6 mm) strip of coating by pulling thetab. The lot shall be acceptable if the coating breaks rather thanseparates from the core wire on all three specimens.13.3 Accelerated AgingThe polymer-coated wire shallwithstand exposure for 1000 h wit

37、hout failure at a black paneltemperature of 145F (63C) when tested in accordance withPractice D 1499. The appropriate apparatus described in Prac-tices G 152 or G 153 shall be used for the test. The productshall be construed to have failed the test if one of the followingoccurs:13.3.1 Shrinkage of t

38、he polymer coating is greater than116in./ft (1.6 mm/305 mm) of wire.13.3.2 There shall be no significant change in color or glossof the polymer surface as determined by visual inspection.13.4 ColorUnless otherwise stipulated by the purchaser,the color of the polymer shall be in accordance with thest

39、andard colors contained in Specification F 934: green, olivegreen, brown, and black.14. Thickness of Polymer Coating14.1 The thickness of the polymer coating shall be inaccordance with Table 2.14.2 The thickness of the polymer coating shall be deter-mined on an individual piece of wire. This specime

40、n may beany length of wire over 12 in. (305 mm).14.3 For Class 1 and Class 2a material, strip the polymercoating mechanically from the wire and measure the minimumand maximum thickness of the polymer coating with a suitablemicrometer.14.4 For Class 2b material, strip the polymer coating bychemical m

41、eans and determine the diameter of the bare wire.Scrape the coating from one side of the wire and measure thereduced diameter with a micrometer. The thickness of thecoating at this point is the difference between the measurementthus obtained and the measured diameter of the bare wire. In asimilar ma

42、nner, determine the thickness of the coating at rightangles to the first determination.14.5 Take care not to remove any of the metallic surfacewhen removing polymer coating by scraping.15. Sampling15.1 For the purpose of the tests, one spool from every 50spools or fraction thereof in a lot shall be

43、selected at random,or a total of seven samples, whichever is less.Alot shall consistof all of the spools of a single type of barbed wire offered fordelivery at the same time.15.2 Test SpecimensA 4-ft (1.2-m) length of barbed wireshall be cut from the end of the spool for the tests prescribedin Secti

44、ons 11-14. Each strand wire shall be tested for itsmetallic and polymer coating. The breaking strength valueshall be determined by having the twisted strand tested as acomposite.15.3 Instead of testing wire for its coating and breakingstrength from the completed barbed wire in accordance with15.2, t

45、he manufacturer may elect to establish compliance withSections 11-14 by tests made on wire prior to fabrication. If themanufacturer makes this election, the purchaser still reservesthe right to test wire from the completed barbed wire forcompliance.15.4 For the purpose of inspection, a maximum of tw

46、ospools from the lot (as described in 15.1) may be subjected toobservations for barb length and spacing, overall length, andgeneral workmanship.15.5 Instead of inspecting for length by unrolling full spoolsin accordance with 15.4, the purchaser and the manufacturermay agree on a weight per spool rel

47、ated to the wire size ormeasuring tools used during manufacturing. The purchaser stillreserves the right to confirm the length by actual measurement.15.6 Inspection for barb spacing is normally performed onthe outer 25-ft (7.6-m) length of a spool; this permits repack-aging of the spool. Any other s

48、election shall be as agreed uponbetween the manufacturer and the purchaser.16. Retests and Rejection16.1 Should one or more of the individual wire specimensfail the coating tests or a strand specimen fail the breakingstrength test, the lot shall be subjected to retest. Four additionalspools of barbe

49、d wire for each 50 spools offered shall besampled for retest purposes. The lot size then becomes 50,except that this lot size may vary slightly to accommodatepallet count when the barbed wire is palletized.16.2 Retesting for CoatingShould more than two of theindividual strand wires of the retest specimens fail to meet thespecified coating, the entire lot represented by the retest may berejected.16.3 Retesting for Breaking StrengthShould any of theretest specimens fail to meet the minimum breaking strengthvalues specified, the entire lot represented by the