ASTM F1860-2010 Standard Specification for Rubber Sheet Floor Covering With Backing《有背面橡胶板铺地材料标准规范》.pdf

1、Designation: F1860 10Standard Specification forRubber Sheet Floor Covering With Backing1This standard is issued under the fixed designation F1860; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number

2、in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers the requirements for the com-pound and physical characteristics of rubber sheet floor cov-ering having a rubber wear

3、 layer with backing. Products mayalso contain intermediate layers.1.2 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.1.3 The following p

4、recautionary statement pertains only tothe test method portion, Section 10, of this specification: Thisstandard does not purport to address all the safety concerns, ifany, associated with its use. It is the responsibility of the userof this standard to establish appropriate safety and healthpractice

5、s and determine the applicability of regulatory limita-tions prior to use.2. Referenced Documents2.1 The following documents if the issue in effect on thedate of the material purchase form a part of this specification tothe extent referenced herein:2.2 ASTM Standards:2D412 Test Methods for Vulcanize

6、d Rubber and Thermo-plastic ElastomersTensionD883 Terminology Relating to PlasticsD1566 Terminology Relating to RubberD2240 Test Method for Rubber PropertyDurometerHardnessF141 Terminology Relating to Resilient Floor CoveringsF387 Test Method for Measuring Thickness of ResilientFloor Covering With F

7、oam LayerF410 Test Method for Wear Layer Thickness of ResilientFloor Coverings by Optical MeasurementF710 Practice for Preparing Concrete Floors to ReceiveResilient FlooringF925 Test Method for Resistance to Chemicals of ResilientFlooringF970 Test Method for Static Load LimitF1482 Practice for Insta

8、llation and Preparation of PanelType Underlayments to Receive Resilient FlooringF1514 Test Method for Measuring Heat Stability of Resil-ient Flooring by Color ChangeF1515 Test Method for Measuring Light Stability of Resil-ient Flooring by Color Change2.3 ANSI Standards:ANSI/ASQC Z1.4 Sampling Proced

9、ures and Tables forInspection by Attributes33. Terminology3.1 DefinitionsFor definitions of other terms used in thisstandard, see Terminology F141.4. Classification4.1 Rubber sheet floor covering covered by this specifica-tion shall conform to the following types:4.1.1 Type IHomogeneous rubber sheet

10、 floor coveringwith backing:4.1.1.1 Fibrous backing, and4.1.1.2 Foamed rubber backing.4.1.2 Type IILayered rubber sheet floor covering withbacking:4.1.2.1 Fibrous backing, and4.1.2.2 Foamed rubber backing.4.2 The above may have either smooth, embossed, ormolded pattern surfaces.4.3 These products sh

11、all not contain asbestos.5. Ordering Information5.1 Purchasers shall state whether this specification is to beused, select the preferred options permitted herein and includethe following information in the invitation to bid or purchaseorder:5.1.1 Title, number, and date of this specification,5.1.2 T

12、ype, color, and surface (see Section 4 and Section 6),5.1.3 Quantity, in square feet, square yards, or squaremetres,1This specification is under the jurisdiction of ASTM Committee F06 onResilient Floor Coverings and is the direct responsibility of Subcommittee F06.80on Specifications.Current edition

13、 approved May 1, 2010. Published June 2010. Originallyapproved in 1998. Last previous edition approved in 2009 as F1860 04(2009)1.DOI: 10.1520/F1860-10.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMSta

14、ndards volume information, refer to the standards Document Summary page onthe ASTM website.3Available from American National Standards Institute (ANSI), 25 W. 43rd St.,4th Floor, New York, NY 10036, http:/www.ansi.org.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohock

15、en, PA 19428-2959, United States.5.1.4 Thickness required. (see 8.3),5.1.5 Overall thickness, if molded pattern flooring is speci-fied (see 8.1),5.1.6 Width required (see 8.4),5.1.7 Length required (see 8.5),5.1.8 Resistance to chemicals, (see 7.4),5.1.9 Lot information, if other than as specified i

16、n AANSI/ASQC Z1.4. (see 10.1 and 11.1),5.1.10 Sampling, if other than as specified in ANSI/ASQCZ1.4 (see 10.1 and 11.1),5.1.11 Statement requesting certification, if certification ofcompliance is required (see 12.1),5.1.12 Packing requirements, if other than as specified (see14.1),5.1.13 Palletizati

17、on, if required,5.1.14 Marking required, if other than specified (see 13.1),and5.1.15 Other requirements.6. Materials and Manufacture6.1 Homogeneous Rubber Sheet Floor CoveringTheproduct shall consist of a wear layer and backing. The surfacecoloring or mottling shall be uniform throughout the entire

18、thickness of the wear layer. The backing shall be fibrous orfoamed rubber and thoroughly bonded to the wear layer so asnot to delaminate under normal use.6.2 Layered Rubber Sheet Floor CoveringThe productshall consist of a wear layer, intermediate layer(s), and abacking. The surface coloring or mott

19、ling shall be uniformthroughout the entire thickness of the wear layer, but need notextend through the intermediate layer(s). The backing shall befibrous or foamed rubber. The wear layer, intermediate layer(s)and backing shall be thoroughly bonded so as not to delaminateunder normal use.6.3 Wear Lay

20、er:6.3.1 The polymeric binder of the wear layer shall satisfythe definition of rubber in Terminology D1566, and have beenvulcanized, as defined in Terminology D1566 (under vulcani-zation), such that it becomes thermoset as defined in Termi-nology D883. The wear layer made from this compound shallbe

21、resistant to neutral pH cleaners.6.3.2 The wear layer must have a minimum thickness of0.040 in. (1.0 mm) when measured in accordance with TestMethod F410.6.3.3 The appearance of the rubber sheet floor covering afterremoving 0.020 in. (0.51 mm) of the wear layer thickness, shallcompare favorably in a

22、ppearance with the sheet flooringsoriginal appearance. The removal of the wear layer may beaccomplished by any suitable method.6.3.4 The wear layer may have a smooth, embossed, ormolded pattern surface.6.4 Intermediate LayersThe layer(s) may consist of, butnot be limited to, rubber, foamed rubber, o

23、r other materials,which are intended to improve the performance characteristicsof the product.6.5 BackingsThe composition of the backings shall befibrous or foamed rubber and may contain other ingredientsprovided the resultant backing is suitable for installation onfloors above-, on-, or below-grade

24、 when installed according tomanufacturers installation recommendations.6.6 Color, Pattern, and Wearing SurfaceThe color, pat-tern, and wear layer surface, as applicable, shall be as specifiedin the contract or order (see 5.1).NOTE 1The colors and patterns that are available are indicated inindividua

25、l manufacturers current catalogs. As manufactured, colors mayvary somewhat in hue or shade from the catalog.NOTE 2Where color match is a concern, samples from the manufac-turer shall be obtained to verify color acceptability.7. Performance Requirements7.1 HardnessThe rubber sheet floor covering shal

26、l have adurometer hardness of not less than 85 (Shore, Type A) whentested in accordance with Test Method D2240. The backingmaterial shall be removed prior to testing and may be accom-plished by any suitable method.7.2 Modulus at 10 % ElongationWhen tested in accor-dance with Test Method D412 at a ra

27、te of 6 in. (152.4mm)/min, using a 1 in. (25.4 mm) by 5 in. (127 mm) gagelength rectangular specimen, the modulus shall not be less than300 psi (2.07 MPa). For molded pattern rubber sheet floorcovering, the raised pattern shall be removed by any suitablemethod. Prior to testing, the backing material

28、 shall be removedand may be accomplished by any suitable method.7.3 Static Load LimitWhen tested in accordance with TestMethod F970, with an applied load of 250 lb (113.4 kg), theresidual indentation shall not be greater than 0.005 in. (0.127mm).7.4 Resistance to ChemicalsWhen tested in accordancewi

29、th Test Method F925, the rubber sheet floor covering shallhave no more than a slight change in surface dulling, surfaceattack, or staining when exposed to the flowing chemicals:7.4.1 White vinegar (5 % acetic acid),7.4.2 Rubbing alcohol (70 % isopropyl alcohol),7.4.3 Sodium hydroxide solution (5 % N

30、aOH),7.4.4 Hydrochloric acid solution (5 % HCl),7.4.5 Sulfuric acid solution (5 % H2SO4),7.4.6 Household ammonia solution (5 % NH4OH),7.4.7 Household bleach solution (5.25 % NaOCl),NOTE 3These basic chemicals are representative of those likely to befound in domestic, commercial, and institutional us

31、e. Many proprietarycompounds contain one or more of these basic chemicals. Should theflooring for an unusual application need to be resistant to a specificchemical, this additional requirement should become part of the procure-ment document, (see 5.1.8).NOTE 4Since standard SBR rubber flooring is no

32、t recoommended forinstallation where the product will be exposed to animal fats, vegetableoils, and petroleum-based reagents, mineral oil, olive oil, kerosene, andgasoline have been removed from the standard chemical list to eliminateany confusion regarding product selection.7.5 Resistance to HeatWh

33、en tested in accordance to TestMethod F1514, the color change of the rubber sheet floorcovering shall have an average DE not greater than 8.0 afterseven days exposure to 158F (70C). The specimen surfaceshall be wiped with a clean, white cotton cloth prior to takingthe initial and post test condition

34、ed period color readings toremove any wax bloom or other contaminants which mayaffect the accuracy of the color readings.F1860 1027.6 Resistance to LightWhen tested in accordance to TestMethod F1515, the color change of the rubber sheet floorcovering shall have an average DE not greater than 8.0 aft

35、er300 h of exposure to light, simulated by a properly fittedxenon-arc radiant energy source.8. Dimensions, Mass, and Permissible Variations8.1 Overall ThicknessMolded pattern rubber sheet floorcovering shall be measured for overall thickness at the thickestcross sectional area of the flooring. The t

36、hickness of themolded pattern shall be uniform throughout the flooring.8.2 Base Thickness Molded pattern rubber sheet floorcovering base thickness shall be measured at the thinnest crosssectional area of the flooring. The thinnest cross sectional areashall be uniform throughout the flooring.8.3 Thic

37、knessThe thickness of the rubber sheet floorcovering shall be as specified in the contract or order (see5.1.4).An average tolerance, based on five individual measure-ments, of 60.008 in. (60.2 mm) from the specified thicknessshall be permitted in the base thickness alone or in combinationwith the ov

38、erall thickness, when measured in accordance withTest Method F387. The difference between the five individualmeasurements can not be greater than 0.010 in. (0.25 mm)from the nominal thickness. In the case of molded patternrubber sheet floor covering, overall thickness and base thick-ness shall be re

39、ported.8.4 WidthThe width shall be as specified in the contract ororder (see 5.1.6). The net width (gross width less selvages)shall not be less than as marked on the label or package whenmeasured in accordance with 8.6.8.5 LengthThe length of the roll shall be as specified inthe contract or order (s

40、ee 5.1.7). The sheet length shall not beless than as marked on the label or package when measured inaccordance with 8.6. Each roll shall be in one piece, except thatless than 20 % of the rolls in any one shipment may consist ofnot more than two pieces, the shortest length shall not be lessthan 5 lin

41、ear yards (4.57 m), or as agreed upon by the purchaserand seller. Such rolls shall be clearly marked.8.6 Length and Width MeasurementsMeasurements shallbe made with a calibrated 100 ft (30 m) steel tape graduated atintervals of116 in. or 1 mm. The roll shall be extended to itsfull length on a flat s

42、urface and all creases and bucklesremoved, insofar as practical, without applying stresses thatcause any significant stretching. Measurements of length shallbe rounded to the nearest inch or 10 mm. Net width shall bemeasured to the nearest116 in. or 1 mm at not less than tenlocations uniformly distr

43、ibuted along the length of each roll,and the results averaged.9. Workmanship, Finish, and Appearance9.1 The rubber sheet floor covering furnished in accordancewith this specification shall be an acceptable match to approvedsamples in color, pattern, and appearance. The product shall befree of defect

44、s, that adversely affect performance or appear-ance. Such defects include: blemishes, spots, lines, indenta-tions, blisters, and delamination.10. Sampling for Test10.1 Sampling for testing physical characteristics listed inTable 1 shall be done in accordance with the provisions setforth in ANSI/ASQC

45、 Z1.4. The inspection level shall bespecial inspection level S-1, as noted in Table I ofANSI/ASQCZ1.4, and the acceptable quality level (AQL) shall be 6.5defects per hundred units as noted in Table II-(A) of ANSI/ASQC Z1.4 or as otherwise specified in 10.2. The lot size shallbe expressed in units. A

46、 unit represents a single, manufactured,inventoried, finished roll.10.1.1 Samples shall be obtained in the required length fromthe outside end of the roll and shall encompass the total widthof the material.10.2 Sampling for testing physical characteristics listed inTable 1 shall be agreed upon by th

47、e purchaser and themanufacturer as part of the procurement document.11. Inspection11.1 Sampling for inspection of the rubber sheet floorcovering for defects that would adversely affect performance(see 9.1) shall be done in accordance with the provisions setforth in ANSI/ASQC Z1.4. The inspection lev

48、el shall be LevelI as noted in Table I of ANSI/ASQC Z1.4 with an acceptablequality level (AQL) of 6.5 defects per hundred as noted inTable II-(A) of ANSI/ASQC Z1.4 or as otherwise specified in11.2. The lot size shall be expressed in units. A unit representsa single, manufactured, inventoried, finish

49、ed roll.11.2 Inspection of the rubber sheet floor covering for defectsthat would adversely affect performance (see 9.1) shall beagreed upon by the purchaser and the manufacturer as part ofthe procurement documents.TABLE 1 Characteristics and TestsCharacteristic Requirement ASTM Test Method ReferenceComposition of Material Certificate of Compliance 6.1Wear Layer Thickness min 0.040 in. (1.0 mm) F410 6.3.2Hardness min 85 Shore A D2240 7.1Modulus at 10 % Elongation min 300 psi (2.07 MPa) D412 7.2Static Load Limit # 0.005 in. (0.127 mm) F970 7.3Resista