1、Designation:F186010 Designation: F1860 12Standard Specification forRubber Sheet Floor Covering With Backing1This standard is issued under the fixed designation F1860; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last
2、 revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers the requirements for the compound and physical characteristics of rubber sheet floor coveringhav
3、ing a rubber wear layer with backing. Products may also contain intermediate layers.1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information only and are not considered standard
4、.1.3 The following precautionary statement pertains only to the test method portion, Section 10, of this specification: Thisstandard does not purport to address all the safety concerns, if any, associated with its use. It is the responsibility of the user ofthis standard to establish appropriate saf
5、ety and health practices and determine the applicability of regulatory limitations priorto use.2. Referenced Documents2.1 The following documents if the issue in effect on the date of the material purchase form a part of this specification to theextent referenced herein:2.2 ASTM Standards:2D412 Test
6、 Methods for Vulcanized Rubber and Thermoplastic ElastomersTensionD883 Terminology Relating to PlasticsD1566 Terminology Relating to RubberD2240 Test Method for Rubber PropertyDurometer HardnessF141 Terminology Relating to Resilient Floor CoveringsF387 Test Method for Measuring Thickness of Resilien
7、t Floor Covering With Foam LayerF410 Test Method for Wear Layer Thickness of Resilient Floor Coverings by Optical MeasurementF710 Practice for Preparing Concrete Floors to Receive Resilient FlooringF925 Test Method for Resistance to Chemicals of Resilient FlooringF970 Test Method for Static Load Lim
8、itF1482 Practice for Installation and Preparation of Panel Type Underlayments to Receive Resilient FlooringF1514 Test Method for Measuring Heat Stability of Resilient Flooring by Color ChangeF1515 Test Method for Measuring Light Stability of Resilient Flooring by Color Change2.3 ANSI Standards:ANSI/
9、ASQC Z1.4 Sampling Procedures and Tables for Inspection by Attributes33. Terminology3.1 DefinitionsFor definitions of other terms used in this standard, see Terminology F141.4. Classification4.1 TypesRubber sheet floor covering covered by this specification shall conform to the following types:4.1.1
10、 Type IHomogeneous rubber sheet floor covering with backing:4.1.1.1Fibrous backing, and4.1.1.2Foamed rubber backing. Homogeneous1This specification is under the jurisdiction of ASTM Committee F06 on Resilient Floor Coverings and is the direct responsibility of Subcommittee F06.80 onSpecifications.Cu
11、rrent edition approved May 1, 2010. Published June 2010. Originally approved in 1998. Last previous edition approved in 2009 as F1860 04(2009)1. DOI:10.1520/F1860-10.Current edition approved May 1, 2012. Published May 2012. Originally approved in 1998. Last previous edition approved in 2010 as F1860
12、-10. DOI: 10.1520/F1860-12.2For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards Document Summary page on the ASTM website.3Available from American Nationa
13、l Standards Institute (ANSI), 25 W. 43rd St., 4th Floor, New York, NY 10036, http:/www.ansi.org.1This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically p
14、ossible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the official document.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700,
15、 West Conshohocken, PA 19428-2959, United States.4.1.2 Type IILayered rubber sheet floor covering with backing:4.1.2.1Fibrous backing, and4.1.2.2Foamed rubber backing.4.2The above may have either smooth, embossed, or molded pattern surfaces.4.3These products shall not contain asbestos. Heterogeneous
16、4.2 GradesRubber sheet floor covering shall be one of the following grades:4.2.1 Grade 1Fibrous backing4.2.2 Grade 2Foamed rubber backing4.3 The above may have either smooth, embossed, or molded pattern surfaces.4.4 These products shall not contain asbestos.5. Ordering Information5.1 Purchasers shal
17、l state whether this specification is to be used, select the preferred options permitted herein and include thefollowing information in the invitation to bid or purchase order:5.1.1 Title, number, and date of this specification,5.1.2 Type, color, and surface (see Section 4 and Section 6),5.1.3 Quant
18、ity, in square feet, square yards, or square metres,5.1.4 Thickness required. (see 8.3),5.1.5 Overall thickness, if molded pattern flooring is specified (see 8.1),5.1.6 Width required (see 8.4),5.1.7 Length required (see 8.5),5.1.8 Resistance to chemicals, (see 7.4),5.1.9 Lot information, if other t
19、han as specified in AANSI/ASQC Z1.4. (see 10.1 and 11.1),5.1.10 Sampling, if other than as specified in ANSI/ASQC Z1.4 (see 10.1 and 11.1),5.1.11 Statement requesting certification, if certification of compliance is required (see 12.1),5.1.12 Packing requirements, if other than as specified (see 14.
20、1),5.1.13 Palletization, if required,5.1.14 Marking required, if other than specified (see 13.1), and5.1.15 Other requirements.6. Materials and Manufacture6.1 Homogeneous Rubber Sheet Floor CoveringThe product shall consist of a wear layer and backing. The surface coloringor mottling shall be unifor
21、m throughout the entire thickness of the wear layer. The backing shall be fibrous or foamed rubber andthoroughly bonded to the wear layer so as not to delaminate under normal use.6.2 Layered Rubber Sheet Floor CoveringHeterogeneous (Layered) Rubber Sheet Floor CoveringThe product shall consistof a w
22、ear layer, intermediate layer(s), and a backing. The surface coloring or mottling shall be uniform throughout the entirethickness of the wear layer, but need not extend through the intermediate layer(s). The backing shall be fibrous or foamed rubber.The wear layer, intermediate layer(s) and backing
23、shall be thoroughly bonded so as not to delaminate under normal use.6.3 Wear Layer:6.3.1 The polymeric binder of the wear layer shall satisfy the definition of rubber in Terminology D1566, and have beenvulcanized, as defined in Terminology D1566 (under vulcanization), such that it becomes thermoset
24、as defined in TerminologyD883. The wear layer made from this compound shall be resistant to neutral pH cleaners.6.3.2 The wear layer must have a minimum thickness of 0.040 in. (1.0 mm) when measured in accordance with Test MethodF410.6.3.3 The appearance of the rubber sheet floor covering after remo
25、ving 0.020 in. (0.51 mm) of the wear layer thickness, shallcompare favorably in appearance with the sheet floorings original appearance. The removal of the wear layer may beaccomplished by any suitable method.6.3.4 The wear layer may have a smooth, embossed, or molded pattern surface.6.4 Intermediat
26、e LayersThe layer(s) may consist of, but not be limited to, rubber, foamed rubber, or other materials, whichare intended to improve the performance characteristics of the product.6.5 BackingsThe composition of the backings shall be fibrous or foamed rubber and may contain other ingredients providedt
27、he resultant backing is suitable for installation on floors above-, on-, or below-grade when installed according to manufacturersinstallation recommendations.6.6 Color, Pattern, and Wearing SurfaceThe color, pattern, and wear layer surface, as applicable, shall be as specified in thecontract or orde
28、r (see 5.1).NOTE 1The colors and patterns that are available are indicated in individual manufacturers current catalogs. As manufactured, colors may varysomewhat in hue or shade from the catalog.NOTE 2Where color match is a concern, samples from the manufacturer shall be obtained to verify color acc
29、eptability.F1860 1227. Performance Requirements7.1 HardnessThe rubber sheet floor covering shall have a durometer hardness of not less than 85 (Shore, TypeA) when testedin accordance with Test Method D2240. The backing material shall be removed prior to testing and may be accomplished by anysuitable
30、 method.7.2 Modulus at 10 % ElongationWhen tested in accordance with Test Method D412 at a rate of 6 in. (152.4 mm)/min, usinga 1 in. (25.4 mm) by 5 in. (127 mm) gage length rectangular specimen, the modulus shall not be less than 300 psi (2.07 MPa).For molded pattern rubber sheet floor covering, th
31、e raised pattern shall be removed by any suitable method. Prior to testing, thebacking material shall be removed and may be accomplished by any suitable method.7.3 Static Load LimitWhen tested in accordance with Test Method F970, with an applied load of 250 lb (113.4 kg), theresidual indentation sha
32、ll not be greater than 0.005 in. (0.127 mm).7.4 Resistance to ChemicalsWhen tested in accordance with Test Method F925, the rubber sheet floor covering shall have nomore than a slight change in surface dulling, surface attack, or staining when exposed to the flowing chemicals:7.4.1 White vinegar (5
33、% acetic acid),7.4.2 Rubbing alcohol (70 % isopropyl alcohol),7.4.3 Sodium hydroxide solution (5 % NaOH),7.4.4 Hydrochloric acid solution (5 % HCl),7.4.5 Sulfuric acid solution (5 % H2SO4),7.4.6 Household ammonia solution (5 % NH4OH),7.4.7 Household bleach solution (5.25 % NaOCl),NOTE 3These basic c
34、hemicals are representative of those likely to be found in domestic, commercial, and institutional use. Many proprietarycompounds contain one or more of these basic chemicals. Should the flooring for an unusual application need to be resistant to a specific chemical, thisadditional requirement shoul
35、d become part of the procurement document, (see 5.1.8).NOTE 4Since standard SBR rubber flooring is not recoommended for installation where the product will be exposed to animal fats, vegetable oils,and petroleum-based reagents, mineral oil, olive oil, kerosene, and gasoline have been removed from th
36、e standard chemical list to eliminate any confusionregarding product selection.7.5 Resistance to HeatWhen tested in accordance to Test Method F1514, the color change of the rubber sheet floor coveringshall have an average DE not greater than 8.0 after seven days exposure to 158F (70C). The specimen
37、surface shall be wipedwith a clean, white cotton cloth prior to taking the initial and post test conditioned period color readings to remove any wax bloomor other contaminants which may affect the accuracy of the color readings.7.6 Resistance to LightWhen tested in accordance to Test Method F1515, t
38、he color change of the rubber sheet floor coveringshall have an average DE not greater than 8.0 after 300 h of exposure to light, simulated by a properly fitted xenon-arc radiantenergy source.8. Dimensions, Mass, and Permissible Variations8.1 Overall ThicknessMolded pattern rubber sheet floor coveri
39、ng shall be measured for overall thickness at the thickest crosssectional area of the flooring. The thickness of the molded pattern shall be uniform throughout the flooring.8.2 Base Thickness Molded pattern rubber sheet floor covering base thickness shall be measured at the thinnest cross sectionala
40、rea of the flooring. The thinnest cross sectional area shall be uniform throughout the flooring.8.3 ThicknessThe thickness of the rubber sheet floor covering shall be as specified in the contract or order (see 5.1.4). Anaverage tolerance, based on five individual measurements, of 60.008 in. (60.2 mm
41、) from the specified thickness shall be permittedin the base thickness alone or in combination with the overall thickness, when measured in accordance with Test Method F387.The difference between the five individual measurements can not be greater than 0.010 in. (0.25 mm) from the nominal thickness.
42、In the case of molded pattern rubber sheet floor covering, overall thickness and base thickness shall be reported.8.4 WidthThe width shall be as specified in the contract or order (see 5.1.6). The net width (gross width less selvages) shallnot be less than as marked on the label or package when meas
43、ured in accordance with 8.6.8.5 LengthThe length of the roll shall be as specified in the contract or order (see 5.1.7). The sheet length shall not be lessthan as marked on the label or package when measured in accordance with 8.6. Each roll shall be in one piece, except that lessthan 20 % of the ro
44、lls in any one shipment may consist of not more than two pieces, the shortest length shall not be less than 5linear yards (4.57 m), or as agreed upon by the purchaser and seller. Such rolls shall be clearly marked.8.6 Length and Width MeasurementsMeasurements shall be made with a calibrated 100 ft (
45、30 m) steel tape graduated atintervals of116 in. or 1 mm. The roll shall be extended to its full length on a flat surface and all creases and buckles removed,insofar as practical, without applying stresses that cause any significant stretching. Measurements of length shall be rounded to thenearest i
46、nch or 10 mm. Net width shall be measured to the nearest116 in. or 1 mm at not less than ten locations uniformlydistributed along the length of each roll, and the results averaged.9. Workmanship, Finish, and Appearance9.1 The rubber sheet floor covering furnished in accordance with this specificatio
47、n shall be an acceptable match to approvedsamples in color, pattern, and appearance. The product shall be free of defects, that adversely affect performance or appearance.Such defects include: blemishes, spots, lines, indentations, blisters, and delamination.F1860 12310. Sampling for Test10.1 Sampli
48、ng for testing physical characteristics listed in Table 1 shall be done in accordance with the provisions set forth inANSI/ASQC Z1.4. The inspection level shall be special inspection level S-1, as noted in Table I of ANSI/ASQC Z1.4, and theacceptable quality level (AQL) shall be 6.5 defects per hund
49、red units as noted in Table II-(A) of ANSI/ASQC Z1.4 or as otherwisespecified in 10.2. The lot size shall be expressed in units. A unit represents a single, manufactured, inventoried, finished roll.10.1.1 Samples shall be obtained in the required length from the outside end of the roll and shall encompass the total width ofthe material.10.2 Sampling for testing physical characteristics listed in Table 1 shall be agreed upon by the purchaser and the manufactureras part of the procurement document.11. Inspection11.1 Sampling for inspection of