ASTM F386-2002 Standard Test Method for Thickness of Resilient Flooring Materials Having Flat Surfaces《有平直表面的弹性铺地板材料厚度的标准试验方法》.pdf

1、Designation: F 386 02Standard Test Method forThickness of Resilient Flooring Materials Having FlatSurfaces1This standard is issued under the fixed designation F 386; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last

2、revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope1.1 This test method covers the determination

3、 of thicknessof resilient nontextile floor coverings including tile and sheethaving flat surfaces. This test method should not be used onmaterials having a foamed layer.1.2 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility o

4、f the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Significance and Use2.1 Measurement of the thickness of the product may berequired for quality control purposes or to ensure compliancewith app

5、licable specifications.3. Apparatus3.1 The apparatus shall consist of a comparator stand havinga flat anvil base at least 6 in. (15 cm) square, equipped with athickness gage graduated to 0.001 in. (0.02 mm). The gageshall be equipped with a flat presser foot 0.2506 0.01 in. (6.356 0.5 mm) in diamete

6、r. The foot shall exert a force of 16 6 0.1ozf (4.45 6 0.03 N) maximum.3.1.1 The contact surfaces of the anvil and the thicknessgage presser foot shall be parallel within 0.0001 in. (0.003mm).3.1.2 Before placing the micrometer into operation, thesurfaces shall be cleaned so the gage zeros properly.

7、4. Test Specimens4.1 The test specimen shall be a minimum of one tile or a 12by 12-in. (300 by 300-mm) piece of sheet flooring.5. Calibration5.1 Calibrate the gage by means of gage blocks or shimstock of known thickness appropriate to the thickness of thematerial being measured.6. Conditioning6.1 Co

8、ndition the test specimen at least 24 h at 736 3F (236 2C) and 50 6 5 % relative humidity and test in the sameenvironment.7. Procedure7.1 Place the specimen with the wearing surface upward onthe comparator stand anvil, taking care that the specimen is flatagainst the anvil.7.2 Lower the presser foot

9、 gently until it contacts thesurface of the specimen.7.3 Upon contact with the surface, take a reading to thenearest 0.001 in. (0.02 mm) from the gage. Take all measure-ments at least 0.75 in. (19 mm) from any edge of the specimen.7.4 Take a total of five measurements on each specimen, atrandomly se

10、lected locations unless otherwise specified.8. Calculation8.1 Calculate the average thickness of each specimen.9. Report9.1 Report the average thickness of each specimen to thenearest 0.001 in. (0.02 mm).9.1.1 Report the minimum or maximum thickness, or both ifrequired by the specification.10. Preci

11、sion and Bias10.1 Precision and Bias are being determined by interlabo-ratory study in compliance with ASTM specifications.11. Keywords11.1 flat surfaces; resilient flooring materials; thickness1This test method is under the jurisdiction of ASTM Committee F06 on ResilientFloor Coverings and is the d

12、irect responsibility of Subcommittee F06.20 on TestMethods Products Construction/Materials.Current edition approved April 10, 2002. Published July 2002. Originallypublished as F 386 73. Last previous edition F 386 93.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocke

13、n, PA 19428-2959, United States.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof

14、infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this st

15、andard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your

16、 views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).F 3862