1、Designation: F 519 08Standard Test Method forMechanical Hydrogen Embrittlement Evaluation of Plating/Coating Processes and Service Environments1This standard is issued under the fixed designation F 519; the number immediately following the designation indicates the year oforiginal adoption or, in th

2、e case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope1.1 This

3、test method describes mechanical test methods anddefines acceptance criteria for coating and plating processesthat can cause hydrogen embrittlement in steels. Subsequentexposure to chemicals encountered in service environments,such as fluids, cleaning treatments or maintenance chemicalsthat come in

4、contact with the plated/coated or bare surface ofthe steel, can also be evaluated.1.2 This test method is not intended to measure the relativesusceptibility of different steels. The relative susceptibility ofdifferent materials to hydrogen embrittlement may be deter-mined in accordance with Test Met

5、hod F 1459 and TestMethod F 1624.1.3 This test method specifies the use of air melted AISIE4340 steel per SAE AMS-S-5000 (formerly MIL-S-5000)heat treated to 260 280 ksi (pounds per square inch x 1000)as the baseline. This combination of alloy and heat treat levelhas been used for many years and a l

6、arge database has beenaccumulated in the aerospace industry on its specific responseto exposure to a wide variety of maintenance chemicals, orelectroplated coatings, or both. Components with ultimatestrengths higher than 260 280 ksi may not be represented bythe baseline. In such cases, the cognizant

7、 engineering authorityshall determine the need for manufacturing specimens from thespecific material and heat treat condition of the component.Deviations from the baseline shall be reported as required bysection 12.1.2. The sensitivity to hydrogen embrittlement shallbe demonstrated for each lot of s

8、pecimens as specified insection 9.5.1.4 Test procedures and acceptance requirements are speci-fied for seven specimens of different sizes, geometries, andloading configurations.1.5 Pass/Fail RequirementsFor plating/coating processes,specimens must meet or exceed 200 h using a sustained loadtest (SLT

9、) at the levels shown in Table 3.1.5.1 The loading conditions and pass/fail requirements forservice environments are specified in Annex A5.1.5.2 If approved by the cognizant engineering authority, aquantitative, accelerated (# 24 h) incremental step-load (ISL)test as defined in Annex A3 may be used

10、as an alternative toSLT.1.6 This test method is divided into two parts. The first partgives general information concerning requirements for hydro-gen embrittlement testing. The second is composed of annexesthat give specific requirements for the various loading andspecimen configurations covered by

11、this test method (seesection 9.1 for a list of types) and the details for testing serviceenvironments.1.7 The values stated in the foot-pound-second (fps) systemin inch-pound units are to be regarded as standard. The valuesgiven in parentheses are mathematical conversions to SI unitsthat are provide

12、d for information only and are not consideredstandard.1.8 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility

13、of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2B 374 Terminology Relating to ElectroplatingB 851 Specification forAutomated Controlled Shot Peeningof Metallic Articles Prior to Nickel, Autocatalytic Nickel,or Chromium Plating, or as Final FinishD 1193 Specification

14、 for Reagent WaterE4 Practices for Force Verification of Testing MachinesE8 Test Methods for Tension Testing of Metallic MaterialsE18 Test Methods for Rockwell Hardness of MetallicMaterialsE29 Practice for Using Significant Digits in Test Data to1This test method is under the jurisdiction of ASTM Co

15、mmittee F07 onAerospace and Aircraft and is the direct responsibility of Subcommittee F07.04 onHydrogen Embrittlement.Current edition approved May 1, 2008. Published July 2008. Originally approvedin 1977. Last previous edition approved in 2006 as F 519 062.2For referenced ASTM standards, visit the A

16、STM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, Uni

17、ted States.Determine Conformance with SpecificationsE 691 Practice for Conducting an Interlaboratory Study toDetermine the Precision of a Test MethodE 709 Guide for Magnetic Particle TestingE 1417 Practice for Liquid Penetrant TestingE 1444 Practice for Magnetic Particle TestingE 1823 Terminology Re

18、lating to Fatigue and Fracture Test-ingF 1459 Test Method for Determination of the Susceptibilityof Metallic Materials to Hydrogen Gas Embrittlement(HGE)F 1624 Test Method for Measurement of Hydrogen Em-brittlement Threshold in Steel by the Incremental StepLoading TechniqueF 2078 Terminology Relatin

19、g to Hydrogen EmbrittlementTestingG5 Reference Test Method for Making Potentiostatic andPotentiodynamic Anodic Polarization MeasurementsG38 Practice for Making and Using C-Ring Stress-Corrosion Test Specimens2.2 SAE AMS Standard:3AMS 2430 (R) Shot Peening, AutomaticAMS 2759/2 Heat Treatment of Low-A

20、lloy Steel PartsMinimum Tensile Strength 220 ksi (1517 MPa) andHigherAMS 2759/11 Stress Relief of Steel PartsAMS 6360 Steel Tubing, Seamless 0.95Cr 0.20Mo (0.28 0.33C) (SAE 4130) Normalized or Stress RelievedAMS-QQ-P-416 Plating, Cadmium (Electrodeposited)AMS-S-5000 Steel, Chrome-Nickel-Molybdenum (

21、E4340)Bars and Reforging Stock2.3 Military and Federal Standards and Commercial ItemDescriptions:4MIL-PRF-16173 Corrosion Preventive Compound, SolventCutback, Cold-ApplicationCommercial Item Description (CID) A-A-55827 ChromiumTrioxide, Technical3. Terminology3.1 DefinitionsDefinitions of terms used

22、 in this testmethod may be found in Terminology B 374, TerminologyE 1823 and Terminology F 2078.3.2 Acronyms and Abbreviations:AISI = American Iron and Steel Institutea/W = notch depth-to-width ratiod/D = ratio of minor to major diameters at the notchESH = Environmental, Safety and Healthfps = foot

23、pound secondHRC = Rockwell Hardness Scale CID = inside diameterISL = incremental step loadkip = pounds load multiplied by 1000ksi = pounds-force per square inch multiplied by 1000Kt= stress concentration factorLS = longitudinal short transverseNFS = notched fracture strengthOD = outside diameterpsi

24、= pounds-force per square inchRMS = root mean squareSAE AMS = Society of Automotive Engineers AerospaceMaterial SpecificationSCE = saturated calomel electrodeSLT = sustained load testT.I.R. = total indicated runout4. Summary of Test Methods4.1 Plating/coating ProcessesUnstressed test specimensare cl

25、eaned, plated/coated, and baked (if applicable) in accor-dance with the specification to which the process is to bequalified. Specimens are then maintained under a sustainedload in air to measure the time to rupture/completion of the testperiod.4.2 Service EnvironmentsSpecimens are tested in theserv

26、ice environment. The sequence of exposure to the environ-ment and loading shall be as defined in Annex A5. If plated/coated test specimens are to be utilized for evaluating a serviceenvironment, then the plating/coating process must first bedetermined to be acceptable in accordance with section 4.1.

27、5. Significance and Use5.1 Plating/coating ProcessesThis test method provides ameans by which to detect possible hydrogen embrittlement ofsteel parts during manufacture by verifying strict controlsduring production operations such as surface preparation,pretreatments, and plating/coating. It is also

28、 intended to beused as a qualification test for new plating/coating processesand as a periodic inspection audit for the control of aplating/coating process.5.2 Service EnvironmentThis test method provides ameans by which to detect possible hydrogen embrittlement ofsteel parts (plated/coated or bare)

29、 due to contact with chemicalsduring manufacturing, overhaul and service life. The details oftesting in a service environment are found in Annex A5.6. Apparatus6.1 Testing MachineTesting machines shall be within theguidelines of calibration, force range, resolution, and verifica-tion of Practices E4

30、.6.2 Gripping DevicesVarious types of gripping devicesmay be used in either tension or bending to transmit the loadapplied by the testing machine or self-loading frame to the testspecimen.6.3 Service Environment TestingFor testing in serviceenvironments, an inert container and fixture arrangement th

31、at issuitably electrically isolated from the specimen or compen-sated to prevent galvanic coupling shall be used for testing inaqueous environments. The corrosion potential of the specimenmay be controlled with a reference Saturated Calomel Elec-trode (SCE) or equivalent reference electrode such as

32、withAg/AgCl in accordance with Reference Test Method G5.3Available from Society of Automotive Engineers (SAE), 400 CommonwealthDr., Warrendale, PA 15096-0001, http:/www.sae.org.4Copies of these documents are available at http:/assist.dups.dla.mil/quicksearch/ or http:/assist.daps.dla.mil or from the

33、 Standardization DocumentOrder Desk, 700 Robins Ave., Building 4D, Philadelphia, PA 19111-5094.F5190827. Materials and Reagents7.1 Materials:7.1.1 Air melted AISI E4340 per AMS-S-5000 (formerlyMIL-S-5000).7.1.2 Aluminum oxide (150 grit or finer), and 180-gritsilicon-carbide paper.7.1.3 Conditioned s

34、hot, in accordance with AMS 2430.7.2 Reagents:7.2.1 Corrosion preventive compound, meeting the require-ments of MIL-PRF-16173, Grade 2.7.2.2 Cadmium cyanide electroplating bath (SAE AMS-QQ-P-416, formerly Federal Specification QQ-P-416. (Table2).7.2.3 Maintenance chemicals, cleaners, paint strippers

35、, andaqueous environments.7.2.4 Chromic acid (CID A-A-55827, formerly FederalSpecification O-C-303D).7.2.5 Water (Specification D 1193 Type IV).8. Hazards8.1 Environmental, Safety and Health (ESH):8.1.1 Equipment, materials, solutions, and emissions (ifapplicable) shall be controlled, handled, used,

36、 and disposed inaccordance with the applicable governing ESH regulations.9. Test Specimens9.1 Configuration9.1.1 Dimensional drawings with tolerances are given forthe two types of specimens in the following annexes:9.1.1.1 Type 1Notched SpecimensType 1a: Notched, Round, TensionType 1a.1Standard Size

37、per Fig. A1.1 Annex A1Type 1a.2Oversizedper Fig. A1.2 Annex A1Type 1b: Notched, Round, Tension Self Loading FixtureperFigs. A2.1-A2.5Annex A2Type 1c: Notched, Round, Bend Self Loading FixtureperFig. A2.6, Fig. A2.7Annex A2Type 1d: Notched, C-Ring, Bend Self Loading FixtureperFig. A2.8, Fig. A2.9Anne

38、x A2Type 1e: Notched, Square, Bendper Fig. A3.1 Annex A39.1.1.2 Type 2Smooth SpecimensType 2a: O-Ring, Bend Self Loading Fixtureper Fig. A4.1,Fig. A4.2Annex A49.1.2 The notched round tension, round bend and squarebend specimens shall be loaded in the longitudinal graindirection, but the C-Ring and O

39、-Ring can only be loadednormal to the longitudinal grain direction.9.2 Manufacture:9.2.1 Stress concentration factors (Kt) for each of thespecimen types were calculated using Finite Element Analysis(FEA) and the dimensions in the drawings.NOTE 1An ASTM Research Report documenting the analysis is inp

40、rocess and a reference number will be included in a future revision.Type KtMinimumANominal MaximumA1a.1 3.16 3.30 3.481a.2 3.31 3.59 3.761b 2.86 3.07 3.331c 3.30 3.45 3.621d 3.73 4.03 4.421e 3.95 4.27 4.602a NA NA NAAMinimum and maximum Kts calculated from worst case combinations ofdimensional toler

41、ances.9.2.2 If the 60 notch angle does not permit plating/coatingto the root of the notch, then an angle of 90 6 1 shall be usedonly with prior approval of the cognizant engineering author-ity.NOTE 2The FEA determined that changing the notch angle from 60to 90 had a negligible affect on the Kt. Ther

42、efore, no dimensional changesare required to compensate for this deviation. However, such deviationshall be reported as required in 12.1.2.9.2.3 The baseline material/condition for test specimens isnormalized and tempered, hot or cold drawn bar stock, airmelted AISI E4340 steel per AMS-S-5000 (forme

43、rly MIL-S-5000) heat treated perAMS 2759/2 ClassAto a tensile strengthbetween 260 and 280 ksi (51 to 53 Rockwell C Hardness Scale(HRC) as determined according to Test Methods E18. Round-ing per Practice E29permits an absolute hardness range of50.6 to 53.4 HRC of the average of three measurements.9.2

44、.3.1 Other steels or final hardnesses may only be substi-tuted if agreed upon by the cognizant engineering authority.Deviations from the baseline shall be reported as required in12.1.2.9.2.4 Rough machine blanks as required.9.2.5 Heat treat as a finished part to a strength level of 260to 280 ksi per

45、 AMS 2759/2 Class A as follows:9.2.5.1 Austenitize at 1500 1550F in a protective atmo-sphere and then quench in oil.9.2.5.2 Double temper, 2 h each, at 425 490F.9.2.6 Verify heat treat response by pulling 4 specimens inaccordance with Test Method E8and Table 1.9.2.7 Finish machine the reduced sectio

46、n and notch configu-ration.9.2.7.1 The entire notch shall be ground to size.9.2.7.2 Single-point machining of the notch is not permit-ted.9.2.7.3 Burnishing of the notch is not permitted.9.2.7.4 Shot peening/blasting/mechanical cleaning of thenotch during specimen manufacturing is not permitted.9.2.

47、8 After grinding, all specimens shall receive a stressrelief bake at 375 6 25F (190 6 14C) per AMS 2759/11 for45 h. A suitable protection from discoloration due to surfaceoxidization shall be used.9.2.9 Acid or cathodic electrolytic cleaning is prohibited.9.2.10 Straightening after final heat treatm

48、ent is prohibited.9.3 Storage:F5190839.3.1 After stress relief baking, all specimens shall beprotected during storage to prevent corrosion.Asuitable meansof protection is to coat the specimen with a corrosion preven-tive compound meeting the requirements of MIL-PRF-16173,Grade 2.9.4 Inspection:9.4.1

49、 A lot shall consist of those specimens cut from thesame heat of steel in the same orientation, heat treated togetherin the same furnace load, quenched and tempered together andsubjected to the same manufacturing processes together.9.4.2 All notched specimens in the lot shall be suitable fortest purposes if the inspection results on samples from that lotconform to the requirements of Table 1 and section 9.5.9.5 Sensitivity Test:9.5.1 The sensitivity to hydrogen embrittlement shall bedemonstrated for each lot of specimens by exposing s