ASTM F605-1988(2011) Standard Practice for Determining Compatibility of One-Time Carbon Paper with Carbonless Copy Papers When Interleaved into the Same Manifold Set《当夹在同一多份打印材料中时测.pdf

1、Designation: F605 88 (Reapproved 2011)Standard Practice forDetermining Compatibility of One-Time Carbon Paper withCarbonless Copy Papers When Interleaved into the SameManifold Set1This standard is issued under the fixed designation F605; the number immediately following the designation indicates the

2、 year of originaladoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A superscriptepsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This practice covers a procedure for determining th

3、ecompatibility of one-time carbon paper with carbonless copypapers, interleaved into the same manifold set by forced aging.1.2 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro

4、-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2D585 Practice for Sampling and Accepting a Single Lot ofPaper, Paperboard, Fiberboard, and Related Product3F221 Terminology Relating to Carbon Paper

5、and InkedRibbon Products and Images Made TherefromF497 Practice for Use of the Electric and Electronic Type-writer as a Test InstrumentF549 Terminology Relating to Carbonless Copy Products3. Terminology Definitions3.1 Refer to Terminology F221 and F549.4. Summary of Practice4.1 An evaluation is made

6、 by comparing the quality ofcarbonless copy images obtained with and without carboninterleaved and force-aged at elevated temperature and pres-sure conditions. One-time carbon paper samples are inter-leaved into the upper half of a business forms set. The set isforce-aged at elevated conditions of t

7、emperature and pressurefor three days on both the upper and lower halves. After aging,the carbon samples are removed and the manifold set is imagedat the top where carbon was interleaved and at the bottomwhere there was no carbon paper. The aged images arecompared for intensity, clarity, and cleanli

8、ness.5. Significance and Use5.1 This practice is used primarily to determine the compat-ibility of carbon paper samples with carbonless copy paper inthe same manifold set. That is, to observe if the carbon paperhas or has not had an adverse effect on the carbonless paperimage quality.5.2 This practi

9、ce can be used as an aid in predicting the fieldperformance of a specific carbon paper grade in an actualcarbonless form of designated composition.5.3 This practice can be used for research and development,production, and quality control purposes.6. Interferences6.1 Different typewriters can affect

10、the carbonless imagequality.6.2 Different pressures and settings on the same typewritercan affect the image quality.6.3 Platens of varying durometer in the same typewriter canaffect the image quality.6.4 Pressure, temperature, and time during forced-aging canaffect image quality.6.5 Different carbon

11、 coatings can affect image quality andcompatibility.7. Apparatus7.1 Commercial Electric Typewriter (see Practice F497).7.2 Paper Cutter (bench model), any size suitable forcutting carbonless copy paper and carbon samples.7.3 Paper Knife, suitable for sampling roll carbon paper.7.4 Parallel Weight Fi

12、xtures (see Fig. 1), used to applyuniform pressure to the manifold set at the interleaved andnoninterleaved areas.7.5 Template (see Fig. 2), used for drawing squares to aid inpositioning the parallel weight fixtures.1This practice is under the jurisdiction of ASTM Committee F05 on BusinessImaging Pr

13、oducts and is the direct responsibility of Subcommittee F05.06 onCarbonless and Thermal Imaging Products.Current edition approved Oct. 1, 2011. Published March 2012. Originallyapproved in 1978. Last previous edition approved in 2006 as F60588 (2006). DOI:10.1520/F0605-88R11.2For referenced ASTM stan

14、dards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Withdrawn. The last approved version of this historical standard is referencedon www.

15、astm.org.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.FIG. 1 Parallel Weight FixturesFIG. 2 TemplateF605 88 (2011)27.6 Drying Oven (constant temperature), equipped withmeans for ensuring adequate temperature and air circulation.7.

16、7 Weights, two 16-lb (7.26-kg), used to apply pressure tothe parallel weight fixtures. They shall be compact enough to fitinto the drying oven.8. Materials8.1 Carbonless Copy Paper Sheets (CF, CFB, and CBSheets).8.2 One-Time Carbon Paper Samples.8.3 Forms Bond Paper, 12 lb (17 by 22 by 500) (45.12g/

17、m2).9. Sampling9.1 Sample the roll or sheet carbon in accordance withMethods D585.10. Test Specimen and Sample10.1 Cut the carbonless sheets to 812 by 11 in. (216 by 279mm). The length should be in the machine direction, ifpossible.10.2 Cut the carbon paper samples to 812 by 412 in. (216 by114 mm),

18、with the 412-in. dimension in the machine direction.The number of carbon paper samples will be one less than thenumber of parts in the manifold set.11. Sample Preparation11.1 Type I Manifold Set Composition (Regular Configura-tion):11.1.1 Assemble a form set consisting of a CB sheet on top(CB side d

19、own); two CFB sheets directly below the CB sheet(CF sides up); a CF sheet below the last CFB sheet (CF sideup); 12-lb bond paper directly below the CF sheet (felt sideup).11.1.2 Staple the test set along the 812-in. (216-mm) width.11.1.3 Using the template, trace squares onto the first sheetof the f

20、orms set.11.1.4 On top of the form, clear of the test area, record thecolor, grade, weight, manufacturer, and other pertinent datarelating to the carbon sample and carbonless paper. Alsoinclude date for start of test.11.1.5 Interleave the carbon sample, coated side down,between the CF and bond paper

21、s on the top half of the form setonly (Note 1).NOTE 1If several manifold sets or carbon grades are to be testedsimultaneously, repeat steps 11.1.1 through 11.1.4 for each form set.11.2 Type II Manifold Set Composition (Upside DownConfiguration):11.2.1 Assemble a manifold set similar to 11.1.1 but om

22、it-ting the bond paper.11.2.2 Staple and trace squares on the top sheet as describedin 11.1.2, 11.1.3, also record information described in 11.1.4.11.2.3 Interleave the carbon sample coated side up betweenthe CB sheet and the CFB sheet so the carbon coating is nextto the CB coating on the CB sheet (

23、Note 2).NOTE 2If several manifold sets or carbon grades are to be testedsimultaneously, repeat 11.2.1 through 11.2.3.12. Procedure12.1 Place two sheets of forms bond paper between eachtest set to ensure no interaction.12.2 Place four sheets of forms bond paper at the top andbottom of the test pack.1

24、2.3 Using the template, trace squares onto the top andbottom sheets of the pack. Make sure the squares are super-imposed when the top and bottom sheets are in position.12.4 Place one parallel weight fixture into the center of thedrying oven.12.5 Insert the test pack into the drying oven, placing the

25、traced squares on the bottom of the pack directly over theparallel weight fixture.12.6 Place the second parallel fixture on top of the tracedsquares on the top sheet, thus superimposing both fixtures.Check for alignment.12.7 Place the two 16-lb weights in position on the top twoweight fixtures.12.8

26、Commence forced aging for 3 days, at 120F.12.9 After aging is completed, remove the weights, weightfixtures and test pack from the oven, and allow the aged formsto come to equilibrium at room temperature (1 to 2 h) withweights removed.12.10 Remove the unattached bond papers from betweenthe copysets

27、and discard.12.11 Remove the interleaved carbon paper samples fromthe copysets and discard.12.12 Type a designated pattern through the center of each2-in. traced square. Record the date, pressure, and settingcontrol as well as manufacturers model of typewriter. Allowapproximately 1 h before comparin

28、g images.12.13 Visually compare the post-aging images at top andbottom with each other. Note any differences in intensity, shadedifference, granularity, sharpness, oil bleed, background dis-coloration, etc.12.14 Repeat 12.11 through 12.13 for each test set agedsimultaneously.13. Interpretation of Re

29、sults13.1 Performing the test with and without carbon paper inthe same manifold set eliminates the effect of differencesbetween the carbonless papers. Any difference in image qualitywhere the carbon paper was interleaved is due to the effect ofthe carbon coating. This is a “go-no-go” test and a cont

30、rolcarbon or carbonless paper is not necessary.14. Precision and Bias14.1 Repeatable ranking order is obtained that is reproduc-ible within a laboratory and between laboratories. The test is acomparative test, is subjective, and no quantitative data areintended.15. Keywords15.1 carbonless copy paper

31、; carbonless paper; carbon paper;compatibility; interleaved set; manifold setF605 88 (2011)3ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determinatio

32、n of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdra

33、wn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your c

34、omments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single

35、or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).F605 88 (2011)4