ASTM F2163-2001(2008) Standard Specification for Ring Bearing Inner for Needle Roller Bearing With Drawn Outer Ring《带拉制外环的滚针滚柱轴承用轴承内环的标准规范》.pdf

1、Designation: F 2163 01 (Reapproved 2008)Standard Specification forRing, Bearing, Inner: for Needle Roller Bearing With DrawnOuter Ring1This standard is issued under the fixed designation F 2163; the number immediately following the designation indicates the year oforiginal adoption or, in the case o

2、f revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope1.1 This specific

3、ation covers inner rings for needle rollerbearings with drawn outer rings.1.2 The inner rings specified in this specification are in-tended for use on unhardened shafts in conjunction with openend needle roller bearings shown on Specification F 2162 andMS52141.1.3 The use of recycled materials that

4、meet the requirementsof the applicable material specification without jeopardizingthe intended use of the item is encouraged.1.4 The inner rings specified in this specification are notintended for use in flight-critical systems of aircraft.1.5 The values stated in inch-pound units are to be regarded

5、as standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.NOTE 1This specification contains many of the requirements ofMS17130, which was originally developed by the Department of Defenseand is currently

6、 maintained by the Defense Supply Center Richmond.2. Referenced Documents2.1 ASTM Standards:2E18 Test Methods for Rockwell Hardness and RockwellSuperficial Hardness of Metallic MaterialsF 2162 Specification for Bearing, Roller, Needle: DrawnOuter Ring, Full Complement, Without Inner Ring, Openand Cl

7、osed End, Standard Type2.2 ASME Standard:ASME B 46.1 Surface Texture Surface Roughness, Wavi-ness, and Lay32.3 SAE Standards:SAE AHS STD-664SAE J-404 Chemical Composition of SAE Alloy Steels42.4 Military Standards:MIL-STD-130 Identification Marking of US Military Prop-erty5MS52141 Bearing, Roller, N

8、eedle: Drawn Outer Ring,Caged, Without Inner Ring, Open and Closed End, Stan-dard Type52.5 American Bearing Manufacturers Association (ABMA)Standard:STD 4 Tolerance Definitions and Gauging Practices ForBall and Roller Bearings62.6 ISO Standard:ISO 5593 Rolling BearingsVocabulary73. Terminology3.1 De

9、finitionsFor definitions of terms used in this speci-fication, refer to ABMA STD 4 and ISO 5593.4. Ordering Information4.1 When ordering parts in accordance with this specifica-tion, specify the following:4.1.1 ASTM designation number, including year of issue;4.1.2 Dash number (see Table 1); and4.1.

10、3 Dimensions of inner rings, including:4.1.3.1 Bore diameter, in.;1This specification is under the jurisdiction ofASTM Committee F34 on RollingElement Bearings and is the direct responsibility of Subcommittee F34.04 onAutomotive/Industrial Bearing.Current edition approved May 1, 2008. Published Octo

11、ber 2008. Originallyapproved in 2001. Last previous edition approved in 2001 as F21630112For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summa

12、ry page onthe ASTM website.3Available from Global Engineering Documents, 15 Inverness Way, EastEnglewood, CO 80112-5704, http:/.4Available from Society of Automotive Engineers (SAE), 400 CommonwealthDr., Warrendale, PA 15096-0001, http:/www.sae.org.5Available from USA Information Systems, 1092 Laski

13、n Rd., Ste. 208, VirginiaBeach, VA 23451.6Available from the American Bearing Manufacturers Association, 1200 19thSt. NW, Ste. 300, Washington, DC 200362401.7Available from American National Standards Institute (ANSI), 25 W. 43rd St.,4th Floor, New York, NY 10036, http:/www.ansi.org.1Copyright ASTM

14、International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.4.1.3.2 Outside diameter, in.;4.1.3.3 Width, in.; and4.1.3.4 Radius, in.5. Materials and Manufacture5.1 Bearing inner rings shall be manufactured of steel, alloyor carbon, carburizing grade 4620, 4720,

15、 8620, 8720, or 1018,1022, or 1117 in accordance with SAE AHS STD-66 or SAEE52100 in accordance with SAE J-404.6. Other Requirements6.1 Heat Treatment:6.1.1 Steel 4620, 4720, 8620, 8720, 1018, 1022, and 1117shall be case hardened to Rockwell HRC58-65, in accordancewith Test Methods E18. Case depth s

16、hall be 0.020 minimum.6.1.2 Steel SAE 52100 shall be through hardened to Rock-well HRC58-65, in accordance with Test Methods E18.6.2 Protective Coating:6.2.1 Unless specified, plain (that is, not plated) inner ringsshall be furnished.6.2.2 Manufacturer shall coat inner rings with rust-preventative f

17、ilm.6.3 Lubrication:6.3.1 Oil hole(s), number (1 to 4) and size optional.6.3.2 An oil grove, centered in the inner ring bore, isoptional in accordance with manufacturers standard practice.7. Dimensions, Mass, and Permissible Variations7.1 Products manufactured in accordance with this specifi-cation

18、shall meet the requirements shown in Table 1.7.1.1 Given the shaft diameter and radial load for a particu-lar bearing application, the bore diameter of the inner ring isselected from the shaft size. The outer diameter and width arechosen by dimensionally mating the inner ring with the outerring (see

19、 Specification F 2162 or MS52141) that exhibits therequired load capacity.7.2 The taper in the shaft shall not exceed 0.0003 in. perinch of bearing length.TABLE 1 Inner Ring DimensionsDashNumberdBore Diameter, in.FOutside Diameter, in.BWidth, in.rRadius, in.MatingBearingsF 2162DashNumbersANominal Mi

20、nimum Maximum Nominal Minimum Maximum Minimum Maximum6138 0.3745 0.3750916 0.5620 0.5625 0.505 0.515 0.025 166238 0.3745 0.3750916 0.5620 0.5625 0.755 0.765 0.025 176338 0.3745 0.375058 0.6245 0.6250 0.505 0.515 0.025 18138 0.3745 0.375058 0.6245 0.6250 0.755 0.765 0.025 1964716 0.4370 0.437558 0.62

21、45 0.6250 0.776 0.789 0.025 196512 0.4995 0.500034 0.7495 0.7500 0.505 0.515 0.040 22212 0.4995 0.500034 0.7495 0.7500 0.755 0.765 0.040 23458 0.6245 0.625078 0.8745 0.8750 0.755 0.765 0.040 266658 0.6245 0.625078 0.8745 0.8750 1.005 1.015 0.040 27534 0.7495 0.7500 1 0.9995 1.0000 0.755 0.765 0.040

22、296734 0.7495 0.7500 1 0.9995 1.0000 1.005 1.015 0.040 3061316 0.8120 0.8125 1 0.9995 1.0000 0.755 0.765 0.040 2971316 0.8120 0.8125 1 0.9995 1.0000 1.005 1.015 0.040 30878 0.8745 0.8750 118 1.1245 1.1250 1.005 1.015 0.040 3391516 0.9370 0.9375 118 1.1245 1.1250 1.005 1.015 0.040 3310 1 0.9995 1.000

23、0 114 1.2495 1.2500 1.005 1.015 0.040 3511 1 0.9995 1.0000 114 1.2495 1.2500 1.255 1.265 0.040 3613 118 1.1245 1.1250 138 1.3745 1.3750 1.255 1.265 0.040 4014 1316 1.1870 1.1875 112 1.4995 1.5000 1.255 1.265 0.040 4315 114 1.2495 1.2500 112 1.4995 1.5000 1.005 1.015 0.060 4216 114 1.2495 1.2500 112

24、1.4995 1.5000 1.255 1.265 0.060 4318 138 1.3745 1.3750 158 1.6245 1.6250 1.255 1.265 0.060 4568 1716 1.4370 1.4375 134 1.7495 1.7500 1.505 1.515 0.060 4821 112 1.4995 1.5000 134 1.7495 1.7500 1.005 1.015 0.060 4769 112 1.4995 1.5000 134 1.7495 1.7500 1.505 1.515 0.060 4824 134 1.7495 1.7500 2116 2.0

25、620 2.0625 1.505 1.515 0.060 7270 178 1.8745 1.8750 218 2.1245 2.1250 1.505 1.515 0.060 5427 2 1.9995 2.0000 212 2.4995 2.5000 1.505 1.515 0.080 5771 212 2.4995 2.5000 234 2.7495 2.7500 1.005 1.015 0.060 59ADash numbers for mating bearings as specified in 7.1.1 of F 2162.FIG. 1 Schematic Drawing of

26、Inner RingF 2163 01 (2008)27.3 The inner ring must clear the maximum shaft filletradius shown in the radius column of Table 1. The radii orchamfers on the inner diameter of the ring may be unequal.Where the radii are unequal, the surface with the larger reliefshould be mounted against the shaft shou

27、lder.8. Workmanship, Finish and Appearance8.1 Surface FinishThe raceway (outside diameter) sur-face shall have a maximum surface roughness in accordancewith ASME B46.1 of 20 in. Ra.9. Inspection9.1 Inspection of the product shall be agreed upon betweenthe purchaser and the supplier as part of the pu

28、rchase contract.10. Rejection and Rehearing10.1 Products that fail to conform to the requirements of thisspecification may be rejected. Rejection should be reported tothe producer or supplier promptly and in writing. In case ofdissatisfaction with the results of the test, the producer orsupplier may

29、 make claim for rehearing.11. Certification11.1 When specified in the purchase order or contract, thepurchaser shall be furnished certification that samples repre-senting each lot have been either tested or inspected as directedin this specification and the requirements have been met. Whenspecified

30、in the purchase order or contract, a report of the testresults shall be furnished.12. Product Marking12.1 Marking shall consist of the part number and themanufacturers identification in accordance with MIL-STD130.12.2 On inner rings where the inside diameter relief radii arenot equal, the marking sh

31、all appear on the surface with thelesser radius.12.3 The part number shall consist of the MS17130 desig-nation number plus the dash number (see Table 1).13. Keywords13.1 drawn outer ring; inner ring; MS 17130; needle rollerbearingASTM International takes no position respecting the validity of any pa

32、tent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revisio

33、n at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your com

34、ments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyright

35、ed by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).F 2163 01 (2008)3