BS 2HC 204-1989 Specification for nickel-cobalt-chromium-aluminium-titanium-molybdenum alloy castings (Nickel base Co 15 0 Cr 10 0 Al 5 5 Ti 4 8 Mo 3 0)《镍-钴-铬-铝-钛-钼合金铸件规范(镍基钴15 0、铬.pdf

1、BRITISH STANDARD AEROSPACE SERIES BS 2HC 204: 1989 Specification for Nickel-cobalt- chromium-aluminium- titanium-molybdenum alloy castings (Nickel base Co 15.0, Cr 10.0, Al 5.5, Ti4.8, Mo 3.0) UDC 629.7:669.2452526712952814BS 2HC 204:1989 This British Standard, having been prepared under the directi

2、onof the Aerospace Standards Policy Committee ACE/-, was published under theauthority of the Board ofBSIand comes into effect on 31 October1989 BSI 12-1999 First published February 1973 First revision 31 October The following BSI references relate to the work on this standard: Committee reference AC

3、E/48 Draft for comment 88/70334 DC ISBN 0 580 17573 1 Committees responsible for this British Standard The preparation of this British Standard was entrusted by the Aerospace Standards Policy Committee (ACE/-) to Technical Committee ACE/48, upon which the following bodies were represented: British I

4、ndustrial Fasteners Federation British Steel Industry Ministry of Defence Seamless Steel Tube Association Society of British Aerospace Companies Limited Amendments issued since publication Amd. No. Date of issue CommentsBS2HC 204:1989 BSI 12-1999 i Contents Page Committees responsible Inside front c

5、over Foreword ii 1 Scope 1 2 References 1 3 Material requirements 1 Table 1 Material requirements 2BS 2HC 204:1989 ii BSI 12-1999 Foreword This revision supersedes BS HC 204:1973, which is withdrawn, and includes trace elements in the chemical composition and is presented in a tabular format. The ba

6、sic specification for the material remains unchanged. A British Standard does not purport to include all the necessary provisions of a contract. Users of British Standards are responsible for their correct application. Compliance with a British Standard does not of itself confer immunity from legal

7、obligations. Summary of pages This document comprises a front cover, an inside front cover, pages i and ii, pages1 and 2 and a back cover. This standard has been updated (see copyright date) and may have had amendments incorporated. This will be indicated in the amendment table on the inside front c

8、over.BS2HC 204:1989 BSI 12-1999 1 1 Scope This British Standard specifies the chemical composition, mechanical properties and inspection and test requirements for a heat resisting nickel alloy (Nickel base, Co 15.0, Cr 10.0, Al 5.5, Ti 4.8, Mo3.0) in the form of castings and remelting stock. 2 Refer

9、ences This standard makes reference to the following British Standards: BS HC 100, Inspection and testing procedure for iron, nickel, copper, cobalt and refractory metal base alloy castings. BS EN 2500, Aerospace series Guidelines for the preparation and use of standards for metallic materials 1) .

10、3 Material requirements The requirements for the material in the delivery and use of conditions are given in Table 1, the format and nomenclature of which complies with the requirements defined in BSEN2500. 1) In preparation.BS 2HC 204:1989 2 BSI 12-1999 Table 1 Material requirements 1 Chemical comp

11、osition % or (parts per million) Element C Si Mn S Ag Al As B Bi Cd Co Cr Cu Fe Ga In Min. 0.15 5.0 0.010 13.0 8.0 Max. 0.20 0.20 0.20 0.015 (5) 6.0 (30) 0.020 (0.5) (0.2) 17.0 11.0 0.20 1.0 (30) (0.2) Element Mg Mo Nb Pb Sb Se Sn Te Ti V W Zn Zr Mi Note (2) Min. 2.0 4.5 0.70 0.030 Base Max. (50) (1

12、) 4.0 0.25 (5) (3) (5) (30) (2) 5.0 1.20 0.20 (5) 0.09 2 1 2 3 3 Method of melting Vacuum melted and cast 4 Form Remelt stock Castings 5 Acceptance standard BS HC 100, sections 1 and 2 BS HC 100, sections 1 and 3 6 Delivery condition and heattreatment As cast 7 Use condition and heattreatment As cas

13、t 8 Test piece heattreatment sampling Cast None BS HC 100, sections 1 and 2 Separate or integral None See note 3 21 Stress rupture Temperature C 950 22 Time t h W 30 25 Rupture stress B R MPa 230 27 NOTES 1The magnesium content of the remelting stock shall be 10 W Mg W 50 p.p.m. 2The chemical compos

14、ition shall be controlled to limit the formation of Sigma phase. The method of control, the limits and the associated calculation shall be agreed between the manufacturer and the purchaser. 3If required, the properties to be obtained on test pieces machined from designated areas of casting shall be

15、agreed between the manufacturer and the purchaser.blankBS 2HC 204: 1989 BSI 389 Chiswick High Road London W4 4AL BSIBritishStandardsInstitution BSI is the independent national body responsible for preparing BritishStandards. It presents the UK view on standards in Europe and at the international lev

16、el. It is incorporated by Royal Charter. Revisions BritishStandards are updated by amendment or revision. Users of BritishStandards should make sure that they possess the latest amendments or editions. It is the constant aim of BSI to improve the quality of our products and services. We would be gra

17、teful if anyone finding an inaccuracy or ambiguity while using this BritishStandard would inform the Secretary of the technical committee responsible, the identity of which can be found on the inside front cover. Tel:02089969000. Fax:02089967400. BSI offers members an individual updating service cal

18、led PLUS which ensures that subscribers automatically receive the latest editions of standards. Buying standards Orders for all BSI, international and foreign standards publications should be addressed to Customer Services. Tel:02089969001. Fax:02089967001. In response to orders for international st

19、andards, it is BSI policy to supply the BSI implementation of those that have been published as BritishStandards, unless otherwise requested. Information on standards BSI provides a wide range of information on national, European and international standards through its Library and its Technical Help

20、 to Exporters Service. Various BSI electronic information services are also available which give details on all its products and services. Contact the Information Centre. Tel:02089967111. Fax:02089967048. Subscribing members of BSI are kept up to date with standards developments and receive substant

21、ial discounts on the purchase price of standards. For details of these and other benefits contact Membership Administration. Tel:02089967002. Fax:02089967001. Copyright Copyright subsists in all BSI publications. BSI also holds the copyright, in the UK, of the publications of the international stand

22、ardization bodies. Except as permitted under the Copyright, Designs and Patents Act 1988 no extract may be reproduced, stored in a retrieval system or transmitted in any form or by any means electronic, photocopying, recording or otherwise without prior written permission from BSI. This does not pre

23、clude the free use, in the course of implementing the standard, of necessary details such as symbols, and size, type or grade designations. If these details are to be used for any other purpose than implementation then the prior written permission of BSI must be obtained. If permission is granted, the terms may include royalty payments or a licensing agreement. Details and advice can be obtained from the Copyright Manager. Tel:02089967070.