BS 2L 93-1971 Specification for plate of aluminium-copper-magnesium-silicon-manganese alloy (solution treated controlled stretched and precipitation treated) (Cu 4 4 Mg 0 5 Si 0 7 .pdf

1、BRITISH STANDARD AEROSPACE SERIES BS 2L 93:1971 (Superseding BSL93) Incorporating Amendment No. 1 Specification for Plate of aluminium- copper-magnesium- silicon-manganese alloy (Solution treated, controlled stretched and precipitation treated) (Cu4.4, Mg0.5, Si0.7, Mn0.8) UDC 629.7:669.715372178274

2、-41BS2L93:1971 This British Standard, having been approved by the Aerospace Industry Standards Committee, was published underthe authorityofthe Executive Boardof the Institutionon 31August1971 BSI 01-2000 The following BSI references relate to the work on this standard: Committee reference ACE/24 Dr

3、aft for comment 69/23023 ISBN 0 580 06984 2 A British Standard does not purport to include all the necessary provisions of a contract. Users of British Standards are responsible for their correct application. Compliance with a British Standard does not of itself confer immunity from legal obligation

4、s. Summary of pages This document comprises a front cover, an inside front cover, pagesi andii, pages1 to3 and a back cover. This standard has been updated (see copyright date) and may have had amendments incorporated. This will be indicated in the amendment table on the inside front cover. Amendmen

5、ts issued since publication Amd. No. Date of issue Comments 6841 November 1991 Indicated by a sideline in the marginBS2L93:1971 BSI 01-2000 i Contents Page 1 Inspection and testing procedure 1 2 Quality of material 1 3 Chemical composition 1 4 Condition 1 5 Heat treatment 1 6 Mechanical properties 2

6、 Appendix A British Standards covering other forms of material of similar composition 3ii blankBS2L93:1971 BSI 01-2000 1 NOTE 1This British Standard covers plate, including that which has been forged as an intermediate operation, which is finished by hot or cold rolling. It does not cover forged pla

7、te which should be ordered to BS L 77. NOTE 2If material to this British Standard is re-solution treated but not again controlled stretched, it must be regarded as being in the solution treated and precipitation treated, but not controlled stretched, condition, even though the specified mechanical p

8、roperties are obtained. Plate of this composition in that condition is covered by BS L 94. NOTE 3The specified chemical composition and mechanical properties meet the requirements of A.I.C.M.A. Recommendation AL.P12. NOTE 4Other forms of material of similar composition are covered by British Standar

9、ds as listed inAppendix A. 1 Inspection and testing procedure This British Standard shall be used in conjunction with Sections1 and14 of BSL 100. 2 Quality of material The material shall be made from aluminium and alloying constituents, with or without approved scrap, at the discretion of the manufa

10、cturer. 3 Chemical composition The chemical composition of the material shall be: 4 Condition 4.1 Except as provided in 4.2, the material shall be supplied solution treated, controlled stretched, to a permanent extension of not less than 1“ % nor more than 3 %, and precipitation treated. 4.2 If agre

11、ed between the manufacturer and the purchaser and stated on the order, the material shall be supplied solution treated and controlled stretched to a permanent extension of not less than 1“ % nor more than 3 %. No other alternative condition of supply is permissible. 5 Heat treatment The material sha

12、ll be heat treated as follows: 1) Solution treat by heating at a temperature of505 5 C and quenching in water at a temperature not exceeding40 C. 2) Precipitation treat by heating uniformly for the requisite period at a temperature between160 C and190 C. Element % min. max. Copper 3.9 5.0 Magnesium

13、0.20 0.8 Silicon 0.50 0.90 Iron 0.5 Manganese 0.40 1.2 Nickel a 0.2 Zinc a 0.2 Lead a 0.05 Tin a 0.05 Titanium plus Zirconium a 0.2 Chromium a 0.10 Aluminium The remainder a Subject to the discretion of the Inspecting Authority, determination of these elements need be made on a small proportion only

14、 of the samples analysed.BS2L93:1971 2 BSI 01-2000 NOTEThe following temperatures and times at temperature have been found appropriate: 6 Mechanical properties 6.1 Tensile test. The mechanical properties obtained from test pieces selected and prepared in accordance with the relevant requirements of

15、BS L 100 shall be not less than the following values: Temperature Time at temperature C hours 165 12 to 18 175 9 to 12 185 3 to6 Nominal thickness Direction 0.2 % proof stress Tensile strength Elongation on gaugelengthof 50 mm 5.65 mm N/mm 2 N/mm 2 % % Over Up to and including 6 12.5 Long transverse

16、 410 460 7 12.5 25 Long transverse 410 460 6 25 40 Longitudinal Long transverse Short transverse 410 400 360 450 450 420 6 5 2.5 40 63 Longitudinal Long transverse Short transverse 400 390 360 430 430 420 6 5 2.5 63 90 Longitudinal Long transverse Short transverse 400 390 360 430 430 420 6 4 2.5 90

17、115 Longitudinal Long transverse Short transverse 380 370 340 430 420 410 6 4 2.5 115 140 Longitudinal Long transverse Short transverse 360 350 340 420 410 400 6 4 2.5 NOTE1 N/mm 2= 1 MN/m 2= 0.102 kgf/mm 2= 0.1 hbar = 0.065 tonf/in 2 . Information on SI units is given in BS3763 “The International S

18、ystem of units (SI)”, and in PD 5686, “The use of SI units”. See also BS350,“Conversion factors and tables”. S o BS2L93:1971 BSI 01-2000 3 Appendix A British Standards covering other forms of material of similar composition Form Solution treated and aged at room temperature Solution treated and prec

19、ipitation treated Supplied for solution treatment by the user Bars and extruded sections (not exceeding200mm diameter or minor sectional dimension) BS L 102 BS L 65 Forging stock and forgings BS L 103 BS L 77 Hexagonal bars for nuts, couplings and hollow machinedparts (free from peripheral and asymm

20、etriccoarse grain) BS L 87 Sheet and strip BS L 70 BS L 104 BS L 106 a Aluminium-coated sheet and strip BS L 72 BS L 73 BS L 107 a Close toleranced sheet and strip (aluminium-coated) BS L 89 BS L 90 BS L 108 a Tube (not exceeding10mm wall thickness) BS L 105 BS L 63 Wire for solid, cold-forged rivet

21、s (notexceeding10mm diameter) BS L 37 Plate: not controlled stretched BS L 94 a In course of preparation.BS 2L 93:1971 BSI 389 Chiswick High Road London W4 4AL BSIBritishStandardsInstitution BSI is the independent national body responsible for preparing BritishStandards. It presents the UK view on s

22、tandards in Europe and at the international level. It is incorporated by Royal Charter. Revisions BritishStandards are updated by amendment or revision. Users of BritishStandards should make sure that they possess the latest amendments or editions. It is the constant aim of BSI to improve the qualit

23、y of our products and services. We would be grateful if anyone finding an inaccuracy or ambiguity while using this BritishStandard would inform the Secretary of the technical committee responsible, the identity of which can be found on the inside front cover. Tel:02089969000. Fax:02089967400. BSI of

24、fers members an individual updating service called PLUS which ensures that subscribers automatically receive the latest editions of standards. Buying standards Orders for all BSI, international and foreign standards publications should be addressed to Customer Services. Tel:02089969001. Fax:02089967

25、001. In response to orders for international standards, it is BSI policy to supply the BSI implementation of those that have been published as BritishStandards, unless otherwise requested. Information on standards BSI provides a wide range of information on national, European and international stand

26、ards through its Library and its Technical Help to Exporters Service. Various BSI electronic information services are also available which give details on all its products and services. Contact the Information Centre. Tel:02089967111. Fax:02089967048. Subscribing members of BSI are kept up to date w

27、ith standards developments and receive substantial discounts on the purchase price of standards. For details of these and other benefits contact Membership Administration. Tel:02089967002. Fax:02089967001. Copyright Copyright subsists in all BSI publications. BSI also holds the copyright, in the UK,

28、 of the publications of the international standardization bodies. Except as permitted under the Copyright, Designs and Patents Act 1988 no extract may be reproduced, stored in a retrieval system or transmitted in any form or by any means electronic, photocopying, recording or otherwise without prior

29、 written permission from BSI. This does not preclude the free use, in the course of implementing the standard, of necessary details such as symbols, and size, type or grade designations. If these details are to be used for any other purpose than implementation then the prior written permission of BSI must be obtained. If permission is granted, the terms may include royalty payments or a licensing agreement. Details and advice can be obtained from the Copyright Manager. Tel:02089967070.