BS EN 1036-1-2007 Glass in building - Mirrors from silver-coated float glass for internal use - Definitions requirements and test methods《建筑玻璃 由镀银浮法玻璃制成的室内用镜子 定义、要求和试验方法》.pdf

1、BS EN1036-1:2007ICS 81.040.20NO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAWBRITISH STANDARDGlass in building Mirrors from silver-coated float glass forinternal usePart 1: Definitions, requirements andtest methodsLicensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 25/06/200

2、9 02:02, Uncontrolled Copy, (c) BSIThis British Standardwas published under theauthority of the StandardsPolicy and StrategyCommittee on 31 March2009 BSI 2009ISBN 978 0 580 58586 9Amendments/corrigenda issued since publicationDate CommentsBS EN 1036-1:2007National forewordThis British Standard is th

3、e UK implementation of EN 1036-1:2007. Itsupersedes BS EN 1036:1999 which is withdrawn.The UK participation in its preparation was entrusted to TechnicalCommittee B/520/1, Basic and transformed glass products.A list of organizations represented on this committee can be obtained onrequest to its secr

4、etary.This publication does not purport to include all the necessary provisionsof a contract. Users are responsible for its correct application.Compliance with a British Standard cannot confer immunityfrom legal obligations.Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 25/06/2009 02:02, Unc

5、ontrolled Copy, (c) BSIBS EN 1036-1:2007EUROPEAN STANDARDNORME EUROPENNEEUROPISCHE NORMEN 1036-1December 2007ICS 81.040.20 Supersedes EN 1036:1999 English VersionGlass in building - Mirrors from silver-coated float glass forinternal use - Part 1: Definitions, requirements and test methodsVerre dans

6、la construction - Miroirs en glace argente pourlintrieur - Partie 1: Dfinitions, exigences et mthodesdessaiGlas im Bauwesen - Spiegel aus silberbeschichtetemFloatglas fr den Innenbereich - Teil 1: Begriffe,Anforderungen und PrfverfahrenThis European Standard was approved by CEN on 12 November 2007.C

7、EN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this EuropeanStandard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such nationalstandards may be obtained on appl

8、ication to the CEN Management Centre or to any CEN member.This European Standard exists in three official versions (English, French, German). A version in any other language made by translationunder the responsibility of a CEN member into its own language and notified to the CEN Management Centre ha

9、s the same status as theofficial versions.CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland,France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portu

10、gal,Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.EUROPEAN COMMITTEE FOR STANDARDIZATIONCOMIT EUROPEN DE NORMALISATIONEUROPISCHES KOMITEE FR NORMUNGManagement Centre: rue de Stassart, 36 B-1050 Brussels 2007 CEN All rights of exploitation in any form and by any means res

11、ervedworldwide for CEN national Members.Ref. No. EN 1036-1:2007: ELicensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 25/06/2009 02:02, Uncontrolled Copy, (c) BSIBS EN 1036-1:2007EN 1036-1:2007 (E) 2 Contents Page Foreword4 1 Scope 5 2 Normative references 5 3 Terms and definitions .5 4 Materials

12、 .7 4.1 Glass products.7 4.2 Reflective coating 7 4.3 Protective coating(s) .7 5 Dimensional requirements7 5.1 Thickness .7 5.2 Length, width and squareness .8 5.2.1 Stock/standard sizes .8 5.2.2 As-cut finished sizes .8 6 Reflection characteristics of silvered mirrors 9 6.1 Measurement9 6.2 Silvere

13、d mirrors made from clear float glass .9 6.3 Silvered mirrors made from tinted float glass 9 7 Quality requirements.9 7.1 General9 7.2 Quality assessment and inspection methods for silvered mirrors 9 7.2.1 Glass, reflective coating, edge and protective coating quality.9 7.2.2 Optical quality 10 7.3

14、Acceptance levels10 7.3.1 Glass faults.10 7.3.2 Reflective silver coating faults.10 7.3.3 Edge faults10 7.3.4 Protective coating(s) faults.11 7.3.5 Optical fault 12 8 Testing of silvered mirror .13 8.1 Durability 13 8.1.1 General13 8.1.2 Test specimens13 8.1.3 Position of specimens.13 8.1.4 Evaluati

15、on.13 8.1.5 Acceptance criteria13 8.2 Protective coating(s) adhesion 14 Annex A (normative) Condensation water test in constant atmosphere .22 A.1 General22 A.2 Test conditions 22 A.3 Climatic testing device22 A.3.1 Climatic chamber.22 A.3.2 Installation of the climatic chamber.23 A.3.3 Device for t

16、he accommodation of the specimens (specimen holder)23 A.4 Procedure .23 A.4.1 Filling the floor trough 23 A.4.2 Specimens 23 A.4.3 Arrangement of the specimens23 Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 25/06/2009 02:02, Uncontrolled Copy, (c) BSIBS EN 1036-1:2007EN 1036-1:2007 (E) 3 A

17、.4.4 Test sequence24 A.4.5 End of test 24 A.4.6 Interruption 24 A.4.7 Cleaning procedure.24 A.5 Test report24 Annex B (informative) Fixing and cleaning of mirrors 26 B.1 General .26 B.2 Factors affecting durability 26 B.3 Factors affecting image distortion 27 Bibliography28 Licensed Copy: Wang Bin,

18、ISO/EXCHANGE CHINA STANDARDS, 25/06/2009 02:02, Uncontrolled Copy, (c) BSIBS EN 1036-1:2007EN 1036-1:2007 (E) 4 Foreword This document (EN 1036-1:2007) has been prepared by Technical Committee CEN/TC 129 “Glass in building”, the secretariat of which is held by NBN. This European Standard shall be gi

19、ven the status of a national standard, either by publication of an identical text or by endorsement, at the latest by June 2008, and conflicting national standards shall be withdrawn at the latest by June 2008. This document supersedes EN 1036:1999. EN 1036 Glass in building Mirrors from silver-coat

20、ed float glass for internal use consists of the following parts: Part 1: Definition, requirements and test methods Part 2: Evaluation of conformity; product standard According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implem

21、ent this European Standard: Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland a

22、nd the United Kingdom. Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 25/06/2009 02:02, Uncontrolled Copy, (c) BSIBS EN 1036-1:2007EN 1036-1:2007 (E) 5 1 Scope This European Standard specifies minimum quality requirements (in respect of optical, visual and edge faults) and durability tests f

23、or mirrors from silvered float glass for internal use in building. This European Standard applies only to mirrors from silvered glass manufactured from flat annealed clear or tinted float glass, 2 mm to 10 mm thickness, and supplied in stock/standard sizes and as-cut finished sizes. This European St

24、andard does not apply to mirrors from silvered glass manufactured from any basic glass other than float glass, any processed glass, i.e. thermally toughened safety glass, heat strengthened glass, chemically strengthened glass and laminated glass, and any bent glass. For mirrors from silvered glass u

25、sed in aggressive and/or constantly high humidity atmospheres, e.g. horse riding halls, swimming pools, medical baths, saunas etc. this European Standard is not applicable. This European Standard is not applicable to reflective glass for external glazing applications. This European Standard does not

26、 apply to framing, fixing or other support systems. NOTE Useful advice on these items is contained in the informative Annex B. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For u

27、ndated references, the latest edition of the referenced document (including any amendments) applies. EN 410, Glass in building Determination of luminous and solar characteristics of glazing EN 572-2, Glass in building Basic soda lime silicate glass products Part 2: Float glass EN ISO 2409, Paints an

28、d varnishes - Cross-cut test (ISO 2409:2007) EN ISO 9227, Corrosion tests in artificial atmospheres Salt spray tests (ISO 9227:2006) 3 Terms and definitions For the purposes of this document, the following terms and definitions apply. 3.1 float glass flat, transparent, clear or tinted soda-lime sili

29、cate glass having parallel and polished faces obtained by continuous casting and flotation on a metal bath (see EN 572-1 and EN 572-2) 3.2 mirror from silver-coated float glass flat annealed clear or tinted float glass whose rear surface has been coated with a protected reflective silver deposit 3.3

30、 copper-free mirror from silver-coated float glass flat annealed clear or tinted float glass whose rear surface has been coated with a protected reflective silver deposit without use of copper Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 25/06/2009 02:02, Uncontrolled Copy, (c) BSIBS EN 10

31、36-1:2007EN 1036-1:2007 (E) 6 3.4 stock/standard sizes panes of mirrors from silver-coated float glass supplied with as-cut edges which are intended for further processing NOTE For dimensions of jumbo sizes and split sizes see EN 572-2. 3.5 as-cut finished sizes finished panes of mirrors from silver

32、-coated float glass cut from stock/standard sizes NOTE They can be subject to further processing, e.g. edge working, drilling, face decoration. 3.6 optical faults faults directly associated with the distortion of the reflected image 3.7 glass appearance faults faults which alter the visual quality o

33、f the mirror from silver-coated float glass. They can be spot and/or linear and/or enlarged area faults 3.8 spot faults nuclei (solid or gaseous inclusions), deposits, crush marks etc. In certain instances spot faults are accompanied by a distortion zone called halo. The nucleus of the spot fault is

34、 measurable 3.9 linear defects scratches, extended spot faults etc. 3.10 brush marks very fine circular scratches that can hardly be seen and are associated with glass cleaning techniques 3.11 scratches any kind of scratches that are not brush marks 3.12 reflective silver coating faults faults in th

35、e reflective silver layer which will alter the appearance of the silvered glass. They consist of scratches, stain, colour spots and edge deterioration 3.13 stain alteration of the reflective coating characterized by a more or less brownish, yellowish or greyish colouration of zones which can sometim

36、es cover the whole reflective surface 3.14 colour spots alteration of the reflective coating in the form of small, generally coloured spots 3.15 edge deterioration discolouration of the reflective silver at the edge of the silvered glass Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 25/06/2

37、009 02:02, Uncontrolled Copy, (c) BSIBS EN 1036-1:2007EN 1036-1:2007 (E) 7 3.16 protective coating(s) faults faults where the metallic layer is exposed. They can be scratches or loss of adhesion of the protective coating(s) 3.17 edge faults faults that affect the as-cut edge of the silvered glass. T

38、hey can include entrant/emergent faults, shelling, corners on/off and vents 3.18 pack area total surface area of the contents of a pack 3.19 cluster group of not less than 3 spot faults, separated by not more than 50 mm 3.20 halo distortion zone around a spot fault (see 3.8) 4 Materials 4.1 Glass pr

39、oducts Mirror from silver-coated float glass, according to this European Standard, shall be manufactured from monolithic float glass conforming to EN 572-2. 4.2 Reflective coating In order to provide the quality of a silvered mirror reflection, the mirror shall be manufactured with at least 0,7 g/m

40、of silver. 4.3 Protective coating(s) The reflective coating described in 4.2 shall be protected by a layer of metallic copper or another material and one or more protective coatings e.g. paint, lacquer. 5 Dimensional requirements 5.1 Thickness The actual thickness shall be the average of four measur

41、ements, taken to the nearest 0,01 mm, one taken at the centre of each side. Measurement shall be by means of an instrument of the calliper micrometer type. The actual thickness, rounded to the nearest 0,1 mm shall not vary from the nominal thickness by more than the tolerances shown in Table 1. Lice

42、nsed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 25/06/2009 02:02, Uncontrolled Copy, (c) BSIBS EN 1036-1:2007EN 1036-1:2007 (E) 8 Table 1 Thickness and tolerances Nominal thickness (mm) Thickness tolerances (mm) 2 3 4 5 6 8 10 0,2 0,2 0,2 0,2 0,2 0,3 0,3 5.2 Length, width and squareness 5.2.1 Sto

43、ck/standard sizes Length, H, and width, B, are defined with reference to the direction of draw of the float glass ribbon as shown in Figure 1. The nominal dimensions for length, H, and width, B, being given, the pane shall not be larger than a prescribed rectangle resulting from the nominal dimensio

44、ns increased by the tolerance, nor smaller than a rectangle defined by their nominal dimensions reduced by the tolerance The sides of the prescribed rectangles shall be parallel to one another and these rectangles shall have a common centre. For stock/standard sizes the tolerances on nominal dimensi

45、ons length, H, and width, B, are 5 mm. The limits of squareness shall also be described by these rectangles (see Figure 2). 5.2.2 As-cut finished sizes For dimensions less than or equal to 2 000 mm, the standard tolerance range is 2 mm, to be stated as 1 mm of the nominal dimension. For dimensions g

46、reater than 2 000 mm, the standard tolerance range is 3 mm to be stated as 1,5 mm of the nominal value. The standard tolerance range to be applied shall be determined by the largest dimension of the pane. The squareness tolerance shall be expressed as the difference in length between the diagonal di

47、mensions of the pane. For plates with both dimensions less than or equal to 2 000 mm the difference shall not exceed 3 mm. For plates with one (or both) dimensions greater than 2 000 mm the difference shall not exceed 4 mm. NOTE The method of determining squareness tolerance is different from that a

48、pplied to standard or stock sizes or in standards for other types of glass products. Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 25/06/2009 02:02, Uncontrolled Copy, (c) BSIBS EN 1036-1:2007EN 1036-1:2007 (E) 9 6 Reflection characteristics of silvered mirrors 6.1 Measurement Measurement o

49、f reflectance shall be undertaken in accordance with the principle of EN 410, but with the angle of incidence of the light within 8 of normal. Illuminant will be D65 and observer 2. 6.2 Silvered mirrors made from clear float glass The regular luminous coefficient of silvered mirrors made from clear float glass shall be at least: - 86 % for float with a thickness between 2 mm and 6 mm; - 83 % for float with a thickness of 8 mm and 10 mm. 6.3 Silvered mirrors made from tinted float glass Silvered mirrors made from tinted float glass have a