BS EN 725-3-2007 Advanced technical ceramics - Methods of test for ceramic powders - Part 3 Determination of the oxygen content of nonoxides by thermal extraction with a carrier ga.pdf

1、BS EN 725-3:2007ICS 81.060.30NO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAWBRITISH STANDARDAdvanced technicalceramics Methodsof test for ceramicpowdersPart 3: Determination of the oxygencontent of nonoxides by thermalextraction with a carrier gasLicensed Copy: Wang Bin, ISO/E

2、XCHANGE CHINA STANDARDS, 13/01/2009 07:01, Uncontrolled Copy, (c) BSIThis British Standardwas published underthe authority of theStandards Policy andStrategy Committee on 31 BSI 2008ISBN 978 0 580 54525 2Amendments/corrigenda issued since publicationDate CommentsBS EN 725-3:2007National forewordThis

3、 British Standard is the UK implementation of . It supersedes BSEN 725-3:1994 which is withdrawn.The UK participation in its preparation was entrusted to TechnicalCommittee RPI/13, Advanced technical ceramics.A list of organizations represented on this committee can be obtained onrequest to its secr

4、etary.This publication does not purport to include all the necessary provisionsof a contract. Users are responsible for its correct application.Compliance with a British Standard cannot confer immunityfrom legal obligations.October 2008Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 13/01/200

5、9 07:01, Uncontrolled Copy, (c) BSIBS EN 725-3:2007EUROPEAN STANDARDNORME EUROPENNEEUROPISCHE NORMEN 725-3January 2007ICS 81.060.30 Supersedes EN 725-3:1994 English VersionAdvanced technical ceramics - Methods of test for ceramicpowders - Part 3: Determination of the oxygen content of non-oxides by

6、thermal extraction with a carrier gasCramiques techniques avances - Mthodes dessaispour poudres cramiques - Partie 3: Dtermination de lateneur en oxygne de poudres non-oxydes par extraction chaud sous gaz porteurHochleistungskeramik - Prfverfahren fr keramischePulver - Teil 3: Bestimmung des Sauerst

7、offgehaltes inNichtoxid-Pulvern mittels TrgergasheiextraktionThis European Standard was approved by CEN on 2 December 2006.CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this EuropeanStandard the status of a national standard witho

8、ut any alteration. Up-to-date lists and bibliographical references concerning such nationalstandards may be obtained on application to the CEN Management Centre or to any CEN member.This European Standard exists in three official versions (English, French, German). A version in any other language ma

9、de by translationunder the responsibility of a CEN member into its own language and notified to the CEN Management Centre has the same status as theofficial versions.CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland,France,

10、 Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal,Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.EUROPEAN COMMITTEE FOR STANDARDIZATIONCOMIT EUROPEN DE NORMALISATIONEUROPISCHES KOMITEE FR NORMUN

11、GManagement Centre: rue de Stassart, 36 B-1050 Brussels 2007 CEN All rights of exploitation in any form and by any means reservedworldwide for CEN national Members.Ref. No. EN 725-3:2007: ELicensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 13/01/2009 07:01, Uncontrolled Copy, (c) BSIBS EN 725-3:

12、2007EN 725-3:2007 (E) 2 Contents Page Foreword3 1 Scope 4 2 Normative references 4 3 Principle4 4 Apparatus .4 5 Sample preparation .5 6 Calibration 5 7 Blank determination 5 8 Procedure .5 9 Test report 6 Annex A (informative) Guidance in the selection of test conditions .7 Licensed Copy: Wang Bin,

13、 ISO/EXCHANGE CHINA STANDARDS, 13/01/2009 07:01, Uncontrolled Copy, (c) BSIBS EN 725-3:2007EN 725-3:2007 (E) 3 Foreword This document (EN 725-3:2007) has been prepared by Technical Committee CEN/TC 184 “Advanced technical ceramics”, the secretariat of which is held by BSI. This European Standard sha

14、ll be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by July 2007, and conflicting national standards shall be withdrawn at the latest by July 2007. This document supersedes EN 725-3:1994. EN 725 Advanced technical ceramics Method

15、s of test for ceramic powders was prepared in Parts as follows: Part 1: Determination of impurities in alumina Part 2: Determination of impurities in barium titanate Part 3: Determination of the oxygen content of non-oxides by thermal extraction with a carrier gas Part 4: Determination of oxygen con

16、tent in aluminium nitride by XRF analysis Part 5: Determination of particle size distribution Part 6: Determination of the specific surface area withdrawn Part 7: Determination of the absolute density withdrawn Part 8: Determination of tapped bulk density Part 9: Determination of un-tapped bulk dens

17、ity Part 10: Determination of compaction properties Part 11: Determination of densification on natural sintering Part 12: Chemical analysis of zirconia Parts 6 and 7 of the series were superseded in 2005 by EN ISO 18757 and EN ISO 18753 respectively. According to the CEN/CENELEC Internal Regulations

18、, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands

19、, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom. Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 13/01/2009 07:01, Uncontrolled Copy, (c) BSIBS EN 725-3:2007EN 725-3:2007 (E) 4 1 Scope This part of EN 725 describes a method for the determ

20、ination of the oxygen content of non-oxide powders used for advanced technical ceramics, using an inert carrier gas thermal extraction method. The method described is suitable for oxygen contents of less than 3 %. NOTE An indication of the limits of determination is usually given by the manufacturer

21、s of the gas analysis apparatus used. However, for a specific measurement procedure, such limits can be determined by experiments conducted by the user. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the ed

22、ition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN ISO/IEC 17025, General requirements for the competence of testing and calibration laboratories (ISO/IEC 17025:2005) 3 Principle A test sample is heated in a graphite cruc

23、ible at a high temperature in a flow of an inert carrier gas. Oxygen in the sample is converted to oxides of carbon, which are extracted and transformed to consist entirely of either carbon monoxide or carbon dioxide. This volume is then determined by a method of gas analysis. NOTE Guidance on the s

24、election of test conditions is given in Annex A. 4 Apparatus 4.1 Scoop, for transferring the test sample. 4.2 Graphite crucible, which is used as a carbon source. The crucible is capable of being electrically heated by two electrodes, or by induction. 4.3 Tin or nickel capsule (optional), to contain

25、 the ceramic powder sample. 4.4 Nickel wire basket (optional), for use as a fluxing agent with certain powders such as aluminium nitride. 4.5 Gas analysis apparatus, based on one of the following techniques: a) volumetric analysis, for measurement of carbon monoxide gas; b) chromatography, for carbo

26、n monoxide; c) thermal conductivity, for carbon monoxide and carbon dioxide; d) coulometric analysis, for carbon dioxide; e) infrared absorption, for carbon dioxide; f) gravimetry, by absorption of carbon dioxide. Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 13/01/2009 07:01, Uncontrolled

27、Copy, (c) BSIBS EN 725-3:2007EN 725-3:2007 (E) 5 4.6 Furnace, normally capable of reaching at least 2500 C operating in an inert gas atmosphere (nitrogen, helium or argon). NOTE A furnace which does not achieve 2500 C may be used for lower test temperatures, but 2500 C will be needed to give the cor

28、rect result for certain types of material. 5 Sample preparation Take a sample of the dry powder, the amount taken being based on the detection limit of the gas analysis apparatus (4.5) used and on the expected oxygen content of the powder. EXAMPLE For infrared absorption (see 4.5 e), samples of 100

29、mg to 300 mg should be used. NOTE The measured (total) oxygen content consists of a contribution from surface and bulk. Use a scoop (4.1) to transfer the powder and place the sample either directly in the crucible (4.2) or in the tin capsule (4.3). If the capsule is used, squeeze it to expel air and

30、 then fold over the open end several times, weighing again after squeezing. 6 Calibration Calibration shall be carried out preferably by using a reference material of certified oxygen content to calibrate the furnace (4.6) and gas analysis apparatus (4.5), using the procedure given in Clause 8. An a

31、lternative method is to use a sample of pure carbon monoxide or carbon dioxide gas to calibrate the gas analysis apparatus, with a minimum of three results being recorded. NOTE Since gas calibration only calibrates the detection and not the extraction efficiency, gas calibration does not automatical

32、ly guarantee correct results. The same applies if sample and calibration material are not very similar. 7 Blank determination Carry out a blank determination for each measurement run. Use the procedure given in Clause 8 and record the amount of gas evolved. Use this blank value to calculate the resu

33、lts for the sample analysis. 8 Procedure 8.1 Heat the empty graphite crucible (4.2) inside the furnace (4.6) to a temperature higher than the temperature for analysis. Record the flow of gas used in the furnace. Cool to ambient temperature. NOTE 1 This is to prevent additional degassing of the cruci

34、ble during the test run, which would produce errors. NOTE 2 A recommendation for gas flow will normally be given by the manufacturer of the gas analysis apparatus (4.5). 8.2 Place the tin (or nickel) capsule (4.3) and sample in the crucible (4.2). Select a temperature which is high enough to dissoci

35、ate the oxides to be determined (see Annex A). Use the nickel wire basket (4.4) if the preliminary tests indicate that it is necessary. Heat the furnace to the test temperature and record the temperature and the length of time at temperature. Collect the gas evolved and measure the amount, using one

36、 of the analytical techniques listed in 4.5. 8.3 Repeat the procedure given in Clause 5 and 8.2 at least four times. Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 13/01/2009 07:01, Uncontrolled Copy, (c) BSIBS EN 725-3:2007EN 725-3:2007 (E) 6 9 Test report The test report shall be in accord

37、ance with the reporting provisions of EN ISO/IEC 17025 and shall include at least the following information: a) name and address of the testing establishment; b) date of the test; c) on each page, a unique report identification and page number; d) customer name and address; e) reference to this stan

38、dard, i.e. determined in accordance with EN 725-3; f) authorising signature; g) any deviation from the method described, with appropriate validation, i.e. demonstrated to be acceptable to the parties involved; h) description of the test material (manufacturer, type, batch or code number); i) type of

39、 analytical equipment used (see 4.5); j) method of calibration (see Clause 6); k) purity of the carrier gas and gas used for calibration; the calibration material used with its certified oxygen content; l) mass of the samples and reference to optional use of the tin capsule (see 4.3); m) test temper

40、ature; n) individual values of oxygen content, mean value and standard deviation; o) comments about the test or test results. Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 13/01/2009 07:01, Uncontrolled Copy, (c) BSIBS EN 725-3:2007EN 725-3:2007 (E) 7 Annex A (informative) Guidance in the s

41、election of test conditions Because of the large variety of ceramic powders in use and number of analytical techniques available, it is not possible to specify test conditions (amount of sample, temperature, gas flow rate, analytical technique) that will be applicable to every determination. It is t

42、herefore recommended that the optimum conditions for testing a material be determined by preliminary tests. This may be done by carrying out successive tests on the same test sample, increasing the heating power until the measured oxygen content reaches a maximum, constant value. Fluxing agents (see

43、 4.4) may also be used. When the test conditions have been established, a certified reference material of the same chemical type as the test sample should be tested to check. Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 13/01/2009 07:01, Uncontrolled Copy, (c) BSIBS EN725-3:2007BSI GroupHe

44、adquarters 389Chiswick High Road,London, W4 4AL, UKTel +44 (0)20 8996 9001Fax +44 (0)20 8996 - British Standards InstitutionBSI is the independent national body responsible for preparing BritishStandards. It presents the UK view on standards in Europe and at theinternational level. It is incorporat

45、ed by Royal Charter.RevisionsBritish Standards are updated by amendment or revision. Users of BritishStandards should make sure that they possess the latest amendments oreditions.It is the constant aim of BSI to improve the quality of our products and services.We would be grateful if anyone finding

46、an inaccuracy or ambiguity while usingthis British Standard would inform the Secretary of the technical committeeresponsible, the identity of which can be found on the inside front cover. Tel:+44 (0)20 8996 9000. Fax: +44 (0)20 8996 7400.BSI offers members an individual updating service called PLUS

47、which ensuresthat subscribers automatically receive the latest editions of standards.Buying standardsOrders for all BSI, international and foreign standards publications should beaddressed to Customer Services. Tel: +44 (0)20 8996 9001. Fax: +44 (0)20 89967001 Email: You may also buy directly using

48、 a debit/creditcard from the BSI Shop on the Website http:/ response to orders for international standards, it is BSI policy to supply theBSI implementation of those that have been published as British Standards,unless otherwise requested.Information on standardsBSI provides a wide range of informat

49、ion on national, European andinternational standards through its Library and its Technical Help to ExportersService. Various BSI electronic information services are also available whichgive details on all its products and services. Contact Information Centre. Tel:+44 (0)20 8996 7111 Fax: +44 (0)20 8996 7048 Email: Subscribing members of BSI are kept up to date with standards developmentsand receive substantial discounts on the purchase price of standards. For detail