BS EN 13301-2010 Bitumen and bituminous binders - Determination of staining tendency of bitumen《沥青和沥青粘合剂 沥青的染色趋势的测定》.pdf

1、BS EN 13301:2010BS 2000-504:2010ICS 75.140; 91.100.50NO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAWBRITISH STANDARDBitumen and bituminous binders Determination of staining tendency of bitumenLicensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 08/07/2010 01:59, Uncontrolled

2、 Copy, (c) BSIThis British Standard was published under the authority of the Standards Policy and Strategy Committee on 31 March 2010 BSI 2010ISBN 978 0 580 62919 8Amendments/corrigenda issued since publicationDate CommentsBS EN 13301:2010National forewordThis British Standard is the UK implementati

3、on of EN 13301:2010. Itsupersedes BS EN 13301:2003 which is withdrawn.The UK participation in its preparation was entrusted to TechnicalCommittee PTI/13, Petroleum Testing and Terminology.A list of organizations represented on this committee can be obtained onrequest to its secretary.Energy Institut

4、e, under the brand of IP, publishes and sells all Parts of BS 2000, and all BS EN petroleum test methods that would be Part of BS 2000, both in its annual publication “Standard methods for analysis and testing of petroleum and related products and British Standard 2000 Parts” and individually.Furthe

5、r information is available from:Energy Institute, 61 New Cavendish Street, London W1G 7AR. Tel: 020 7467 7100. Fax: 020 7255 1472.This publication does not purport to include all the necessary provisionsof a contract. Users are responsible for its correct application. Compliance with a British Stand

6、ard cannot confer immunityfrom legal obligations.Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 08/07/2010 01:59, Uncontrolled Copy, (c) BSIBS EN 13301:2010EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 13301 March 2010 ICS 75.140; 91.100.50 Supersedes EN 13301:2003English Version Bitu

7、men and bituminous binders - Determination of staining tendency of bitumen Bitumes et liants bitumineux - Determination de la tendance lexsudation des bitumes Bitumen und bitumenhaltige Bindemittel - Bestimmung der Auslneigung von Bitumen This European Standard was approved by CEN on 23 January 2010

8、. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on

9、 application to the CEN Management Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN Management Ce

10、ntre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, No

11、rway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG Management Centre: Avenue Marnix 17, B-1000 Brussels 2010 CEN All rights of exploitation in any for

12、m and by any means reserved worldwide for CEN national Members. Ref. No. EN 13301:2010: ELicensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 08/07/2010 01:59, Uncontrolled Copy, (c) BSIBS EN 13301:2010EN 13301:2010 (E) 2 Contents Page Foreword 31 Scope 42 Normative references 43 Terms and definit

13、ions .44 Principle 45 Apparatus .46 Sampling .67 Procedure .67.1 Sample preparation .67.2 Filling of the rings 67.3 Filling of the rings (alternative procedure to 7.2) .67.4 Oven conditioning and measurement .68 Calculation 79 Expression of results 710 Precision .710.1 Repeatability .710.2 Reproduci

14、bility .711 Test report 7Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 08/07/2010 01:59, Uncontrolled Copy, (c) BSIBS EN 13301:2010EN 13301:2010 (E) 3 Foreword This document (EN 13301:2010) has been prepared by Technical Committee CEN/TC 336 “Bituminous binders”, the secretariat of which is

15、 held by AFNOR. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by September 2010, and conflicting national standards shall be withdrawn at the latest by September 2010. Attention is drawn to the pos

16、sibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. This document supersedes EN 13301:2003. This document contains three significant changes compared to EN 13301:2003:

17、 1) The filter paper specified in Clause 5.4 is now described in technical terms, and not by reference to commercial grades of filter paper (like Whatman No. 40). 2) Now there exist two procedures of equal standing for filling the rings (Clause 7.2 and Clause 7.3) to be chosen by the individual labo

18、ratory. 3) Results are rounded to nearest 0,5 mm. According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland,

19、France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and the United Kingdom. Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 08/07/2010 01:59, Uncontrolle

20、d Copy, (c) BSIBS EN 13301:2010EN 13301:2010 (E) 4 1 Scope This European Standard specifies a method for the determination of the staining tendency of bitumen. This method is applicable to bitumen having a Ring-and-Ball softening point greater than or equal to 80 C. For softer bitumen, the test cond

21、itions may be modified by agreement between the involved parties. The procedure described in this document may be used to compare results against a material for which the staining tendency is known. NOTE Staining properties are related to the colloidal stability of the bitumen with higher values ind

22、icating lower stability. WARNING The use of this standard can involve hazardous materials, operations and equipment. This standard does not purport to address all of the safety problems associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and

23、 health practices and to determine the applicability of regulatory limitations prior to use. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edit

24、ion of the referenced document (including any amendments) applies. EN 58, Bitumen and bituminous binders Sampling bituminous binders EN 1427, Bitumen and bituminous binders Determination of softening point Ring and Ball method EN 12594, Bitumen and bituminous binders Preparation of test samples 3 Te

25、rms and definitions For the purposes of this document, the following terms and definitions apply. 3.1 staining tendency tendency of oil components to separate spontaneously from bitumen NOTE The separation of oil components can cause staining in bitumen roofing products and others bituminous product

26、s with eventual damage of adjacent materials in storage and use. 4 Principle A retaining ring, filled with molten bitumen on a sheet of filter paper and supported on a flat horizontal plate is heated in an oven at a specified temperature for a specified time. The width of the resulting stained circl

27、e around the bitumen is calculated to determine the staining tendency of the bitumen. The staining tendency has the dimension of length and results are rounded to nearest 0,5 mm. 5 Apparatus 5.1 Rings, square-shouldered as specified in EN 1427 (see Figure 1). The precision of the method depends upon

28、 accurate measurement of the diameter and precise alignment of the face and rim of the ring on a flat surface and it is essential that deformed rings shall not be used. Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 08/07/2010 01:59, Uncontrolled Copy, (c) BSIBS EN 13301:2010EN 13301:2010 (E

29、) 5 Dimensions in millimetres Key 1 Bitumen 2 Ring according to EN 1427 3 Filter paper 4 Inner diameter of ring 5 Diameter of stained circle Figure 1 Ring 5.2 Baking paper, silicone treated paper to be used when casting discs of bitumen in the rings. 5.3 Release agent, mixture of glycerol and dextri

30、n or mineral talc, or other commercially available release agent. To prevent adhesion of bituminous binder to the pouring plate when casting discs, the surface of the metal pouring plate shall be thinly coated just before use with the release agent. NOTE Applying the release agent coating is easier

31、when the plate is warmed to approximately 40 C. 5.4 Filter paper, standard cellulose fibre ashless analytical grade. The filter paper shall be of sufficient area to accommodate the number of samples under test. A filter paper having a porosity of approximately 8 m with a thickness of approximately 2

32、10 m or a basis mass of approximately 92 g/m2has been found to be suitable. 5.5 Support plate, a flat, clean, smooth metal plate approximately 1,5 mm thick and with an area at least sufficient to support the size of filter paper used. 5.6 Oven, constant temperature, capable of maintaining a sample t

33、emperature of (80 1) C. 5.7 Thermometer, with a reading accuracy of 0,1 C in the required temperature range. 5.8 Measuring rule or device, with a reading accuracy of 0,5 mm or better. Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 08/07/2010 01:59, Uncontrolled Copy, (c) BSIBS EN 13301:2010E

34、N 13301:2010 (E) 6 6 Sampling The material under test shall be sampled in accordance with EN 58 and prepared in accordance with EN 12594. 7 Procedure 7.1 Sample preparation The bulk binder sample shall be placed in an oven maintained at a temperature of about 80 C above the expected ring and ball so

35、ftening point temperature or at a maximum of 200 C whichever is the lower. The container shall be filled to at least 50 % of its volume and shall be covered with a loose lid to protect it against oxidation. The total heating time shall be within 1 h 15 min to 1 h 45 min for samples of 100 ml to 500

36、ml and 1 h 45 min to 2 h 15 min for samples of 500 ml to 1 000 ml. 7.2 Filling of the rings Place preheated rings on the baking paper no closer than 40 mm from each other (preheated to a maximum of 90 C above the softening point). Ensure that the lower face and rim of the ring diameter is clean and

37、that the bitumen disc will completely fill the ring and is flush with the lower face. Ensure that there are no traces of any release agent on the support plate or the ring. Pour the bitumen sample into a preheated ring, using 2 rings per sample, placed on the baking paper on the support plate. Allow

38、 to cool to ambient temperature and trim off the excess bitumen from the top of the ring as described in EN 1427. Place the filled rings on the filter paper, placed on the support plate, no closer than 40 mm from the edge of the paper or from another ring. NOTE When the sample is highly viscous, it

39、may be difficult to pour into the rings. If excess bitumen has flown over the ring edge to the filter paper, it may stain the paper before the actual test. Continue to 7.4. 7.3 Filling of the rings (alternative procedure to 7.2) Place rings no closer than 40 mm from the edge of the filter paper or f

40、rom another ring, ensuring that the lower face and rim of the ring diameter is clean and that the bitumen disc will completely fill the ring and is flush with the lower face. Ensure that there are no traces of any release agent on the support plate or the ring. Pour the bitumen sample into a preheat

41、ed ring (preheated to a maximum of 90 C above softening point) using 2 rings per sample, placed on the filter paper on the support plate. Allow to cool to ambient temperature, and trim off the excess bitumen from the top of the ring as described in EN 1427. 7.4 Oven conditioning and measurement Iden

42、tify each bitumen sample by appropriately marking the filter paper in pencil near its ring. Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 08/07/2010 01:59, Uncontrolled Copy, (c) BSIBS EN 13301:2010EN 13301:2010 (E) 7 Place the entire assembly in the oven, preheated and stabilised at (80 1)

43、 C and allow remaining at this temperature for (120 1) h. The assembly shall be placed on a shelf inside the oven; it shall not be placed on the bottom of the oven. Remove the assembly on the support plate from the oven and allow cooling to room temperature. For each ring, make measurements on the u

44、nderside of the filter paper of the diameter of the stained circle to the nearest 0,5 mm. Make four measurements approximately 45 apart. 8 Calculation Calculate the arithmetic mean of the four measurements for each stained circle and subtract the inner diameter of the ring. Divide the result by 2 to

45、 obtain the width of the stained ring in units of 0,5 mm. 9 Expression of results Report the mean stained ring width of the two test rings for the sample, rounded to the nearest 0,5 mm. 10 Precision 10.1 Repeatability The difference between two successive results, obtained by the same operator with

46、the same apparatus under constant operating conditions on identical test material would, in the long run, in the normal and correct operations of the test method, differ by more than 0,5 mm in only one case in twenty. 10.2 Reproducibility The difference between two single and independent results obt

47、ained by different operators working in different laboratories on identical test material would, in the long run, in the normal and correct operation of the test method, differ by more than 1,0 mm in only one case in twenty. 11 Test report The test report shall contain at least the following informa

48、tion: a) type and complete identification of the sample under test; b) reference to this European Standard; c) result obtained (see Clause 9); d) any deviation, by agreement or otherwise, from the procedure specified; e) date of the test. Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 08/07/

49、2010 01:59, Uncontrolled Copy, (c) BSIEnergy InstituteBuying Parts of BS 2000Orders for BS 2000 publications should be addressed to either:Energy Institute Library and Information Service61 New Cavendish StreetLondonW1G 7ARTel: +44 (0)20 7467 7100Fax: +44 (0)20 7255 1472www.energyinst.org.ukOrder standards securely via:www.energyinstpubs.org.ukor:British Standards Institution Customer Services389 Chiswick High RoadLondonW4 4ALTel: +44 (0)20 8996 9001Fax: +44 (0)20 8996 70