BS EN 14323-2017 Wood-based panels Melamine faced boards for interior uses Test methods《木基板材 内部用三聚氰胺面板 试验方法》.pdf

1、BS EN 14323:2017Wood-based panels Melamine faced boards forinterior uses Test methodsBSI Standards PublicationWB11885_BSI_StandardCovs_2013_AW.indd 1 15/05/2013 15:06BS EN 14323:2017 BRITISH STANDARDNational forewordThis British Standard is the UK implementation of EN 14323:2017. Itsupersedes BS EN

2、14323:2004 which is withdrawn.The UK participation in its preparation was entrusted to TechnicalCommittee B/541, Wood based panels.A list of organizations represented on this committee can beobtained on request to its secretary.This publication does not purport to include all the necessaryprovisions

3、 of a contract. Users are responsible for its correctapplication. The British Standards Institution 2017. Published by BSI Standards Limited 2017ISBN 978 0 580 87138 2ICS 79.060.01Compliance with a British Standard cannot confer immunity fromlegal obligations.This British Standard was published unde

4、r the authority of theStandards Policy and Strategy Committee on 31 March 2017.Amendments/corrigenda issued since publicationDate Text affectedBS EN 14323:2017EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 14323 March 2017 ICS 79.060.20 Supersedes EN 14323:2004English Version Wood-based panels

5、 - Melamine faced boards for interior uses - Test methods Panneaux base de bois - Panneaux surfacs mlamins pour usages intrieurs - Mthodes dessaisHolzwerkstoffe - Melaminbeschichtete Platten zur Verwendung im Innenbereich - Prfverfahren This European Standard was approved by CEN on 9 January 2017. C

6、EN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on ap

7、plication to the CEN-CENELEC Management Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC

8、Management Centre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, L

9、atvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Serbia, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG CEN-CENELEC Management Centre:

10、Avenue Marnix 17, B-1000 Brussels 2017 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN 14323:2017 EBS EN 14323:2017EN 14323:2017 2 Contents Page European foreword . 4 1 Scope 5 2 Normative references 5 3 Test pieces . 5 4 Condition

11、ing of test pieces . 5 5 Test methods 5 5.1 Dimensions (thickness, length and width) 5 5.2 Flatness . 5 5.2.1 Principle . 5 5.2.2 Apparatus . 5 5.2.3 Test pieces . 6 5.2.4 Procedure. 6 5.2.5 Expression of results 6 5.3 Edge damage . 6 5.3.1 Principle . 6 5.3.2 Apparatus . 6 5.3.3 Test pieces . 6 5.3

12、.4 Procedure. 6 5.3.5 Expression of results 6 5.4 Surface defects . 6 5.4.1 Principle . 6 5.4.2 Apparatus . 6 5.4.3 Test pieces . 7 5.4.4 Procedure. 7 5.4.5 Expression of results 7 5.5 Resistance to scratching . 8 5.5.1 Principle . 8 5.5.2 Apparatus . 8 5.5.3 Test pieces . 8 5.5.4 Procedure. 8 5.5.5

13、 Expression of results 8 5.6 Resistance to staining 8 5.6.1 Principle . 8 5.6.2 Staining agents . 8 5.6.3 Apparatus . 9 5.6.4 Test pieces . 9 5.6.5 Procedure. 9 5.6.6 Expression of results 9 5.7 Resistance to cracking 10 5.7.1 Principle 10 5.7.2 Apparatus 10 5.7.3 Test pieces 10 5.7.4 Procedure 10 5

14、.7.5 Expression of results . 10 BS EN 14323:2017EN 14323:2017 3 5.8 Colour matching and surface texture 10 5.8.1 Principle . 10 5.8.2 Reference sample . 11 5.8.3 Test piece . 11 5.8.4 Apparatus 11 5.8.5 Procedure 11 5.9 Resistance to abrasion of the decorative surface layer 12 5.9.1 Principle . 12 5

15、.9.2 Test pieces . 12 5.9.3 Preconditioning of the test pieces and abrasive paper. 12 5.9.4 Apparatus 12 5.9.5 Materials 12 5.9.6 Procedure 12 5.9.7 Expression of results . 12 5.10 Resistance to water vapour . 12 5.10.1 Principle . 12 5.10.2 Apparatus 13 5.10.3 Test pieces . 13 5.10.4 Procedure 13 5

16、.10.5 Expression of results . 13 5.11 Resistance to colour change in xenon arc light 13 5.11.1 Principle . 13 5.11.2 Apparatus 13 5.11.3 Test pieces . 13 5.11.4 Procedure 13 5.11.5 Expression of results . 13 5.12 Gloss level 14 5.12.1 Principle . 14 5.12.2 Test piece . 14 5.12.3 Apparatus 14 5.12.4

17、Procedure 14 5.12.5 Expression of results . 14 5.13 Resistance to impact by large-diameter steel ball 15 5.13.1 Principle . 15 5.13.2 Apparatus 15 5.13.3 Test pieces . 15 5.13.4 Procedure 15 5.13.5 Expression of results . 15 6 Test report 15 Annex A (informative) Staining agents 16 Bibliography . 17

18、 BS EN 14323:2017EN 14323:2017 4 European foreword This document (EN 14323:2017) has been prepared by Technical Committee CEN/TC 112 “Wood-based panels”, the secretariat of which is held by DIN. This European Standard shall be given the status of a national standard, either by publication of an iden

19、tical text or by endorsement, at the latest by September 2017, and conflicting national standards shall be withdrawn at the latest by September 2017. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN shall not be held responsibl

20、e for identifying any or all such patent rights. This document has been prepared under a mandate given to CEN by the European Commission and the European Free Trade Association. This document supersedes EN 14323:2004. Compared to EN 14323:2004 the following modifications have been made: a) reference

21、 to new EN 438-2:2016;b) change for light source in 5.4.2 and 5.6.3;c) to principle of resistance to scratching in 5.5.1;d) deletion of wear point for resistance to abrasion in 5.9;e) deletion of resistance to cigarette burn in 5.10.According to the CEN-CENELEC Internal Regulations, the national sta

22、ndards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania,

23、Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Serbia, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom. BS EN 14323:2017EN 14323:2017 5 1 Scope This European Standard specifies test methods for the determination of characteristics of melamine faced b

24、oards (MFB) as defined in EN 14322. 2 Normative references The following documents, in whole or in part, are normatively referenced in this document and are indispensable for its application. For dated references, only the edition cited applies. For undated references, the latest edition of the refe

25、renced document (including any amendments) applies. EN 324-1, Wood-based panels Determination of dimensions of boards Part 1: Determination of thickness, width and length EN 438-2:2016, High-pressure decorative laminates (HPL) Sheets based on thermosetting resins (usually called laminates) Part 2: D

26、etermination of properties EN ISO 2813, Paints and varnishes Determination of gloss value at 20, 60 and 85 (ISO 2813) EN ISO 3668, Paints and varnishes Visual comparison of the colour of paints (ISO 3668) EN ISO 4892-2:2013, Plastics Methods of exposure to laboratory light sources Part 2: Xenon-arc

27、lamps (ISO 4892-2:2013) ISO 9352, Plastics Determination of resistance to wear by abrasive wheels 3 Test pieces The test pieces for the following tests shall be taken at least 150 mm from the edge of the product. When needed, the longitudinal or transverse direction of the decorative surface shall b

28、e specified by the manufacturer for the tests on the products. 4 Conditioning of test pieces Unless specified otherwise for the individual tests, the test pieces shall be tested in the received state. In cases of dispute or for type approval, the test pieces shall be conditioned in an atmosphere of

29、(23 2) C and (50 5) % relative humidity to constant mass prior to testing. 5 Test methods 5.1 Dimensions (thickness, length and width) These properties shall be determined in accordance with EN 324-1. 5.2 Flatness 5.2.1 Principle Flatness is determined by measuring the maximal deviation of the board

30、 surface from a metal straight edge placed at two selected positions parallel to the long and short edges of the board or panel. 5.2.2 Apparatus Straight edge, of (1 000 1) mm length, with dial indicator gauge (comparator) graduated to permit a reading accuracy of 0,1 mm. BS EN 14323:2017EN 14323:20

31、17 6 5.2.3 Test pieces The test piece shall be the complete board under test, as received, stored in the conditions recommended by the manufacturer. 5.2.4 Procedure Place the board in a vertical position free from restraint with one long edge resting on an essentially horizontal floor. Place the fla

32、tness gauge on the concave surface at various positions. At each position, measure the greatest distance between board surface and the flatness gauge with an accuracy of 0,1 mm. 5.2.5 Expression of results The result of the test is the highest recorded reading on the dial gauge in millimetres to the

33、 nearest 0,1 mm. 5.3 Edge damage 5.3.1 Principle Edge damage is determined by placing a graduated mask or tape measure on the board or panel under test and measuring the size of chips of paper removed from the edges. 5.3.2 Apparatus A metal tape measure or mask graduated in divisions of 1 mm. 5.3.3

34、Test pieces The test piece is the board or panel as received. 5.3.4 Procedure The test piece is laid level on a protective surface. Loose surface contamination is to be removed using a soft brush. Using the metal tape measure or the mask the size of the chip is measured at right angles to the board

35、edge, across the chip towards the centre of the board. 5.3.5 Expression of results Record the dimensions of the largest chip of paper removed to the nearest millimetre (mm). 5.4 Surface defects 5.4.1 Principle Inspection of boards for surface appearance under standardized conditions of lighting and

36、viewing. Surface defects are larger than 0,8 mm2and those that can be identified when the surface texture is viewed from a distance of 0,7 m and at an angle about of 45. 5.4.2 Apparatus The light source shall provide a diffused illumination of (1 200 400) lx over the whole area. This may either be d

37、iffused daylight or be diffused artificial light. The daylight shall be unaffected by surrounding trees, etc. When artificial daylight is used, it shall have a correlated colour temperature of (5 000 to 6 500) K and a Ra greater than 92, by using a colour matching booth in accordance with EN ISO 366

38、8. A convenient distance of the lights from the inspection table is approximately 1,5 m. BS EN 14323:2017EN 14323:2017 7 5.4.3 Test pieces The test piece shall be the board under test, as received. 5.4.4 Procedure Place the board, decorative face uppermost, on the inspection table and wipe it free o

39、f any loose contamination, if necessary, with a soft cloth and any suitable cleaning agent if necessary. Inspect it from the distance required (specified in 5.4.1) for defects such as smudges, smears, finger-prints, scratches, foreign particles, damage or any other form of blemish evident within the

40、 decorative surface. In case of cut to size panels the inspection shall be performed on the edges too. The evaluation of the total area of spot-type defects in square millimetres and of the total length of hair-like defects in millimetres may be carried out with the help of the Tappi Size Estimation

41、 Chart1)or with an equivalent system. In case of dispute the inspection shall be carried out by three observers using the Tappi Chart or an equivalent system. The inspector shall have normal vision, corrected if necessary. No magnifying glass shall be used in viewing the sheet. In cases of doubt or

42、dispute, three observers are required for the visual assessment. All observers shall have good colour vision. In case of three observers, the reported rating for the test surface shall be the average to the nearest nominal value. 5.4.5 Expression of results Record all defects identifying type, numbe

43、r and size of defects and sum up surfaces and length. The admissible size of defects is based on a maximum contamination area equivalent to a unit of defects and is proportional to the standard delivery size of the manufacturer. The total admissible area of contamination may be concentrated in one s

44、pot or dispersed over an amount of smaller defects. In case of pre-cut panels the cumulative defect is referred to the standard delivery sizes of the manufacturers or amount of delivery. EXAMPLE Permitted unit of defect (see EN 14322) in this sample is 2 mm2/m2Standard delivery size of the manufactu

45、rer: 5 000 mm 2 000 mm Points: The permissible total error (TE) is calculated as follows: TE = Board length Board width Permitted unit of defect = 5 000 mm 2 000 mm 2 mm2/m2= 20 mm2The following errors are therefore permitted: 1 20mm2defect,or 2 10mm2defect,or 3 6,6 mm2defect etc. Length: The permis

46、sible total error (TE) is calculated as follows: TE = Board length Board width Permitted unit of defect = 5000 mm 2000 mm 20 mm/m2= 200 mm 1)“Tappi Size Estimation Chart” is the trade name of a product supplied by TAPPI, Technology Park, P.O. Box 105113,Atlanta, GA 30348-5113, USA, tel. +1 770 446 1

47、400, fax +1 770 446 6947. The article reference is: TAPPI - Dirt size estimation chart. “Tappi size estimation chart” is an example of a suitable product available commercially. This information is given for the convenience of users of this European Standard and does not constitute an endorsement by

48、 CEN-CENELEC of this product. BS EN 14323:2017EN 14323:2017 8 The following errors are therefore permitted: 1 200 mm defect 2 100 mm defect 3 66 mm defect etc. 5.5 Resistance to scratching 5.5.1 Principle Increasing loads are applied in specified steps to a diamond scratching point of defined geomet

49、ry. The resistance to scratching of the melamine faced board under test is expressed as a numerical rating which defines the minimum applied load which is producing a continuous surface scratch. The test result is verified by visually confirming that the next higher load-step produces a continuous scratch. 5.5.2 Apparatus Scratch testing apparatus and viewing enclosure as described in EN 438-2:2016, 25.3. 5.5.3 Test pieces Cut a test piece 100 mm 100 mm from the board under test. Wipe the surface using cotton