BS EN 15386-2007 Packaging - Flexible laminate and plastic tubes - Test method to determine the print adhesion《包装 柔性叠层板和塑料管 测定印刷附着力的试验方法》.pdf

1、Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 14/05/2008 02:03, Uncontrolled Copy, (c) BSIg49g50g3g38g50g51g60g44g49g42g3g58g44g55g43g50g56g55g3g37g54g44g3g51g40g53g48g44g54g54g44g50g49g3g40g59g38g40g51g55g3g36g54g3g51g40g53g48g44g55g55g40g39g3g37g60g3g38g50g51g60g53g44g42g43g55g3g47g36g58d

2、etermine the print adhesionICS 55.120Packaging Flexible laminate and plastic tubes Test method to BRITISH STANDARDBS EN 15386:2007BS EN 15386:2007Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 14/05/2008 02:03, Uncontrolled Copy, (c) BSIThis British Standard was published under the authority

3、 of the Standards Policy and Strategy Committee on 29 February 2008 BSI 2008ISBN 978 0 580 55648 7Amendments/corrigenda issued since publicationDate CommentsCompliance with a British Standard cannot confer immunity from legal obligations.National forewordThis British Standard is the UK implementatio

4、n of EN 15386:2007.The UK participation in its preparation was entrusted to Technical Committee PKW/0, Packaging.A list of organizations represented on this committee can be obtained on request to its secretary.This publication does not purport to include all the necessary provisions of a contract.

5、Users are responsible for its correct application.EUROPEAN STANDARDNORME EUROPENNEEUROPISCHE NORMEN 15386November 2007ICS 55.120English VersionPackaging - Flexible laminate and plastic tubes - Test method todetermine the print adhesionEmballage - Tubes souples plastiques et tubes soupleslamins - Mth

6、ode dessai pour dterminer ladhrence delimpressionPackmittel - Laminat- und Kunststofftuben - Prfverfahrenzur Bestimmung der Haftfestigkeit der BedruckungThis European Standard was approved by CEN on 30 September 2007.CEN members are bound to comply with the CEN/CENELEC Internal Regulations which sti

7、pulate the conditions for giving this EuropeanStandard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such nationalstandards may be obtained on application to the CEN Management Centre or to any CEN member.This European Standard e

8、xists in three official versions (English, French, German). A version in any other language made by translationunder the responsibility of a CEN member into its own language and notified to the CEN Management Centre has the same status as theofficial versions.CEN members are the national standards b

9、odies of Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland,France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal,Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.EUR

10、OPEAN COMMITTEE FOR STANDARDIZATIONCOMIT EUROPEN DE NORMALISATIONEUROPISCHES KOMITEE FR NORMUNGManagement Centre: rue de Stassart, 36 B-1050 Brussels 2007 CEN All rights of exploitation in any form and by any means reservedworldwide for CEN national Members.Ref. No. EN 15386:2007: ELicensed Copy: Wa

11、ng Bin, ISO/EXCHANGE CHINA STANDARDS, 14/05/2008 02:03, Uncontrolled Copy, (c) BSIEN 15386:2007 (E) 2 Contents . page Foreword. 3 1 Scope . 4 2 Principle. 4 3 Apparatus 4 4 Procedure 4 5 Test report. 5 Annex A (normative) Peel adhesion (180 ) at 300 mm/min . 6 Licensed Copy: Wang Bin, ISO/EXCHANGE C

12、HINA STANDARDS, 14/05/2008 02:03, Uncontrolled Copy, (c) BSIEN 15386:2007 (E) 3 Foreword This document (EN 15386:2007) has been prepared by Technical Committee CEN/TC 261 “Packaging”, the secretariat of which is held by AFNOR. This European Standard shall be given the status of a national standard,

13、either by publication of an identical text or by endorsement, at the latest by May 2008, and conflicting national standards shall be withdrawn at the latest by May 2008. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or C

14、ENELEC shall not be held responsible for identifying any or all such patent rights. This standard is based on the professional recommendations of the European Tube Manufacturers Association (etma). According to the CEN/CENELEC Internal Regulations, the national standards organizations of the followi

15、ng countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Sloven

16、ia, Spain, Sweden, Switzerland and the United Kingdom. Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 14/05/2008 02:03, Uncontrolled Copy, (c) BSIEN 15386:2007 (E) 4 1 Scope This standard specifies a method for the determination of the print adhesion on flexible laminate and plastic tubes. I

17、t is applicable to flexible laminate and plastic tubes used for packing pharmaceutical, cosmetic, hygiene, food and other household products. 2 Principle The adhesive tape test serves to gauge the adhesion properties of printing ink films on flexible laminate and plastic tubes. The printing ink film

18、 is tested by rapidly tearing-off a previously applied adhesive tape. After the tape has been torn off, the divided surfaces are judged by pre-established criteria. 3 Apparatus An adhesive tape of commercial quality equipped with an upper surface made of tear-proof plastic and a pressure sensitive a

19、dhesive coating, of which the adhesive power is: minimum 5 N/25 mm and maximum 7 N/25 mm, tested according to Annex A against a glass testing surface. 4 Procedure Place the printed sample on an even surface. Apply the adhesive tape on the sample and press it on manually across the length of the deco

20、ration. It is important that there is full contact with the surface over the whole area and that no air bubbles remain between adhesive tape and sample surface. Approximately 10 s to 30 s after pressing-on, manually tear off the free end of the adhesive tape in one go from the surface at an angle of

21、 about 150 . Examine the divided surfaces (printing surface and reverse side of the adhesive tape). Analyse the divided surfaces according to Table 1. Table 1 Evaluation of test results Appearance of the divided surfaces Assessment Category No damage of the print or the printing material, pure adhes

22、ion fracture Adhesive tape resistant Pass Damage to the print and printing material. Not adhesive tape resistant Fail The severity of the failure mode should be defined between customer and supplier. Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 14/05/2008 02:03, Uncontrolled Copy, (c) BSIE

23、N 15386:2007 (E) 5 5 Test report If not otherwise agreed between supplier and customer the test report shall contain the following information: a) Reference to this standard and if necessary a specification for the method of sampling and acceptance of the batch, b) Complete identification of the bat

24、ch and of the tubes checked, c) Date of printing, d) Number of tubes checked, e) Number of defects, f) Test result, g) All factors which could have affected the results or all operating details not specified in this standard, h) Date, place of test and name of tester. Licensed Copy: Wang Bin, ISO/EX

25、CHANGE CHINA STANDARDS, 14/05/2008 02:03, Uncontrolled Copy, (c) BSIEN 15386:2007 (E) 6 Annex A (normative) Peel adhesion (180 ) at 300 mm/min A.1 Scope This test method is designed to quantify the permanence of adhesion or peel ability of self-adhesive, pressure sensitive materials A.2 Definition P

26、eel adhesion is defined as the force required to remove pressure sensitive coated material, which has been applied to a standard test plate under specified conditions from the plate at a specified angle and speed. Adhesion is measured at 20 min after the application and 24 h after application, the l

27、atter being considered as the ultimate adhesion. A.3 Apparatus and reagents A tensile tester or similar machine, capable of peeling a laminate through an angle of 180 with a jaw separation rate of 300 mm/min with an accuracy of 2 %. Test plates made of float glass or similar plate glass. A 2 kg roll

28、er. NOTE 1 The standard FINAT test roller is recommended for this purpose1. The test plates shall be thoroughly cleaned so that no trace of adhesive, grease, silicone or moisture is left on the surface. The following solvents can be used to clean the test plates: Diacetone alcohol non-residual, tech

29、nical grade or better Methyl Ethyl Ketone (MEK) Acetone Methanol 95 % n-Heptane Ethyl Acetate 1Information on how to obtain a FINAT hand roller is available from FINAT,Laan Copes van Cattenburch 79, 2585 EW The Hague, Netherlands, e-mail: URL: 1. The FINAT test roller is an example of a suitable pr

30、oduct available commercially. This information is given for the convenience of users of this European Standard and does not constitute an endorsement by CEN of this product. Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 14/05/2008 02:03, Uncontrolled Copy, (c) BSIEN 15386:2007 (E) 7 The cle

31、aning material shall be absorbent, e.g. surgical gauze, cotton wool or tissue. To be suitable, materials shall be lint-free during use, absorbent, contain no additives that are soluble in the solvents listed above, and made exclusively from virgin materials. Dispense one of the solvents listed above

32、 onto the panel, wiping it to dryness with fresh absorbent cleaning material. Repeat for a total of three washes with the solvent. Final wipe shall be with MEK or acetone. Alternative methods that remove contamination properly can be adopted, e.g. ultrasonic cleaning. Prior to use, the cleaned plate

33、s should be left for 4 hours under standard test conditions. Care should be taken to handle clean plates by the edge only. Alternative surfaces to plate glass can be used such as stainless steel aluminium or polyester film, but this must be clearly stated alongside the results. If adhesion values ar

34、e required when paper tear has occurred, then this test can be conducted at lower jaw separation rates quoting the latter against the results. NOTE 2 Conversion 1 Kgf = 9,81 N. A.4 Test Pieces These should be strips taken from a representative sample of material. The strips should be 25 mm wide and

35、have a minimum length of 175 mm in the machine direction. The cuts should be clean and straight. At least three strips should be taken from each material sample. A.5 Conditioning Temperature 23 C 2 C, 50 % RH 5% RH. The test sample or test strips should be conditioned for not less than 4 h before te

36、sting. Figure A.1 Test strips A.6 Procedure Remove the backing material from each strip and place the adhesive coated facing material, adhesive side down, on to a clean test plate using light finger pressure. Roll twice in each direction with the roller at a speed of approximately 10 mm/s to obtain

37、intimate contact between the adhesive mass and the surface. After applying the strips to the test plate, leave for a period of 20 min before testing. Repeat the procedure with a second set of strips and leave for a period of 24 h before testing. Fix the test plate and strip in the machine so that th

38、e angle of peel is 180 . Set the machine at 300 mm/min jaw separation rate. Carry out the test taking at least five readings at 10 mm intervals from the centre section of each test strip. Average the five or more readings for each strip. Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 14/05/2

39、008 02:03, Uncontrolled Copy, (c) BSIEN 15386:2007 (E) 8 A.7 Results Peel adhesion (180 ) is expressed as the average result for the strips tested in Newtons per 25 mm width for either 20 min or 24 h application time. A.8 Failure Description Code CP Clear Panel - no visible stain on panel. PS Panel

40、Stain - discoloration of test area, but no tacky residue. CF Cohesive Failure - the adhesive film is split during the test, leaving residue of adhesive on both the panel and the front material. AT Adhesive Transfer - the adhesive separates cleanly from the front material, leaving adhesive film on th

41、e test panel. The approximate extent of transfer should be quoted as a percentage. PT Paper Tear - the adhesive force exceeds the strength of a paper facing material. The results quoted should be the maximum reached before the paper tears. Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 14/05

42、/2008 02:03, Uncontrolled Copy, (c) BSIEN 15386:2007 (E) 9 Bibliography 1 FINAT Technical Handbook Section 2: Test Equipment 2.1 Standard FINAT Test Roller (FINAT website : http:/)12 EN 12374, Packaging Flexible tubes - Terminology 3 EN 13045, Packaging Flexible cylindrical plastic tubes Dimensions

43、and tolerances 4 EN 13461, Packaging Cylindrical flexible laminated tubes Dimensions and tolerances Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 14/05/2008 02:03, Uncontrolled Copy, (c) BSIBS EN BSILicensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 14/05/2008 02:03, Uncontrolled Copy,

44、(c) BSI389 Chiswick High RoadLondonW4 4AL15386:2007BSI British Standards InstitutionBSI is the independent national body responsible for preparing British Standards. It presents the UK view on standards in Europe and at the international level. It is incorporated by Royal Charter.RevisionsBritish St

45、andards are updated by amendment or revision. Users of British Standards should make sure that they possess the latest amendments or editions.It is the constant aim of BSI to improve the quality of our products and services. We would be grateful if anyone finding an inaccuracy or ambiguity while usi

46、ng this British Standard would inform the Secretary of the technical committee responsible, the identity of which can be found on the inside front cover. Tel: +44 (0)20 8996 9000. Fax: +44 (0)20 8996 7400.BSI offers members an individual updating service called PLUS which ensures that subscribers au

47、tomatically receive the latest editions of standards.Buying standardsOrders for all BSI, international and foreign standards publications should be addressed to Customer Services. Tel: +44 (0)20 8996 9001. Fax: +44 (0)20 8996 7001. Email: ordersbsi-. Standards are also available from the BSI website

48、 at http:/www.bsi-.In response to orders for international standards, it is BSI policy to supply the BSI implementation of those that have been published as British Standards, unless otherwise requested.Information on standardsBSI provides a wide range of information on national, European and intern

49、ational standards through its Library and its Technical Help to Exporters Service. Various BSI electronic information services are also available which give details on all its products and services. Contact the Information Centre. Tel: +44 (0)20 8996 7111. Fax: +44 (0)20 8996 7048. Email: infobsi-.Subscribing members of BSI are kept up to date with standards developments and receive substantial discounts on the purchase price of standa