BS EN 60684-3-214-2014 Flexible insulating sleeving Specifications for individual types of sleeving Heat-shrinkable polyolefin sleeving not flame retarded thick and medium wall《绝缘软.pdf

1、BSI Standards PublicationFlexible insulating sleevingPart 3: Specifications for individual types of sleeving Sheet 214: Heat-shrinkable, polyolefin sleeving, not flame retarded, thick and medium wallBS EN 60684-3-214:2014National forewordThis British Standard is the UK implementation of EN 60684-3-2

2、14:2014. It is identical to IEC 60684-3-214:2013. It supersedes BS EN 60684-3-214:2005which is withdrawn.The UK participation in its preparation was entrusted to TechnicalCommittee GEL/15, Solid electrical insulating materials.A list of organizations represented on this committee can be obtained onr

3、equest to its secretary.This publication does not purport to include all the necessary provisions ofa contract. Users are responsible for its correct application. The British Standards Institution 2014.Published by BSI Standards Limited 2014ISBN 978 0 580 79803 0ICS 29.035.20Compliance with a Britis

4、h Standard cannot confer immunity fromlegal obligations.This British Standard was published under the authority of theStandards Policy and Strategy Committee on 31 March 2014. Amendments/corrigenda issued since publicationDate Text affectedBRITISH STANDARDBS EN 60684-3-214:2014EUROPEAN STANDARD EN 6

5、0684-3-214 NORME EUROPENNE EUROPISCHE NORM February 2014 CENELEC European Committee for Electrotechnical Standardization Comit Europen de Normalisation Electrotechnique Europisches Komitee fr Elektrotechnische Normung CEN-CENELEC Management Centre: Avenue Marnix 17, B - 1000 Brussels 2014 CENELEC -

6、All rights of exploitation in any form and by any means reserved worldwide for CENELEC members. Ref. No. EN 60684-3-214:2014 E ICS 29.035.20 Supersedes EN 60684-3-214:2005 English version Flexible insulating sleeving - Part 3: Specifications for individual types of sleeving - Sheet 214: Heat-shrinka

7、ble, polyolefin sleeving, not flame retarded, thick and medium wall (IEC 60684-3-214:2013) Gaines isolantes souples - Partie 3: Spcifications pour types particuliers de gaines - Feuille 214: Gaines thermortractables en polyolfine, non ignifuges, paroi paisse et moyenne (CEI 60684-3-214:2013) Isolier

8、schluche - Teil 3: Anforderungen fr einzelne Schlauchtypen - Blatt 214: Polyolefin-Wrmeschrumpfschluche, nicht-flammwidrig, dickwandig und mittlere Wanddicke (IEC 60684-3-214:2013) This European Standard was approved by CENELEC on 2013-12-24. CENELEC members are bound to comply with the CEN/CENELEC

9、Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to

10、 any CENELEC member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CENELEC member into its own language and notified to the CEN-CENELEC Management Centre has the same status as the

11、 official versions. CENELEC members are the national electrotechnical committees of Austria, Belgium, Bulgaria, Croatia, Cyprus, the Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembo

12、urg, Malta, the Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom. BS EN 60684-3-214:2014EN 60684-3-214:2014 - 2 - Foreword The text of document 15/718/FDIS, future edition 3 of IEC 60684-3-214, prepared by IEC/TC 15 “Solid

13、electrical insulating materials“, was submitted to the IEC-CENELEC parallel vote and approved by CENELEC as EN 60684-3-214:2014. The following dates are fixed: latest date by which the document has to be implemented at national level by publication of an identical national standard or by endorsement

14、 (dop) 2014-09-24 latest date by which the national standards conflicting with the document have to be withdrawn (dow) 2016-12-24 This document supersedes EN 60684-3-214:2005. EN 60684-3-214:2014 includes the following significant technical changes with respect to EN 60684-3-214:2006: Alignment with

15、 EN 60684-3-247 (dual wall) since this Part 3 specification represents a single wall option using identical material. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CENELEC and/or CEN shall not be held responsible for identifying

16、 any or all such patent rights. Endorsement notice The text of the International Standard IEC 60684-3-214:2013 was approved by CENELEC as a European Standard without any modification. In the official version, for Bibliography, the following notes have to be added for the standards indicated: IEC 606

17、84-3 Series NOTE Harmonised in EN 60684-3 series (not modified). BS EN 60684-3-214:2014- 3 - EN 60684-3-214:2014 Annex ZA (normative) Normative references to international publications with their corresponding European publications The following documents, in whole or in part, are normatively refere

18、nced in this document and are indispensable for its application. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. NOTE When an international publication has been modified by common modifica

19、tions, indicated by (mod), the relevant EN/HD applies. Publication Year Title EN/HD Year IEC 60296 2012 Fluids for electrotechnical applications - Unused mineral insulating oils for transformers and switchgear EN 60296 2012 IEC 60684-1 2003 Flexible insulating sleeving - Part 1: Definitions and gene

20、ral requirements EN 60684-1 2003 IEC 60684-2 2011 Flexible insulating sleeving - Part 2: Methods of test EN 60684-2 2011 IEC 60757 1983 Code for designation of colours HD 457 S1 1985 ISO 868 2003 Plastics and ebonite - Determination of indentation hardness by means of a durometer (Shore hardness) EN

21、 ISO 868 2003 ISO 11358 1997 Plastics - Thermogravimetry (TG) of polymers - General principles EN ISO 11358 1997 BS EN 60684-3-214:2014 2 60684-3-214 IEC:2013 CONTENTS INTRODUCTION . 5 1 Scope 6 2 Normative references . 6 3 Designation . 6 4 Conditions of test . 7 5 Requirements 7 6 Sleeving conform

22、ance 7 Annex A (informative) Guide to the available sizes and wall thicknesses . 11 Bibliography 13 Table 1 Property requirements (1 of 2) . 8 Table 2 Requirements for breakdown voltage . 10 Table 3 Resistance to selected fluids 10 Table A.1 Type A medium wall . 11 Table A.2 Type B thick wall 12 BS

23、EN 60684-3-214:201460684-3-214 IEC:2013 5 INTRODUCTION This International Standard is one of a series which deals with flexible insulating sleeving for electrical purposes. The series consists of three parts: Part 1: Definitions and general requirements (IEC 60684-1) Part 2: Methods of test (IEC 606

24、84-2) Part 3: Specifications for individual types of sleeving (IEC 60684-3) This standard gives one of the sheets comprising Part 3 as follows: Sheet 214: Heat-shrinkable, polyolefin sleeving, not flame retarded, thick and medium wall. BS EN 60684-3-214:2014 6 60684-3-214 IEC:2013 FLEXIBLE INSULATIN

25、G SLEEVING Part 3: Specifications for individual types of sleeving Sheet 214: Heat-shrinkable, polyolefin sleeving, not flame retarded, thick and medium wall 1 Scope This standard gives the requirements for two types of heat-shrinkable, polyolefin sleeving, not flame retarded, thick and medium wall

26、with a nominal shrink ratio of 3:1. This sleeving has been found suitable for use at temperatures of up to 100 C. Type A: Medium wall internal diameter up to 200 mm typically. Type B: Thick wall internal diameter up to 200 mm typically. These sleevings are normally supplied in colour black. Since th

27、ese types of sleevings cover a significantly large range of sizes and wall thicknesses, Tables A.1 and A.2 of this document provides a guide to the range of sizes available. The actual size will be agreed between the user and supplier. Materials which conform to this specification meet established l

28、evels of performance. However, the selection of a material by a user for a specific application should be based on the actual requirements necessary for adequate performance in that application and not based on this specification alone. 2 Normative references The following documents, in whole or in

29、part, are normatively referenced in this document and are indispensable for its application. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. IEC 60296:2012, Fluids for electrotechnical app

30、lications Unused mineral insulating oils for transformers and switchgear IEC 60684-1:2003, Flexible insulating sleeving Part 1: Definitions and general requirements IEC 60684-2:2011, Flexible insulating sleeving Part 2: Methods of test IEC 60757:1983, Code for designation of colours ISO 868:2003, Pl

31、astics and ebonite Determination of indentation hardness by means of a durometer (Shore hardness) ISO 11358:1997, Plastics Thermogravimetry (TG) of polymers General principles 3 Designation The sleeving shall be identified by the following designation: BS EN 60684-3-214:201460684-3-214 IEC:2013 7 De

32、scription IEC publication number IEC Part number IEC sheet number Type Size (expanded and recovered internal diameter in mm) Colour Sleeving IEC 60684 - 3 - 214 - B - 85,0/25,0 - BK Any colour abbreviation shall comply with IEC 60757, where applicable. Non-standard colours shall be written out in fu

33、ll. NOTE This information is for package labelling only in accordance with IEC 60684-1. 4 Conditions of test Unless otherwise specified, the sleeving shall be shrunk in a forced air circulation oven for (10 1) min at 200 C 3 K prior to testing. 5 Requirements In addition to the general requirements

34、given in IEC 60684-1, the sleeving shall comply with the requirements of Tables 1, 2, and 3, where applicable. 6 Sleeving conformance Conformance to the requirements of this specification shall normally be based on the results from typical sizes Type A: Recovered ID 25 mm 30 mm Type B: Recovered ID

35、25 mm 30 mm BS EN 60684-3-214:2014 8 60684-3-214 IEC:2013 Table 1 Property requirements (1 of 2) Property IEC 60684-2:2011 clause or subclause Units Max. or Min. Requirements Remarks Dimensions Internal Diameter Wall thickness Concentricity expanded recovered 3 3.1.2 3.3.2 3.3.3 mm mm % Min. Min. To

36、 be agreed between purchaser and supplier 50 85 Heat shock Tensile strength Elongation at break 6 19.1 and 19.2 19.1 and 19.2 MPa % Min. Min. 10 200 Heat at 200 C 5 K Longitudinal change 9 % Max. - 10 + 5 Heat expanded sleeving at 200 C 3 K for (10 1) min Bending at low temperature 14 - - No crackin

37、g shall be visible Test at 20 C For strips, the mandrel shall be between 20 and 22 times the wall thickness. Full section sleeving is tested and the mandrel shall be between 20 and 22 times the outer diameter. Dimensional stability on storage 16 - - The dimensions shall remain as agreed See Clause 1

38、 (Scope) Tensile Strength Elongation at break 19.1 and 19.2 19.1 and 19.2 MPa % Min. Min. 13 350 Use a jaw separation rate of 100 mm/min. Below 6,5 mm as sleeving. At 6,5 mm and above as dumbbells Secant modulus at 2 % elongation 19.5 MPa Min. Max. 80 160 BS EN 60684-3-214:201460684-3-214 IEC:2013 9

39、 Table 1 (2 of 2) Property IEC 60684-2:2011 clause or subclause Units Max. or Min. Requirements Remarks Breakdown voltage 21 kV Min. Table 2 Volume resistivity at room temperature after damp heat 23 23.5.2 23.5.4 .m .m Min. Min. 10121011 Colour fastness to light Standard identification Number 34 Min

40、. The colour standard contrast between the exposed and unexposed parts of the specimen shall be equal to or less than that of the fastness standard Fastness standard 5 Resistance to selected fluids Tensile strength Elongation at break 36 19.1 and 19.2 19.1 and 19.2 MPa % Min. Min. 10 250 Use the flu

41、ids and test temperatures specified in Table 3. Heat ageing Tensile strength Elongation at break 39 19.1 and 19.2 19.1 and 19.2 MPa % Min. Min. 10 200 Heat at 150 C 3 K Jacket only Long term heat ageing Elongation at break 50 19.2 % Min. 175 The ageing temperature shall be 100 C 3 K Carbon black con

42、tent ISO 11358 % Min. 2,5 Hardness ISO 868 Shore D Min. 40 Water Absorption 40 % Max. 0,5 BS EN 60684-3-214:2014 10 60684-3-214 IEC:2013 Table 2 Requirements for breakdown voltage Expanded wall thickness mm Dielectric strength aMin. All dimensions Expanded ID Dielectric strength kV/mm Type A 10-25 1

43、4 26-50 12 51-120 10 121 and above 8 Type B 10-25 12 26-50 10 51-120 8 121 and above 6 The breakdown voltage shall be determined by the method described in 21.4 of IEC 60684-2:2011. The central value shall comply with the minimum value in this table. The sleeving shall be tested in the expanded cond

44、ition. The rate of application of the voltage shall be 500 V/s. Care should be taken on selection of sizes based on these values. Refer to the manufacturer for actual values on installed conditions. a Measure the expanded wall thickness and calculate the dielectric strength by dividing the breakdown

45、 voltage by this value. Table 3 Resistance to selected fluids Test fluid No. Fluids Type Standard or symbol Immersion temperature C 2 K 1 Insulating Oil Transformer oil IEC 60296 23 2 Cleaning fluids Iso propyl alcohol 23 3 - Water De - ionized 85 Other fluids and/or temperatures may be specified fo

46、r customers with specific needs. These additional fluids and/or temperatures shall be applicable when incorporated into agreements between the supplier and customer. BS EN 60684-3-214:201460684-3-214 IEC:2013 11 Annex A (informative) Guide to the available sizes and wall thicknesses Table A.1 Type A

47、 medium wall Internal diameter Wall Expanded Min. mm Recovered Max. mm Recovered wall thickness Min. mm 10 3 1,0 10 4 1,4 12 3 1,4 16 5 1,4 19 6 2,0 25 8 2,0 28 10 2,0 33 10 2,0 35 12 2,0 38 13 2,3 43 13 2,3 50 18 2,3 63 19 2,3 70 26 2,3 85 25 2,5 90 36 2,5 115 34 2,5 120 54 2,5 140 42 2,8 152 48 2,

48、8 160 50 3,0 180 60 3,0 200 77 3,3 BS EN 60684-3-214:2014 12 60684-3-214 IEC:2013 Table A.2 Type B thick wall Internal diameter Wall Expanded Min. mm Recovered Max. mm Recovered wall thickness Min. mm 9 3 1,8 13 4 2,4 19 6 2,4 20 6 2,4 28 9 3,0 33 8 3,2 38 12 4,0 43 12 4,0 48 15 4,0 51 16 4,0 68 22

49、4,0 70 21 4,0 85 25 4,0 90 30 4,0 105 26 4,0 105 30 4,0 115 40 4,0 130 36 4,0 130 40 4,2 150 48 4,3 160 50 4,3 170 60 4,3 200 77 4,3 BS EN 60684-3-214:201460684-3-214 IEC:2013 13 Bibliography IEC 60684-3 (all sheets), Flexible insulating sleeving Part 3: Specifications for individual types of sleeving _ BS EN 60684-3-214:2014This page deliberately left blankThis page deliberately left blankBSI is th