BS EN 61249-2-39-2013 Materials for printed boards and other interconnecting structures Reinforced base materials clad and unclad High performance epoxide and non-epoxide woven E-gr.pdf

1、raising standards worldwideNO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAWBSI Standards PublicationMaterials for printed boards and other interconnecting structuresPart 2-39: Reinforced base materials clad and unclad High performance epoxide and non-epoxide, woven E-glass lami

2、nate sheets of defined flammability (vertical burning test), copper-clad for lead-free assemblyBS EN 61249-2-39:2013National forewordThis British Standard is the UK implementation of EN 61249-2-39:2013. It is identical to IEC 61249-2-39:2012.The UK participation in its preparation was entrusted to T

3、echnical Committee EPL/501, Electronic assembly technology 1 065 mm 1 155 mm; 1 065 mm 1 280 mm; 1 000 mm 1 000 mm; 1 000 mm 1 200 mm. 6.8.2 Tolerances for sheet sizes The size of sheet delivered by the supplier shall not deviate by more than +20/0 mm from the ordered size. 6.9 Cut panels 6.9.1 Cut

4、panel sizes Cut panel sizes shall be, when delivered, in accordance with the purchasers specification. 6.9.2 Size tolerances for cut panels For panels cut to size according to the purchasers specification, the following tolerances for length and width shall apply, as shown in Table 7. Tolerances ind

5、icated as normal shall be in effect unless otherwise specified by in the purchasing specification. Table 7 Size tolerances for cut panels Panel size mm Tolerance requirement mm Normal Close 300 2,0 0,5 300 600 2,0 0,8 600 2,0 1,6 NOTE The specified tolerances include all deviations caused by cutting

6、 the panels. BS EN 61249-2-39:201361249-2-39 IEC:2012 13 6.9.3 Rectangularity of cut panels For panels cut to size according to the purchasers specification, the following requirements for rectangularity shall apply as shown in Table 8. Tolerance indicated as normal shall be in effect unless otherwi

7、se specified in the purchasing specification. Table 8 Rectangularity of cut panels Property Test method IEC 61189-2 Requirement mm/m Normal Close Rectangularity of cut panels 2M23 3 2 7 Non-electrical properties of the base material after complete removal of the copper foil 7.1 Appearance of the die

8、lectric base material The etched specimens shall be inspected to verify that no surface or subsurface imperfections of the dielectric material exceed those shown below. The panels shall be inspected using an optical aid apparatus which provides a minimum magnification of 4X. Referee inspection shall

9、 be conducted at 10X magnification. Lighting conditions of inspection shall be appropriate to the material under inspection or as agreed upon between user and supplier. Surface and subsurface imperfections (such as weave texture, resin starvation, voids, foreign inclusions) shall be acceptable provi

10、ded that the imperfections meet the following: the reinforcement fibres are not cut or exposed; the foreign inclusions are not conductive; the imperfections do not propagate as a result of thermal stress; the foreign inclusions are translucent; opaque foreign fibres are less than 15 mm in length and

11、 average no more than 1,0 per 300 mm 300 mm area; opaque foreign inclusions other than fibres shall not exceed 0,50 mm. Opaque foreign inclusions less than 0,15 mm shall not be counted. Opaque foreign inclusions between 0,50 mm and 0,15 mm shall average no more than two spots per 300 mm 300 mm area;

12、 voids (sealed voids or surface void) have a longest dimension less than 0,075 mm and there should not be more than three voids in a 3,5 mm diameter circle. 7.2 Flexural strength When the laminate is tested in accordance with test method 2M20 of IEC 61189-2, the flexural strength shall be as shown i

13、n Table 9. BS EN 61249-2-39:2013 14 61249-2-39 IEC:2012 Table 9 Flexural strength requirements Property Test method IEC 61189-2 Requirement Flexural strength: Length direction Cross-direction (applicable to sheets 1,0 mm in thickness) 2M20 400 N/mm2300 N/mm2Flexural strength: Length direction Elevat

14、ed temperature (applicable to sheets1,0 mm in thickness) Not specified 7.3 Flammability When the laminate is tested in accordance with test method 2C08 (thickness 0,05 0,3 mm) or method 2C06 (thickness 0,3 3,2 mm) of IEC 61189-2 the flammability shall be as shown in Table 10. The performance labelle

15、d V-0 shall be in effect unless otherwise noted on the purchase order. Table 10 Flammability requirements Property Test method IEC 61189-2 Requirements Designation V-0 Flammability: Flaming combustion time after each application of the flame for each test specimen Total flaming combustion time for t

16、he 10 flame applications for each set of five specimens Glowing combustion time after the second removal of the test flame Flaming or glowing combustion up to the holding clamp Dripping flaming particles that ignite the tissue paper 2C06 10 s 50 s 30 s None None BS EN 61249-2-39:201361249-2-39 IEC:2

17、012 15 7.4 Water absorption When the laminate is tested in accordance with test method 2N02 of IEC 61189-2, the maximum water absorption shall be as shown in Table 11. Table 11 Water absorption requirements Property Test method IEC 61189-2 Thickness mm Requirement % Water absorption 2N02 0,05 Tg) 25

18、0 ppm/C Specific heat capacity 1,25 kJ/ (kgC) Thermal conductivity 0,3 W/(mC) UL temperature index (mechanical) 130 C UL temperature index (electrical) 130 C Maximum operating temperature (MOT) 130 C BS EN 61249-2-39:201361249-2-39 IEC:2012 21 Annex B (informative) Common laminate constructions Tabl

19、e B.1 gives the nominal thicknesses. Table B.1 Thickness Nominal thickness mm Common construction 0,075 1 080 0,080 2 106 0,100 2 106 0,100 2 113 0,100 2 116 0,125 2 116 0,125 2 165 0,125 2 1 080 0,15 2 157 0,15 2 165 0,16 1 500 0,18 7 628 0,18 1 500 0,20 2 2 113 0,20 2 2 116 0,20 7 628 0,25 2 2 116

20、 0,25 2 2 165 0,26 1 080/2 116/1 080 0,30 2 2 157 0,30 2 2 165 0,30 2 116/2 112/2 116 0,30 1 080/7 628/1 080 0,36 2 7 628 0,37 2 113/7 628/2 113 0,38 1 500/1 080/1 500 0,41 7 628/1 080/7 628 0,43 2 116/7 628/2 116 0,45 3 1 500 0,46 7 628/2 112/7 628 0,48 7 628/2 116/7 628 0,51 7 628/2 165/7 628 0,51

21、 1 080/2 7 628/1 080 0,54 3 7 628 BS EN 61249-2-39:2013 22 61249-2-39 IEC:2012 Nominal thickness mm Common construction 0,61 3 7 628/1 080 0,61 2 116/2 7 628/2 116 0,66 7 628/2 2 165/7 628 0,67 7 628/2 1 500/7 628 0,74 4 7 628 0,74 2 113/3 7 628/2 113 0,80 4 7 628/1 080 0,90 5 7 628 1,08 6 7 628 1,4

22、6 8 7 628 NOTE Prepreg made from a specific style of glass used in different constructions may have different resin contents. BS EN 61249-2-39:201361249-2-39 IEC:2012 23 Annex C (informative) Guideline for qualification and conformance inspection See Table C.1 for qualification and conformance testi

23、ng. Table C.1 Qualification and conformance testing Property Test method IEC-61189-2 Qualification testing Conformance testing Conformance frequency Peel strength after thermal shock 2M14 Yes Yes Lot Peel strength at 125 C 2M15 Yes Yes Quarterly Peel strength after solvent vapour 2M06 Yes Yes Quarte

24、rly Peel strength after simulated plating 2M16 Yes No Pull off strength 2M05 Yes No Dimensional stability 2X02 Yes Yes Monthly Flexural strength 2M20 Yes Yes Annually Flammabilty 2C06 Yes Yes Monthly Thermal stress, unetched 2C05 Yes Yes Lot Solderabilty 2MXX Yes No Glass transition temperature 2M11

25、 Yes Yes Monthly Cure factor 2M03 Yes Yes Monthly Permittivity at 1 MHz, as received 2E10 Yes Yes Monthly Decomposition temperature 2MXX Yes Yes Annually Thermal resistance 2MXX Yes Yes Quarterly Z-axis expansion 2MXX Yes Yes Quarterly Dissipation factor at 1 MHz, as received 2E10 Yes Yes Monthly Su

26、rface resistance after damp heat/recovery 2E03 Yes Yes Annually Volume resistance after damp heat/recovery 2E04 Yes Yes Annually Arc resistance 2E14 Yes Yes Annually Dielectric breakdown 2E15 Yes Yes Quarterly Electric strength 2E11 Yes Yes Quarterly Water absorption 2N02 Yes Yes Quarterly Bow and t

27、wist 2M01 Yes Yes Lot Surface waviness 2M12 Yes No Appearance of the dielectric base material See 7.1 Yes Yes Lot NOTE Users of this standard are encouraged to supply information to be included in the annex. BS EN 61249-2-39:2013 24 61249-2-39 IEC:2012 Bibliography IEC 60194:2006, Printed board desi

28、gn, manufacture and assembly Terms and definitions ISO 9000:2005, Quality management systems Fundamentals and vocabulary ISO 14001:2004, Environmental management systems Requirements with guidance for use _ BS EN 61249-2-39:2013This page deliberately left blankBSI is the independent national body re

29、sponsible for preparing British Standards and other standards-related publications, information and services. It presents the UK view on standards in Europe and at the international level. BSI is incorporated by Royal Charter. British Standards and other standardisation products are published by BSI

30、 Standards Limited.British Standards Institution (BSI)raising standards worldwideBSI389 Chiswick High Road London W4 4AL UKTel +44 (0)20 8996 9001Fax +44 (0)20 8996 Standards and PASs are periodically updated by amendment or revision. Users of British Standards and PASs should make sure that they p

31、ossess the latest amendments or editions.It is the constant aim of BSI to improve the quality of our products and services. We would be grateful if anyone finding an inaccuracy or ambiguity while using British Standards would inform the Secretary of the technical committee responsible, the identity

32、of which can be found on the inside frontcover. Similary for PASs, please notify BSI Customer Services.Tel: +44 (0)20 8996 9001 Fax: +44 (0)20 8996 7001BSI offers BSI Subscribing Members an individual updating service called PLUS which ensures that subscribers automatically receive the latest editio

33、ns of British Standards and PASs.Tel: +44 (0)20 8996 7669 Fax: +44 (0)20 8996 7001Email: Buying standardsYou may buy PDF and hard copy versions of standards directly using acredit card from the BSI Shop on the website addition all orders for BSI, international and foreign standards publicationscan

34、be addressed to BSI Customer Services.Tel: +44 (0)20 8996 9001 Fax: +44 (0)20 8996 7001Email: In response to orders for international standards, BSI will supply the British Standard implementation of the relevant international standard, unless otherwise requested.Information on standardsBSI provides

35、 a wide range of information on national, Europeanand international standards through its Knowledge Centre.Tel: +44 (0)20 8996 7004 Fax: +44 (0)20 8996 7005Email: BSI Subscribing Members are kept up to date with standards developments and receive substantial discounts on the purchase priceof standar

36、ds. For details of these and other benefits contact Membership Administration. Tel: +44 (0)20 8996 7002 Fax: +44 (0)20 8996 7001 Email: Information regarding online access to British Standards and PASs via British Standards Online can be found at information about British Standards is available on

37、 the BSI website at www.bsi- the data, software and documentation set out in all British Standards and other BSI publications are the property of and copyrighted by BSI, or some person or entity that own copyright in the information used (such as the international standardisation bodies) has formall

38、y licensed such information to BSI for commerical publication and use. Except as permitted under the Copyright, Designs and Patents Act 1988 no extract may be reproduced, stored in a retrieval system or transmitted in any form or by any means electronic, photocopying, recording or otherwise without

39、prior written permission from BSI. This does not preclude the free use, in the course of implementing the standard, of necessary details such as symbols, and size, type or grade designations. If these details are to be used for any other purpose than implementation then the prior written permission of BSI must be obtained. Details and advice can be obtained from the Copyright & Licensing Department.Tel: +44 (0)20 8996 7070Email: