BS EN ISO 11126-3-1994 Preparation of steel substrates before application of paints and related products - Specifications for non-metallic blast-cleaning abrasives - Copper refiner.pdf

1、BRITISH STANDARD CONFIRMED DECEMBER1998 BS EN ISO 11126-3:1998 BS 7079-F3: 1994 Incorporating Amendment No. 1 to BS 7079-F3:1994 (which it renumbers as BS EN ISO 1126-3:1998) Preparation of steel substrates before application of paints and related products Specifications for non-metallic blast clean

2、ing abrasives Part 3: Copper refinery slag The European Standard EN ISO 11126-3:1997 has the status of a British Standard ICS 87.020BSENISO11126-3:1998 This British Standard, having been prepared under the directionof the Surface Treatments and Coatings Standards Policy Committee, was published unde

3、r the authority of the Standards Board and comes effect on 15 March 1994 BSI 04-1999 The following BSI references relate to the work on this standard: Committee reference STC/21 Draft for comment 92/50242 DC ISBN 0 580 23059 7 Committees responsible for this British Standard The preparation of this

4、British Standard was entrusted by the Surface Treatments and Coatings Standards Policy Committee (STC/-) to Technical Committee STC/21, upon which the following bodies were represented: Association of Consulting Engineers British Chemical Engineering Contractors Association British Coatings Federati

5、on Ltd. British Constructional Steelwork Association Ltd. British Grit Association British Railways Board British Steel Industry Department of Transport Electricity Association Institute of Corrosion National Federation of Painting and Decorating Contractors Oil and Colour Chemists Association Paint

6、 Research Association Royal Society of Chemistry Amendments issued since publication Amd. No. Date Comments 9843 February 1998 Indicated by a sideline in the marginBSENISO11126-3:1998 BSI 04-1999 i Contents Page Committees responsible Inside front cover National foreword ii Foreword 2 Text of EN ISO

7、 11126-3 3BSENISO11126-3:1998 ii BSI 04-1999 National foreword This British Standard has been prepared by Technical Committee STI/21 and is the English language version of EN ISO11126-3:1997 Preparation of steel substrates before application of paints and related products Specifications for non-meta

8、llic blast-cleaning abrasives Part 3: Copper refinery slag, published by the European Committee for Standardization (CEN). It is identical with ISO11126-3:1993, published by the International Organization for Standardization (ISO). International Standard ISO11126-3 was prepared by Technical Committe

9、e ISO/TC 35, Paints and varnishes, SubcommitteeSC12, Preparation of steel substrates before application of paints and related products. Cross-references The British Standards which implement international or European publications referred to in this document may be found in the BSI Standards Catalog

10、ue under the section entitled “International Standards Correspondence Index”, or by using the “Find” facility of the BSI Standards Electronic Catalogue. A British Standard does not purport to include all the necessary provisions of a contract. Users of British Standards are responsible for their cor

11、rect application. Compliance with a British Standard does not of itself confer immunity from legal obligations. Summary of pages This document comprises a front cover, an inside front cover, pages i and ii, the EN ISO title page, pages 2 to 5and a back cover. This standard has been updated (see copy

12、right date) and may have had amendments incorporated. This will be indicated in the amendment table on theinside front cover.EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN ISO 11126-3 July 1997 ICS 87.020 Descriptors: Paints, varnishes, substrates, steel products, blast-cleaning, abrasives, no

13、n-metallic abrasives, specifications. English version Preparation of steel substrates before application of paints and related products Specifications for non-metallic blast-cleaning abrasives Part 3: Copper refinery slag (ISO 11126-3:1993) Prparation des subjectiles dacier avant application de pein

14、tures et de produits assimils Spcifications pour abrasifs non mtalliques destins la prparation par projection Partie 3: Scories de raffinage du cuivre (ISO11126-3:1993) Vorbereitung von Stahloberflchen vor dem Auftragen von Beschichtungsstoffen Anforderungen an nichtmetallische Strahlmittel Teil 3:

15、Strahlmittel aus Kupferhttenschlacke (ISO 11126-3:1993) This European Standard was approved by CEN on 1997-06-16. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any a

16、lteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the Central Secretariat or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by tr

17、anslation under the responsibility of a CEN member into its own language and notified to the Central Secretariat has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, CzechRepublic, Denmark, Finland, France, Germany, Greece, Iceland, Ireland

18、, Italy, Luxembourg, Netherlands, Norway, Portugal, Spain, Sweden, Switzerland and United Kingdom. CEN European Committee for Standardization Comit Europen de Normalisation Europisches Komitee fr Normung Central Secretariat: rue de Stassart 36, B-1050 Brussels 1997 CEN All rights of exploitation in

19、any form and by any means reserved worldwide for CEN national Members Ref.No.EN ISO 11126-3:1997 EENISO11126-3:1997 BSI 04-1999 2 Foreword The text of the International Standard from Technical Committee ISO/TC 35, Paints and varnishes, of the International Organization for Standardization (ISO) has

20、been taken over as a European Standard by Technical Committee CEN/TC 139, Paints and varnishes, the secretariat of which is held by DIN. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by January 199

21、8, and conflicting national standards shall be withdrawn at the latest by January 1998. According to CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, CzechRepublic, Denmark, Finland, Fra

22、nce, Germany, Greece, Iceland, Ireland, Italy, Luxembourg, Netherlands, Norway, Portugal, Spain, Sweden, Switzerland and the United Kingdom. NOTENormative references to International Standards are listed in Annex ZA (normative). Contents Page Foreword 2 1 Scope 3 2 Normative references 3 3 Definitio

23、n 3 4 Designation of abrasives 3 5 Sampling 4 6 Requirements 4 7 Identification and marking 4 8 Information to be supplied by the manufacturer or supplier 4 Annex A (informative) Bibliography 5 Annex ZA (normative) Normative references to international publications with their relevant European publi

24、cations 5 Table 1 Particle size distribution 4 Table 2 Particular requirements for copper refinery slag abrasives 4ENISO11126-3:1997 BSI 04-1999 3 WARNING Equipment, materials and abrasives used for surface preparation can be hazardous if used carelessly. Many national regulations exist for those ma

25、terials and abrasives that are considered to be hazardous during or after use (waste management), such as free silica or carcinogenic or toxic substances. These regulations are therefore to be observed. It is important to ensure that adequate instructions are given and that all required precautions

26、are exercised. 1 Scope This part of ISO11126 specifies requirements for copper refinery slag abrasives, as supplied for blast-cleaning processes. It specifies ranges of particle sizes and values for apparent density, Mohs hardness, moisture content, conductivity of aqueous extract and water-soluble

27、chlorides. The requirements specified in this part of ISO11126 apply to abrasives supplied in the “new” condition only. They do not apply to abrasives either during or after use. Test methods for non-metallic blast-cleaning abrasives are given in the various parts of ISO11127. NOTE 1Information on c

28、ommonly referenced national standards for non-metallic abrasives is given in Annex A. NOTE 2Although this part of ISO11126 has been developed specifically to meet requirements for preparation of steelwork, the properties specified will generally be appropriate for use when preparing other material s

29、urfaces, or components, using blast-cleaning techniques. These techniques are described in ISO8504-2:1992, Preparation of steel substrates before application of paints and related products Surface preparation methods Part 2: Abrasive blast-cleaning. 2 Normative references The following standards con

30、tain provisions which, through reference in this text, constitute provisions of this part of ISO11126. At the time of publication, the editions indicated were valid. All standards are subject to revision, and parties to agreements based on this part of ISO11126 are encouraged to investigate the poss

31、ibility of applying the most recent editions of the standards indicated below. Members of IEC and ISO maintain registers of currently valid International Standards. ISO 11127-1:1993, Preparation of steel substrates before application of paints and related products Test methods for non-metallic blast

32、-cleaning abrasives Part 1: Sampling. ISO 11127-2:1993, Preparation of steel substrates before application of paints and related products Test methods for non-metallic blast-cleaning abrasives Part 2: Determination of particle size distribution. ISO 11127-3:1993, Preparation of steel substrates befo

33、re application of paints and related products Test methods for non-metallic blast-cleaning abrasives Part 3: Determination of apparent density. ISO 11127-4:1993, Preparation of steel substrates before application of paints and related products Test methods for non-metallic blast-cleaning abrasives P

34、art 4: Assessment of hardness by a glass slide test. ISO 11127-5:1993, Preparation of steel substrates before application of paints and related products Test methods for non-metallic blast-cleaning abrasives Part 5: Determination of moisture. ISO 11127-6:1993, Preparation of steel substrates before

35、application of paints and related products Test methods for non-metallic blast-cleaning abrasives Part 6: Determination of water-soluble contaminants by conductivity measurement. ISO 11127-7:1993, Preparation of steel substrates before application of paints and related products Test methods for non-

36、metallic blast-cleaning abrasives Part 7: Determination of water-soluble chlorides. 3 Definition For the purposes of this part of ISO11126, the following definition applies. 3.1 copper refinery slag a synthetic mineral blast-cleaning abrasive manufactured, by granulation in water, drying and sieving

37、, with or without mechanical crushing processes, from slag originating from copper smelting. It is basically iron silicate slag NOTE 3Slags manufactured by air cooling instead of granulation in water are generally of a different mineral structure and are therefore not covered by this part of ISO1112

38、6. 4 Designation of abrasives Copper refinery slag abrasives shall be identified by “Abrasive ISO11126” and the abbreviation N/CU indicating non-metallic, copper refinery slag abrasive. This shall be followed, without spaces, by an oblique stroke and then by the symbol G to indicate the required par

39、ticle shape of the abrasive, when purchased, as grit. The designation shall be completed by numbers denoting the particle size range, in millimetres, required (seeTable 1).ENISO11126-3:1997 4 BSI 04-1999 EXAMPLE 1 Abrasive ISO 11126 N/CU/G 0,5-1 denotes an abrasive of the non-metallic copper refiner

40、y slag type, complying with the requirements of this part of ISO11126, of initial particle shape grit and particle size range0,5mm to1mm. It is essential that this full product designation is quoted on all orders. 5 Sampling Sampling procedures shall be as specified in ISO11127-1. 6 Requirements 6.1

41、 General requirements Copper refinery slag abrasives shall be vitreous amorphous materials that absorb no water but may be wetted on the surface only. Silica in copper refinery slag abrasives shall be present as bonded silicate. The content of free crystalline silica (such as quartz, tridimite or cr

42、ystobalite) shall not exceed1% (m/m), as determined by X-ray diffraction. The material shall be free from corrosive constituents and adhesion-impairing contaminants. NOTE 4Copper refinery slag abrasives as supplied have a predominantly angular shape. More spherical particle shapes are not excluded a

43、s their effect on the surface profile obtained corresponds generally to that produced by angular abrasive particles. 6.2 Particular requirements Particular requirements for copper refinery slag abrasives shall be as specified inTable 2. 7 Identification and marking All supplies shall be clearly mark

44、ed or identified using the appropriate designation as specified in clause4, either directly or by the accompanying delivery note. 8 Information to be supplied by the manufacturer or supplier The manufacturer or supplier shall supply, if requested, a test report detailing results for any relevant pro

45、perty as determined by the appropriate method specified in Table 2. Table 1 Particle size distribution Table 2 Particular requirements for copper refinery slag abrasives Particle size range a mm 0,2 to 0,5 0,2 to 1 0,2 to 1,4 0,2 to 2 0,2 to 2,8 0,5 to 1 0,5 to 1,4 1,0 to 2 1,4 to 2,8 Oversize Sieve

46、 size mm 0,5 1 1,4 2 2,8 1 1,4 2 2,8 Residue % (m/m) max. 10 10 10 10 10 10 10 10 10 Nominal size Sieve size mm 0,2 0,2 0,2 0,2 0,2 0,5 0,5 1 1,4 Residue % (m/m) min. 85 85 85 85 85 80 80 80 80 Undersize Sieve size mm 0,2 0,2 0,2 0,2 0,2 0,5 0,5 1 1,4 Through-flow % (m/m) max. 5 5 5 5 5 10 10 10 10

47、a By agreement between the interested parties, abrasives of different particle size ranges may be mixed together. Details of proportions of nominal size, oversize and undersize shall be specified. The maximum particle size shall not exceed3,15mm and the proportion of particles less than0,2mm shall n

48、ot exceed5% (m/m). Property Requirement Test method Particle size range and distribution See Table 1 ISO 11127-2 Apparent density kg/m 3 kg/dm 3 (3,3 to 3,9) 10 3 3,3 to 3,9 ISO 11127-3 Mohs hardness a min. 6 ISO 11127-4 Moisture % (m/m) max. 0,2 ISO 11127-5 Conductivity of aqueous extract mS/m max.

49、 25 ISO 11127-6 Water-soluble chlorides % (m/m) max. 0,002 5 ISO 11127-7 a Another method for assessing hardness may be used, together with an appropriate minimum requirement, by agreement between the interested parties.ENISO11126-3:1997 BSI 04-1999 5 Annex A (informative) Bibliography Commonly referenced national standards for non-metallic abrasives are as follows: 1 DIN 8200:1982, Strahlverfahrenstechnik; Begriffe, Einordnung der Strahlverfahren (Blasting; terms, classification of blas