BS EN ISO 11126-5-1994 Preparation of steel substrates before application of paints and related products - Specifications for non-metallic blast-cleaning abrasives - Nickel refiner.pdf

1、BRITISH STANDARD CONFIRMED DECEMBER1998 BS EN ISO 11126-5:1998 BS7079-F5: 1994 Incorporating Amendment No. 1 to BS 7079-F5:1994 (which it renumbers as BSENISO 11126-5:1998) Preparation of steel substrates before application of paints and related products Specifications for non-metallic blast-cleanin

2、g abrasives Part 5: Nickel refinery slag The European Standard EN ISO11126-5:1998 has the status of a British Standard ICS25.220.10; 87.020BSENISO11126-5:1998 This British Standard, having been prepared under the directionof the Surface Treatments and Coatings Standards Policy Committee, waspublishe

3、d under the authorityof the Standards Boardand comes into effect on 15 March 1994 BSI 04-1999 The following BSI references relate to the work on this standard: Committee reference STC/21 Draft for comment 92/50244 DC ISBN 0 580 23051 1 Committees responsible for this British Standard The preparation

4、 of this British Standard was entrusted by the Surface Treatments and Coatings Standards Policy Committee (STC/-) to Technical Committee STC/21, upon which the following bodies were represented: Association of Consulting Engineers British Chemical Engineering Contractors Association British Coatings

5、 Federation Ltd. British Constructional Steelwork Association Ltd. British Grit Association British Railways Board British Steel Industry Department of Transport Electricity Association Institute of Corrosion National Federation of Painting and Decorating Contractors Oil and Colour Chemists Associat

6、ion Paint Research Association Royal Society of Chemistry Amendments issued since publication Amd.No. Date Comments 10089 August 1998 Indicated by a side line in the marginBSENISO11126-5:1998 BSI 04-1999 i Contents Page Committees responsible Inside front cover National foreword ii Foreword 2 1 Scop

7、e 3 2 Normative references 3 3 Definition 3 4 Designation of abrasives 3 5 Sampling 4 6 Requirements 4 7 Identification and marking 4 8 Information to be supplied by the manufacturer or supplier 4 Annex A (informative) Bibliography 5 Annex ZA (normative) Normative references to international publica

8、tions withtheir relevant European publications 6 Table 1 Particle size distribution 4 Table 2 Particular requirements for nickel refinery slag abrasives 4BSENISO11126-5:1998 ii BSI 04-1999 National foreword This British Standard has been prepared by Technical Committee STI/21 and is the English lang

9、uage version of EN 11126-5:1998 Preparation of steel substrates before application of paints and related products Specification for non-metallic blast-cleaning abrasives Part 5: Nickel refinery slag, published by the European Committee for Standardization (CEN). It is identical with ISO11126-5:1993,

10、 published by the International Organization for Standardization (ISO). International Standard ISO11126-5 was prepared by Technical Committee ISO/TC35, Paints and varnishes, Subcommittee SC12, Preparation of steel substrates before application of paints and related products. Cross-references The Bri

11、tish Standards which implement international or European publications referred to in this document may be found in the BSI Standards Catalogue under the section entitled “International Standards Correspondence Index”, or by using the “Find” facility of the BSI Standards Electronic Catalogue. A Briti

12、sh Standard does not purport to include all the necessary provisions of a contract. Users of British Standards are responsible for their correct application. Compliance with a British Standard does not of itself confer immunity from legal obligations. Summary of pages This document comprises a front

13、 cover, an inside front cover, pagesi andii, theEN ISO title page, pages2 to6 and a back cover. This standard has been updated (see copyright date) and may have had amendments incorporated. This will be indicated in the amendment table on the inside front cover.EUROPEAN STANDARD NORME EUROPENNE EURO

14、PISCHE NORM EN ISO 11126-5 March 1998 ICS 87.020 Descriptors: Paints, varnishes, substrates, steel products, blast-cleaning, abrasives, non-metallic abrasives, specifications English version Preparation of steel substrates before application of paints and related products Specifications for non-meta

15、llic blast-cleaning abrasives Part 5: Nickel refinery slag (ISO 11126-5:1993) Prparation des subjectiles dacier avant application de peintures et de produits assimils Spcifications pour abrasifs non mtalliques destines la prparation par projection Partie 5: Scories de raffinage dunickel (ISO 11126-5

16、:1993) Vorbereitung von Stahloberflchen vor dem Auftragen von Beschichtungsstoffen Anforderungen an nichtmetallische Strahlmittel Teil 5: Strahlmittel aus Nickelhttenschlacke (ISO11126-5:1993) This European Standard was approved by CEN on 2 March1998. CEN members are bound to comply with the CEN/CEN

17、ELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the Central Secretariat or to any

18、CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the Central Secretariat has the same status as the official versions. CEN

19、 members are the national standards bodies of Austria, Belgium, CzechRepublic, Denmark, Finland, France, Germany, Greece, Iceland, Ireland, Italy, Luxembourg, Netherlands, Norway, Portugal, Spain, Sweden, Switzerland and United Kingdom. CEN European Committee for Standardization Comit Europen de Nor

20、malisation Europisches Komitee fr Normung Central Secretariat: rue de Stassart 36, B-1050 Brussels 1998 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN ISO 11126-5:1998ENISO11126-5:1998 BSI 04-1999 2 Foreword The text of the Intern

21、ational Standard from Technical Committee ISO/TC 35, Paints and varnishes, of the International Organization for Standardization (ISO) has been taken over as a European Standard by Technical Committee CEN/TC 139, Paints and varnishes, the secretariat of which is held by DIN. This European Standard s

22、hall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by September 1998, and conflicting national standards shall be withdrawn at the latest by September 1998. According to CEN/CENELEC Internal Regulations, the following countrie

23、s are bound to implement this European Standard: Austria, Belgium, CzechRepublic, Denmark, Finland, France, Germany, Greece, Iceland, Ireland, Italy, Luxembourg, Netherlands, Norway, Portugal, Spain, Sweden, Switzerland and theUnitedKingdom. NOTENormative references to International standards are li

24、sted in Annex ZA (normative).ISO11126-5:1993(E) BSI 04-1999 3 WARNING Equipment, materials and abrasives used for surface preparation can be hazardous if used carelessly. Many national regulations exist for those materials and abrasives that are considered to be hazardous during or after use (waste

25、management), such as free silica or carcinogenic or toxic substances. These regulations are therefore to be observed. It is important to ensure that adequate instructions are given and that all required precautions are exercised. 1 Scope This part of ISO 11126 specifies requirements fornickel refine

26、ry slag abrasives, as supplied for blast-cleaning processes. It specifies ranges of particle sizes and values for apparent density, Mohs hardness, moisture content, conductivity of aqueous extract and water-soluble chlorides. The requirements specified in this part of ISO11126 apply to abrasives sup

27、plied in the “new” condition only. They do not apply to abrasives either during or after use. Test methods for non-metallic blast-cleaning abrasives are given in the various parts of ISO11127. NOTE 1Information on commonly referenced national standards for non-metallic abrasives is given in Annex A.

28、 NOTE 2Although this part of ISO 11126 has been developed specifically to meet requirements for preparation of steelwork, the properties specified will generally be appropriate for use when preparing other material surfaces, or components, using blast-cleaning techniques. These techniques are descri

29、bed in ISO 8504-2:1992, Preparation of steel substrates before application of paints and related products Surface preparation methods Part 2: Abrasive blast-cleaning. 2 Normative references The following standards contain provisions which, through reference in this text, constitute provisions of thi

30、s part of ISO 11126. At the time of publication, the editions indicated were valid. All standards are subject to revision, and parties to agreements based on this part of ISO 11126 are encouraged to investigate the possibility of applying the most recent editions of the standards indicated below. Me

31、mbers of IEC and ISO maintain registers of currently valid International Standards. ISO 11127-1:1993, Preparation of steel substrates before application of paints and related products Test methods for non-metallic blast-cleaning abrasives Part 1: Sampling. ISO 11127-2:1993, Preparation of steel subs

32、trates before application of paints and related products Test methods for non-metallic blast-cleaning abrasives Part 2: Determination of particle size distribution. ISO 11127-3:1993, Preparation of steel substrates before application of paints and related products Test methods for non-metallic blast

33、-cleaning abrasives Part 3: Determination of apparent density. ISO 11127-4:1993, Preparation of steel substrates before application of paints and related products Test methods for non-metallic blast-cleaning abrasives Part 4: Assessment of hardness by a glass slide test. ISO 11127-5:1993, Preparatio

34、n of steel substrates before application of paints and related products Test methods for non-metallic blast-cleaning abrasives Part 5: Determination of moisture. ISO 11127-6:1993, Preparation of steel substrates before application of paints and related products Test methods for non-metallic blast-cl

35、eaning abrasives Part 6: Determination of water-soluble contaminants by conductivity measurement. ISO 11127-7:1993, Preparation of steel substrates before application of paints and related products Test methods for non-metallic blast-cleaning abrasives Part 7: Determination of water-soluble chloride

36、s. 3 Definition For the purposes of this part of ISO 11126, the following definition applies. 3.1 nickel refinery slag a synthetic mineral blastcleaning abrasive manufactured, by granulation in water, drying and sieving, with or without mechanical crushing processes, from slag originating from nicke

37、l smelting. It is basically iron silicate slag NOTE 3Slags manufactured by air cooling instead of granulation in water are generally of a different mineral structure and are therefore not covered by this part of ISO11126. 4 Designation of abrasives Nickel refinery slag abrasives shall be identified

38、by “Abrasive ISO 11126” and the abbreviation N/NI indicating non-metallic, nickel refinery slag abrasive. This shall be followed, without spaces, by an oblique stroke and then by the symbol G to indicate the required particle shape of the abrasive, when purchased, as grit. The designation shall be c

39、ompleted by numbers denoting the particle size range, in millimetres, required (see Table 1).ISO11126-5:1993(E) 4 BSI 04-1999 EXAMPLE 1 Abrasive ISO 11126 N/NI/G 0,2-1 denotes an abrasive of the non-metallic nickel refinery slag type, complying with the requirements of this part of ISO 11126, of ini

40、tialparticle shape grit and particle size range0,2 mm to 1 mm. It is essential that this full product designation is quoted on all orders. 5 Sampling Sampling procedures shall be as specified in ISO 11127-1. 6 Requirements 6.1 General requirements Nickel refinery slag abrasives shall be vitreous amo

41、rphous materials that absorb no water but may be wetted on the surface only. Silica in nickel refinery slag abrasives shall be present as bonded silicate. The content of free crystalline silica (such as quartz, tridimite or crystobalite) shall not exceed 1 % (m/m), as determined by X-ray diffraction

42、. The material shall be free from corrosive constituents and adhesion-impairing contaminants. NOTE 4Nickel refinery slag abrasives as supplied have a predominantly angular shape. More spherical particle shapes are not excluded as their effect on the surface profile obtained corresponds generally to

43、that produced by angular abrasive particles. 6.2 Particular requirements Particular requirements for nickel refinery slag abrasives shall be as specified in Table 2. 7 Identification and marking All supplies shall be clearly marked or identified using the appropriate designation as specified in clau

44、se 4, either directly or by the accompanying delivery note. 8 Information to be supplied by the manufacturer or supplier The manufacturer or supplier shall supply, if requested, a test report detailing results for any relevant property as determined by the appropriate method specified in Table 2. Ta

45、ble 1 Particle size distribution Table 2 Particular requirements for nickel refinery slag abrasives Particle size range a mm 0,2 to 0,5 0,2 to 1 0,2 to 1,4 0,2 to 2 0,2 to 2,8 0,5 to 1 0,5 to 1,4 1,0 to 2 1,4 to 2,8 Oversize Sieve size mm 0,5 1 1,4 2 2,8 1 1,4 2 2,8 Residue % (m/m) max. 10 10 10 10

46、10 10 10 10 10 Nominal size Sieve size mm 0,2 0,2 0,2 0,2 0,2 0,5 0,5 1 1,4 Residue % (m/m) min. 85 85 85 85 85 80 80 80 80 Undersize Sieve size mm 0,2 0,2 0,2 0,2 0,2 0,5 0,5 1 1,4 Through-flow % (m/m) max. 5 5 5 5 5 10 10 10 10 a By agreement between the interested parties, abrasives of different

47、particle size ranges may be mixed together. Details of proportions of nominal size, oversize and undersize shall be specified. The maximum particle size shall not exceed 3,15 mm and the proportion of particles less than 0,2 mm shall not exceed 5 % (m/m). Property Requirement Test method Particle siz

48、e range and distribution see Table 1 ISO 11127-2 Apparent density kg/m 3 kg/dm 3 (3,3 to 3,9) 10 3 3,3 to 3,9 ISO 11127-3 Mohs hardness a min. 6 ISO 11127-4 Moisture % (m/m) max. 0,2 ISO 11127-5 Conductivity of aqueous extract mS/m max. 25 ISO 11127-6 Water-soluble chlorides % (m/m) max. 0,0025 ISO

49、11127-7 a Another method for assessing hardness may be used, together with an appropriate minimum requirement, by agreement between the interested parties.ISO11126-5:1993(E) BSI 04-1999 5 Annex A (informative) Bibliography Commonly referenced national standards for non-metallic abrasives are as follows: 1 DIN 8200:1982, Strahlverfahrenstechnik; Begriffe, Einordnung der Strahlverfahren (Blasting; terms, classification of blasting techniques). 2 DIN 8201 Teil 1:1985, Feste Strahlmittel; Eint