DIN 17751-2002 Tubes of wrought nickel and nickel alloys - Properties《精制镍和镍合金管 性能》.pdf

1、ICS 77.150.40Rohre aus Nickel und Nickelknetlegierungen EigenschaftenIn keeping with current practice in standards published by the International Organization for Standardization(ISO), a comma has been used throughout as the decimal marker.Ref. No. DIN 17751 : 2002-09English price group 06 Sales No.

2、 000603.03DEUTSCHE NORM September 200217751 No part of this translation may be reproduced without the prior permission ofDIN Deutsches Institut fr Normung e.V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).Translation by DIN-Sprac

3、hendienst.In case of doubt, the German-language original should be consulted as the authoritative text.Wrought nickel and nickel alloy pipes and tubesRequirements and testingContinued on pages 2 to 5.SupersedesFebruary 1983 edition.ForewordThis standard has been prepared by the Normenausschuss Nicht

4、eisenmetalle (Nonferrous Metals StandardsCommittee), Technical Committee Nickelwerkstoffe.See Other relevant standards for further standards covering requirements for nickel semi-finished products.AmendmentsThis standard differs from the February 1983 edition in that it has been revised in form and

5、substance,11 grades have been included and grades NiCr22Mo6Cu and NiCr21Mo6Cu have been dropped.Previous editionsDIN 17751: 1973-12, 1983-02.1 ScopeThis standard specifies requirements for the mechanical properties of wrought nickel and nickel alloy pipesand tubes having the dimensions specified in

6、table 1, and gives details on the relevant methods of test.Where products are to have dimensions other than those covered by this standard, this shall be subject toagreement.ContentsPage1 Scope . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .

7、. . . 12 Normative references . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 23 Ordering details . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 24 Mechanical properties at ambient temperature . . . . . . . . . .

8、. . . . . . . . . . . . 25 Chemical composition . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 26 Dimensions and tolerances . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 27 Testing . . . . . . . . . . . . . . . . . . . . . . . .

9、. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 2Other relevant standards . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 5Page 2DIN 17751 : 2002-092 Normative referencesThis standard incorporates, by dated or undated reference, provisions from oth

10、er publications. These norma-tive references are cited at the appropriate places in the text and the titles of the publications are listed below.For dated references, subsequent amendments to or revisions of any of these publications apply to thisstandard only when incorporated in it by amendment or

11、 revision. For undated references, the latest edition ofthe publication referred to applies.DIN 1333 Presentation of numerical dataDIN 17740 Wrought nickel Chemical compositionDIN 17742 Wrought nickel-chromium alloys Chemical compositionDIN 17743 Wrought nickel-copper alloys Chemical compositionDIN

12、17744 Wrought nickel-chromium-molybdenum alloys Chemical compositionDIN 50125 Test pieces for the tensile testing of metallic materialsDIN 59755 Cold produced wrought nickel and nickel alloy pipes and tubes Dimensions and toler-ancesDIN EN 10002-1 Metallic materials Tensile testing Method of test at

13、 ambient temperature (includingCorrigendum AC 1 : 1990)DIN EN ISO 6506-1 Metallic materials Brinell hardness test Part 1: Test method (ISO 6506-1 : 1999)DIN EN ISO 6507-1 Metallic materials Vickers hardness test Part 1: Test method (ISO 6507-1 : 1997)3 Ordering detailsThe grade and the form of produ

14、ct supplied is at the purchasers discretion. It is recommended that the intendeduse of the product and any further processing be indicated at the time of ordering. For designating the product,the designation specified in the relevant dimensional standard shall be used.Any properties the products are

15、 to have shall be specified when ordering, together with the relevant testmethods.4 Mechanical properties at ambient temperatureThe products shall have the properties specified in table 1.5 Chemical compositionThe chemical composition of wrought nickel and nickel alloy pipes and tubes shall be as sp

16、ecified in the relevantstandards referred to in table 1.6 Dimensions and tolerancesDimensions and tolerances for wrought nickel and nickel alloy pipes and tubes shall be as specified inDIN 59755.7 TestingTensile strength, proof strength and percentage elongation after fracture shall be tested in acc

17、ordance withDIN 50125 and DIN EN 10002-1. It is recommended that the hardness be determined based onDIN EN ISO 6506-1, using a ball diameter of 2,5 mm and a test force of 612,9 N (HBW 2,5/62,5). Where this isnot possible, the Vickers hardness test in accordance with DIN EN ISO 6507-1 shall be carrie

18、d out, hardnessvalues higher by 15% than for the Brinell test being acceptable.When expressing the result, rounding shall be in accordance with DIN 1333, to the same number of places asis given in table 1.Page 3DIN 17751 : 2002-09DesignationNameNumberTable1:Mechanical propertiesMaterialTemperHeat tr

19、eatmentcondition1)Wall thickness,inmmFromToMin.tensilestrength,RmMin. 0,2%proofstrength,Rp0,2Wrought nickel (with composition as in DIN17740)Nickel-chromium alloys (with composition as in DIN17742)Soft annealed Half-hard Hard Soft annealed Half-hard Hard Soft annealed Half-hard Hard Soft annealed Ha

20、lf-hard Hard Solution treated Solution treated Solution treated Soft annealed Solution treated Soft annealed Solution treated Soft annealed Solution treated Solution treated(continued)Min. 1%proofstrength,Rp1,0Min.percent-ageelongationafterfracture,A5Brinell hardness(HBW 2,5/62,5)Max.Approx.Page 4DI

21、N 17751 : 2002-09DesignationNameNumberTable1(concluded)MaterialTemperHeat treatmentcondition1)Wall thickness,inmmFromToMin.tensilestrength,RmMin. 0,2%proofstrength,Rp0,2Nickel-copper alloys (with composition as in DIN17743)Nickel-chromium-molybdenum alloys (with composition as in DIN17744)Soft annea

22、led Half-hard Hard Soft annealed Solution treated Solution treated Solution treated Solution treated Solution treated Solution treated Solution treated Soft annealed Solution treated Solution treated Solution treated2)Solution treated Solution treated Soft annealed Soft annealedMin. 1%proofstrength,

23、Rp1,0Min.percent-ageelongationafterfracture,A5Brinell hardness(HBW 2,5/62,5)Max.Approx.1)Heat treatment condition as declared by manufacturer.2)At temperatures from 1204C to 1246C.Page 5DIN 17751 : 2002-09Other relevant standardsDIN 17745 Wrought nickel-iron alloys Chemical compositionDIN 17750 Wrought nickel and nickel alloy sheet, plate and strip Requirements and testingDIN 17752 Wrought nickel and nickel alloy bars and rod Requirements and testingDIN 17753 Wrought nickel and nickel alloy wire Requirements and testing