1、September 2013 Translation by DIN-Sprachendienst.English price group 13No part of this translation may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).
2、ICS 77.140.50!%(t“2058198www.din.deDDIN EN 10209Cold rolled low carbon steel flat products for vitreous enamelling Technical delivery conditions;English version EN 10209:2013,English translation of DIN EN 10209:2013-09Kaltgewalzte Flacherzeugnisse aus weichen Sthlen zum Emaillieren Technische Liefer
3、bedingungen;Englische Fassung EN 10209:2013,Englische bersetzung von DIN EN 10209:2013-09Produits plats lamins froid, en acier doux pour maillage par vitrification Conditions techniques de livraison;Version anglaise EN 10209:2013,Traduction anglaise de DIN EN 10209:2013-09SupersedesDIN EN 10209:1996
4、-05www.beuth.deIn case of doubt, the German-language original shall be considered authoritative.Document comprises 27 pages 08.13 DIN EN 10209:2013-09 2 A comma is used as the decimal marker. National foreword This document (EN 10209:2013) has been prepared by Technical Committee ECISS/TC 109 “Coate
5、d and uncoated flat products to be used for cold forming” (Secretariat: AFNOR, France). The responsible German body involved in its preparation was the Normenausschuss Eisen und Stahl (Iron and Steel Standards Committee), Working Committee NA 021-00-01-01 UA Flacherzeugnisse aus Stahl zum Kaltumform
6、en. Amendments This standard differs from DIN EN 10209:1996-05 as follows: a) normative references in Clause 2 and throughout the standard have been updated; b) in Subclause 5.4.1, quality DC05EK has been supplemented; c) Clause 7 “Identification” has been completely revised; d) in Table 2, footnote
7、 l has been added; e) the former Annex A “Method for determining the coefficient of plastic anisotropy (r-Werte)” has been deleted; f) Subclause C.6.1 has been revised; g) Subclause C.6.2 concerning thinner sheet steel has been added; h) Figure C.2 has been revised; i) the standard has been editoria
8、lly revised. Previous editions DIN 1623-3: 1983-02, 1987-01 DIN EN 10209: 1996-05 EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 10209 June 2013 ICS 77.140.50 Supersedes EN 10209:1996English Version Cold rolled low carbon steel flat products for vitreous enamelling -Technical delivery conditio
9、ns Produits plats lamins froid, en acier doux pour maillage par vitrification - Conditions techniques de livraison Kaltgewalzte Flacherzeugnisse aus weichen Sthlen zum Emaillieren - Technische Lieferbedingungen This European Standard was approved by CEN on 11 April 2013. CEN members are bound to com
10、ply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN-CENELE
11、C Management Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the s
12、ame status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembour
13、g, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG Management Centre: Avenue Marnix 17, B-1000 Brussels 2013 CEN All
14、rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN 10209:2013: EEN 10209:2013 (E) 2 Contents Page Foreword 3 1 Scope 4 2 Normative references 4 3 Terms and definitions .5 4 Designation 5 5 Requirements .5 6 Tests 8 7 Identification .9 8 Packa
15、ging .9 9 Disputes 9 10 Information to be supplied by the purchaser at the time of ordering 9 Annex A (normative) Methods for determining the resistance to fish scaling of a steel sheet for enamelling . 13 Annex B (normative) Method for determining mass loss (iron loss) due to pickling for steel gra
16、des for direct enamelling in accordance with 5.4.2 17 Annex C (normative) Method for determining the adherence level of enamel applied to a steel sheet . 20 Annex D (informative) Characteristics for the selection of enamelling steel grades 25 DIN EN 10209:2013-09EN 10209:2013 (E) 3 Foreword This doc
17、ument (EN 10209:2013) has been prepared by Technical Committee ECISS/TC 109 “ ”, the secretariat of which is held by AFNOR. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by December 2013, and confl
18、icting national standards shall be withdrawn at the latest by December 2013. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. This docu
19、ment supersedes EN 10209:1996. According to the CEN-CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Rep
20、ublic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom. Coated and uncoatedflat products to be used for cold for
21、mingDIN EN 10209:2013-09EN 10209:2013 (E) 4 1 Scope This European Standard applies to cold rolled non-coated low carbon steel flat products in rolled widths equal to or over 600 mm and in thicknesses equal to or less than 3 mm, delivered in sheet, wide strip, slit wide strip or cut lengths obtained
22、from slit wide strip or sheet. It does not apply to cold rolled narrow strip (rolling width 1,6 m 5.9 Stretcher strain marks All the products are generally subjected to a light skin-pass after annealing at the manufacturers works to avoid the formation of stretcher strain marks during subsequent for
23、ming. The tendency to form such marks may reappear a certain time after the skin-pass. It is therefore in the purchasers interest to form the products as soon as possible. Quality DC06EK and DC06ED products do not exhibit stretcher strain marks after deformation. For the other qualities the absence
24、of stretcher strain marks may be guaranteed for six months after the products are made available. 5.10 Weldability The material is specified as suitable for normal welding procedures as long as the products are degreased beforehand. The welding procedure shall be specified at the time of ordering (s
25、ee 10 h). 5.11 Tolerances on dimensions and shape Tolerances on dimensions and shape are given in EN 10131. DIN EN 10209:2013-09EN 10209:2013 (E) 8 6 Tests 6.1 General 6.1.1 The purchaser shall specify at the time of ordering his requirements for: type of inspection and testing: specific or non-spec
26、ific, see EN 10021; type of inspection document, see EN 10204. 6.1.2 Specific inspection and testing shall be carried out in accordance with 6.2, 6.3, 6.4, 6.5 and 6.6. 6.1.3 Specific inspection and testing may not be specified either for the product analysis or the surface finish. 6.2 Inspection un
27、its The inspection unit is 30 t or a fraction of 30 t products of the same grade and nominal thickness. When a wide coil exceeds 30 t, it constitutes a single inspection unit, as do its products. 6.3 Number of tests For each inspection unit a tensile test shall be carried out, and if required, a det
28、ermination of r and of the suitability for enamelling shall be performed (see Table 2 and Annex A, Annex B and Annex C). 6.4 Sampling The requirements of EN ISO 377 and EN 10021 are supplemented by the following specific requirements. For sheet and cut lengths the selection of products to be tested
29、and the position of the samples in the products is left to the discretion of the inspection representative. In the case of wide strip and slit wide strip, the sample should preferably be taken from the outer end. If the width of the product permits, the test pieces for the tensile test shall be take
30、n perpendicular to the direction of rolling at a distance of at least 50 mm from the edge of the product. 6.5 Test methods 6.5.1 The products shall be tested in the as-delivered condition. The tests shall be carried out at ambient temperature. 6.5.2 The tensile test shall be carried out as specified
31、 in EN ISO 6892-1 using type 2 test pieces (initial gauge length Lo= 80 mm, width b = 20 mm). 6.5.3 Surface roughness shall be measured in accordance with EN 10049. 6.5.4 The determination of the plastic strain ratio r shall be carried out in accordance with ISO 10113. 6.5.5 The tests for suitabilit
32、y for enamelling (see 5.4.3) shall be carried out in accordance with Annex A for the fish scaling resistance test; Annex B for the mass loss due to pickling test; Annex C for the adherence test. DIN EN 10209:2013-09EN 10209:2013 (E) 9 6.5.6 For the determination of the chemical composition the corre
33、sponding European Standards shall apply in cases of dispute. 6.6 Retests The requirements of EN 10021 shall apply. For coils, in the event of the test results giving rise to dispute, the samples for retests shall be taken at intervals of at least one lap but also at a maximum distance of 20 m from t
34、he appropriate end. 6.7 Inspection documents If agreed at the time of ordering, an inspection document chosen from those given in EN 10204 shall be supplied (see also 6.1.1). 7 Identification All materials shall be identified with at least the following information: the conventional designation as d
35、escribed in Clause 4; the coil or bundle number; the suppliers mark. Typically, the identification is applied by either a label or using an easily removable non-corrosive ink on the inspected surface. Other identification requirements shall be agreed at the time of ordering. 8 Packaging The packagin
36、g requirements shall be agreed at the time of ordering. 9 Disputes With regard to any claims and actions, EN 10021 shall apply. 10 Information to be supplied by the purchaser at the time of ordering To permit the manufacturer to supply products conforming to this standard, the following information
37、should be given in the order: a) the full designation as given in Clause 4; b) nominal dimensions and quantities; c) if the products are to be supplied non skin-passed, d) if the products are to be delivered with mill edges or sheared edges; e) limits on mass and sizes of coils and individual bundle
38、s; f) intended application for the products; g) enamelling process used (see Annex D); DIN EN 10209:2013-09EN 10209:2013 (E) 10 h) if the products are to be welded, indication of the method to be used; i) if the products are to be supplied as suitable for making a specific part; j) if inspection doc
39、uments are requested and type; k) if an external inspection is to be carried out at the manufacturers works; l) if oiling is not required; m) detailed description of all other special requirements; n) any special requirements for packaging and marking; o) the position of the surface of better surfac
40、e finish quality. DIN EN 10209:2013-09EN 10209:2013 (E) 11 Table 2 Characteristics a iDesignation in accordance with EN 100271 Designation in accordance with EN 100272 Method of deoxidation Validity of mechanical properties and absence of stretcher strain marks ReMPa max b c lRmMPa lA80% min d l_ r
41、average min e lChemical composition (ladle analysis) % max C content (product analysis) % max C Ti Mn P S DC01EK 1.0390 Fully killed f6 months f270 270/390 30 0.08 0.60 0,045 0,050 DC04EK 1.0392 Fully killed 6 months 220k270/350 36 0.08 0,50 0,030 0,050 DC05EK 1.0386 Fully killed 6 months 220k270/35
42、0 36 1.5 0.08 0,50 0,025 0,050 DC06EK 1.0869 Fully killed 6 months 190 270/350 38 1.6 0.02 0.30h0,50 0,020 0,050 DC03ED 1.0399 Fully killed f6 months f240 270/370 34 j 0,40 0,035 0,050 0,004 DC04ED 1.0394 Fully killed 6 months 210g270/350 38 j 0,40 0,030 0,050 0,004 DC06ED 1.0872 Fully killed 6 mont
43、hs 190 270/350 38 1.6 0.02 0.30h0,35 0,020 0,050 aThe mechanical properties apply only to skin-passed product. bThe value for yield stress is the Rp0,2 % for products which do not present a definite yield point and the lower yield stress (Rel,) for the others. When the thickness is less than or equa
44、l to 0,7 mm and greater than 0,5 mm, the value for yield stress is increased by 20 MPa. For thicknesses less than or equal to 0,5 mm, the value is increased by 40 MPa. cFor design purposes, the lower limit of Refor qualities DCO1EK, DC04EK, DC05EK, DC03ED and DC04ED may be assumed to be 140 MPa and
45、for qualities DC06EK and DC06ED as 120 MPa. dWhen the thickness is less than or equal to 0,7 mm, and greater than 0,5 mm, the minimum elongation value after fracture is reduced by 2 units. For thicknesses equal to or less than 0,5 mm, the minimum value is reduced by 4 units. eThe value of r average
46、only applies to products of thicknesses equal to or greater than 0,5 mm. When the thickness is over 2,0 mm, the value of r average is reduced by 0,2 units. fSubject to agreement at the time of ordering, other deoxidation methods may be used. If so, the periods for validity of the mechanical properti
47、es and the absence of stretcher strain marks shall be agreed at the time of ordering. DIN EN 10209:2013-09EN 10209:2013 (E) 12 gIf the thickness is greater than or equal to 1,5 mm, the maximum value for the yield stress may reach 225 MPa. hTitanium may be replaced by niobium if agreed upon at the ti
48、me of ordering. Carbon and nitrogen shall be completely bound. iSubject to agreement at the time of ordering, other steels may be supplied which have the same mechanical properties. If so, the chemical composition of these steels shall be agreed at the time of ordering. jThe decarburisation of qualities DC03ED and DC04ED can take place in the solid or the liquid phase. The carbon content, determined by product analysis after decarburisation shall be 0,004 % maximum. If agreed at the time of ordering, qualities DC03ED and