DIN EN 10238-2009 Automatically blast-cleaned and automatically prefabrication primed structural steel products English version of DIN EN 10238 2009-10《自动爆破清理 并自动预制涂漆结构钢产品 德文版本EN 1.pdf

1、October 2009DEUTSCHE NORM English price group 8No part of this standard may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).ICS 77.140.10!$Z7“1552098ww

2、w.din.deDDIN EN 10238Automatically blast-cleaned and automatically prefabrication primedstructural steel productsEnglish version of DIN EN 10238:2009-10Automatisch gestrahlte und automatisch fertigungsbeschichtete Erzeugnisse ausBausthlenEnglische Fassung DIN EN 10238:2009-10SupersedesDIN EN 10238:1

3、996-11www.beuth.deDocument comprises pages13DIN EN 10238:2009-10 National foreword This standard has been prepared by Technical Committee ECISS/TC 10 “Structural steels Qualities” (Secretariat: DIN, Germany). The responsible German body involved in its preparation was the Normenausschuss Eisen und S

4、tahl (Iron and Steel Standards Committee), Technical Committee NA 021-00-04-04 UA Gestrahlte und beschichtete Stahlerzeugnisse. Amendments This standard differs from DIN EN 10238:1996-11 as follows: a) Normative references in clauses 2, 5, 8, 12 and in Annex B have been updated. b) In clause 5, exam

5、ple 1, the material number has been corrected to read 1.0490 (instead of 1.0486). c) The standard has been editorially revised. Previous editions DIN EN 10238: 1996-11 2 EUROPEAN STANDARDNORME EUROPENNEEUROPISCHE NORMEN 10238July 2009ICS 77.140.10 Supersedes EN 10238:1996 English VersionAutomaticall

6、y blast-cleaned and automatically prefabricationprimed structural steel productslments mtalliques prfabriqus automatiquement etdcaps automatiquement par projection dabrasifAutomatisch gestrahlte und automatischfertigungsbeschichtete Erzeugnisse aus BausthlenThis European Standard was approved by CEN

7、 on 12 June 2009.CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this EuropeanStandard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such nationalstandards may b

8、e obtained on application to the CEN Management Centre or to any CEN member.This European Standard exists in three official versions (English, French, German). A version in any other language made by translationunder the responsibility of a CEN member into its own language and notified to the CEN Ma

9、nagement Centre has the same status as theofficial versions.CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland,France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Nor

10、way, Poland, Portugal,Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.EUROPEAN COMMITTEE FOR STANDARDIZATIONCOMIT EUROPEN DE NORMALISATIONEUROPISCHES KOMITEE FR NORMUNGManagement Centre: Avenue Marnix 17, B-1000 Brussels 2009 CEN All rights of exploitation in any form and

11、by any means reservedworldwide for CEN national Members.Ref. No. EN 10238:2009: EEN 10238:2009 (E) 2 Contents Page Foreword 3 1 Scope 4 2 Normative references 4 3 Definitions 4 4 Information to be supplied by the purchaser .5 4.1 Mandatory information 5 4.2 Additional optional information .5 5 Desig

12、nation 5 6 Manufacture 6 7 Preparation grade 6 8 Surface roughness 7 9 Prefabrication primers 7 9.1 Types of prefabrication primers .7 9.2 Measurement of primer thickness .7 10 Flame cutting and weldability .8 11 Handling and storage 8 11.1 Handling 8 11.2 Storage 8 12 Inspection and testing .8 13 M

13、arking .9 Annex A (normative) Positions of test pieces for measuring the primer thickness . 10 Annex B (normative) Flame cutting - Welding 11 DIN EN 10238:2009-10 EN 10238:2009 (E) 3 Foreword This document (EN 10238:2009) has been prepared by Technical Committee ECISS/TC 10 “Structural steels - Qual

14、ities”, the secretariat of which is held by DIN. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by January 2010, and conflicting national standards shall be withdrawn at the latest by January 2010.

15、Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. This document supersedes EN 10238:1996. According to the CEN/CENELEC Internal Regulati

16、ons, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherla

17、nds, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and the United Kingdom. DIN EN 10238:2009-10 EN 10238:2009 (E) 4 1 Scope This European Standard specifies requirements for automatically blast-cleaned and automatically prefabrication primed structural steel produ

18、cts. This European Standard does not cover manual blast cleaning and/or manual spray painting. NOTE Where the steel is less than 5 mm thick, care should be exercised to ensure it is not deformed by blast cleaning. 2 Normative references The following referenced documents are indispensable for the ap

19、plication of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 10021, General technical delivery conditions for steel products EN 10025-2, Hot rolled products of structural

20、 steels - Part 2: Technical delivery conditions for non-alloy structural steels EN 10025-3, Hot rolled products of structural steels - Part 3: Technical delivery conditions for normalized/normalized rolled weldable fine grain structural steels EN 10204, Metallic products Types of inspection document

21、s EN ISO 2808:2007, Paints and varnishes Determination of film thickness (ISO 2808:2007) EN ISO 8501-1, Preparation of steel substrates before application of paints and related products Visual assessment of surface cleanliness Part 1: Rust grades and preparation grades of uncoated steel substrates a

22、nd of steel substrates after overall removal of previous coatings (ISO 8501-1:2007) EN ISO 8503-2, Preparation of steel substrates before application of paints and related products Surface roughness characteristics of blast-cleaned steel substrates Part 2: Method for the grading of surface profile o

23、f abrasive blast-cleaned steel Comparator procedure (ISO 8503-2:1998) EN ISO 17652-1:2003, Welding Test for shop primers in relation to welding and allied processes Part 1: General requirements (ISO 17652-1:2003) EN ISO 17652-2:2003, Welding Test for shop primers in relation to welding and allied pr

24、ocesses Part 2: Welding properties of shop primers (ISO 17652-2:2003) EN ISO 17652-3:2003, Welding Test for shop primers in relation to welding and allied processes Part 3: Thermal cutting (ISO 17652-3:2003) EN ISO 17652-4:2003, Welding Test for shop primers in relation to welding and allied process

25、es Part 4: Emission of fumes and gases (ISO 17652-4:2003) 3 Definitions For the purposes of this document, the following definitions apply: DIN EN 10238:2009-10 EN 10238:2009 (E) 5 3.1 automatic blast cleaning use of mechanical plant where the product being blast-cleaned is passed through a machine

26、where turbines are used to project the abrasive onto the steel in a uniform manner 3.2 automatic priming After automatic blast cleaning, the product is primed by passing through a paint booth where reciprocating paint guns apply a continuous coating to the required thickness. 3.3 prefabrication prim

27、er thin coating which is automatically applied to blast cleaned steel and serves to provide temporary corrosion protection for steel components during their processing, transport and storage 4 Information to be supplied by the purchaser 4.1 Mandatory information The following information shall be su

28、pplied by the purchaser at the time of enquiry and order: a) designation of the steel; b) type of prefabrication primer (see 9.1 table 1); c) type of inspection document (clause 12). 4.2 Additional optional information a) Preparation grade if different from Sa 2 (clause 7); b) surface roughness if s

29、pecified (clause 8); c) dry film thickness if different from that given in 9.1; d) information on manufacturing process (clause 6); e) flame cutting and weldability characteristics of prefabrication primers (clause 10); f) special requirements for marking (clause 13); g) position of test pieces (ann

30、ex A). In the event that the purchaser does not indicate his wish to implement any of the additional information, the manufacturer shall supply the blast-cleaned and primed product in accordance with the basic specification. 5 Designation The products covered by this European Standard shall be desig

31、nated as follows, in the order given: a) type of product (plate, beam ); b) number of this European Standard (EN 10238); c) preparation grade (see clause 7); DIN EN 10238:2009-10 EN 10238:2009 (E) 6 d) if the surface roughness is specified at time of enquiry and order, the surface roughness agreed;

32、e) type of prefabrication primer (see 9.1); f) nominal prefabrication dry film thickness if it differs from that specified in this Standard (see 9.1); g) designation of steel following the appropriate Standard. EXAMPLE 1 Designation of H heavy section made of steel S275N (or 1.0490) in accordance wi

33、th EN 10025-3, with preparation grade Sa 2 coated with epoxy-zinc (EPZ). H heavy section EN 10238-Sa 2 EPZ EN 10025-3 S275N; or H heavy section EN 10238-Sa 2 EPZ EN 10025-3 1.0490. EXAMPLE 2 Designation of a nominal dry film thickness different from that specified in this standard and agreed at the

34、time of the enquiry and order and with a roughness also agreed at the time of order. Sheet made of steel S275JR (or 1.0044) in accordance with EN 10025-2 with preparation grade Sa 2 with roughness F, coated on both sides with polyvinyl butyral-iron oxide (PVBF), with nominal thickness 15 m. Sheet EN

35、 10238-Sa 2 -F-PVBF15 EN 10025-2 S275JR; or Sheet EN 10238-Sa 2 -F-PVBF15 EN 10025-2 1.0044. 6 Manufacture The surface treatment process and application of prefabrication primer shall be at the manufacturers discretion. If specified at the time of the enquiry and order, this shall be provided to the

36、 purchaser. At the end of production line, repairs to any damaged areas of the primer shall be undertaken to ensure they meet the requirements of this European Standard. 7 Preparation grade Unless otherwise agreed at the time of enquiry and order, the preparation grade, as specified in accordance wi

37、th EN ISO 8501-1, shall be Sa 2 minimum. Appearance variations resulting from: a) the steel grade; b) surface condition of the steel, c) thickness of the steel, d) consequences of the heat treatment, e) marks from the fabrication of the steel DIN EN 10238:2009-10 EN 10238:2009 (E) 7 shall be deemed

38、acceptable provided they do not affect the preparation grade. 8 Surface roughness At the time of enquiry and order, a surface roughness class may be specified, in which case it shall be given in the product designation using the symbols F for fine, M for medium and C for coarse. The measurement meth

39、od to be used shall be in accordance with EN ISO 8503-2. 9 Prefabrication primers 9.1 Types of prefabrication primers Table 1 lists the most commonly used groups of primers. The most usual nominal thickness specified is 20 m 5 m. In case of sections, greater dry film thickness in single regions is p

40、ermitted. Table 1 Prefabrication primers Basic Characteristics Symbol Binder Pigmentation Epoxy (EP) Iron oxide (F) EPF Polyvinyl butyral (PVC) Iron oxide (F) PVBF Alkyd (AK) Iron oxide (F) AKF Acrylic (AY) Iron oxide (F) AYF Epoxy (EP) Zinc dust (Z) EPZ Ethyl Silicate (ESI) Zinc dust (Z) ESIZ Other

41、 nominal dry film thickness ranges and/or other types of prefabrication primer shall be applied if agreed at the time of enquiry and order. 9.2 Measurement of primer thickness The thickness of the dry film shall be measured according to EN ISO 2808:2007 method 3 (dial gauge method). The test piece f

42、or measuring the dry film thickness shall be perfectly smooth. Glass plates or thin steel sheets are the most commonly used type of test pieces. The test pieces shall be attached to the products at the end of the blast cleaning process and shall be primed at the same time as the product. Annex A (no

43、rmative) specifies the position(s) of test pieces for measuring the primer thickness for different products. Following the removal of the thickness test pieces, the unpainted area shall be primed with the same primer as used for the initial coating. DIN EN 10238:2009-10 EN 10238:2009 (E) 8 The test

44、pieces for the thickness control of the dry primer film shall be stored by the manufacturer for at least one year. 10 Flame cutting and weldability If required at the time of enquiry and order, the flame cutting and weldability characteristics of prefabrication primers shall be measured according to

45、 one of the procedures specified in Annex B. It is the responsibility of the purchaser to obtain, from the manufacturer, the results of these tests. 11 Handling and storage 11.1 Handling The following precautions shall be taken when handling primed products: a) avoid excessive rubbing of lifting app

46、liances against the products; b) avoid friction of products against each other; c) avoid impact to the products; d) avoid dragging products over any surfaces. 11.2 Storage It is recommended that blast-cleaned and primed products be stored indoors as it allows optimum conservation. The following elem

47、entary precautions shall be taken by the manufacturer when storing the products: a) isolate products from ground moisture by appropriate means (e.g. gravel and beams etc.); b) store the products on a slightly inclined slope to avoid water stagnation; c) keep primed and untreated products separate; d

48、) prevent personnel from walking on the treated products. NOTE The purchaser should take the same precautions as the manufacturer. 12 Inspection and testing The products can be supplied with inspection and testing with respect to their compliance with the requirements of this European Standard. If i

49、nspection is required, the purchaser shall specify at the time of enquiry and order: a) the type of inspection and testing (specific or non specific) see EN 10021); b) the type of inspection document (see EN 10204). DIN EN 10238:2009-10 EN 10238:2009 (E) 9 13 Marking In addition to the initial marking of the steel, each product or bundle shall be identified by a label or marked by an easily removed non-corrosive ink with at least the following information: a) name or mark of the manufacture