DIN EN 13523-10-2017 Coil coated metals - Test methods - Part 10 Resistance to fluorescent UV radiation and water condensation German version EN 13523-10 2017《卷材镀层金属 试验方法 第10部分 耐荧光.pdf

1、May 2017 English price group 7No part of this translation may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).ICS 25.220.60!%eQ5“2664618www.din.deDIN E

2、N 13523-10Coil coated metals Test methods Part 10: Resistance to fluorescent UV radiation and water condensation;English version EN 1352310:2017,English translation of DIN EN 13523-10:2017-05Bandbeschichtete Metalle Prfverfahren Teil 10: Bestndigkeit gegen UVStrahlung mit Leuchtstofflampen und Konde

3、nsation von Wasser;Englische Fassung EN 1352310:2017,Englische bersetzung von DIN EN 13523-10:2017-05Tles prlaques Mthodes dessai Partie 10: Rsistance un rayonnement UV fluorescent et la condensation de leau;Version anglaise EN 1352310:2017,Traduction anglaise de DIN EN 13523-10:2017-05SupersedesDIN

4、 EN 1352310:201007www.beuth.deDocument comprises 10 pagesDTranslation by DIN-Sprachendienst.In case of doubt, the German-language original shall be considered authoritative.05.17 DIN EN 13523-10:2017-05 2 A comma is used as the decimal marker. National foreword This document (EN 13523-10:2017) has b

5、een prepared by Technical Committee CEN/TC 139 “Paints and varnishes” (Secretariat: DIN, Germany), Working Group WG 9 “Testing of coil coated metals” (Secretariat: DIN, Germany). The responsible German body involved in its preparation was DIN-Normenausschuss Beschichtungsstoffe und Beschichtungen (D

6、IN Standards Committee Coatings and Coating Materials), Working Committee NA 002-00-07 AA “General test methods for coating materials and coatings”. The European Standards referred to in this document have been published as DIN EN or DIN EN ISO Standards with the same number. Amendments This standar

7、d differs from DIN EN 13523-10:2010-07 as follows: a) the distance of the test specimens to the lamps depends on the device used and is not necessary for carrying out the test; for this reason, the requirement to expose the face of the test specimens at a distance of about 50 mm from the nearest sur

8、face of the lamp has been deleted; b) a note on repositioning of the specimens during exposure has been added; c) a note on removing or re-arranging the test panels during the process has been added; d) the text has been editorially revised and normative references have been updated. Previous editio

9、ns DIN EN 13523-10: 2001-12, 2010-07 EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 13523-10 February 2017 ICS 25.220.60 Supersedes EN 13523-10:2010English Version Coil coated metals - Test methods - Part 10: Resistance to fluorescent UV radiation and water condensation Tles prlaques - Mthodes

10、 dessai - Partie 10 : Rsistance un rayonnement UV fluorescent et la condensation de leau Bandbeschichtete Metalle - Prfverfahren - Teil 10: Bestndigkeit gegen UV-Strahlung mit Leuchtstofflampen und Kondensation von Wasser This European Standard was approved by CEN on 18 December 2016. CEN members ar

11、e bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to

12、the CEN-CENELEC Management Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Ce

13、ntre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithua

14、nia, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Serbia, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG CEN-CENELEC Management Centre: Avenue Marnix

15、 17, B-1000 Brussels 2017 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN 13523-10:2017 E2 Contents Page European foreword . 3 1 Scope 5 2 Normative references 5 3 Terms and definitions . 5 4 Principle . 5 5 Apparatus and materials

16、 5 6 Sampling . 6 7 Test panels . 6 8 Procedure. 6 8.1 Exposure . 6 8.2 Calibration and maintenance of calibration . 6 8.3 Evaluation of test specimens . 7 9 Expression of results 7 10 Precision . 7 11 Test report . 7 Bibliography 8 EN 13523-10:2017 (E) DIN EN 13523-10:2017-05 3 European foreword Th

17、is document (EN 13523-10:2017) has been prepared by Technical Committee CEN/TC 139 “Paints and varnishes”, the secretariat of which is held by DIN. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by

18、August 2017, and conflicting national standards shall be withdrawn at the latest by August 2017. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN shall not be held responsible for identifying any or all such patent rights. This

19、 document supersedes EN 13523-10:2010. The main changes are: a) the distance of the test specimen to the lamps is device-specific and not necessary for carrying out the test; so the requirement to expose the face of the test specimens at a distance of about 50 mm from the nearest surface of the lamp

20、 has been deleted; b) a remark on repositioning of the specimens during exposure has been added; c) a remark on removing or re-arranging the test panels during the process has been added; d) the text has been editorially revised and the normative references have been updated. The EN 13523 series, Co

21、il coated metals Test methods, consists of the following parts: Part 0: General introduction Part 1: Film thickness Part 2: Gloss Part 3: Colour difference Instrumental comparison Part 4: Pencil hardness Part 5: Resistance to rapid deformation (impact test) Part 6: Adhesion after indentation (cuppin

22、g test) Part 7: Resistance to cracking on bending (T-bend test) Part 8: Resistance to salt spray (fog) Part 9: Resistance to water immersion Part 10: Resistance to fluorescent UV radiation and water condensation Part 11: Resistance to solvents (rubbing test) Part 12: Resistance to scratching EN 1352

23、3-10:2017 (E) DIN EN 13523-10:2017-05 4 Part 13: Resistance to accelerated ageing by the use of heat Part 14: Chalking (Helmen method) Part 15: Metamerism Part 16: Resistance to abrasion Part 17: Adhesion of strippable films Part 18: Resistance to staining Part 19: Panel design and method of atmosph

24、eric exposure testing Part 20: Foam adhesion Part 21: Evaluation of outdoor exposed panels Part 22: Colour difference Visual comparison Part 23: Resistance to humid atmospheres containing sulfur dioxide Part 24: Resistance to blocking and pressure marking Part 25: Resistance to humidity Part 26: Res

25、istance to condensation of water Part 27: Resistance to humid poultice (Cataplasm test) Part 29: Resistance to environmental soiling (Dirt pick-up and striping) According to the CEN-CENELEC Internal Regulations, the national standards organisations of the following countries are bound to implement t

26、his European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Serbi

27、a, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom. EN 13523-10:2017 (E) DIN EN 13523-10:2017-05 5 1 Scope This part of the EN 13523 series specifies the basic principles and procedure for determining the resistance of an organic coating on a metallic substrate (coil co

28、ating) to a combination of fluorescent UV radiation, and water condensation and temperature under controlled conditions. Due to varied conditions which occur during natural weathering and the extreme nature of accelerated testing, correlation between the two cannot be expected. Not all organic coati

29、ngs will perform on an equal basis but a degree of correlation between the same generic type might be observed. 2 Normative references The following documents, in whole or in part, are normatively referenced in this document and are indispensable for its application. For dated references, only the e

30、dition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 13523-0, Coil coated metals - Test methods - Part 0: General introduction EN 13523-2, Coil coated metals - Test methods - Part 2: Gloss EN 13523-3, Coil coated metals -

31、Test methods - Part 3: Colour difference - Instrumental comparison EN 13523-14, Coil coated metals - Test methods - Part 14: Chalking (Helmen method) EN 13523-22, Coil coated metals - Test methods - Part 22: Colour difference - Visual comparison EN ISO 16474-3, Paints and varnishes - Methods of expo

32、sure to laboratory light sources - Part 3: Fluorescent UV lamps (ISO 16474-3) 3 Terms and definitions For the purposes of this document, the terms and definitions given in EN 13523-0 apply. 4 Principle The coating is exposed in a cyclic manner to UV radiation, condensation of water and temperature u

33、nder controlled conditions. One of two types of fluorescent UV lamps, UVA-340 or UVB-313, is used. After exposure to UV radiation under controlled conditions, chalking and changes in gloss and colour are assessed. 5 Apparatus and materials Ordinary laboratory apparatus and glassware, together with t

34、he following. 5.1 Test chamber. The test chamber shall be constructed of corrosion resistant materials. Enclosed within the test chamber shall be eight fluorescent lamps (5.2), a heater pan, racks for test specimens, and provisions for indicating and controlling operating times and temperatures. The

35、 lamps shall be in banks of four on either side of the cabinet. Electrical operating conditions for the lamps shall be as given by the manufacturer. EN 13523-10:2017 (E) DIN EN 13523-10:2017-05 6 5.2 UV lamps. Either UVA-340 or UVB-313, as specified in EN ISO 16474-3: UVA-340 starting at a wavelengt

36、h of approximately 300 nm with a peak emission at 340 nm; UVB-313 starting at a wavelength of approximately 280 nm with a peak emission at 313 nm. 5.3 Water supply, deionized water. 6 Sampling Shall be according to EN 13523-0. 7 Test panels Shall be according to EN 13523-0. The test specimens shall

37、be flat and about 150 mm 75 mm in size. Deviations from the standard methods of panel shape, size, previous working, or conditioning may be agreed between the interested parties. 8 Procedure 8.1 Exposure Place the test specimens in racks which are made of inert material. Expose the face of the test

38、specimens parallel to the lamps. If there are empty spaces within the racks fill these with blanks to maintain the conditions within the test chamber. Repositioning of the specimens during exposure is desirable and might be necessary to ensure uniformity of all exposure stresses. Cycle the test spec

39、imens through periods of 4 h of dry UV exposure at a black panel temperature of (60 3) C, followed by a period of 4 h of water condensation exposure, without radiation, at a black panel temperature of (40 3) C. (One cycle consists of 8 h exposure.) Arrange the test specimens to allow the condensate

40、to freely run off the surface under gravity. Conclude the exposure at an agreed time, for example 2 000 h for UVA-340 or 1 000 h for UVB-313, or an agreed number of cycles, for example 250 cycles for UVA-340 or 125 cycles for UVB-313. Where possible, use an agreed irradiance level, typically 0,83 W/

41、m2for UVA-340 or 0,71 W/m2for UVB-313. For safety reasons (UV radiation), it is recommended to remove or re-arrange the test panels when the UV lamps are switched off (e.g. during the humidity cycle). 8.2 Calibration and maintenance of calibration Calibration of the UV-lamps depends on the type of w

42、eathering apparatus, whether the irradiance level can be set or not. For apparatus without the possibility to set the irradiance, after every usage of 400 radiation hours, replace one lamp and rotate the others within the bank with the oldest lamp being taken out of service unless otherwise specifie

43、d by the equipment manufacturer. EN 13523-10:2017 (E) DIN EN 13523-10:2017-05 7 For apparatus with irradiance measurement, the apparatus indicates when the radiation sensors need to be calibrated. Carry out the calibration of the radiation sensors according to the method provided by the equipment ma

44、nufacturer using the calibration equipment. When the irradiance of a lamp falls below the set point, it shall be replaced. This is usually triggered by an alarm on the equipment. 8.3 Evaluation of test specimens At the conclusion of the exposure, evaluate the test specimens for chalking, changes of

45、gloss and colour. Assess the coating for chalking, change of gloss and change of colour at ambient temperature. For more accurate measurements, as required for instance in case of dispute, the temperature shall be (23 2) C and the relative humidity (50 5) %, in accordance with EN 23270. 9 Expression

46、 of results The results shall be expressed as comparison between an unexposed test specimen and an exposed test specimen for properties defined in EN 13523-2, EN 13523-3, EN 13523-14 and EN 13523-22, if appropriate in terms of, for example, x % gloss retention according to EN 13523-2, y= according t

47、o EN 13523-3, z chalking according to EN 13523-14. 10 Precision No precision data are currently available. 11 Test report The test report shall contain at least the following information: a) all details necessary to identify the product tested; b) a reference to this part of the EN 13523 series (EN

48、13523-10); c) the type of UV lamps used; d) the duration of exposure in hours (h); e) the results of the test, as indicated in Clause 9; f) any deviation, by agreement or otherwise, from the test method specified; g) the date of the test. EN 13523-10:2017 (E) DIN EN 13523-10:2017-05 8 Bibliography 1

49、 EN 1396, Aluminium and aluminium alloys - Coil coated sheet and strip for general applications - Specifications 2 EN 10169, Continuously organic coated (coil coated) steel flat products Technical delivery conditions 3 EN ISO 4892-3, Plastics - Methods of exposure to laboratory light sources - Part 3: Fluorescent UV lamps (ISO 4892-3) 4 EN 23270, Paints and varnishes and their