DIN EN 13614-2011 en 7882 Bitumen and bituminous binders - Determination of adhesivity of bituminous emulsions by water immersion test German version EN 13614 2011《沥青和含沥青粘合剂 浸水试验中沥.pdf

1、June 2011 Translation by DIN-Sprachendienst.English price group 8No part of this translation may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).ICS 75

2、.140; 91.100.50!$r(“1799705www.din.deDDIN EN 13614Bitumen and bituminous binders Determination of adhesivity of bituminous emulsions by waterimmersion testEnglish translation of DIN EN 13614:2011-06Bitumen und bitumenhaltige Bindemittel Bestimmung des Haftverhaltens von Bitumenemulsionen bei Wasserl

3、agerungEnglische bersetzung von DIN EN 13614:2011-06Bitumes et liants bitumineux Dtermination de ladhsivit des mulsions de bitume par lessai dimmersion dans leauTraduction anglaise de DIN EN 13614:2011-06SupersedesDIN EN 13614:2004-05www.beuth.deDocument comprises pagesIn case of doubt, the German-l

4、anguage original shall be considered authoritative.06.11 11DIN EN 13614:2011-06 A comma is used as the decimal marker. National foreword This standard has been prepared by Technical Committee CEN/TC 336 “Bituminous binders” (Secretariat: AFNOR, France). The responsible German bodies involved in its

5、preparation were the Normenausschuss Materialprfung (Materials Testing Standards Committee) and the Normenausschuss Bauwesen (Building and Civil Engineering Standards Committee), Joint Committee NA 062-03-32 GA Gemeinschaftsarbeitsausschuss NMP/NABau/FGSV 7.2.0.1: Bitumen; Prfverfahren und Anforderu

6、ngen fr die Bindemittel. In Germany, the reference aggregate as specified in Subclause 5.1 is Taunus-Quarzit 8/101). NOTE Taunus-Quarzit 8/101)can be obtained from CEMEX Kies b) new terms have been added in Clause 3: “immediate adhesivity” (3.3) and “water effect on binder adhesion” (3.4); c) in Cla

7、use 8, a distinction is made between “determination of immediate adhesivity” and “water effect on binder adhesion”; a distinction between “emulsions of limited storage stability” and “emulsions which can be stored” is no longer made. Previous editions DIN EN 13614: 2004-05 National Annex NA (informa

8、tive) Bibliography DIN ISO 3696, Water for analytical laboratory use Specification and test methods 1) This information is given for the convenience of users of this standard and does not constitute an endorsement by DIN of the product named. 2 EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 13

9、614 March 2011 ICS 75.140 Supersedes EN 13614:2004English Version Bitumen and bituminous binders - Determination of adhesivity of bituminous emulsions by water immersion test Bitumes et liants bitumineux - Dtermination de ladhsivit des mulsions de bitume par lessai dimmersion dans leauBitumen und bi

10、tumenhaltige Bindemittel - Bestimmung des Haftverhaltens von Bitumenemulsionen bei Wasserlagerung This European Standard was approved by CEN on 12 February 2011. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard

11、 the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member. This European Standard exists in three official versions (English, F

12、rench, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgar

13、ia, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom. EUROPEAN COMMITTEE FOR S

14、TANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG Management Centre: Avenue Marnix 17, B-1000 Brussels 2011 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN 13614:2011: EEN 13614:2011 (E) 2 Contents Page F

15、oreword 31 Scope 42 Normative references 43 Terms and definitions . 44 Principle 55 Reagents and materials 56 Apparatus . 57 Sampling . 58 Procedure . 69 Expression of results 710 Precision . 711 Test report 7Annex A (informative) Guidance for the marking of coated surface area . 8Bibliography 9DIN

16、EN 13614:2011-06 EN 13614:2011 (E) 3 Foreword This document (EN 13614:2011) has been prepared by Technical Committee CEN/TC 336 “Bituminous binders”, the secretariat of which is held by AFNOR/BNP. This European Standard shall be given the status of a national standard, either by publication of an id

17、entical text or by endorsement, at the latest by September 2011, and conflicting national standards shall be withdrawn at the latest by September 2011. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not b

18、e held responsible for identifying any or all such patent rights. This document supersedes EN 13614:2004. This revised version (EN 13614:2011) makes a distinction between “immediate” adhesivity and water effect on binder adhesion. Compliance to the adhesivity requirements set by EN 13808 is verified

19、 according to the procedure defined for testing water effect on binder adhesion. According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republ

20、ic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom. DIN EN 13614:2011-06 EN 13614:2011 (E) 4 1 Scope This Eur

21、opean Standard specifies a method for determining the adhesion of a bituminous emulsion coated onto aggregate when immersed in water. The method considers two different aspects of adhesivity, i.e. immediate adhesivity and water effect on binder adhesion. The method may be used with a reference aggre

22、gate. In that case, it measures the intrinsic adhesion behaviour of a bituminous emulsion. The method may also be used with a specific aggregate as used on a job site. WARNING The use of this European Standard may involve hazardous materials, operations and equipment. This European Standard does not

23、 purport to address all of the safety problems associated with its use. It is the responsibility of the user of this European Standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. 2 Normative references The following ref

24、erenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 58, Bitumen and bituminous binders Sampling bituminous binders

25、EN 12594, Bitumen and bituminous binders Preparation of test samples EN 13808, Bitumen and bituminous binders Framework for specifying cationic bituminous emulsions EN ISO 3696, Water for analytical laboratory use Specification and test methods (ISO 3696:1987) 3 Terms and definitions For the purpose

26、s of this document, the following terms and definitions apply. 3.1 adhesion ability of a binder to coat the surface of an aggregate and to remain bonded over time in the presence of water 3.2 adhesivity qualitative assessment of the measurement of the adhesion 3.3 immediate adhesivity qualitative as

27、sessment of the ability of the binder from a bituminous emulsion to resist the action of water just after coating of the aggregate 3.4 water effect on binder adhesion qualitative assessment of the ability of the binder from a bituminous emulsion to resist the action of water after coating of the agg

28、regate and a period of curing DIN EN 13614:2011-06 EN 13614:2011 (E) 5 4 Principle The bituminous emulsion is mixed thoroughly with the considered aggregate under specified conditions. When testing immediate adhesivity, the mixture is immediately washed under running water and the percentage of the

29、aggregate surface covered with binder is assessed visually under specified conditions. When testing water effect on binder adhesion, the mixture is first left to cure and then immersed under water under specified conditions. The percentage of the aggregate surface covered with binder is assessed vis

30、ually under specified conditions. Conformity to the “adhesivity” requirement specified in EN 13808 is to be assessed while measuring the water effect on binder adhesion with a reference aggregate. 5 Reagents and materials 5.1 Reference aggregate, as light in colour as possible, or aggregate from a s

31、pecific job site, which either passes through a sieve having a mesh size of 10 mm and is retained on a sieve having a mesh size of 6,3 mm (sieve sizes belonging to the “basic set plus set 2” sizes specified in EN 13043), or passes through a sieve having a mesh size of 11 mm and is retained on a siev

32、e having a mesh size of 8 mm (sieve sizes belonging to the “basic set plus set 1” sizes specified in EN 13043). NOTE Each country should define petrographically its own reference aggregates, for instance, in a national informative annex. 5.2 Water, distilled or deionised, conforming to EN ISO 3696.

33、5.3 Cleaning agents, conventionally used in a laboratory. 6 Apparatus 6.1 Ventilated oven, capable of maintaining a temperature of (60 3) C. 6.2 Spatula. 6.3 Two heat resistant dishes, diameter approximately 15 cm to 20 cm. 6.4 Timer, accurate to at least 1 s over 60 s. 6.5 Two beakers, approximatel

34、y 500 ml capacity. 6.6 Set of five watch glasses, diameter of at least 15 cm. 6.7 Balance, of sufficient capacity, accurate to 1 g. 6.8 Measuring cylinder, 250 ml to 500 ml capacity. 6.9 Thermometer, of adequate range, allowing measuring the specified temperatures with an accuracy of 1 C. 6.10 Venti

35、lated oven, capable of maintaining a temperature of (110 5) C. 7 Sampling Sample the test material in accordance with EN 58. Prepare the test samples in accordance with EN 12594. DIN EN 13614:2011-06 EN 13614:2011 (E) 6 8 Procedure 8.1 General Carry out the procedure under normal laboratory conditio

36、ns (23 5) C. If the intrinsic adhesivity of the emulsion is controlled, the procedure shall be carried out with the reference aggregate(s). The reference aggregate(s) shall be washed with water (5.2) and dried in the ventilated oven (6.10) at (110 5) C for about 2 h. If the adhesivity behaviour of a

37、 specific emulsion/aggregate combination is controlled for a specific job site, the aggregate shall be used in its job site conditions (5.1). 8.2 Determination of immediate adhesivity 8.2.1 Weigh (100 5) g of aggregate (5.1) into a dish (6.3) and (150 5) g of emulsion into another dish (6.3). 8.2.2

38、Pour the aggregate into the emulsion and allow contacting for (60 5) s without stirring; the dish may be gently shaken to disperse any air bubbles which might prevent proper moistening of the aggregate. 8.2.3 Remove excess emulsion by carefully tilting the dish and wash the aggregate at room tempera

39、ture, holding the dish tilted under a slow stream of water (5.2) until the water runs clear. 8.2.4 Introduce the coated aggregate into a beaker (6.5) and cover with approximately 300 ml of water (5.2) at room temperature. 8.2.5 Immediately assess the surface coated with the film of binder and grade

40、it according to the scheme indicated in Clause 9. 8.3 Water effect on binder adhesion 8.3.1 General This procedure shall be used, with reference aggregate(s), to check conformity to the intrinsic “adhesivity” requirement specified in EN 13808. The reference aggregate(s) is (are) then washed with wat

41、er (5.2) and dried in the ventilated oven (6.10) at (110 5) C for about 2 h. It may also be used to check water effect on binder adhesion for a specific emulsion/aggregate combination used on a specific job site. The aggregate shall then be used in its job site conditions (5.1). 8.3.2 Weigh (200 5)

42、g of aggregate (5.1) into a dish (6.3) and an amount of emulsion corresponding to (10 1) g of bituminous binder into another dish (6.3). 8.3.3 Pour the aggregate into the emulsion and thoroughly mix by means of a spatula (6.2). 8.3.4 If full coating (100 % of coverage) is not achieved, restart the p

43、rocedure as from 8.3.1 by increasing the amount of residual bitumen to (20 1) g. The amount of residual bitumen actually used shall be mentioned in the test report (Clause 11 f). 8.3.5 Spread the mixture on a watch-glass (6.6) and place it in the ventilated oven (6.10) at (60 3) C for (24 1) h. DIN

44、EN 13614:2011-06 EN 13614:2011 (E) 7 8.3.6 Transfer the mixture in a beaker (6.5), pour approximately 300 ml of water (5.2), heated to (60 3) C onto the mixture and cover with a watch-glass (6.6). Place the beaker in the ventilated oven (6.10), at (60 3) C for (20 4) h. 8.3.7 Assess the surface coat

45、ed with the film of binder and grade it according to the scheme indicated in Clause 9. 9 Expression of results The surface coated with the film of binder shall be graded according to the following scheme: 100: all the surface is coated; 90: more than approximately 90 % of the surface is coated; 75:

46、approximately 75 % to 90 % of the surface is coated; 50: approximately 50 % to 75 % of the surface is coated; 50: less than approximately 50 % of the surface is coated; 0: the binder is separate from the aggregates, except for some faint marks. The simple coloration of the aggregate surface by adsor

47、bed light binder fractions shall not qualify this surface as a coated surface. NOTE 1 A guidance for the grading of the surface covered with binder is given, in the form of indicative sketches, in Annex A. NOTE 2 If necessary, to facilitate the assessment, it should be compared with an untreated and

48、 immersed aggregate. 10 Precision The method is qualitative and it is not possible to quantify the precision. However, tests carried out by the same operator have shown that the same result is generally achieved for any given bitumen emulsion. 11 Test report The test report shall contain at least th

49、e following information: a) reference to this European Standard; b) type and complete identification of the emulsion sample under test; c) type and complete identification (reference aggregate or other aggregate) of the aggregate and fraction used (either 6/10 mm or 8/11 mm); d) test used : immediate adhesivity or water effect on binder adhesion; e) result of the test (see Clause 9); f) in case of a test performed according to 8.2, the co