DIN EN 13702-2010 en 8342 Bitumen and bituminous binders - Determination of dynamic viscosity of modified bitumen by cone and plate method German version EN 13702 2010《沥青和沥青粘合剂 锥板式.pdf

1、November 2010 Translation by DIN-Sprachendienst.English price group 6No part of this translation may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).IC

2、S 75.140; 91.100.50!$l(z“1730587www.din.deDDIN EN 13702Bitumen and bituminous binders Determination of dynamic viscosity of modified bitumen by cone andplate methodEnglish translation of DIN EN 13702:2010-11Bitumen und bitumenhaltige Bindemittel Bestimmung der dynamischen Viskositt von modifiziertem

3、 Bitumen mit demPlatte-Kegel-VerfahrenEnglische bersetzung von DIN EN 13702:2010-11Bitumes et liants bitumineux Dtermination de la viscosit dynamique des bitumes modifis par la mthode cne etplateauTraduction anglaise de DIN EN 13702:2010-11SupersedesDIN EN 13702-1:2004-03www.beuth.deDocument compris

4、es pagesIn case of doubt, the German-language original shall be considered authoritative.81 .10 0DIN EN 13702:2010-11 A comma is used as the decimal marker. National foreword This standard has been prepared by Technical Committee CEN/TC 336 “Bituminous binders” (Secretariat: AFNOR, France). The resp

5、onsible German bodies involved in its preparation were the Normenausschuss Materialprfung (Materials Testing Standards Committee) and the Normenausschuss Bauwesen (Building and Civil Engineering Standards Committee), Joint Working Committee NA 062-03-32 GA Bitumen; Prfverfahren und Anforderungen fr

6、die Bindemittel. Amendments This standard differs from DIN EN 13702-1:2004-03 as follows: a) the number of the standard has been changed to EN 13702; b) in Clause 6, NOTES 1 and 2 have been included in the normative text; c) the standard has been editorially revised. Previous editions DIN EN 13702-1

7、: 2004-03 2 EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 13702 May 2010 ICS 75.140; 91.100.50 Supersedes EN 13702-1:2003English Version Bitumen and bituminous binders - Determination of dynamic viscosity of modified bitumen by cone and plate method Bitumes et liants bitumineux - Dtermination

8、 de la viscosit dynamique des bitumes modifis thode cne et plateau Bitumen und bitumenhaltige Bindemittel - Bestimmung der dynamischen Viskositt von modifiziertem Bitumen mit dem Platte-Kegel-Verfahren This European Standard was approved by CEN on 23 April 2010. CEN members are bound to comply with

9、the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN Management Cent

10、re or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN Management Centre has the same status as the officia

11、l versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovak

12、ia, Slovenia, Spain, Sweden, Switzerland and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG Management Centre: Avenue Marnix 17, B-1000 Brussels 2010 CEN All rights of exploitation in any form and by any means reserved worldwide f

13、or CEN national Members. Ref. No. EN 13702:2010: Epar la mEN 13702:2010 (E) 2 Contents Foreword 31 Scope 42 Normative references 43 Principle 44 Apparatus . 55 Sampling . 56 Procedure . 57 Expression of results 68 Precision . 68.1 Repeatability . 68.2 Reproducibility . 69 Test report 6DIN EN 13702:2

14、010-11 PageEN 13702:2010 (E) 3 Foreword This document (EN 13702:2010) has been prepared by Technical Committee CEN/TC 336 “Bituminous binders”, the secretariat of which is held by AFNOR/BNP. This European Standard shall be given the status of a national standard, either by publication of an identica

15、l text or by endorsement, at the latest by November 2010, and conflicting national standards shall be withdrawn at the latest by November 2010. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held r

16、esponsible for identifying any or all such patent rights. This document supersedes EN 13702-1:2003. This document was formerly known as EN 13702 Part 1. As Part 2 of this standard was merged with another standard into EN 13302, this standard was renumbered into EN 13702. According to the CEN/CENELEC

17、 Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania,

18、Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and the United Kingdom. DIN EN 13702:2010-11 EN 13702:2010 (E) 4 1 Scope This European Standard specifies a method for determining the dynamic viscosity of a modified bituminous binder o

19、ver a range of temperatures by means of a cone and plate viscometer. Although the method has been developed for modified binders, it is also suitable for other bituminous binders. NOTE Unlike penetration grade bitumen, polymer modified bitumens (PMBs) may not show a straight line on the Heukelom-Dia

20、gram. This implies that in order to obtain information about the temperature susceptibility of PMBs, viscosity should be measured at different temperatures. WARNING The use of this European Standard can involve hazardous materials, operations and equipment. This European Standard does not purport to

21、 address all of the safety problems associated with its use. It is the responsibility of the user of this European Standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. 2 Normative references The following referenced doc

22、uments are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 58, Bitumen and bituminous binders Sampling bituminous binders EN 12594, B

23、itumen and bituminous binders Preparation of test samples 3 Principle The sample is placed on a plate, a cone is pressed onto the sample and the system is brought to the test temperature. A stress is applied to the sample by rotation. The torque is measured from the applied shear rate and dynamic vi

24、scosity is calculated by: =(1) where is the shear rate expressed in s-1; is the stress expressed in Pa, calculated by: dMA= (2) where A is the cone factor expressed in m-3; Mdis the torque in expressed N m. NOTE The advantages of this method are the use of a very small sample and the speed of the me

25、thod, especially regarding thermal conditioning of the specimen. DIN EN 13702:2010-11 EN 13702:2010 (E) 5 4 Apparatus Cone and plate viscometer, with the following minimum capabilities: range of shear rate: 5 x 10-2s-1to 5 x 102s-1; range of viscosity: 5 x 10-2Pa s to 105Pa s; range of temperature:

26、60 C to 150 C. The sample temperature shall be maintained within 0,5 C up to 100 C and within 1,0 C above 100 C. 5 Sampling Take the sample in accordance with EN 58 and prepare the sample in accordance with EN 12594. 6 Procedure Select the appropriate size (diameter and angle) of cone to allow measu

27、rement at the selected shear rate. Place the sample on the plate and press the selected cone onto the sample. Remove any surplus sample and bring the system to the test temperature. Commence the first measurement at the lowest temperature: Temperature: (60 0,5) C; Shear rate: 5 x 10-2s-1. Check the

28、reading after a delay of 15 min when reaching the temperature and note the temperature, the cone size, the shear rate and the reading. Repeat the test and calculate the result as an average of two tests. Replace the specimen and increase the temperature to the next test temperature. Commence the sec

29、ond measurement: Temperature: (100 0,5) C; Shear rate: 5 x 101s-1. Replace the specimen and increase the temperature to the next test temperature. Commence the third measurement: Temperature: (150 1,0) C; Shear rate: 5 x 102s-1. It should be ensured that the complete specimen has reached the test te

30、mperature before starting the test. The sample should not contain any filler. NOTE In addition to these test temperatures and shear rates any other temperature and shear rate can be used. DIN EN 13702:2010-11 EN 13702:2010 (E) 6 7 Expression of results Record the results of the measurement of dynami

31、c viscosity with the corresponding shear rate and the test temperature. Express the viscosity values in Pa s as follows: (1,000 x 10x) Pa s. 8 Precision NOTE The following precision data are the best currently estimated and are proposed until results of further round robin tests are available. 8.1 R

32、epeatability The difference between two successive results, obtained by the same operator with the same apparatus under constant operating conditions on identical test material would, in the long run, in the normal and correct operation of the test method, differ by more than 5 % in only one case in

33、 twenty. 8.2 Reproducibility The difference between two single and independent results, obtained by different operators working in different laboratories on identical test material would, in the long run, in the normal and correct operation of the test method, differ by more than 15 % in only one ca

34、se in twenty. 9 Test report The test report shall contain at least the following information: a) type and complete identification of the sample under test; b) reference to this European Standard; c) temperature, shear rate and the result of the test (see Clause 7); d) diameter and angle of the cone; e) date of the test; f) any deviation, by agreement or otherwise, from the specified procedure. DIN EN 13702:2010-11