DIN EN 15466-2-2009 en 3903 Primers for cold and hot applied joint sealants - Part 2 Determination of resistance against alkali English version of DIN EN 15466-2 2009-10《冷和热对接密封胶底漆.pdf

1、October 2009DEUTSCHE NORM English price group 6No part of this standard may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).ICS 93.080.20!$ZC“1553259ww

2、w.din.deDDIN EN 15466-2Primers for cold and hot applied joint sealants Part 2: Determination of resistance against alkaliEnglish version of DIN EN 15466-2:2009-10Voranstriche fr kalt und hei verarbeitbare Fugenmassen Teil 2: Bestimmung der AlkalibestndigkeitEnglische Fassung DIN EN 15466-2:2009-10ww

3、w.beuth.deDocument comprises pages9DIN EN 15466-2:2009-10 National foreword This standard has been prepared by Technical Committee CEN/TC 227 “Road materials” (Secretariat: DIN, Germany). The responsible German body involved in its preparation was the Normenausschuss Bauwesen (Building and Civil Eng

4、ineering Standards Committee), Technical Committee NA 005-10-07 AA Materialien fr Betonstraen. 2 EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 15466-2 July 2009 ICS 93.080.20 English Version Primers for cold and hot applied joint sealants Part 2: Determination of resistance against alkali Pri

5、maires pour produits de scellement de joints appliqus froid et chaud Partie 2: Dtermination de la rsistance aux produits alcalins Voranstriche fr kalt und hei verarbeitbare Fugenmassen Teil 2: Bestimmung der Alkalibestndigkeit This European Standard was approved by CEN on 6 June 2009. CEN members ar

6、e bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this EuropeanStandard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to t

7、he CEN Management Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN Management Centre has the same

8、 status as theofficial versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal,Roma

9、nia, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG Management Centre: Avenue Marnix 17, B-1000 Brussels 2009 CEN All rights of exploitation in any form and by any means reserved

10、worldwide for CEN national Members. Ref. No. EN 15466-2:2009: EEN 15466-2:2009 (E) 2 Contents Page Foreword 31 Scope 42 Normative references 43 Terms and definitions .44 Principle 45 Apparatus .46 Procedure .56.1 Conditioning of primer and glass plates .56.2 Painting of the glass plates 56.3 Immersi

11、ng of the glass plates 56.4 Tests on the solution in glass beaker with immersed glass plates .56.5 Tests on the immersed glass plates in wet condition .56.6 Tests on the immersed glass plates in dry condition 67 Expression of results 68 Test report 6Bibliography 7DIN EN 15466-2:2009-10 EN 15466-2:20

12、09 (E) 3 Foreword This document (EN 15466-2:2009) has been prepared by Technical Committee CEN/TC 227 “Road Materials”, the secretariat of which is held by DIN. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at t

13、he latest by January 2010, and conflicting national standards shall be withdrawn at the latest by January 2010. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any o

14、r all such patent rights. This European Standard is one of a series of standards as listed below: EN 15466-1, Primers for cold and hot applied joint sealants Part 1: Determination of homogeneity EN 15466-2, Primers for cold and hot applied joint sealants Part 2: Determination of resistance against a

15、lkali EN 15466-3, Primers for cold and hot applied joint sealants Part 3: Determination of solids content and evaporation behaviour of volatiles. According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European St

16、andard: Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and the United Kingdo

17、m. DIN EN 15466-2:2009-10 EN 15466-2:2009 (E) 4 1 Scope This European Standard describes a method for determining the resistance against alkali of primers for cold and hot applied joint sealants. 2 Normative references The following referenced documents are indispensable for the application of this

18、European Standard. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 14188-4:2009, Joint fillers and sealants Part 4: Specifications for primers to be used with joint sealants EN 15466-3,

19、 Primers for cold and hot applied joint sealants Part 3: Determination of solids content and evaporation behaviour of volatiles 3 Terms and definitions For the purposes of this European Standard, the terms and definitions given in EN 14188-4:2009 and the following apply. 3.1 standard atmosphere stan

20、dard atmosphere 23/50, class 2 (see EN ISO 291) 3.2 resistance against alkali resistance against alkali of a primer defined by the behaviour of the primer painted on a glass surface to insolubility, no changes in hardness and no peelings during immersion in an alkali solution 4 Principle Two glass p

21、lates, each with one side painted with the primer, are immersed, one in a glass beaker filled with water and the other one in a glass beaker filled with a solution of potassium hydroxide in water. After conditioning in a test enclosure or conditioning room at standard atmosphere for 24 hours record

22、any changes in the condition of the test liquids and the painted glass plates. 5 Apparatus 5.1 Clear glass beaker, diameter approximately 120 mm, height approximately 200 mm, with an upper flat rim, no spout, and with a glass cover. 5.2 Glass plates, without scratches, dimensions approximately 90 mm

23、 120 mm. 5.3 Preparation needle, (e. g. penetration needle). 5.4 Paint brush 5.5 Water, distilled or totally deionised. 5.6 Solution of potassium hydroxide in water, 0,5 % by mass/volume, freshly prepared. DIN EN 15466-2:2009-10 EN 15466-2:2009 (E) 5 NOTE Note-0,5% by mass/volume means 5 g of potass

24、ium hydroxide in 1000 ml solution. 5.7 Round rod, diameter (10 2) mm, length (600 100) mm. 6 Procedure 6.1 Conditioning of primer and glass plates The primer shall be homogenized by shaking the container or by stirring with a suitable rod. The primer shall be conditioned in a test enclosure or condi

25、tioning room at Standard atmosphere for at least 24 hours. The glass plates shall be cleaned, totally degreased, dried and conditioned at Standard atmosphere for at least 1 hour. 6.2 Painting of the glass plates One side of each of the two glass plates shall be painted all over with the primer so th

26、at it is uniformly distributed. Store the painted glass plates for a duration recommended by the manufacturer in a test enclosure or conditioning room at standard atmosphere. The quantity of the primer on a glass plate is calculated on the base of the solids content in accordance with EN 15466-3, th

27、at the amount of the painting in the dried condition shall be between 15 g/m and 20 g/m. 6.3 Immersing of the glass plates One glass beaker shall be filled with water to a depth of 80 mm and the other glass beaker shall be filled with the solution of potassium hydroxide to a depth of 80 mm. In each

28、glass beaker one painted glass plate shall be placed vertically. Each glass beaker shall be covered with a glass cover. The glass beakers shall be allowed to stand for 24 h 15 min in a test enclosure or conditioning room at standard atmosphere. 6.4 Tests on the solution in glass beaker with immersed

29、 glass plates The following criteria shall be inspected and reported: a) changes in colour and turbidity in both test liquids; b) presence of deposits on the bottom of both glass beakers. 6.5 Tests on the immersed glass plates in wet condition The glass plates shall be taken out of the glass beakers

30、. The painting on each glass plate shall be immediately scratched by pulling the preparation needle over the whole length of the glass plates. The following criteria shall be inspected and reported: a) presence of cloudiness and bubbles in both paintings; b) presence of peelings of the painting alon

31、g the scratched line; c) apparent difference in the hardness of the paintings between the immersed and not-immersed parts of the glass plates; d) apparent difference in the hardness of the paintings between the immersed parts of both test liquids. DIN EN 15466-2:2009-10 EN 15466-2:2009 (E) 6 6.6 Tes

32、ts on the immersed glass plates in dry condition After testing to 6.5, the glass plates shall be washed in water and allowed to dry for 5 h 15 min in a test enclosure or conditioning room at standard atmosphere. The painting on each glass plate shall be immediately scratched by pulling the preparati

33、on needle over the whole length of the glass plates. The following criteria shall be inspected and reported: a) presence of cloudiness and bubbles in both paintings; b) presence of peelings of the painting along the scratched line; c) apparent difference in the hardness of the paintings between the

34、immersed and not-immersed parts of the glass plates; d) apparent difference in the hardness of the paintings between the immersed parts of both test liquids. 7 Expression of results Report the primer as resistant against alkali, if all of the following criteria are fulfilled: a) the solution of pota

35、ssium hydroxide has no changes in colour and turbidity and no presence of deposits on the bottom of the glass beaker; b) the painting in wet condition has no presence of cloudiness and bubbles; c) the painting in wet condition has no apparent difference in the hardness of the paintings between the i

36、mmersed parts of the two glass plates; d) the painting in dry condition has no peelings along the scratched line; e) the painting in dry condition has no apparent difference in the hardness between the immersed and not-immersed parts of the glass plates. 8 Test report The test report shall confirm t

37、hat the test was carried out in accordance with this European Standard and shall include the following information: a) product name and type; b) source of sample, batch number, date of manufacture and use by date; c) date of testing; d) test results; e) name of analyst and test laboratory. DIN EN 15466-2:2009-10 EN 15466-2:2009 (E) 7 Bibliography 1 EN ISO 291, Plastics - Standard atmospheres for conditioning and testing (ISO 291:2008) DIN EN 15466-2:2009-10