DIN EN 941-2014 Aluminium and aluminium alloys - Circle and circle stock for the production of general applications - Specifications German version EN 941 2014《铝和铝合金 一般用途产品的圆片和圆片坯料.pdf

1、July 2014 Translation by DIN-Sprachendienst.English price group 9No part of this translation may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).ICS 77

2、.150.10!%7=g“2202668www.din.deDDIN EN 941Aluminium and aluminium alloys Circle and circle stock for the production of general applications Specifications;English version EN 941:2014,English translation of DIN EN 941:2014-07Aluminium und Aluminiumlegierungen Ronden und Rondenvormaterial fr allgemeine

3、 Anwendungen Spezifikationen;Englische Fassung EN 941:2014,Englische bersetzung von DIN EN 941:2014-07Aluminium et alliages daluminium Disques et bauches pour disques pour applications gnrales Spcifications;Version anglaise EN 941:2014,Traduction anglaise de DIN EN 941:2014-07SupersedesDIN EN 941:19

4、95-09www.beuth.deDocument comprises 1 pagesIn case of doubt, the German-language original shall be considered authoritative.306.14DIN EN 941:2014-07 2 A comma is used as the decimal marker. National foreword This document (EN 941:2014) has been prepared by Technical Committee CEN/TC 132 “Aluminium a

5、nd aluminium alloys” (Secretariat: AFNOR, France), Working Group WG 7 “Sheets, strips and plates” (Secretariat: AFNOR, France). The responsible German body involved in its preparation was the Normenausschuss Nichteisenmetalle (Nonferrous Metals Standards Committee), Working Committee NA 066-01-06 AA

6、 Bnder, Bleche, Platten. Amendments This standard differs from DIN EN 941:1995-09 as follows: a) Clause 2 “Normative references” has been updated; b) the standard has been editorially revised. Previous editions DIN 59600: 1955-09, 1964-11 DIN 59603: 1964-11, 1981-04 DIN 59602: 1981-04 DIN EN 941: 19

7、95-09 EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 941 April 2014 ICS 77.150.10 Supersedes EN 941:1995English Version Aluminium and aluminium alloys - Circle and circle stock for the production of general applications - Specifications Aluminium et alliages daluminium - Disques et bauches pou

8、r disques pour applications gnrales - Spcifications Aluminium und Aluminiumlegierungen - Ronden und Rondenvormaterial fr allgemeine Anwendungen - Spezifikationen This European Standard was approved by CEN on 13 March 2014. CEN members are bound to comply with the CEN/CENELEC Internal Regulations whi

9、ch stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member. This Eu

10、ropean Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the same status as the official versions. CEN members

11、are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal,

12、Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG CEN-CENELEC Management Centre: Avenue Marnix 17, B-1000 Brussels 2014 CEN All rights of exploitation in any form an

13、d by any means reserved worldwide for CEN national Members. Ref. No. EN 941:2014 EEN 941:2014 (E) 2 Contents Page Foreword 3 1 Scope 4 2 Normative references 4 3 Terms and definitions .4 4 Technical conditions for inspection and delivery 5 4.1 General 5 4.2 Orders or tenders.5 5 Mechanical propertie

14、s .6 6 Tolerances on dimensions and form .6 6.1 General 6 6.2 Diameter 6 6.3 Thickness .6 6.4 Tolerances on flatness for circles6 DIN EN 941:2014-07 EN 941:2014 (E) 3 Foreword This document (EN 941:2014) has been prepared by Technical Committee CEN/TC 132 “Aluminium and aluminium alloys”, the secret

15、ariat of which is held by AFNOR. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by October 2014 and conflicting national standards shall be withdrawn at the latest by October 2014. Attention is draw

16、n to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. This document supersedes EN 941:1995. With regard the previous version, Clause 2 Normative references w

17、as updated; no new alloys were added. According to the CEN-CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugos

18、lav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom. DIN EN 941:2014-07 EN 941:2014 (E) 4 1 Scope This

19、 European Standard specifies the particular requirements for wrought aluminium and aluminium alloys in the form of circle or circle stock for general applications. It applies to: Circles made out of hot or cold rolled circles stock by: Blanking: thickness 0,2 mm up to including 12 mm and with a diam

20、eter up to 1 000 mm; Sawing or shearing: thickness 0,2 mm up to and including 200 mm with a diameter up to 3 500 mm; Hot or cold rolled circle stock with a thickness from 0,2 mm up to and including 200 mm and with a width up to 3 500 mm. It does not apply to slugs for impact extrusions or to circle

21、and circle stock for culinary utensils applications which are dealt with in other European Standards. 2 Normative references The following documents, in whole or in part, are normatively referenced in this document and are indispensable for its application. For dated references, only the edition cit

22、ed applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 485-1:2008+A1:2009, Aluminium and aluminium alloys - Sheet, strip, and plate - Part 1: Technical conditions for inspection and delivery EN 485-2, Aluminium and aluminium alloys -

23、Sheet, strip and plate - Part 2: Mechanical properties EN 485-3:2003, Aluminium and aluminium alloys - Sheet, strip and plate - Part 3: Tolerances on dimensions and form for hot-rolled products EN 485-4:1993, Aluminium and aluminium alloys - Sheet, strip and plate - Part 4: Tolerances on shape and d

24、imensions for cold-rolled products EN 515, Aluminium and aluminium alloys - Wrought products - Temper designations 3 Terms and definitions For the purposes of this document, the following terms and definitions apply. 3.1 circle circular flat product obtained by circular sawing or shearing, or by bla

25、nking of a flat rolled product with a uniform thickness over 0,20 mm DIN EN 941:2014-07 EN 941:2014 (E) 5 3.2 circle stock flat rolled product of rectangular cross-section with uniform thickness over 0,20 mm, supplied in coils, sheets, or plates, usually with sheared or sawn edges, and intended to b

26、e sawn, sheared or blanked into flat shapes to be subsequently formed, drawn, etc. Note 1 to entry: The thickness does not exceed one tenth of the width. 3.3 hot rolled circle and circle stock circle or circle stock whose final thickness is obtained by hot rolling 3.4 cold rolled circle and circle s

27、tock circle or circle stock whose final thickness is obtained by cold rolling 4 Technical conditions for inspection and delivery 4.1 General All the provisions of EN 485-1 shall apply, except Clause 4 (orders and tenders) which is modified as follows: 4.2 Orders or tenders The order or tender shall

28、define the product required and shall contain the following information: a) the form and the type of product: 1) the form of the product (circle and circle stock); 2) the designation of the aluminium or aluminium alloy; 3) the customer application, b) the metallurgical temper of the material for del

29、ivery according to EN 515 (degree of hardness or heat treatment condition) and, if different, the metallurgical temper for use; c) the number of this European Standard or Specification number, or where none exists, the properties greed between purchaser and supplier; d) the dimensions and shape of t

30、he product as applicable: 1) thickness; 2) diameter of the circle; 3) width of the strip, sheet, or plate; 4) length of the sheet or plate; 5) internal and external diameters of the coil; e) whether hot rolled or cold rolled tolerances apply; f) quantity: DIN EN 941:2014-07 EN 941:2014 (E) 6 1) mass

31、 or number of pieces; 2) tolerances on quantity if required; g) any requirements for certificates of conformity, test and/or analysis reports or inspection certificates; h) any special requirements agreed between purchaser and supplier : 1) marking of products; 2) references to drawings, etc. 5 Mech

32、anical properties The mechanical properties shall conform to the requirements specified in EN 485-2. 6 Tolerances on dimensions and form 6.1 General All provisions of EN 485-3 and EN 485-4 shall apply with the following amendments and additions. 6.2 Diameter Tolerances on diameters for circle shall

33、conform to Table 1. These tolerances include the tolerances on roundness. NOTE For circle obtained by blanking the recommended standard diameters are: From 100 mm up to 500 mm nominal diameter: every multiple of 5; Over 500 mm up to 1 000 mm nominal diameter: every multiple of 10. 6.3 Thickness Tole

34、rances on thickness for hot rolled circle and circle stock shall conform to Table 2. They are identical to those specified in Table 1 of EN 485-3:2003 and are reproduced here for convenience. The tolerances on thickness for cold rolled circle and circle stock shall conform to Table 3. They are ident

35、ical to those specified in Table 1 of EN 485-4:1993 and are reproduced here for convenience. The partition into group I and group II of most common materials which may be used for the present application shall be as shown in Table 4. 6.4 Tolerances on flatness for circles Tolerances on flatness for

36、circles, expressed as a percentage of the diameter D and/or the measured chord length L, shall conform to Table 5. Deviation from flatness d, resulting from arching or buckling, shall be measured as shown in Figures 1 and 2, using a lightweight straightedge and a feeler gauge, dial gauge or scale, w

37、hile the circle is resting on a horizontal base plate, concave side upwards. Two measurements shall be carried out with the straight edge respectively parallel and perpendicular to the rolling direction. DIN EN 941:2014-07 EN 941:2014 (E) 7 These tolerances do not apply to circles supplied in O or F

38、 tempers except for special agreement between supplier and purchaser. Table 1 Tolerances on diameter Dimensions in millimetres Specified thickness Method of production Diameter tolerances for specified diameter aover up to up to 600 over 600 up to 1 000 over 1 000 up to 1 600 over 1 600 up to 3 000

39、over 3 000 up to 3 500 0,2 4 Blanking 0,5 0,5 - - - circular sawing or shearing + 3 0 + 4 0 + 7 0 + 9 0 + 11 0 4 6 Blanking 0,7 0,7 - - - circular sawing or shearing + 4 0 + 5 0 + 8 0 + 9 0 + 11 0 6 12 Blanking 1 1 - - - circular sawing or shearing + 4 0 + 5 0 + 8 0 + 10 0 + 12 0 12 50 circular sawi

40、ng or shearing + 7 0 + 7 0 + 9 0 + 12 0 + 14 0 50 200 circular sawing or shearing + 10 0 + 10 0 + 12 0 + 14 0 + 16 0 aThese tolerances include the tolerances on roundness. DIN EN 941:2014-07 EN 941:2014 (E) 8 Table 2 Thickness tolerances for hot rolled circle and circle stock Dimensions in millimetr

41、es Specified thickness Thickness tolerance for specified diameter or width over up to up to 1 250 over 1 250 up to 1 600 over 1 600 up to 2 000 over 2 000 up to 2 500 over 2 500 up to 3 500 2,5 4,0 0,28 0,28 0,32 0,35 0,40 4,0 5,0 0,30 0,30 0,35 0,40 0,45 5,0 6,0 0,32 0,32 0,40 0,45 0,50 6,0 8,0 0,3

42、5 0,40 0,40 0,50 0,55 8,0 10 0,45 0,50 0,50 0,55 0,60 10 15 0,50 0,60 0,65 0,65 0,80 15 20 0,60 0,70 0,75 0,80 0,90 20 30 0,65 0,75 0,85 0,90 1,0 30 40 0,75 0,85 1,0 1,1 1,2 40 50 0,90 1,0 1,1 1,2 1,5 50 60 1,1 1,2 1,4 1,5 1,7 60 80 1,4 1,5 1,7 1,9 2,0 80 100 1,7 1,8 1,9 2,1 2,2 100 150 2,2 2,2 2,7

43、2,8 - 150 200 2,8 2,8 3,3 3,3 - DIN EN 941:2014-07 EN 941:2014 (E) 9 Table 3 Thickness tolerances for cold-rolled circle and circle stock Dimensions in millimetres Specified thickness Thickness tolerances afor specified diameter or width up to 1 000 over 1 000 over 1 250 over 1 600 over 2 000 over 2

44、 500 over 3 000 up to 1 250 up to 1 600 up to 2 000 up to 2 500 up to 3 000 up to 3 500 over Up to Material Group Material Group Material Group Material Group Material Group Material Group Material Group Group I Group II Group I Group II Group I Group II Group I Group II Group I Group II Group I Gro

45、up II Group I Group II 0,2 0,4 0,02 0,03 0,04 0,05 0,05 0,06 - - - - - 0,4 0,5 0,03 0,03 0,04 0,05 0,05 0,06 0,06 0,07 0,10 - - 0,5 0,6 0,03 0,04 0,05 0,06 0,06 0,07 0,07 0,08 0,11 - - 0,6 0,8 0,03 0,04 0,06 0,07 0,07 0,08 0,08 0,09 0,12 - - 0,8 1 0,04 0,05 0,06 0,08 0,08 0,09 0,09 0,10 0,13 - - 1,0

46、 1,2 0,04 0,05 0,07 0,09 0,09 0,10 0,10 0,12 0,14 - - 1,2 1,5 0,05 0,07 0,09 0,11 0,10 0,12 0,11 0,14 0,16 - - 1,5 1,8 0,06 0,08 0,10 0,12 0,11 0,13 0,12 0,15 0,17 - - 1,8 2 0,06 0,09 0,11 0,13 0,12 0,14 0,14 0,16 0,19 - - 2,0 2,5 0,07 0,10 0,12 0,14 0,13 0,15 0,15 0,17 0,20 - - 2,5 3 0,08 0,11 0,13

47、 0,15 0,15 0,17 0,17 0,19 0,23 - - 3,0 3,5 0,10 0,12 0,15 0,17 0,17 0,19 0,18 0,20 0,24 - - 3,5 4 0,15 0,20 0,22 0,23 0,25 0,34 0,38 4,0 5 0,18 0,22 0,24 0,25 0,29 0,36 0,42 5,0 6 0,20 0,24 0,25 0,26 0,32 0,40 0,46 6,0 8 0,24 0,30 0,31 0,32 0,38 0,44 0,50 8 10 0,27 0,33 0,36 0,38 0,44 0,50 0,56 10 1

48、2 0,32 0,38 0,40 0,41 0,47 0,53 0,59 12 15 0,36 0,42 0,43 0,45 0,51 0,57 0,63 15 20 0,38 0,44 0,46 0,48 0,54 0,60 0,66 20 25 0,40 0,46 0,48 0,50 0,56 0,62 0,68 25 30 0,45 0,50 0,53 0,55 0,60 0,65 0,70 30 40 0,50 0,55 0,58 0,60 0,65 0,70 0,75 40 50 0,55 0,60 0,63 0,65 0,70 0,75 0,80 aWhen measuring the thickness,