DIN EN 15820-2011 Polymer modified bituminous thick coatings for waterproofing - Determination of watertightness German version EN 15820 2011《防水用聚合物改性沥青厚涂层 水密性测定 德文版本EN 15820-2011》.pdf

1、June 2011 Translation by DIN-Sprachendienst.English price group 7No part of this translation may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).ICS 91

2、.100.50!$rE“1792534www.din.deDDIN EN 15820Polymer modified bituminous thick coatings for waterproofing Determination of watertightnessEnglish translation of DIN EN 15820:2011-06Kunststoffmodifizierte Bitumendickbeschichtungen zur Bauwerksabdichtung Bestimmung der WasserdichtheitEnglische bersetzung

3、von DIN EN 15820:2011-06Revtements bitumineux pais modifis aux polymres pour impermabilisation Dtermination de ltanchit leauTraduction anglaise de DIN EN 15820:2011-06www.beuth.deDocument comprises pagesIn case of doubt, the German-language original shall be considered authoritative.905.11 DIN EN 15

4、820:2011-06 A comma is used as the decimal marker. National foreword This standard has been prepared by Technical Committee CEN/TC 361 “Project Committee Polymer modified bituminous thick coatings for waterproofing Definitions/requirements and test methods” (Secretariat: DIN, Germany). The responsib

5、le German body involved in its preparation was the Normenausschuss Bauwesen (Building and Civil Engineering Standards Committee), Working Committee NA 005-02-19 AA Kunststoffmodifizierte Bitumendickbeschichtung zur Bauwerksabdichtung (SpA zu CEN/TC 361). 2 EUROPEAN STANDARD NORME EUROPENNE EUROPISCH

6、E NORM EN 15820 March 2011 ICS 91.100.50 English Version Polymer modified bituminous thick coatings for waterproofing Determination of watertightness Revtements bitumineux pais modifis aux polymres pour impermabilisation Dtermination de ltanchit leau Kunststoffmodifizierte Bitumendickbeschichtungen

7、zur Bauwerksabdichtung Bestimmung der Wasserdichtheit This European Standard was approved by CEN on 13 February 2011. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this EuropeanStandard the status of a national standard without an

8、y alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other langua

9、ge made by translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark,

10、 Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland,Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION

11、EUROPISCHES KOMITEE FR NORMUNG Management Centre: Avenue Marnix 17, B-1000 Brussels 2011 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN 15820:2011: EEN 15820:2011 (E) 2 Contents Page Foreword 31 Scope 42 Normative references 43 Te

12、rms and definitions .44 Principle 45 Apparatus .56 Test specimens 66.1 General 66.2 Preparation .66.3 Conditioning of test specimens .66.4 Dimensions of the test specimens.67 Procedure .77.1 Test conditions 77.2 Procedure .78 Expression of results and precision 78.1 Expression of results 78.2 Precis

13、ion .79 Test report 7DIN EN 15820:2011-06 EN 15820:2011 (E) 3 Foreword This document (EN 15820:2011) has been prepared by Technical Committee CEN/TC 361 “Project Committee Polymer modified bituminous thick coatings for waterproofing Definitions/requirements and test methods”, the secretariat of whic

14、h is held by DIN. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by September 2011, and conflicting national standards shall be withdrawn at the latest by September 2011. Attention is drawn to the p

15、ossibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countrie

16、s are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia

17、, Spain, Sweden, Switzerland and United Kingdom. DIN EN 15820:2011-06 EN 15820:2011 (E) 4 1 Scope This European Standard specifies a procedure for determining the watertightness of polymer modified bituminous thick coatings for waterproofing (i.e. the resistance to hydraulic pressure). 2 Normative r

18、eferences The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. FprEN 15814:2011, Polymer modified bitu

19、minous thick coatings for waterproofing Definitions and requirements ISO 554, Standard atmospheres for conditioning and/or testing Specifications 3 Terms and definitions For the purposes of this document, the terms and definitions given in FprEN 15814:2011 apply. 3.1 watertightness the coating can b

20、e deemed watertight if the side of the specimen that is not exposed to water does not exhibit any leakage of water 4 Principle Test procedure for polymer modified bituminous thick coatings intended for use in pressure application, e.g. pressured water in soil. Submission of a test specimen to a spec

21、ified water pressure for at least 24 h against a disk containing four slots of specified form and dimensions. The test specimen is observed to establish whether it remains watertight. DIN EN 15820:2011-06 EN 15820:2011 (E) 5 5 Apparatus The apparatus consists of a device (see Figures 1 and 2) by whi

22、ch a pressure can be applied to one side of a test specimen. Key 1 slots 2 cover 3 test specimen 4 hydrostatic pressure 5 observation gap 6 slotted plate Figure 1 Slot pressure testing device for watertightness at high pressures Figure 2 Device for the slot pressure test: sketch of the cover The tes

23、t specimen is covered by a circular disk containing four slots. The form and dimensions of the slots are specified by the requirements indicated in Figure 3. DIN EN 15820:2011-06 EN 15820:2011 (E) 6 Dimensions in millimetres Key aall edges of the slotted plate are rounded to a radius of 0,5 mm appro

24、ximately Figure 3 Slotted plate 6 Test specimens 6.1 General 3 circular test specimen with a diameter equal to the extend diameter of the slotted plate (approximately 130 mm). 6.2 Preparation Production of a membrane from the polymer modified bituminous thick coatings in accordance with classes defi

25、ned in FprEN 15814:2011, Table 1. In case reinforcement is used the first layer is placed on a release layer with approximately half the thickness of the bitumen layer. Subsequently the reinforcement is incorporated and finally the second layer of bitumen is applied. The wet layer has to be that thi

26、ck, that after drying process the designated dry layer thickness will be achieved. To provide the designated dry layer thickness the wet coating has to be levelled off with the help of a frame or gauge of accordant height. 6.3 Conditioning of test specimens The test specimens shall be stored for at

27、least 28 days at a normal climate of (23 2) C and a relative humidity of (50 5) % in accordance with ISO 554 prior to testing. 6.4 Dimensions of the test specimens The thickness of the dry layer shall be measured using vernier callipers permitting a reading to 0,1 mm. 12 readings shall be taken. The

28、 highest and lowest values shall be ignored and the mean value calculated from the remaining 10 values. DIN EN 15820:2011-06 EN 15820:2011 (E) 7 7 Procedure 7.1 Test conditions The test shall be carried out at (23 2) C. The test pressure shall be specified in the product specification. It shall be e

29、nsured that the margins are watertight. 7.2 Procedure Fill the apparatus in accordance with Figure 1 with water until overflowing. Place the test specimen with its upper side downwards in the apparatus and cover with the specified slotted plate. Place the cover and progressively tighten until the sp

30、ecimen is tightly in place. Pressurise progressively to the specified test pressure. Once the test pressure is reached, maintain the pressure for a period according to the product specific but minimum 24 h. Observe the watertightness of the test specimen after the testing time (sudden pressure drop

31、or presence of water on the non exposed face of the test specimen). 8 Expression of results and precision 8.1 Expression of results The watertightness test is considered passed if all test specimens remain watertight on the side subjected to the test pressure after the specified testing time. 8.2 Pr

32、ecision Precision data are currently not available. 9 Test report The test report shall include at least the following information: a) all details necessary to identify the product tested; b) a reference to this European Standard (i.e. EN 15820) and any deviation from it; c) details of preparation of test specimens in accordance with Clause 6; d) test procedure including: test pressure; test period; specimen thickness; deviation of test conditions; DIN EN 15820:2011-06 e) the test results in accordance with Clause 8; f) the dates of the tests.