DIN EN 16653-2015 Rubber or plastics-coated fabrics - Determination of stitch tear resistance (using a needle) - Test method German version EN 16653 2015《橡胶或塑料涂层织物 缝合抗撕裂性的测定 (使用针) .pdf

1、May 2015 Translation by DIN-Sprachendienst.English price group 7No part of this translation may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).ICS 59.

2、080.40!%Bj?“2317128www.din.deDDIN EN 16653Rubber or plastics-coated fabrics Determination of stitch tear resistance (using a needle) Test method;English version EN 16653:2015,English translation of DIN EN 16653:2015-05Mit Kautschuk oder Kunststoff beschichtete Textilien Bestimmung des Stichausreiwid

3、erstands (unter Verwendung einer Nadel) Prfverfahren;Englische Fassung EN 16653:2015,Englische bersetzung von DIN EN 16653:2015-05Supports textiles revtus de caoutchouc ou de plastique Dtermination de la rsistance au dchirement au point de couture ( laide duneaiguille) Mthode dessai;Version anglaise

4、 EN 16653:2015,Traduction anglaise de DIN EN 16653:2015-05www.beuth.deDocument comprises 10 pagesIn case of doubt, the German-language original shall be considered authoritative.04.15DIN EN 16653:2015-05 2 A comma is used as the decimal marker. National foreword This document (EN 16653:2015) has bee

5、n prepared by Technical Committee CEN/TC 248 “Textiles and textile products” (Secretariat: BSI, United Kingdom). The responsible German body involved in its preparation was the DIN-Normenausschuss Kunststoffe (DIN Standards Committee Plastics), Working Committee NA 054-04-04 AA Kunststoff-Folien und

6、 kunststoffbeschichtete Flchengebilde (Kunstleder); allgemeine Eigenschaften. The European Standards referred to in this document have been published as DIN EN ISO Standards with the same number. EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 16653 March 2015 ICS 59.080.40 English Version Rubb

7、er or plastics-coated fabrics - Determination of stitch tear resistance (using a needle) - Test method Supports textiles revtus de caoutchouc ou de plastique - Dtermination de la rsistance au dchirement au point de couture ( laide dune aiguille) - Mthode dessai Mit Kautschuk oder Kunststoff beschich

8、tete Textilien - Bestimmung des Stichausreiwiderstands (unter Verwendung einer Nadel) - Prfverfahren This European Standard was approved by CEN on 7 February 2015. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standa

9、rd the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member. This European Standard exists in three official versions (English,

10、 French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulg

11、aria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Tu

12、rkey and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG CEN-CENELEC Management Centre: Avenue Marnix 17, B-1000 Brussels 2015 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members.

13、 Ref. No. EN 16653:2015 EEN 16653:2015 (E) 2 Contents Page Foreword 3 1 Scope 4 2 Normative references 4 3 Terms and definitions .4 4 Test apparatus and materials .4 5 Sampling and conditioning .6 6 Test method 7 7 Expression of results 8 8 Test report 8 DIN EN 16653:2015-05 EN 16653:2015 (E) 3 Fore

14、word This document (EN 16653:2015) has been prepared by Technical Committee CEN/TC 248 “Textiles and textile products”, the secretariat of which is held by BSI. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at t

15、he latest by September 2015 and conflicting national standards shall be withdrawn at the latest by September 2015. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying an

16、y or all such patent rights. According to the CEN-CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Repub

17、lic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom. DIN EN 16653:2015-05 EN 16653:2015 (E) 4 1 Scope This Euro

18、pean Standard specifies a method for the determination of the resistance of the seams of rubber or plastic-coated fabrics against tearing out a needle perpendicular to the stitching direction. This resistance is characterized by determining the stitch tear force. 2 Normative references The following

19、 documents, in whole or in part, are normatively referenced in this document and are indispensable for its application. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN ISO 2231, Rubber-

20、 or plastics-coated fabrics Standard atmospheres for conditioning and testing (ISO 2231) EN ISO 2286-3, Rubber- or plastics-coated fabrics Determination of roll characteristics Part 3: Method for determination of thickness (ISO 2286-3) EN ISO 7500-1, Metallic materials Verification of static uniaxia

21、l testing machines Part 1: Tension/compression testing machines Verification and calibration of the force-measuring system (ISO 7500-1) EN ISO 10012, Measurement management systems Requirements for measurement processes and measuring equipment (ISO 10012) 3 Terms and definitions For the purposes of

22、this document, the following terms and definitions apply. 3.1 stitch tear resistance resistance to pull a needle from a sample perpendicular to the stitching direction 3.2 stitch tear force stitch tear resistance, recorded as the maximum tearing force 3.3 stitch tear strength stitch tear force divid

23、ed by the thickness 4 Test apparatus and materials The following test apparatus and materials shall be used: 4.1 CRE machine. Metrological confirmation system of the tensile-testing machine shall be in accordance with EN ISO 10012. The constant-rate-of-extension (CRE) machine shall have the general

24、characteristics given in 4.1.1 to 4.1.4. DIN EN 16653:2015-05 EN 16653:2015 (E) 5 4.1.1 The tensile-testing machine shall be provided with means for indicating or recording the force applied to the test specimen. Under conditions of use, the accuracy of the apparatus shall be class 1 of EN ISO 7500-

25、1. The error of the indicated or recorded maximum force at any point in the range in which the machine is used shall not exceed 1 %. 4.1.2 If a class 2 tensile-testing machine according to EN ISO 7500-1 is to be used, this shall be stated in the test report. 4.1.3 If recording of force is obtained b

26、y means of data acquisition boards and software, the frequency of data collection shall be at least eight per second. 4.1.4 The machine shall be capable of constant rate of extension of (100 10) mm/min. 4.2 Needle. Either a smooth needle of stainless steel having a diameter of (1,0 0,1) mm and a con

27、ical tip or a corresponding piece of spring steel wire having the same diameter, also made of stainless steel and having a conical tip. 4.3 Clamping device. As an example, Figure 1 shows a schematic view of a clamping device. The bearing bushes for the needle shall be parallel and adjustable such th

28、at they can be set in accordance with the thickness of the test specimen. The clamping device shall be provided with a suitable safety device which prevents the needle from jumping out. DIN EN 16653:2015-05 EN 16653:2015 (E) 6 Key 1 supporting bracket 2 spacer 3 steel needle 4 specimen 5 scissor cla

29、mp Figure 1 Schematic view of a clamping device 5 Sampling and conditioning The test specimens to be tested are sampled in the warp and weft directions. For each direction, five test specimens shall be sampled. The test specimens consist of strips with a length of (50 1) mm and a width of (20 1) mm.

30、 All test specimens shall be conditioned for at least 24 h prior to testing in accordance with EN ISO 2231. The final result shall be based on test specimens of the same type only, and the type shall be indicated in the test report. DIN EN 16653:2015-05 EN 16653:2015 (E) 7 6 Test method The test is

31、carried out after conditioning in a standard atmosphere in accordance with EN ISO 2231. The thickness of the test specimen shall be measured in accordance with EN ISO 2286-3. A needle having a diameter of 1 mm (see 4.2) is inserted into the test specimen 5 mm from the edge in the centre of the narro

32、w side (see Figure 1), as perpendicularly as possible, by means of a template. Prior to this, the test specimen shall not have been pierced or punched in any manner. The needle, which is now held (fixed) inside the test specimen, is placed into the clamping device (see 4.3). The distance between the

33、 spacers shall be adjusted such that they just barely touch the test specimen. The lower end of the test specimen is clamped into the lower jaw (shown as a scissor clamp in Figure 1). The test specimen is elongated at 100 mm/min. Record the maximum force, in newtons, which occurs while the needle is

34、 being torn out (see Figure 2). Key X displacement in millimetres F force in newtons Fmaxstitch tear force Figure 2 Force displacement diagram for the needle DIN EN 16653:2015-05 EN 16653:2015 (E) 8 7 Expression of results 7.1 Stitch tear force The stitch tear force is calculated as the arithmetic m

35、ean of the highest individual values (Fmax) of the five test specimens, given for each direction, expressed in N and rounded to the nearest 0,5 N. 7.2 Stitch tear strength If required, the stitch tear strength, expressed in N/mm, is calculated as follows: maxStitch tear strength =Fdwhere Fmaxis the

36、maximum stitch tear force, in newtons; d is the thickness of the test specimen, in millimetres. 8 Test report The test report shall contain the following information: a) a reference to this test method; b) the complete marking of the tested sample, including commercially available types, codes, colours, condition, etc.; c) the date of the test; d) the standard atmosphere used; e) the results in accordance with Clause 7: stitch tear force (7.1) and, if required, stitch tear strength (7.2); f) any deviation from the given procedure. DIN EN 16653:2015-05