DIN EN ISO 2898-1-1999 Plastics - Plasticized poly(vinyl chloride) (PVC-P) moulding and extrusion materials - Part 1 Designation system and basis for specifications (ISO 2898-1 199.pdf

1、DEUTSCHE NORM October 1999 Plasticized poly(viny1 chloride) (PVC-P) moulding and extrusion materials Part 1 : Designation system and basis for specifications (IS0 2898-1 : 1996) English version of DIN EN IS0 2898-1 DIN - EN IS0 2898-1 ICs 83.080.20 Supersedes DIN 7749-1, September 1985 edition. Kuns

2、tstoffe - Weichmacherhaltige Polyvinylchlorid (PVC-P)- Formmassen - Teil 1 : Bezeichnungssystem und Basis fr Spezifikationen (IS0 2898-1 : 1996) European Standard EN IS0 2898-1 : 1999 has the status of a DIN Standard. A comma is used as the decimal marker. National foreword This standard has been pu

3、blished in accordance with a decision taken by CEN/TC 249 to adopt, without alteration, International Standard IS0 2898-1 as a European Standard. The responsible German body involved in its preparation was the Normenausschu Kunststoffe (Plastics Standards Committee), Technical Committee PVC-Formmass

4、en. DIN EN IS0 1043-1 and DIN EN IS0 2898-2 are the standards corresponding to International Standards IS0 1043-1 and IS0 2898-2, respectively, referred to in clause 2 of the EN. Amendments DIN 7749-1, September 1985 edition, has been superseded by the specifications of EN IS0 2898-1, which is ident

5、ical to IS0 2898-1. Previous editions DIN 7749-1: 1979-07, 1985-09. National Annex NA Standards referred to (and not included in Normative references and Annex ZA) DIN EN IS0 1043-1 DIN EN IS0 2898-2 Plastics - Symbols - Part 1: Basic polymers and their special characteristics Plasticized poly(viny1

6、 chloride) (PVC-P) moulding and extrusion materials - Part 2: Preparation of test specimens and determination of properties (IS0 2898-2 : 1997) (IS0 1043-1 : 1997) EN comprises 7 pages. No pari of this standard may be reproduced without the prior permission of Ref. No. DIN EN IS0 2898-1 : 1999-1 Y D

7、eutsches Institut fr Normung e. V., Berlin. wth Verlag GmbH, D-10772 Berlin, has the exclusive right of sale for German Standards (DIN-Normen). English price group O7 Sales No. 1107 03.00 EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN IS0 2898-1 June 1999 ICs 83.080.20 English version Plastics

8、 Plasticized poly(viny1 chloride) (PVC-P) moulding and extrusion mater als Part 1 : Designation system and basis for specifications (IS0 2898-1 : 1996) Plastiques - Matriaux base de poly(ch1orure de vinyle) plastifi (PVC-P) pour moulage et extrusion - Partie 1 : Systme de dsignation et Kunststoffe -

9、 Weichmacherhaltige Polyvinylchlorid (PVC-P)- Formmassen - Teil 1 : Bezeichnungs- system und Basis fr Spezifikationen base de spcification (IS0 2898-1 : 1996) (IS0 2898-1 : 1996) This European Standard was approved by CEN on 1999-05-06. CEN members are bound to comply with the CENKENELEC Internal Re

10、gulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national stand- ards may be obtained on application to the Central Secretariat or to any CEN member. Th

11、e European Standards exist in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the Central Secretariat has the same status as the official versions. CEN members are th

12、e national standards bodies of Austria, Belgium, the Czech Republic, Denmark, Finland, France, Germany, Greece, Iceland, Ireland, Italy, Luxembourg, the Netherlands, Norway, Portugal, Spain, Sweden, Switzerland, and the United Kingdom. CEN European Committee for Standardization Comit Europen de Norm

13、alisation Europisches Komitee fr Normung Central Secretariat: rue de Stassart 36, B-1050 Brussels O 1999. CEN - All rights of exploitation in any form and by any means reserved worldwide for CEN national members. Ref. No. EN IS0 2898-1 : 1999 E Page 2 EN IS0 2898-1 : 1999 Foreword International Stan

14、dard IS0 2898-1 : 1996 Plastics - Plasticized poly(viny1 chloride) (PVC-P) moulding and extrusion materials - Part 1 : Designation system and basis for specifications, which was prepared by ISO/TC 61 Plastics of the International Organization for Standardization, has been adopted by Technical Commit

15、tee CEN/TC 249 Plastics, the Secretariat of which is held by IBN, as a European Standard. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, and conflicting national standards withdrawn, by December 1999 at the lates

16、t. In accordance with the CENKENELEC Internal Regulations, the national standards organizations of the follow- ing countries are bound to implement this European Standard: Austria, Belgium, the Czech Republic, Denmark, Finland, France, Germany, Greece, Iceland, Ireland, Italy, Luxembourg, the Nether

17、lands, Norway, Portugal, Spain, Sweden, Switzerland, and the United Kingdom. Endorsement notice The text of the International Standard IS0 2898-1 : 1996 was approved by CEN as a European Standard without any modification. NOTE: Normative references to international publications are listed in Annex Z

18、A (normative). 1 Scope 1.1 This part of IS0 2898 establishes a system of designation for plasticized thermoplastic material which may be used as the basis for specifications. 1.2 The types of PVC-P plastics are differentiated from each other by a classification system based on appropriate levels of

19、the designatory properties a) Shore hardness b) density c) and on information about physical form, intended application and/or method of processing, important properties, additives and colorants. torsional-stiffness temperature at 300 MPa 1.3 This part of IS0 2898 is applicable to all plasticized co

20、mpositions of homopolymers and copolymers that con- tain at least 50 % (dm) of vinyl chloride. It is also applicable to plasticized compositions containing chlorinated poly(viny1 chloride) and to plasticized compositions containing blends of one or more of the above-mentioned poly- mers, provided th

21、at the total amount of these polymers represents at least 50 % (nh) of the polymer content of the comoosition. This part of IS0 2898 applies to materials ready for normal use in the form of powder (dry blends), granules or pel- lets, unmodified or modified by colorants, additives, fillers, etc. This

22、 part of IS0 2898 does not apply to cellular plastics or to paste compositions (plastisols). 1.4 It is not intended to imply that materials having the same designation give necessarily the same performance. This part of IS0 2898 does not provide engineering data, performance data or data on processi

23、ng conditions which may be required to specify a material for a particular application and/or method of processing. If such additional properties are required, they shall be determined in accordance with the test methods specified in part 2 of this International Standard, if suitable. 1.5 In order t

24、o specify a thermoplastic material for a particular application or to ensure reproducible processing, additional requirements may be given in data block 5 (see clause 3, first paragraph). Page 3 EN IS0 2898-1 : 1999 Description block (optional) 2 Normative references Identity block International Ind

25、ividual-item block Standard Data Data Data Data Data Number block block block block block block 1 2 3 4 5 The following standards contain provisions which, through reference in this text, constitute provisions of this part of IS0 2898. At the time of publication, the editions indicated were valid. A

26、ll standards are subject to revision, and parties to agreements based on this part of IS0 2898 are encouraged to investigate the possibility of applying the most recent editions of the standards indicated below. Members of IEC and IS0 maintain registers of currently valid International Standards. IS

27、0 1043-1 :- I), Plastics - Symbols and abbreviated terms - Part I: Basic polymers and their special character- is tics. IS0 2898-2:- 2), Plastics - Plasticized polylvinyl chloride) IPVC-PI mouldmg and extrusion matenals - Part 2: Preparation of test specimens and determination of properties. 3 Desig

28、nation and specification system The designation and specification system for thermoplastics is based on the following standardized pattern: I Designation The designation consists of an optional description block, reading “Thermoplastics“, and an identity block compris- ing the International Standard

29、 number and an individual-item block. For unambiguous coding, the individual-item block is subdivided into 5 data blocks comprising the following information: Data block 1: Identification of the plastic by its symbol PVC-P in accordance with IS0 1043-1 and information about the polymerization proces

30、s or the composition of the polymer. Data block 2: Position 1 : Intended application or method of processing (see 3.2). Positions 2 to 8: Important properties, additives and supplementary information (see 3.2). Data block 3: Designatory properties (see 3.3). Data block 4: Fillers or reinforcing mate

31、rials and their nominal content (not included in this part of IS0 2898). Data block 5: For the purpose of specifications, a fifth data block may be added containing additional infor- mation. The first character of the individual-item block shall be a hyphen. The data blocks shall be separated from e

32、ach other by commas. If a data block is not used, this shall be indicated by doubling the separation sign, .e. by two commas (,I. 3.1 Data block 1 In this data block, after the hyphen, plasticized poly(viny1 chloride) plastics are identified by the symbol PVC-P, in accordance with IS0 1043-1. 1) To

33、be published. (Revision of IS0 1043-1 :I 987) 2) To be published. (Revision of IS0 2898-21 989) Page 4 EN IS0 2898-1 : 1999 Code-letter Position 1 B Blow moulding 3.2 Data block 2 Code-letter Positions 2 to 8 B Antiblockinq In this data block, information about intended application and/or method of

34、processing is given in position 1 and in- formation about important properties, additives and colour in positions 2 to 8. The code-letters used are specified in table 1 C E If information is presented in positions 2 to 8 and no specific information is given in position 1, the letter X shall be inser

35、ted in position 1. Calendering C Coloured D Powder dry blend Extrusion E Expandable Table 1 - Code-letters used in data block 2 H K Coating H Heat-ageing stabilized Cable and wire coating M I F I Extrusion of films I F I SDecial burninq characteristics I L Light or weather stabilized I niection moul

36、dinq E General use N P I G I Granules Natural (no colour added) Impact modified T X Tape manufacture T Transparent No indication Y z I O I Compression moulding I I I Increased electrical conductivity Antistatic I R I Rotational mouldinci I R I Mould release agent I I s I sintering I S I Lubricated I

37、 3.3 Data block 3 In this data block, the Shore hardness is represented by a 2-figure code number (see 3.3.1), the range of density by a 2-figure code number (see 3.3.2) and the range of torsional-stiffness temperature at 300 MPa by a 2-figure code- number (see 3.3.3). The code numbers are separated

38、 from each other by hyphens. If a property value falls on or near a range limit. the manufacturer shall state which range will designate the ma- terial If subsequent individual test values lie on, or on either side of, the limit, because of manufacturing toler- ances the designation is not affected

39、NOTE 1 Not all combinations of the values of designatory properties are provided in currently available polymers 3.3.1 Shore hardness The Shore A or D hardness shall be determined in accordance with IS0 2898-2. The value of the Shore hardness is represented by a 2-figure code-number as specified in

40、table 2. The scale used is indicated by a single code-letter (A or D) immediately preceding the code-number indicating the hardness value. Page 5 EN IS0 2898-1 : 1999 3.3.2 Density The density shall be determined in accordance with IS0 2898-2 The possible values of density are divided into 17 ranges

41、 each represented by a 2-figure code-number as specified in table 2 3.3.3 Torsional-stiffness temperature at 300 MPa The torsional-stiffness temperature at 300 MPa shall be determined in accordance with IS0 2898-2 The possible values of the torsional-stiffness temperature at 300 MPa are divided into

42、 7 ranqes, each represented by a 2-figure code-number as specified in table 2 Table 2 - Code-numbers used for designatory properties Shore hardness -he Shore hardness is desig- iated by the letter A or D fol- owed by the hardness value, for :xample, A82 for a measured ;bore A value of 82. 4 toleranc

43、e of I3 is permitted Jse the D scale when the 4 scale value exceeds 85. Code- number 15 20 25 30 35 40 45 50 55 60 65 70 75 80 85 90 95 3.4 Data block 4 Not included in this part of IS0 2898. 3.5 Data block 5 Density Range g/cm3 1.17 buts 1.22 1.22 but s 1,27 1,27 but s 1,32 1.32 but s 1.37 1.37 but

44、 s 1,42 1.42 but s 1,47 1.47 but s 1.52 1,52 but 1,57 but s 1,62 1.62 but s 1,67 1.67 but s 1,72 1,72 but S 1,77 1,77 but 1,82 but 1,87 but c 1,92 1.92 Torsional-stiffness temperature at 300 MPa Code- number 00 10 20 30 40 50 60 Range “C a -5 -35 i -35 but 3 -45 -45 but + -55 - 55 Indication of addi

45、tional requirements in this optional data block is a way of transforming the designation of a ma- terial into a specification for a particular application This may be done for example by reference to a suitable na- tional standard or to a standard-like, generally established specification Page 6 EN

46、IS0 2898-1 : 1999 Description block (optional) 4 Examples of designations International Standard Individual-item block Number block 11 21 3 4 5 4.1 Designation only Description block (optional) A plasticized poly(viny1 chloride) thermoplastic material (PVC-Pl, intended for cable and wire coating ext

47、rusion (KI, in the form of a granular material (GI, natural and not coloured (N), with a Shore A hardness of 82 (A82), a density of 1,24 g/cm3 (25) and a torsional-stiffness temperature at 300 MPa of - 31 “C (30), would be designated: International Standard Individual-item block Number block 1 2 131

48、 4 15 Data btock 1: symbol T Data block 2: Position 1: extrusion Position 2: dry blend Position 3: cotoured Position 4: antistatic Position 2: density Data block 3. Position 1: Shore D hardness a bluck a block Position 3: torsional-stiffness temperature at 300 MPa 1: symbol 2: Position 1: for cable

49、and wire coating Position 2: granules Position 3: natural (not coloured) 1 1 Data block 3: Position 1: Shore A hardness Position 2: density Position 3: torsional-stiffness temoerature at 300 MPa Designation IS02898-PVC-P,KGN,A82-2530 4.2 Designation transformed into a specification A plasticized poly(viny1 chloride) thermoplastic material (PVC-P), intended for extrusion (E), in the form of a dry blend (D), coloured (C), with an antistatic additive (Z), having a Shore D hardness of 60 (D60), a density of 1,34 g/cm3 (35). a torsional-stiffness temperature at 30