DIN EN ISO 8394-1-2011 Building construction - Jointing products - Part 1 Determination of extrudability of sealants (ISO 8394-1 2010) German version EN ISO 8394-1 2010《房屋建筑 焊接产品 第.pdf

1、May 2011 Translation by DIN-Sprachendienst.English price group 7No part of this translation may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).ICS 91.

2、100.50!$p_“1776057www.din.deDDIN EN ISO 8394-1Building construction Jointing products Part 1: Determination of extrudability of sealants (ISO 8394-1:2010)English translation of DIN EN ISO 8394-1:2011-05Hochbau Fugendichtstoffe Teil 1: Bestimmung der Verarbeitbarkeit von Dichtstoffen (ISO 8394-1:2010

3、)Englische bersetzung von DIN EN ISO 8394-1:2011-05Construction immobilire Produits pour joints Partie 1: Dtermination de lextrudabilit des mastics (ISO 8394-1:2010)Traduction anglaise de DIN EN ISO 8394-1:2011-05SupersedesDIN EN 28394:1991-05www.beuth.deDocument comprises pagesIn case of doubt, the

4、 German-language original shall be considered authoritative.1004.11 DIN EN ISO 8394-1:2011-05 2 A comma is used as the decimal marker. National foreword This standard has been prepared by Technical Committee ISO/TC 59 “Buildings and civil engineering works” in collaboration with Technical Committee

5、CEN/TC 349 “Sealants for joints in building construction” (Secretariat: AFNOR, France). The responsible German body involved in its preparation was the Normenausschuss Bauwesen (Building and Civil Engineering Standards Committee), Working Committee NA 005-02-16 AA Fugendichtstoffe. EN ISO 8394 consi

6、sts of the following parts, under the general title Building construction Jointing products: Part 1: Determination of extrudability of sealants Part 2: Determination of extrudability of sealants using standardized apparatus In addition to the legal units of measurement, this standard also uses the u

7、nit “inch”. It is important to note that according to the German law on units in metrology, the use of the unit “inch” is not permitted in official or business communications within Germany. The indication of this unit solely serves to facilitate the communication with those countries where this uni

8、t is used (import-export business). Conversion: Non-S unit S unit Conversion in (inch) mm 1 inch = 25,4 mm Amendments This standard differs from DIN EN 28394:1991-05 as follows: a) the content of the standard has been technically revised. Previous editions DIN EN 28394: 1991-05 I IEUROPEAN STANDARD

9、NORME EUROPENNE EUROPISCHE NORM EN ISO 8394-1 October 2010 ICS 91.100.50 Supersedes EN 28394:1990English Version Building construction - Jointing products - Part 1: Determination of extrudability of sealants (ISO 8394-1:2010) Construction immobilire - Produits pour joints - Partie 1: Dtermination de

10、 lextrudabilit des mastics (ISO 8394-1:2010) Hochbau - Fugendichtstoffe - Teil 1: Bestimmung der Verarbeitbarkeit von Dichtstoffen (ISO 8394-1:2010) This European Standard was approved by CEN on 30 September 2010. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipul

11、ate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN Management Centre or to any CEN member. This European Standard e

12、xists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN Management Centre has the same status as the official versions. CEN members are the national standard

13、s bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and Unit

14、ed Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG Management Centre: Avenue Marnix 17, B-1000 Brussels 2010 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN ISO 8394-1:2

15、010: EContents EN ISO 8394-1:2010 (E) DIN EN ISO 8394-1:2011-05 2 Page Foreword3 1 Scope 4 2 Normative references 4 3 Terms and definitions .4 4 Principle4 5 Apparatus .4 6 General5 7 Conditioning.5 8 Test procedure.5 9 Expression of results 6 9.1 Extrusion rate, expressed as mass per minute 6 9.2 E

16、xtrusion rate, expressed as volume per minute.6 10 Test report 6 Foreword The text of ISO 8394-1:2010 has been prepared by Technical Committee ISO/TC 59 “Buildings and civil engineering works” of the International Organization for Standardization (ISO) and has been taken over as EN ISO 8394-1:2010 b

17、y Technical Committee CEN/TC 349 “Sealants for joints in building construction” the secretariat of which is held by AFNOR. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by April 2011, and conflicti

18、ng national standards shall be withdrawn at the latest by April 2011. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. This document su

19、persedes EN 28394:1990. According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, H

20、ungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and the United Kingdom. Endorsement notice The text of ISO 8394-1:2010 has been approved by CEN as a EN ISO 8394-1:2010 without any mo

21、dification. EN ISO 8394-1:2010 (E) DIN EN ISO 8394-1:2011-05 3 1 Scope This part of ISO 8394 specifies a method for determining the extrudability of sealants. The method is for use in testing the extrudability of a sealant. It is not applicable to the classification of sealants. 2 Normative referenc

22、es The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. ISO 6927, Building construction Jointing produ

23、cts Sealants Vocabulary 3 Terms and definitions For the purposes of this document, the terms and definitions given in ISO 6927 apply. 4 Principle A sealant is extruded from its package, under defined conditions. The mass of the extruded sealant is determined. This part of ISO 8394 indicates referenc

24、e test conditions, such as temperature, pressure, extrusion time, geometry of nozzle. Deviation from these conditions is possible. Deviation modifies the final result; therefore, any deviation shall be described in the test report. The comparison of results is possible, only if all the test conditio

25、ns are the same. 5 Apparatus 5.1 Enclosure, regulated to (5 2) C, (23 2) C, (35 2) C or a temperature agreed on by the parties concerned. 5.2 Nozzle, as specified in this subclause, shall be used in conjunction with the package. The dimensions and nature of the nozzle shall be determined by the part

26、ies concerned. EN ISO 8394-1:2010 (E) DIN EN ISO 8394-1:2011-05 4 The nozzle shall be either metallic (see Figures 1 and 2 for the dimensions of two different metallic nozzles), or plastic. The plastic nozzle shall be cut at internal diameter of between 3 mm and 6 mm. The default internal diameter s

27、hall be 6 mm. Acceptable tolerances of the internal diameter shall be 5 %. 5.3 Pneumatically operated extrusion gun, supplied with compressed air up to 700 kPa. 5.4 Stopwatch, accurate to 0,1 s. 5.5 Balance, accurate to 0,1 g. 6 General For each tested sealant, perform three extrusion tests. For eac

28、h extrusion test, use one package. Perform the three measurements under the same conditions (same batch number, temperature, nozzle and diameter, same pressure, etc.). 7 Conditioning Condition the three packages containing the tested sealant, at the testing temperature in the regulated enclosure (5.

29、1) for a minimum of 12 h, before testing. The default conditioning temperature is (23 2) C. This conditioning temperature may be at (5 2) C, (23 2) C or (35 2) C, or a temperature agreed on by the parties concerned. 8 Test procedure The measurements may be carried out at usual laboratory room temper

30、ature. All the following operations shall be carried out within 5 min. Prepare the packages, removing all elements which can prevent the extrusion of the sealant during testing (i.e. screw, setting, internal membrane between the nozzle and the cartridge). Attach the nozzle (5.2), at the end of the p

31、ackage. This test of extrudability may be also performed with any other metallic or plastic nozzles, as agreed on by the parties concerned. Insert the package in the pneumatic gun (5.3). Extrude sufficient sealant to remove the air from the nozzle. Set the air pressure of the compressor to (300 10)

32、kPa, or a pressure agreed on by the parties concerned. Extrude the sealant out of the package for 30 s. Measure this time with the stopwatch (5.4). Do not take into account the quantity of sealant coming out of the nozzle after the end of test time. The package shall not be empty after testing. EN I

33、SO 8394-1:2010 (E) DIN EN ISO 8394-1:2011-05 5 NOTE In the case of a low viscosity sealant, the extrusion time can be lower. In the case of a high viscosity sealant, the extrusion time can be higher. After the pneumatic extrusion, weigh the quantity of extruded sealant, with the balance (5.5). 9 Exp

34、ression of results 9.1 Extrusion rate, expressed as mass per minute The result of each measurement, expressed in grams of extruded sealant per minute, is rounded to the nearest gram, using Equation (1): m60mEt= (1) where Emis the extrusion rate of the sealant, expressed in grams per minute; m is the

35、 mass of the extruded sealant, expressed in grams; t is the time of extrusion, expressed in seconds. Calculate the mean value of the three measurements, rounded to the nearest gram per minute. 9.2 Extrusion rate, expressed as volume per minute If needed, the result can be expressed in millilitres of

36、 extruded sealant per minute, rounded to the nearest millilitre, using Equation (2): mvEED= (2) where Evis the extrusion rate of the sealant, expressed in millilitres per minute; Emis the extrusion rate of the sealant, expressed in grams per minute; D is the density of the sealant, expressed to 2 de

37、cimal places, at the test temperature of the sealant. Calculate the mean value of the three values of Ev, rounded to the nearest millilitre per minute. 10 Test report The test report shall contain the following information: a) a reference to this part of ISO 8394, i.e. ISO 8394-1:2010; b) the name o

38、f the test laboratory and the date of test; c) the name, type (chemical family) and colour of sealant; d) the batch number of the sealant; EN ISO 8394-1:2010 (E) DIN EN ISO 8394-1:2011-05 6 e) the conditioning temperature; f) the extrusion pressure; g) the extrusion time; h) the type of nozzle. If a

39、nother nozzle is used, the nature (plastic or metallic), the geometry, commercial reference and diameter of the nozzle shall be indicated; i) the result of each extrusion rate, in grams per minute, and the mean value; j) the result of the extrusion rate, in millilitres per minute, the mean value and

40、 the density, if necessary; k) any deviation from this part of ISO 8394. Dimensions in millimetres (inches) a in NPT threads. Figure 1 First metallic nozzle scheme EN ISO 8394-1:2010 (E) DIN EN ISO 8394-1:2011-05 7 Dimensions in millimetres aPitch of 2,5 mm. bChamfer of 0,5 mm. c316 Inox. Figure 2 Second metallic nozzle scheme EN ISO 8394-1:2010 (E) DIN EN ISO 8394-1:2011-05 8