DIN ISO 4384-2-2014 Plain bearings - Hardness testing of bearing metals - Part 2 Solid materials (ISO 4384-2 2011)《滑动轴承 轴承金属的硬度检验 第2部分 固体材料》.pdf

1、July 2014 Translation by DIN-Sprachendienst.English price group 6No part of this translation may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).ICS 21

2、.100.10!%2o“2159776www.din.deDDIN ISO 4384-2Plain bearings Hardness testing of bearing metals Part 2: Solid materials (ISO 4384-2:2011),English translation of DIN ISO 4384-2:2014-07Gleitlager Hrteprfung an Lagermetallen Teil 2: Massivwerkstoffe (ISO 4384-2:2011),Englische bersetzung von DIN ISO 4384

3、-2:2014-07Paliers lisses Essai de duret des matriaux antifriction Partie 2: Matriaux massifs (ISO 4384-2:2011),Traduction anglaise de DIN ISO 4384-2:2014-07SupersedesDIN ISO 4384-2:1982-10www.beuth.deIn case of doubt, the German-language original shall be considered authoritative.Document comprises

4、7 pages06.14 A comma is used as the decimal marker. Contents Page National foreword .3 National Annex NA (informative) Bibliography .4 1 Scope .5 2 Specimen .5 3 Procedure 6 Bibliography 7 2DIN ISO 4384-2:2014-07National foreword This document (ISO 4384-2:2011) has been prepared by Technical Committ

5、ee ISO/TC 123 “Plain bearings” (Secretariat: JISC, Japan), Subcommittee SC 2 “Materials and lubricants, their properties, characteristics, test methods and testing conditions”. The responsible German body involved in its preparation was the Normenausschuss Wlz- und Gleitlager (Rolling Bearings and P

6、lain Bearings Standards Committee), Working Committee NA 118-02-02 AA Werkstoffe, Schmierung, Prfung. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. DIN and/or DKE shall not be held responsible for identifying any or all such pat

7、ent rights. DIN ISO 4384 consists of the following parts, under the general title Plain bearings Hardness testing of bearing metals: Part 1: Multilayer bearing materials Part 2: Solid materials The DIN Standard corresponding to the International Standard referred to in this document is as follows: I

8、SO 6506-1 DIN EN ISO 6506-1 Amendments This standard differs from DIN ISO 4384-2:1982-10 as follows: a) Clause 3 “Procedure” has been revised; b) Table 1 “Test conditions” has been updated. Previous editions DIN ISO 4384-2: 1982-10 3DIN ISO 4384-2:2014-07National Annex NA (informative) Bibliography

9、DIN EN ISO 6506-1, Metallic materials Brinell hardness test Part 1: Test method 4DIN ISO 4384-2:2014-071 Scope This International Standard specifies parameters for the hardness testing of solid materials for plain bearings made from cast and wrought copper and aluminium alloys by machining and formi

10、ng their wrought products and ingots, and of tin-based ingots. It represents a supplement to existing International Standards on hardness testing and, therefore, includes only the extensions and restrictions for observation compared to those publications. Owing to the heterogeneous structural compos

11、ition of the majority of these bearing metals, a Brinell test is used. 2 Specimen The surface of the specimen in the test area shall be metallic bright and conditioned in such a way that a satisfactory measurement of the test impression is possible. During the preparation of the specimens, it shall

12、be ensured that the material is not heated. The testing of cast and wrought copper and aluminium alloys shall always be carried out on turned or flied and subsequently prepared surfaces, with the exception of hot-pressed parts. If the manufacturing method permits, the specimens shall be carefully po

13、lished. In the case of lead and tin alloys with a roughness value of Rt 6 m, the polishing may be carried out with abrasive paper of grain size 240 and in the case of copper and aluminium alloys with a roughness value of Rt 4 m, with abrasive paper of grain size 320 and with a suitable lubricant. Pl

14、ain bearings Hardness testing of bearing metals Part 2: Solid materials5DIN ISO 4384-2:2014-073 Procedure The test conditions shall be in accordance with Table 1. Table 1 Test conditions Thickness of bearing material Test temperature Form and nature of bearing material mm Test conditionaC Bars, tube

15、s based on Cu and Al Preferably: HBW 2,5/62,5/10 Or, if the test surface is too small: HBW 1/10/10 In the case of cast alloys with larger porosity: HBW 5/250/10 Ingots based on Sn 7 HBW 10/250/180 Ingots based on Cu and Al 7 HBW 10/1000/10 18 to 24 a EXAMPLE HBW 5/250/10 = Brinell hardness determined with a ball of 5 mm in diameter and with a test force of 2 452 N applied for 10 s.6DIN ISO 4384-2:2014-07Bibliography 1 ISO 6506-1, Metallic materials Brinell hardness test Part 1: Test method 7DIN ISO 4384-2:2014-07