1、_ SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising there

2、from, is the sole responsibility of the user.” SAE reviews each technical report at least every five years at which time it may be reaffirmed, revised, or cancelled. SAE invites your written comments and suggestions. Copyright 2010 SAE International All rights reserved. No part of this publication m

3、ay be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: 724-776-4970 (outside USA)

4、 Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org SAE values your input. To provide feedback on this Technical Report, please visit http:/www.sae.org/technical/standards/AMS2410K AEROSPACE MATERIAL SPECIFICATION AMS2410 REV. K Issued 1945-08 Revised 2010-04 Supersed

5、ing AMS2410J Plating, Silver Nickel Strike, High Bake RATIONALE AMS2410K results from a Five Year Review and update of this specification. NOTICE ORDERING INFORMATION: The following information shall be provided to the plating processor by the purchaser. 1) Purchase order shall specify not less than

6、 the following: some provisions omitted because this spec is different AMS2410K Pre-plate stress relief to be performed by plating processor (time and temperature) if different from 3.1.1 Plating thickness desired (3.4.1) Basis metal to be plated Tensile strength or hardness of the basis metal Speci

7、al features, geometry or processing present on parts that requires special attention by the plating processor Optional: Periodic testing frequency (4.2.2) and sample quantity (4.3.2) Quantity of pieces to be plated 2) Parts manufacturing operations such as heat treating, forming, joining and media f

8、inishing can affect the condition of the substrate for plating, or if performed after plating, could adversely affect the plated part. The sequencing of these types of operations should be specified by the cognizant engineering organization or purchaser and is not controlled by this specification. S

9、AE AMS2410K Page 2 of 8 1. SCOPE 1.1 Purpose This specification covers the requirements for electrodeposited silver on other metals, usually with a nickel strike between the basis metal and the silver. 1.2 Application Silver plating has been used typically to provide a bearing surface and to prevent

10、 galling or seizing of surfaces of parts made of corrosion-resistant steels and of parts made of other metals not deleteriously affected by high-temperature baking, but usage is not limited to such applications. Silver plating is the most commonly used coating for turbine engine fasteners providing

11、an even degree of lubrication up to a maximum service temperature of about 1200 F (650 C). 1.3 Safety-Hazardous Materials While the materials, methods, applications, and processes described or referenced in this specification may involve the use of hazardous materials, this specification does not ad

12、dress the hazards that may be involved in such use. It is the sole responsibility of the user to ensure familiarity with the safe and proper use of any hazardous materials and to take necessary precautionary measures to ensure the health and safety of all personnel involved. 2. APPLICABLE DOCUMENTS

13、The issue of the following documents in effect on the date of the purchase order forms a part of this specification to the extent specified herein. The supplier may work to a subsequent revision of a document unless a specific document issue is specified. When the referenced document has been cancel

14、led and no superseding document has been specified, the last published issue of that document shall apply. 2.1 SAE Publications Available from SAE International, 400 Commonwealth Drive, Warrendale, PA 15096-0001, Tel: 877-606-7323 (inside USA and Canada) or 724-776-4970 (outside USA), www.sae.org. A

15、MS2759/9 Hydrogen Embrittlement Relief (Baking) of Steel Parts AS2390 Chemical Process Test Specimen Material 2.2 ASTM Publications Available from ASTM International, 100 Barr Harbor Drive, P.O. Box C700, West Conshohocken, PA 19428-2959, Tel: 610-832-9585, www.astm.org. ASTM B 487 Measurement of Me

16、tal and Oxide Coating Thicknesses by Microscopical Examination of a Cross Section ASTM B 499 Measurement of Coating Thicknesses by The Magnetic Method: Nonmagnetic Coatings on Magnetic Basis Metals ASTM B 504 Measurement of Thickness of Metallic Coatings by the Coulometric Method ASTM B 571 Qualitat

17、ive Testing Adhesion of Metallic Coatings ASTM E 376 Measuring Coating Thickness by Magnetic-Field or Eddy-Current (Electromagnetic) Test Methods SAE AMS2410K Page 3 of 8 3. TECHNICAL REQUIREMENTS 3.1 Preparation 3.1.1 Stress Relief Treatment All steel parts having a hardness of 40 HRC and above and

18、 which are machined, ground, cold formed or cold straightened shall be cleaned to remove surface contamination and thermally stress relieved before plating for the relief of residual tensile stresses. Residual tensile stresses have been found to be damaging during electrofinishing. 3.1.1.1 For parts

19、 having a hardness of 55 HRC and above, including carburized and induction hardened parts, stress relieve at 275 F 25 (135 C 14) for a minimum of 5 hours. 3.1.1.2 For parts having a hardness less than 55 HRC, stress relieve at 375 F 25 (191 C 14) for a minimum of 4 hours. Higher temperatures shall b

20、e used only when specified or approved by the cognizant engineering organization. 3.1.1.3 For peened parts: If stress relief temperatures above 375 F (191 C) are elected, the stress relief shall be performed prior to peening or the cognizant engineering organization shall be consulted and shall appr

21、ove the stress relief temperature. 3.1.2 The plating shall be applied over a surface free of waterbreaks. The cleaning procedure shall not produce pitting or intergranular attack of the basis metal and shall preserve dimensional requirements. 3.1.3 Except for barrel plating, electrical contact point

22、s shall be as follows. For parts that are to be plated all over, locations shall be acceptable to the purchaser. For parts that are not to be plated all over, locations shall be on areas on which plating is not required. 3.2 Procedure 3.2.1 Parts shall be plated in the following sequence except as p

23、ermitted by 3.2.1.1, 3.2.1.2, or 3.2.1.3: Nickel strike Silver strike Silver plate 3.2.1.1 The nickel strike may be omitted when plating copper and copper alloys. 3.2.1.2 A gold or palladium strike may be used in place of the silver strike when approved by the cognizant engineering organization. 3.2

24、.1.3 When approved by the cognizant engineering organization, silver may be plated directly onto the substrate without the use of either the nickel or silver strike. 3.2.2 Parts shall be plated by electrodeposition of silver from a suitable plating bath. Spotting-in or double plating are not permitt

25、ed. The use of organic base grain refining and brightener additives shall be prohibited in both the silver strike and silver plate solutions unless approved by the cognizant engineering organization. 3.3 Post Treatment 3.3.1 Hydrogen Embrittlement Relief Treatment of steel parts shall be in accordan

26、ce with AMS2759/9. SAE AMS2410K Page 4 of 8 3.3.2 Except as specified herein, all parts, except nuts, shall be heated to 935 to 965 F (502 to 518 C) after plating, rinsing, and drying and held at heat for 20 to 60 minutes. Heat up and cool down times should be minimized to prevent undesirable change

27、s in the coating or substrate, e.g., oxidation or diffusional changes. Dwell times at 400 F (204 C) shall not exceed 7 hours during the heating and cooling thermal cycle. Above 400 F (204 C), the heating and cooling medium shall be a neutral or reducing atmosphere (except that hydrogen shall not be

28、used) or shall be a neutral or nonoxidizing molten salt bath. If such heating would lower hardness or properties of parts below drawing limits or otherwise deleteriously affect the parts, heating shall be at the highest practicable temperature that will maintain specified properties. Heating of nuts

29、 is not required. When this thermal treatment starts within four hours after the parts have been removed from the plating bath, hydrogen embrittlement relief in accordance with 3.3.1 is not required. 3.4 Properties The deposited silver shall conform to the following requirements: 3.4.1 Thickness Thi

30、ckness of silver shall be as specified on the drawing, determined on representative parts or on test specimens as in 4.3.3 in accordance with any of the following methods as applicable: ASTM B 487, ASTM B 499, ASTM B 504, ASTM E 376, or other method acceptable to the cognizant engineering organizati

31、on. 3.4.1.1 Where silver flash only is specified, plate thickness shall be approximately 0.0001 inch (2.5 m). 3.4.1.2 Thickness of plate, other than flash, shall be as specified on the part drawing. If machining of plated metal is required, plate thickness as deposited shall be sufficient to allow m

32、achining of all areas of plated surfaces to the dimensions specified on the drawing. 3.4.1.3 All surfaces of the part, except those that cannot be touched by a sphere 0.75 inch (19 mm) in diameter, shall be plated to the specified thickness. Unless otherwise specified, surfaces such as holes, recess

33、es, threads, and other areas where a controlled deposit cannot be obtained under normal plating conditions, may be under the specified limit provided they show visual evidence of plating coverage. 3.4.2 Composition Silver, as plated, shall be not less than 99.9% pure, determined by a method acceptab

34、le to the cognizant engineering organization. The plating process and solution chemistry shall be controlled to ensure the required purity. 3.4.3 Adhesion Both nondestructive and destructive tests shall be performed. 3.4.3.1 Visual Test Plated metal shall be firmly and continuously bonded to the und

35、erlying metal. Plating, after heating in accordance with in 3.3, shall show no evidence of blisters or other indications of poor bond. 3.4.3.2 Destructive Test Adhesion on parts, other than nuts, after heating as in 3.3, shall meet the requirements of ASTM B 571 chisel-knife test. 3.4.3.3 Destructiv

36、e Test Nuts shall show no peeling of the silver when scratched using the knife option of the Chisel-Knife test in accordance with ASTM B 571. SAE AMS2410K Page 5 of 8 3.5 Quality Plating as received by the customer shall be smooth, continuous, free from delamination within the plating, uniform in ap

37、pearance and free from imperfections detrimental to usage of the plating. Plating shall be visually free from frosty areas, pin holes, porosity, blisters, nodules, and pits. Slight staining or discoloration is permissible after plating and during storage. 3.5.1 Abrasion of plating on corners and edg

38、es of nuts is acceptable but plate shall be continuous on the threads. Marking or marring of the cone section of self-locking nuts, produced in offsetting the locking beams or other locking feature, is acceptable. 4. QUALITY ASSURANCE PROVISIONS 4.1 Responsibility for Inspection The processor shall

39、supply all samples for processors tests and shall be responsible for the performance of all required tests. When parts are to be tested, the parts shall be supplied by the purchaser. The cognizant engineering organization reserves the right to sample and to perform any confirmatory testing deemed ne

40、cessary to ensure that processing conforms to the specified requirements. 4.2 Classification of Tests 4.2.1 Acceptance Tests Thickness (3.4.1), adhesion (3.4.3), and quality (3.5) are acceptance tests and shall be performed on parts, or specimens representing parts when permitted herein, from each l

41、ot. See 4.3.3. 4.2.2 Periodic Tests Composition (3.4.2) is a periodic test and shall be performed at least quarterly unless frequency of testing is specified by the cognizant engineering organization. Tests of cleaning and plating solutions are periodic tests and shall be performed at a frequency es

42、tablished by the processor unless frequency of testing is specified by the cognizant engineering organization. See 8.3 and 4.4.3. 4.2.3 Preproduction Tests All property verification tests (section 3.4) are preproduction tests and shall be performed prior to or on the first-article shipment of plated

43、 parts to a purchaser and when the cognizant engineering organization requires confirmatory testing. 4.3 Sampling for Testing 4.3.1 Acceptance Tests Acceptance test samples shall be randomly selected from all parts in the lot. A lot shall be all parts of the same part number, processed in a continuo

44、us series of operations (3.1 through 3.3), in not longer than 24 consecutive hours, and presented for processors inspection at one time. Unless the cognizant engineering organization provides a sampling plan, the minimum number of samples shall be as shown in Table 1. SAE AMS2410K Page 6 of 8 TABLE

45、1 - Sampling For Acceptance Tests Number of Parts in Lot Visual for Adhesion, Coverage, and Quality Thickness (Non-Destructive)Thickness (Destructive) Adhesion (Destructive) Up to 7 all all 0 0 8 to 15 7 3 16 to 40 10 4 0 0 41 to 150 15 5 1 1 151 to 300 25 6 301 to 500 35 7 1 1 Over 500 50 8 2 2 4.3

46、.1.1 When a statistical sampling plan has been agreed upon by purchaser and processor, sampling shall be in accordance with such plan in lieu of sampling as in 4.3.1 and the report of 4.5 shall state that such plan was used. 4.3.2 Periodic Tests One sample shall be used for composition (3.4.2) unles

47、s otherwise specified by the cognizant engineering organization. 4.3.3 Sample Configuration 4.3.3.1 Separate test specimens may be used under any one of the following circumstances: The plated parts are of such configuration or size as to be not readily adaptable to specified tests, nondestructive t

48、esting is not practical on actual parts, or it is not economically acceptable to perform destructive tests on actual parts. Except as specified below, acceptance test specimens shall be made of the same generic class of alloy as the parts, established in accordance with AS2390, distributed within th

49、e lot, cleaned, plated, and post treated with the parts represented. 4.3.3.2 For adhesion and thickness tests, specimens shall be 0.032-0.064 x 4 x 1 inch (0.8-1.6 x 102 x 25 mm). For thickness tests, bars approximately 0.5 inch (13 mm) in diameter and 4 inches (102 mm) long may be used. Because thickness may differ from parts on specimens, correlation with actual parts shall be esta