DLA MIL-C-11015 10 G-2013 CAPACITORS FIXED CERAMIC DIELECTRIC (GENERAL PURPOSE) STYLE CK61.pdf

1、 AMSC N/A FSC 5910 INCH-POUND MIL-C-11015/10G 29 March 2013 SUPERSEDING MIL-C-11015/10F 14 May 2001 MILITARY SPECIFICATION SHEET CAPACITORS, FIXED, CERAMIC DIELECTRIC (GENERAL PURPOSE), STYLE CK61 This specification sheet is approved for use by all Departments and Agencies of the Department of Defen

2、se. The requirements for acquiring the product described herein shall consist of this specification sheet and MIL-C-11015. NOTES: 1. Dimensions are in inches. 2. Metric equivalents are given for general information only. 3. Insulating coating shall not extend more than .125 inch (3.18 mm) along lead

3、 wires measured from a tangent to the coating surface drawn perpendicular to the lead wires. FIGURE 1. Dimensions and configuration. Inches mm .001 0.03 .004 0.10 .025 0.64 .035 0.89 .040 1.02 .060 1.52 .120 3.05 .250 6.35 .350 8.89 1.250 31.75 INACTIVE FOR NEW DESIGN AFTER 31 MARCH 1999. FOR REPLAC

4、EMENT PURPOSES ONLY. Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-C-11015/10G 2 TABLE I. Style CK61 characteristics. Part or Indentifying Number (PIN) 1/ Rated Voltage (Volts, dc) Rated temperature and voltage- temperature limits Capacitance (

5、pF) Capacitance tolerance CK61CZ2R2- 500 CZ 2.2 K, M CK61CZ3R3- 500 CZ 3.3 K, M CK61CZ4R7- 500 CZ 4.7 K, M CK61CZ6R8- 500 CZ 6.8 K, M CK61CZ100- 500 CZ 10 K, M CK61CZ150- 500 CZ 15 K, M CK61CZ220- 500 CZ 22 K, M CK61CZ330- 500 CZ 33 K, M CK61CZ470- 500 CZ 47 K, M CK61CZ680- 500 CZ 68 K, M CK61CZ101-

6、 500 CZ 100 K, M CK61CZ151- 500 CZ 150 K, M CK61BX221- 500 BX 220 K, M CK61CZ221- 500 CZ 220 K, M CK61BX331- 500 BX 330 K, M CK61CZ331- 500 CZ 330 K, M CK61BX471- 500 BX 470 K, M CK61CZ471- 500 CZ 470 K, M CK61BX681- 500 BX 680 K, M CK61AW222M- 500 AW 2,200 M 1/ Where applicable, the complete PIN wi

7、ll include an additional symbol to indicate capacitance tolerance. The PIN will also include the letter “E” to indicate an epoxy coated capacitor (when applicable) or “-“ will be deleted for wax impregnated case. REQUIREMENTS Design and construction: Dimensions and configuration: See figure 1. Case

8、type: Disk, wax impregnated or epoxy coated (E). Capacitance value: See table I. Capacitance tolerance: 10 percent (K) or 20 percent (M) as shown in table I. Rated temperature: -55C to +85C (A), or -55C to +125C (B), or -55C to +150C (C), as shown in table I. Dielectric withstanding voltage(DWV): In

9、 accordance with MIL-C-11015. Dielectric: Test voltage: 250 percent of rated voltage. Body insulation: Test potential: 1,300 volts dc. Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-C-11015/10G 3 Barometric pressure (reduced): In accordance with

10、 MIL-C-11015 and method 105 of MIL-STD-202, .82 inch of mercury (80,000 ft). Test potential: 150 percent of rated voltage. Insulation resistance (IR): In accordance with MIL-C-11015 and method 302 of MIL-STD-202, condition B. 200,000 megohms, minimum. Dissipation factor (DF): 2.0 percent maximum. Vi

11、bration, high frequency: In accordance with MIL-C-11015 and method 204 of MIL-STD-202, condition D (20 gs). Thermal shock and immersion: In accordance with MIL-C-11015. DWV: 250 percent of rated voltage. IR: 150,000 megohms, minimum. Salt atmosphere (corrosion): Not applicable. Terminal strength: In

12、 accordance with MIL-C-11015. Moisture resistance: In accordance with MIL-C-11015. DWV: 250 percent of rated voltage. IR: 150,000 megohms, minimum. Cap.: Within tolerance of table I value. Solderability: In accordance with MIL-C-11015. 2 terminals. Resistance to soldering heat: In accordance with MI

13、L-C-11015. IR: 200,000 megohms, minimum. Cap.: 5 percent of initial measurement. DF: 0.5 percent, maximum. Voltage-temperature limits: In accordance with MIL-C-11015. Life (at elevated ambient temperature): In accordance MIL-C-11015. Test potential: 200 percent of rated voltage. DWV: 250 percent of

14、rated voltage. (at +25C). IR: 100,000 megohms, minimum (at high temperature and +25C). Cap.: Within tolerance of table I value (at +25C). DF: 2.0 percent, maximum. Marking: In accordance with MIL-C-11015. Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,

15、-,-MIL-C-11015/10G 4 Referenced documents: In addition to MIL-C-11015, this specification sheet references the following document: MIL-STD-202 Changes from previous issue: The margins of this specification sheet are marked with vertical lines to indicate where changes from the previous issue were ma

16、de. This was done as a convenience only and the Government assumes no liability whatsoever for any inaccuracies in these notations. Bidders and contractors are cautioned to evaluate the requirements on this document on the entire content irrespective of the marginal notations and relationship to the

17、 last previous issue. Custodians: Preparing activity: Army - CR DLA - CC Navy - EC Air Force - 85 DLA - CC (Project 5910-2013-008) Review activities: Army - MI Navy AS, OS, SH Air Force 19, 99 NOTE: The activities listed above were interested in this document as of the date of this document. Since organizations and responsibilities can change, you should verify the currency of the information above using the ASSIST Online database at https:/assist.dla.mil. Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-